CN108178948A - A kind of ink printing carton, printing ink and its production technology - Google Patents
A kind of ink printing carton, printing ink and its production technology Download PDFInfo
- Publication number
- CN108178948A CN108178948A CN201810156535.6A CN201810156535A CN108178948A CN 108178948 A CN108178948 A CN 108178948A CN 201810156535 A CN201810156535 A CN 201810156535A CN 108178948 A CN108178948 A CN 108178948A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing
- adjusting agents
- printing ink
- ink
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ink to print carton, including box body, printing layer one is provided on the outside of the box body, film layer is provided in the printing layer one, the printing layer two being made of printing ink is provided in the film layer, with better appearance, and the printing ink includes 40 50 parts of composite polypropylene acid esters lotions, 40 50 parts of mill bases, 0.2 0.5 parts of antifoaming agent, 0.4 0.8 parts of levelling agents, 0.1 1 parts of thickeners, 0.5 2 parts of aerosils, 0.1 0.5 parts of wetting agents, 15 parts of pH adjusting agents, 5 10 parts of water, the polyacrylate dispersion includes the component of following weight proportion：20 35 parts of acrylic monomers, 13 parts of lauryl mercaptans, 15 parts of hydroxy-ethyl acrylates, 1 10 parts of emulsifiers, 5 15 portions of soybean oils, 0.1 0.5 parts of phosphite esters, 0.5 1.5 parts of initiators, 15 parts of pH adjusting agents, 1 10 parts of deionized waters, while the present invention also provides the production technologies of the printing ink, the ink has low stain, the characteristics of good storge quality, the strong adhesive force on the plastic basis materials such as PP, PE, printing effect is good.
Description
Technical field
The present invention relates to printing technologies, and in particular to a kind of printing carton, printing ink and its production technology.
Background technology
Packing box can classify such as the term suggests being exactly the box for packing product by material：Carton, can,
Wooden box, cloth box, skin box, acrylic box, corrugated package box, pvc boxes etc., can also classify such as by the title of product：Moon cake
Box, tea caddy, matrimony vine box, bonbon box, exquisite gift box, local and special products box, wine box, chocolate box, food and medicine health products box, food
Packing box, tea packaging box, writing case etc..Pack kit function：Ensure the safety of product in transport, promote class of product etc.,
The characteristics of wherein carton is at low cost by its, good moldability, easy processing, is the common material of packing box, carton is producing and processing
Molding, mainly including design ,-slice-draws a design, and-printing-is surface-treated-several production stages of post-processing-packaging, wherein
Most important functions are played to carton appearance be also as obvious effect be print steps, the selection of good ink and good
Processing technology can greatly improve printing quality, improve the class of carton, then promote sales volume.
With Social Culture, science and technology, expanding economy, printing industry is developing at a speed unheard of before, wherein oil
Ink is also innovated and is produced constantly, and still, pollution sources of the ink as printing industry maximum, world's ink yield is
Up to 3,500,000 tons, organic volatile discharge amount of pollution up to 500,000 tons, seriously pollutes atmospheric environment, directly as caused by ink every year
Human health is endangered, it is environmentally protective as the theme and Main way that develop now with the continuous improvement of people's environmental consciousness,
Therefore, research, development and application meet the ink of print request while less pollution as main task now.Now,
Through having begun with relevant technology, for example, disclosing a kind of plastic film in the patent of invention of Patent No. CN101028194
Aqueous intaglio printing ink discloses a kind of One-step production pleasant sensation shape in the patent of invention of Patent No. 103936910
Expect the method for water-based ink acrylic resin binder, still, still there are tinting strength, tinting power, glossiness, adhesive force, storages for such ink
Sustainability can imperfect problem.
Invention content
Under the basis of above-mentioned background, the present invention provides a kind of printing ink, production technology and applies the ink
Printing carton, which has a low stain, good storge quality, the strong adhesive force on the plastic basis materials such as PP, PE, and printing is suitable
The characteristics of answering property and excellent printing quality, " water wave " phenomenon is substantially improved, printing quality is excellent.
The purpose of the present invention is what is be achieved through the following technical solutions：
A kind of printing carton, including box body, the box body includes bottom surface, first side, second side, third side, the 4th side
Face and top surface, the first side and second side are arranged on the left and right sides of bottom surface, the third side and the 4th
Side is arranged on the front and rear sides of bottom surface, and the top surface is arranged on the rear side of the 4th side, the top surface and the 4th unilateral copulation
Place is provided with opening, and the opening is arranged on top surface, is provided with printing layer one on the outside of the box body, is set in the printing layer one
Film layer is equipped with, the printing layer two being made of printing ink is provided in the film layer.
And a kind of printing ink, include the component of following weight proportion：
40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levelling agents,
0.1-1 parts of thickeners, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water.
Wherein, the polyacrylate dispersion includes the component of following weight proportion：
20-35 parts of acrylic monomers, 1-3 parts of part lauryl mercaptans, 1-5 parts of hydroxy-ethyl acrylates, 1-10 parts of emulsifiers, 5-15 parts
Soybean oil, 0.1-0.5 parts of phosphite esters, 0.5-1.5 parts of initiators, 1-5 parts of pH adjusting agents, 1-10 parts of deionized waters.
Preferably, printing ink includes the component of following weight proportion：46 parts of composite polypropylene acid esters lotions, 45 parts of colors
Slurry, 0.3 part of antifoaming agent, 0.5 part of levelling agent, 0.7 part of thickener, 0.7 part of aerosil, 0.4 part of wetting agent, 3 parts of pH tune
Save agent, 8 parts of water；Wherein composite polypropylene acid esters lotion includes the component of following weight proportion：28 parts of acrylic monomers, 1 part ten
Two mercaptan, 3 parts of hydroxy-ethyl acrylates, 5 parts of emulsifiers, 10 portions of soybean oils, 0.2 part of phosphite ester, 1.2 parts of initiators, 4 parts of pH
Conditioning agent, 5 parts of deionized waters.
Preferably, the initiator is azo-bis-isobutyl cyanide, and the emulsifier is lauryl sodium sulfate.
And a kind of production technology of printing ink, include the following steps：
S1, by the raw material of following weight proportion：10-15 parts of acrylic monomers, 1-2 parts of pH adjusting agents, 1-5 parts of emulsifiers, 5-15
Part soybean oil, 0.1-0.5 parts of phosphite esters, 1-3 parts of lauryl mercaptans, 1-5 parts of hydroxy-ethyl acrylates and 1-5 parts of deionized waters are mixed
It closes, forms pre-emulsion, when being heated to 85-95 DEG C, its pre-emulsification, mixing time are made under the mixing speed of 350r/min
For 20min；
S2 adds in 0.1-0.5 parts of initiators in pre-emulsion, keeps the mixing speed of 150r/min in a nitrogen atmosphere, stirs
The time is mixed as 35min, forms semi-emulsifying liquid；
S3 adds in 10-20 parts of acrylic monomers, 1-5 parts of deionized waters, 1-3 parts of pH adjusting agents, 1-5 parts of breasts in semi-emulsifying liquid
Agent, 0.5-1 parts of initiators stir 3h under the mixing speed of 280r/min, and emulsification is cooled to 25 DEG C, forms composite polypropylene
Acid esters lotion；
S4, by 40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levellings
Agent, 0.1-1 parts of thickeners, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water warps
Dispersion, grinding, filtering, form final printing ink.
Preferably, in S3, initiator and emulsifier are added in a manner of being added dropwise in semi-emulsifying liquid, and wherein initiator drips
It is longer than the time for adding of emulsifier between added-time, whole time for adding is completed in 50-90min.
Preferably, include the following steps：
S1, by the raw material of following weight proportion：10 parts of acrylic monomers, 2 parts of pH adjusting agents, 2 parts of emulsifiers, 10 portions of soybean oils,
0.2 part of phosphite ester, 1 part of lauryl mercaptan, 3 parts of hydroxy-ethyl acrylates and 2 parts of deionized water mixing, form pre-emulsion, will
When it is heated to 85-95 DEG C, its pre-emulsification, mixing time 20min are made under the mixing speed of 350r/min；S2, in pre- breast
Change and 0.2 part of initiator is added in liquid, keep the mixing speed of 150r/min in a nitrogen atmosphere, mixing time 35min is formed
Semi-emulsifying liquid；S3,18 parts of acrylic monomers of addition in semi-emulsifying liquid, 3 parts of deionized waters, 2 parts of pH adjusting agents, 3 parts of emulsifiers,
1 part of initiator stirs 3h under the mixing speed of 280r/min, and emulsification is cooled to 25 DEG C, forms composite polypropylene acid esters lotion；
S4, by 46 parts of composite polypropylene acid esters lotions, 45 parts of mill bases, 0.3 part of antifoaming agent, 0.5 part of levelling agent, 0.7 part of thickener, 0.7
Part aerosil, 0.4 part of wetting agent, 3 parts of pH adjusting agents, 8 parts of water are dispersed through, grind, filter, and form final printing and use
Ink.
Compared with prior art, the present invention it has the following advantages that：
First, carton provided by the invention has two layers of printing layer, and one layer is to be printed on carton surface, and one layer is printed on film table
Face, Film laminated make it have stereovision, while Tear Film also has another layer of printing on the carton surface with printing layer
Pattern substantially increases the packaging effect of carton, and the ink used in film layer is special ink, has preferably printing
Effect, the ink have low stain, good storge quality, the strong adhesive force on the plastic basis materials such as PP, PE, printing adaptability and
The characteristics of printing quality is excellent, substantially improves " water wave " phenomenon, and printing quality is excellent.
Description of the drawings
Fig. 1 is the expanded schematic diagram of box body in the present invention；
Fig. 2 is the structure diagram of box body in the present invention.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment shall fall within the protection scope of the present invention.
With reference to figure 1-2, the present invention provides a kind of ink printing carton, and including box body 100, the box body includes bottom surface 1, the
One side 2, second side 3, third side 4, the 4th side 5 and top surface 6, the first side 2 and second side 3 are set
In the left and right sides of bottom surface 1,4 and the 4th side 5 of third side is arranged on the front and rear sides of bottom surface 1, and the top surface 6 is set
Put the rear side in the 4th side 5, which is characterized in that be provided with opening at the top surface and the 4th unilateral copulation, the opening is set
It puts on top surface, 100 outside of box body is provided with printing layer 1, and film layer 12, institute are provided in the printing layer 1
State the printing layer 2 13 for being provided in film layer 12 and being made of printing ink.
Corresponding, the present invention provides the printing inks suitable for the carton, include the group of following weight proportion
Part：40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levelling agents, 0.1-
1 part of thickener, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water；Wherein, institute
State the component that polyacrylate dispersion includes following weight proportion：20-35 parts of acrylic monomers, 1-3 parts of lauryl mercaptans, 1-5 parts
Hydroxy-ethyl acrylate, 1-10 parts of emulsifiers, 5-15 portions of soybean oils, 0.1-0.5 parts of phosphite esters, 0.5-1.5 parts of initiators, 1-5
Part pH adjusting agent, 1-10 parts of deionized waters.
Initiator is azo-bis-isobutyl cyanide, and the emulsifier is lauryl sodium sulfate.
At the same time, the present invention also provides the production technology of the printing ink, include the following steps：
S1, by the raw material of following weight proportion：10-15 parts of acrylic monomers, 1-2 parts of pH adjusting agents, 1-5 parts of emulsifiers, 5-15
Part soybean oil, 0.1-0.5 parts of phosphite esters, 1-3 parts of lauryl mercaptans, 1-5 parts of hydroxy-ethyl acrylates and 1-5 parts of deionized waters are mixed
It closes, forms pre-emulsion, when being heated to 85-95 DEG C, its pre-emulsification, mixing time are made under the mixing speed of 350r/min
For 20min；S2 adds in 0.1-0.5 parts of initiators in pre-emulsion, keeps the stirring speed of 150r/min in a nitrogen atmosphere
Degree, mixing time 35min form semi-emulsifying liquid；S3 adds in 10-20 parts of acrylic monomers in semi-emulsifying liquid, and 1-5 parts are gone
Ionized water, 1-3 parts of pH adjusting agents, 1-5 parts of emulsifiers, 0.5-1 parts of initiators stir 3h under the mixing speed of 280r/min,
Emulsification is cooled to 25 DEG C, forms composite polypropylene acid esters lotion, and initiator and emulsifier are added in semi-emulsifying in a manner of being added dropwise
In liquid, wherein initiator time for adding is longer than the time for adding of emulsifier, and whole time for adding is completed in 50-90min；S4,
By 40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levelling agents, 0.1-1
Part thickener, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water are dispersed through, grind
Mill, filtering, form final printing ink.
The ink provided in the present invention is further detailed below according to embodiment.
Embodiment 1：
The production technology of printing ink includes the following steps：S1, by the raw material of following weight proportion：10 parts of acrylic monomers,
1 part of pH adjusting agent, 2 parts of emulsifiers, 5 portions of soybean oils, 0.2 part of phosphite ester, 1 part of lauryl mercaptan, 1 part of hydroxy-ethyl acrylate and
2 parts of deionized water mixing, form pre-emulsion, when being heated to 85 DEG C, its pre- breast are made under the mixing speed of 350r/min
Change, mixing time 20min；S2 adds in 0.3 part of initiator in pre-emulsion, keeps 150r/min's in a nitrogen atmosphere
Mixing speed, mixing time 35min form semi-emulsifying liquid；S3 adds in 10 parts of acrylic monomers in semi-emulsifying liquid, and 2 parts are gone
Ionized water, 2 parts of pH adjusting agents, 2 parts of emulsifiers, 0.2 part of initiator stir 3h, emulsification drop under the mixing speed of 280r/min
Temperature forms composite polypropylene acid esters lotion to 25 DEG C；S4, by 40 parts of composite polypropylene acid esters lotions, 40 parts of mill bases, 0.2 part disappears
Infusion, 0.4 part of levelling agent, 0.1 part of thickener, 0.5 part of aerosil, 0.1 part of wetting agent, 1 part of pH adjusting agent, 5 parts of water
It is dispersed through, grinds, filters, form final printing ink.
Embodiment 2
The production technology of printing ink includes the following steps：S1, by the raw material of following weight proportion：10 parts of acrylic monomers, 2
Part water, 2 parts of pH adjusting agents, 2 parts of emulsifiers, 10 portions of soybean oils, 0.2 part of phosphite ester, 1 part of lauryl mercaptan, 3 parts of acrylic acid hydroxyl second
Ester and 2 parts of deionized water mixing, form pre-emulsion, when being heated to 85-95 DEG C, under the mixing speed of 350r/min
Make its pre-emulsification, mixing time 20min；S2 adds in 0.2 part of initiator in pre-emulsion, keeps in a nitrogen atmosphere
The mixing speed of 150r/min, mixing time 35min form semi-emulsifying liquid；S3 adds in 18 parts of acrylic acid in semi-emulsifying liquid
Monomer, 3 parts of deionized waters, 2 parts of pH adjusting agents, 3 parts of emulsifiers, 1 part of initiator stir under the mixing speed of 280r/min
3h, emulsification are cooled to 25 DEG C, form composite polypropylene acid esters lotion；S4, by 46 parts of composite polypropylene acid esters lotions, 45 parts of colors
Slurry, 0.3 part of antifoaming agent, 0.5 part of levelling agent, 0.7 part of thickener, 0.7 part of aerosil, 0.4 part of wetting agent, 3 parts of pH tune
Agent is saved, 8 parts of water are dispersed through, grind, filter, and form final printing ink.
Embodiment 3
The production technology of printing ink includes the following steps：S1, by the raw material of following weight proportion：20 parts of acrylic monomers, 3
Part pH adjusting agent, 5 parts of emulsifiers, 10 portions of soybean oils, 0.2 part of phosphite ester, 2 parts of lauryl mercaptans, 5 parts of hydroxy-ethyl acrylates and
5 parts of deionized water mixing, form pre-emulsion, when being heated to 85-95 DEG C, make its pre- under the mixing speed of 350r/min
Emulsification, mixing time 20min；S2 adds in 1 part of initiator in pre-emulsion, keeps 150r/min's in a nitrogen atmosphere
Mixing speed, mixing time 35min form semi-emulsifying liquid；S3 adds in 15 parts of acrylic monomers in semi-emulsifying liquid, and 5 parts are gone
Ionized water, 2 parts of pH adjusting agents, 5 parts of emulsifiers, 1 part of initiator stir 3h, emulsification cooling under the mixing speed of 280r/min
To 25 DEG C, composite polypropylene acid esters lotion is formed；S4, by 50 parts of composite polypropylene acid esters lotions, 50 parts of mill bases, 0.5 part of defoaming
Agent, 0.8 part of levelling agent, 1 part of thickener, 2 parts of aerosils, 1.5 parts of wetting agents, 5 parts of pH adjusting agents, 10 parts of water are through dividing
It dissipates, grinding, filter, form final printing ink.
According to above-described embodiment, after testing, it is as follows to obtain technical data：
Claims (8)
1. a kind of ink prints carton, including box body, the box body include bottom surface, first side, second side, third side,
4th side and top surface, the first side and second side are arranged on the left and right sides of bottom surface, the third side with
And the 4th side be arranged on the front and rear sides of bottom surface, the top surface is arranged on the rear side of the 4th side, which is characterized in that the top
Opening is provided at face and the 4th unilateral copulation, the opening is arranged on top surface, and printing layer one is provided on the outside of the box body,
Film layer is provided in the printing layer one, the printing layer two being made of printing ink is provided in the film layer.
2. a kind of printing ink, which is characterized in that include the component of following weight proportion：
40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levelling agents,
0.1-1 parts of thickeners, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water.
3. a kind of printing ink according to claim 2, which is characterized in that the polyacrylate dispersion includes following heavy
Measure the component of proportioning：
20-35 parts of acrylic monomers, 1-3 parts of lauryl mercaptans, 1-5 parts of hydroxy-ethyl acrylates, 1-10 parts of emulsifiers are 5-15 parts big
Soya-bean oil, 0.1-0.5 parts of phosphite esters, 0.5-1.5 parts of initiators, 1-5 parts of pH adjusting agents, 1-10 parts of deionized waters.
4. a kind of printing ink according to claim 3, which is characterized in that include the component of following weight proportion：46 parts
Composite polypropylene acid esters lotion, 45 parts of mill bases, 0.3 part of antifoaming agent, 0.5 part of levelling agent, 0.7 part of thickener, 0.7 part of gas phase dioxy
SiClx, 0.4 part of wetting agent, 3 parts of pH adjusting agents, 8 parts of water；Wherein composite polypropylene acid esters lotion includes the group of following weight proportion
Point：28 parts of acrylic monomers, 1 part of lauryl mercaptan, 3 parts of hydroxy-ethyl acrylates, 5 parts of emulsifiers, 10 portions of soybean oils, 0.2 part of phosphorous
Acid esters, 1.2 parts of initiators, 4 parts of pH adjusting agents, 5 parts of deionized waters.
5. a kind of printing ink according to claim 3, which is characterized in that the initiator be azo-bis-isobutyl cyanide, institute
Emulsifier is stated as lauryl sodium sulfate.
6. a kind of production technology of printing ink, which is characterized in that include the following steps：
S1, by the raw material of following weight proportion：10-15 parts of acrylic monomers, 1-2 parts of pH adjusting agents, 1-5 parts of emulsifiers, 5-15
Part soybean oil, 0.1-0.5 parts of phosphite esters, 1-3 parts of lauryl mercaptans, 1-5 parts of hydroxy-ethyl acrylates and 1-5 parts of deionized waters are mixed
It closes, forms pre-emulsion, when being heated to 85-95 DEG C, its pre-emulsification, mixing time are made under the mixing speed of 350r/min
For 20min；
S2 adds in 0.1-0.5 parts of initiators in pre-emulsion, keeps the mixing speed of 150r/min in a nitrogen atmosphere, stirs
The time is mixed as 35min, forms semi-emulsifying liquid；
S3 adds in 10-20 parts of acrylic monomers, 1-5 parts of deionized waters, 1-3 parts of pH adjusting agents, 1-5 parts of breasts in semi-emulsifying liquid
Agent, 0.5-1 parts of initiators stir 3h under the mixing speed of 280r/min, and emulsification is cooled to 25 DEG C, forms composite polypropylene
Acid esters lotion；
S4, by 40-50 parts of composite polypropylene acid esters lotions, 40-50 parts of mill bases, 0.2-0.5 parts of antifoaming agent, 0.4-0.8 parts of levellings
Agent, 0.1-1 parts of thickeners, 0.5-2 parts of aerosils, 0.1-0.5 parts of wetting agents, 1-5 parts of pH adjusting agents, 5-10 parts of water warps
Dispersion, grinding, filtering, form final printing ink.
7. a kind of production technology of printing ink according to claim 6, which is characterized in that in S3, initiator and
Emulsifier is added in a manner of being added dropwise in semi-emulsifying liquid, and wherein initiator time for adding is longer than the time for adding of emulsifier, whole
Time for adding is completed in 50-90min.
8. a kind of production technology of printing ink according to claim 6, which is characterized in that include the following steps：
S1, by the raw material of following weight proportion：10 parts of acrylic monomers, 2 parts of pH adjusting agents, 2 parts of emulsifiers, 10 portions of soybean oils,
0.2 part of phosphite ester, 1 part of lauryl mercaptan, 3 parts of hydroxy-ethyl acrylates and 2 parts of deionized water mixing, form pre-emulsion, will
When it is heated to 85-95 DEG C, its pre-emulsification, mixing time 20min are made under the mixing speed of 350r/min；
S2 adds in 0.2 part of initiator in pre-emulsion, the mixing speed of 150r/min is kept in a nitrogen atmosphere, during stirring
Between for 35min, form semi-emulsifying liquid；
S3 adds in 18 parts of acrylic monomers in semi-emulsifying liquid, and 3 parts of deionized waters, 2 parts of pH adjusting agents, 3 parts of emulsifiers, 1 part is drawn
Agent is sent out, 3h is stirred under the mixing speed of 280r/min, emulsification is cooled to 25 DEG C, forms composite polypropylene acid esters lotion；
S4, by 46 parts of composite polypropylene acid esters lotions, 45 parts of mill bases, 0.3 part of antifoaming agent, 0.5 part of levelling agent, 0.7 part of thickener,
0.7 part of aerosil, 0.4 part of wetting agent, 3 parts of pH adjusting agents, 8 parts of water are dispersed through, grind, filter, and form final print
Brush ink.