CN108192227A - A kind of cable insulation layer material - Google Patents
A kind of cable insulation layer material Download PDFInfo
- Publication number
- CN108192227A CN108192227A CN201711219199.7A CN201711219199A CN108192227A CN 108192227 A CN108192227 A CN 108192227A CN 201711219199 A CN201711219199 A CN 201711219199A CN 108192227 A CN108192227 A CN 108192227A
- Authority
- CN
- China
- Prior art keywords
- parts
- account
- insulation layer
- fiber
- cable insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of cable insulation layer materials, are made of according to parts by weight following raw material:26 parts of haloflex, heat filling account for 69 parts, antimony oxide account for 14 parts, antioxidant account for 48 parts, 36 parts of modified filler, anti-hydrolysis agent account for 49 parts, 7 10 parts of butadiene rubber, 48 parts of aluminium hydroxide, 37 parts of spider's thread fiber, 25 parts of precipitated calcium carbonate, 15 parts of 1,2 mercaptobenzimidazole, 27 parts of tribasic lead sulfate, 36 parts of acetate ethylene copolymer, 38 parts of 59 parts of accelerator mixture and chitin fiber.A kind of cable material of the present invention can improve the physical and chemical performance that can improve alloy, and the features such as improve Alloy At Room Temperature and high-temperature mechanical property.
Description
Technical field
The present invention relates to cable correlative technology field more particularly to a kind of cable insulation layer materials.
Background technology
At present, with the development of science and technology, the research of new material is always the theme of our state research projects, if you are enough
Research and develop and produce that an ingredient is simple, and can reach the green wood material formula of good effect, this by be to the mankind one
Big contribution.
Invention content
The purpose of the present invention is to solve shortcoming in the prior art, and a kind of cable insulation material proposed
Material.
To achieve these goals, present invention employs following technical solutions:
A kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:2-6 parts of haloflex is led
Hot filler account for 6-9 parts, antimony oxide account for 1-4 parts, antioxidant account for 4-8 parts, 3-6 parts of modified filler, anti-hydrolysis agent account for 4-9
Part, 7-10 parts of butadiene rubber, 4-8 parts of aluminium hydroxide, 3-7 parts of spider's thread fiber, 2-5 parts of precipitated calcium carbonate, 1,2- sulfydryl benzo miaows
1-5 parts of azoles, 2-7 parts of tribasic lead sulfate, 3-6 parts of acetate ethylene copolymer, 5-9 parts of accelerator mixture and chitin fiber 3-
8 parts.
Above-mentioned a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:Chlorinated polyethylene
2-5 parts of alkene, heat filling account for 6-8 parts, antimony oxide account for 1-3 parts, antioxidant account for 4-7 parts, 3-5 parts of modified filler, water resistant
Solution agent account for 4-8 parts, 7-9 parts of butadiene rubber, 4-7 parts of aluminium hydroxide, 3-6 parts of spider's thread fiber, 2-4 parts of precipitated calcium carbonate, 1,2- mercaptos
1-4 parts of base benzimidazole, 2-6 parts of tribasic lead sulfate, 3-5 parts of acetate ethylene copolymer, 5-8 parts of accelerator mixture and crust
3-7 parts of cellulose fiber.
Above-mentioned a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:Chlorinated polyethylene
3-5 parts of alkene, heat filling account for 7-8 parts, antimony oxide account for 2-3 parts, antioxidant account for 5-7 parts, 4-5 parts of modified filler, water resistant
Solution agent account for 5-8 parts, 8-9 parts of butadiene rubber, 5-7 parts of aluminium hydroxide, 4-6 parts of spider's thread fiber, 3-4 parts of precipitated calcium carbonate, 1,2- mercaptos
3-4 parts of base benzimidazole, 3-6 parts of tribasic lead sulfate, 4-5 parts of acetate ethylene copolymer, 6-8 parts of accelerator mixture and crust
4-7 parts of cellulose fiber.
Above-mentioned a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:Chlorinated polyethylene
4 parts of alkene, heat filling account for 7.5 parts, antimony oxide account for 2.5 parts, antioxidant account for 6 parts, 4.5 parts of modified filler, anti-hydrolysis agent
Account for 6.5 parts, 8.5 parts of butadiene rubber, 6 parts of aluminium hydroxide, 5 parts of spider's thread fiber, 3.5 parts of precipitated calcium carbonate, 1,2- sulfydryl benzo miaows
5.5 parts of 3 parts of azoles, 4.5 parts of tribasic lead sulfate, 4.5 parts of acetate ethylene copolymer, 7 parts of accelerator mixture and chitin fiber.
Compared with prior art, beneficial effects of the present invention are:
A kind of cable insulation layer material of the present invention can improve the physical and chemical performance that can improve alloy, and improve alloy room
The advantageous effects such as temperature and high-temperature mechanical property.
Specific embodiment
Embodiment 1
A kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:2 parts of haloflex, heat conduction
Filler account for 6 parts, antimony oxide account for 1 part, antioxidant account for 4 parts, 3 parts of modified filler, anti-hydrolysis agent account for 4 parts, butadiene rubber 7
Part, 4 parts of aluminium hydroxide, 3 parts of spider's thread fiber, 2 parts of precipitated calcium carbonate, 1,1 part of 2-mercaptobenzimidazole, 2 parts of tribasic lead sulfate,
3 parts of 3 parts of acetate ethylene copolymer, 5 parts of accelerator mixture and chitin fiber.
Embodiment 2
Above-mentioned a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:Haloflex 6
Part, heat filling account for 9 parts, antimony oxide account for 4 parts, antioxidant account for 8 parts, 6 parts of modified filler, anti-hydrolysis agent account for 9 parts, along fourth
10 parts of rubber, 8 parts of aluminium hydroxide, 7 parts of spider's thread fiber, 5 parts of precipitated calcium carbonate, 1,5 parts of 2-mercaptobenzimidazole, three alkali formula sulfuric acid
8 parts of 7 parts of lead, 6 parts of acetate ethylene copolymer, 9 parts of accelerator mixture and chitin fiber.
Embodiment 3
Above-mentioned a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:Haloflex 4
Part, heat filling accounts for 7.5 parts, antimony oxide accounts for 2.5 parts, antioxidant accounts for 6 parts, 4.5 parts of modified filler, anti-hydrolysis agent account for
6.5 parts, 8.5 parts of butadiene rubber, 6 parts of aluminium hydroxide, 5 parts of spider's thread fiber, 3.5 parts of precipitated calcium carbonate, 1,2-mercaptobenzimidazole 3
Part, 4.5 parts of tribasic lead sulfate, 4.5 parts of acetate ethylene copolymer, 7 parts of accelerator mixture and 5.5 parts of chitin fiber.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (4)
1. a kind of cable insulation layer material, which is characterized in that be made of according to parts by weight following raw material:2-6 parts of haloflex,
Heat filling account for 6-9 parts, antimony oxide account for 1-4 parts, antioxidant account for 4-8 parts, 3-6 parts of modified filler, anti-hydrolysis agent account for 4-9
Part, 7-10 parts of butadiene rubber, 4-8 parts of aluminium hydroxide, 3-7 parts of spider's thread fiber, 2-5 parts of precipitated calcium carbonate, 1,2- sulfydryl benzo miaows
1-5 parts of azoles, 2-7 parts of tribasic lead sulfate, 3-6 parts of acetate ethylene copolymer, 5-9 parts of accelerator mixture and chitin fiber 3-
8 parts.
2. a kind of cable insulation layer material according to claim 1, which is characterized in that have following raw material group according to parts by weight
Into:2-5 parts of haloflex, heat filling account for 6-8 parts, antimony oxide account for 1-3 parts, antioxidant account for 4-7 parts, modified filler
3-5 parts, anti-hydrolysis agent account for 4-8 parts, 7-9 parts of butadiene rubber, 4-7 parts of aluminium hydroxide, 3-6 parts of spider's thread fiber, precipitated calcium carbonate 2-4
Part, 1,1-4 parts of 2-mercaptobenzimidazole, 2-6 parts of tribasic lead sulfate, 3-5 parts of acetate ethylene copolymer, accelerator mixture 5-
8 parts and 3-7 parts of chitin fiber.
3. a kind of cable insulation layer material according to claim 1, which is characterized in that have following raw material group according to parts by weight
Into:3-5 parts of haloflex, heat filling account for 7-8 parts, antimony oxide account for 2-3 parts, antioxidant account for 5-7 parts, modified filler
4-5 parts, anti-hydrolysis agent account for 5-8 parts, 8-9 parts of butadiene rubber, 5-7 parts of aluminium hydroxide, 4-6 parts of spider's thread fiber, precipitated calcium carbonate 3-4
Part, 1,3-4 parts of 2-mercaptobenzimidazole, 3-6 parts of tribasic lead sulfate, 4-5 parts of acetate ethylene copolymer, accelerator mixture 6-
8 parts and 4-7 parts of chitin fiber.
4. a kind of cable insulation layer material according to claim 1, which is characterized in that have following raw material group according to parts by weight
Into:4 parts of haloflex, heat filling account for 7.5 parts, antimony oxide account for 2.5 parts, antioxidant account for 6 parts, modified filler 4.5
Part, anti-hydrolysis agent account for 6.5 parts, 8.5 parts of butadiene rubber, 6 parts of aluminium hydroxide, 5 parts of spider's thread fiber, 3.5 parts of precipitated calcium carbonate, 1,2-
3 parts of mercaptobenzimidazole, 4.5 parts of tribasic lead sulfate, 4.5 parts of acetate ethylene copolymer, 7 parts of accelerator mixture and chitin
5.5 parts of fiber.