CN108082701A - A kind of printing carton and its production technology - Google Patents
A kind of printing carton and its production technology Download PDFInfo
- Publication number
- CN108082701A CN108082701A CN201810156555.3A CN201810156555A CN108082701A CN 108082701 A CN108082701 A CN 108082701A CN 201810156555 A CN201810156555 A CN 201810156555A CN 108082701 A CN108082701 A CN 108082701A
- Authority
- CN
- China
- Prior art keywords
- parts
- printing
- carton
- stirred
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of production technologies for printing carton and the carton, including box body, the box body includes bottom surface, the first side being connected on front side of bottom surface and the second side for being connected to bottom surface back, interconnection face is respectively connected at left and right sides of the first side and second side, stationary plane is connected at left and right sides of the bottom surface, the box body is made of composite honeycomb cardboard, wherein, include the component of following weight proportion filled with compounded mix, the compounded mix in the honeycomb hole of composite honeycomb paper intralamellar part：15 parts of Aragonite Style Calcium Carbonate Whiskers, 1 10 parts of konjaku glucomannans, 1 10 parts of N, N methylene-bisacrylamides, 20 30 parts of acrylic acid, 20 30 parts of sodium hydroxides, 10 20 parts of acrylamides, 10 15 parts of rosin milks, 13 parts of aluminum sulfate, 13 parts of sorbitan tristearates and 0.1 1 parts of potassium peroxydisulfates.Printing carton provided by the invention has better printing quality, while compressive property, elasticity are more preferable, have good hygroscopic desiccation performance.
Description
Technical field
The present invention relates to printing technologies, and in particular to a kind of printing carton and its production technology.
Background technology
Packing box can classify such as the term suggests being exactly used for packing the box of product by material：Carton, can,
Wooden box, cloth box, skin box, acrylic box, corrugated package box, pvc boxes etc., can also classify such as by the title of product：Moon cake
Box, tea caddy, matrimony vine box, bonbon box, exquisite gift box, local and special products box, wine box, chocolate box, food and medicine health products box, food
Packing box, tea packaging box, writing case etc..Pack kit function：Ensure the safety of product in transport, promote class of product etc.,
The characteristics of wherein carton is at low cost by its, good moldability, easy processing, is the common material of packing box, carton is producing and processing
Shaping, mainly including design ,-slice-draws a design, and-printing-is surface-treated-several production stages of post-processing-packaging, wherein
Most important functions are played to carton appearance be also as obvious effect be print steps, the selection of good ink and good
Processing technology can greatly improve printing quality, improve the class of carton, then promote sales volume.
With Social Culture, science and technology, expanding economy, packaging industry is also constantly developing, from initial simple and crude tool
There is packaging function, by now on the basis of with packaging function, it is also necessary to which there is good appearance and structure, Dan Cong
Just there are thin plate carton, slab carton and corrugated paper box and honeycomb carton etc. in the mechanism of cardboard, there is brown paper, blank sheet of paper from material
Plate, papers for books and periodicals etc. how on the premise of paperboard structure is promoted, ensure good printing effect, to improve packaging class,
Through the major demands and developing direction that become society now.There is certain achievement in research now, such as in Patent No.
In the patent of invention of CN104608421A, a kind of production method of flanging corrugated paper box is disclosed, improves the anti-of carton itself
It goes mouldy characteristic, while keeps the good deflection of carton so that the shape of carton is more beautiful, still, how increasingly complex
It is studied and is innovated on paperboard structure, obtain the carton of functional collection and aesthetic appearance and one or be badly in need of solution at present
The problem of.
The content of the invention
It is of the invention to provide to a kind of printing carton and its production technology, outside beautiful under the basis of above-mentioned background
It sees, good carton intensity and elasticity have the effect of hygroscopic desiccation, and printing quality is excellent.
The purpose of the present invention is what is be achieved through the following technical solutions：
A kind of printing carton, including box body, the box body top surface is provided with opening, and the box body includes bottom surface, is connected to bottom surface
The left and right two of the first side of front side and the second side for being connected to bottom surface back, the first side and second side
Side is respectively connected with interconnection face, and stationary plane is connected at left and right sides of the bottom surface, and the box body uses composite honeycomb cardboard system
Into the box surface is provided with printing layer.
Preferably, V-shaped groove mouth is offered on the interconnection face, be arranged in two interconnection faces of the same side
The opening direction of V-shaped groove mouth is opposite.
Wherein, filled with compounded mix in the honeycomb hole of the composite honeycomb paper intralamellar part, the compounded mix include with
The component of lower weight proportion：1-5 parts of Aragonite Style Calcium Carbonate Whiskers, 1-10 parts of konjaku glucomannans, 1-10 parts of N, N- di-2-ethylhexylphosphine oxides
Acrylamide, 20-30 parts of acrylic acid, 20-30 parts of sodium hydroxides, 10-20 parts of acrylamides, 10-15 parts of rosin milks, 1-3 parts
Aluminum sulfate, 1-3 parts of sorbitan tristearates and 0.1-1 parts of potassium peroxydisulfates.
Preferably, the compounded mix includes the component of following weight proportion：3 parts of Aragonite Style Calcium Carbonate Whiskers, 2 portions of konjakus
Glucomannan, 8 parts of N, N- methylene-bisacrylamides, 25 parts of acrylic acid, 25 parts of sodium hydroxides, 15 parts of acrylamides, 10 portions of pines
Fragrant lotion, 3 parts of aluminum sulfate, 3 parts of sorbitan tristearates and 0.2 part of potassium peroxydisulfate.
And a kind of production technology for printing carton, comprise the following steps：
S1：Mixed solution：20-30 parts of sodium hydroxides are dissolved in water, the sodium hydroxide solution that concentration is 30% are configured to, by this
Sodium hydroxide solution is at the uniform velocity instilled in 30min in 20-30 parts of acrylic acid, then, adds in 1-5 parts of Aragonite Style Calcium Carbonate Whiskers,
It stirs 5min and forms mixed solution；
S2：Pre-composite solution：10-20 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min,
15min is stirred to react in the environment of 25 DEG C, forms pre-composite solution；
S3：Compounded mix：By 1-10 konjaku glucomannans, 10-15 parts of rosin milks, 1-3 parts of aluminum sulfate add in pre-composite solution
In, 15min is stirred at 30 DEG C, then adds in 1-10 parts of N, N- methylene-bisacrylamides continue to stir 10min, then will
1-3 parts of sorbitan tristearates and 0.1-1 parts of potassium peroxydisulfates, are stirred to react 25min, gelatinous are obtained by filtration through non-woven fabrics
Compounded mix；
S3：Paper is filled：It chooses honeycomb and becomes the honeycomb cardboard of a length of 6-10mm, thickness into 25-40mm, draw quantitative compound fill out
Expect and in injection fillers to honeycomb hole, and honeycomb cardboard is carried out to foaming processing 1-2min in the case where microwave power is 125w, formed
Composite honeycomb cardboard；
S4：Coating process：Composite honeycomb cardboard is placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡,
The solid content of coating is 55%,
S5：Printing：Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process using Flexographic printing equipment, is being printed
Pressure is 200-250N, and coating pH value is between 8-9, viscosity 55s, latex content be 13% and anilox roll in screen density be
In the environment of 220l/CM, printing process is completed；
S6：Carton forming：The composite honeycomb cardboard being completed for printing is cut into corresponding shape, is formed and printed by manual assembly
Carton.
Preferably, the production process of compounded mix comprises the following steps：25 parts of sodium hydroxides are dissolved in water, are configured to dense
The sodium hydroxide solution for 30% is spent, which is at the uniform velocity instilled in 30min in 25 parts of acrylic acid, then, is added in
3 parts of Aragonite Style Calcium Carbonate Whiskers, stirring 5min form mixed solution；15 parts of acrylamides are at the uniform velocity added to this to mix in 5min
It closes in solution and is stirred, be stirred to react 15min in the environment of 25 DEG C, form pre-composite solution；By 2 parts of konjak portuguese gansu polyoses
Sugar, 10 parts of rosin milks, 3 parts of aluminum sulfate are added in pre-composite solution, and 15min is stirred at 30 DEG C, then add in 8 parts of N, and N- is sub-
Bisacrylamide continues to stir 10min, then by 3 parts of sorbitan tristearates and 0.2 part of potassium peroxydisulfate, stirring
25min is reacted, gelatinous compounded mix is obtained by filtration through non-woven fabrics.
Compared with prior art, the present invention it has the following advantages that：
First, carton provided by the invention is molded by the way of Self-crossover fastening, reduces glue or other adhesive materials
It uses, it is more environmentally friendly, while with more novel structure, meet the aesthetic of modern times；Carton is made of honeycomb cardboard, honeycomb paper
Plate is made according to nature honeycomb structure, is to connect into the countless hollow regular hexagons of individual using fluting medium, is formed
Honeycomb paper core, and facial tissue is bonded on refill two sides, have the characteristics that structure novel, it is inexpensive it is light, cushion performance is excellent, and utilize
Composite filling material is filled foaming in honeycomb hole, and crushing resistance, the bullet of cardboard can be greatly improved using the packing material
Property and hygroscopic desiccation performance, and flexible version printing is carried out to paperboard surface on this basis, in printing process to cardboard into
Row mild crush so that cardboard after filling is thinner, structure is more stable and printing layer is bright in luster, clarity higher, rank
Adjust level more horn of plenty.
Description of the drawings
Fig. 1 is the structure diagram of carton in the present invention.
Specific embodiment
Below in conjunction with the attached drawing in the embodiment of the present invention, the technical solution in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other without making creative work
Embodiment belongs to the scope of protection of the invention.
With reference to figure 1, the present invention provides a kind of printing carton, and including box body, the box body top surface is provided with opening, the box
Body includes bottom surface, the first side being connected on front side of bottom surface and the second side for being connected to bottom surface back, the first side
And interconnection face is respectively connected at left and right sides of second side, it is connected with stationary plane, the box at left and right sides of the bottom surface
Body is made of composite honeycomb cardboard, and the box surface is provided with printing layer.
V-shaped groove mouth is offered on interconnection face, is arranged on V-shaped groove mouth in two interconnection faces of the same side
Opening direction reduces the use of glue on the contrary, by the way that two V-shaped groove mouth cross-fixings being realized, the connection of carton side is fixed
Amount, more greenization.
Wherein, can be carried significantly filled with compounded mix, the compounded mix in the honeycomb hole of composite honeycomb paper intralamellar part
The elasticity and compressive property of high cardboard, while the hygroscopic desiccation performance of cardboard can be greatly improved, it reduces in wet environment
Cardboard water suction excessively soften it is damaged or it is excessively dry cardboard is caused to become fragile breakage, greatly improve service life, it is described compound to fill out
Material includes the component of following weight proportion：1-5 parts of Aragonite Style Calcium Carbonate Whiskers, 1-10 parts of konjaku glucomannans, 1-10 parts of N, N-
Methylene-bisacrylamide, 20-30 parts of acrylic acid, 20-30 parts of sodium hydroxides, 10-20 parts of acrylamides, 10-15 parts of rosin breasts
Liquid, 1-3 parts of aluminum sulfate, 1-3 parts of sorbitan tristearates and 0.1-1 parts of potassium peroxydisulfates.
At the same time, the present invention also provides the production technology of the printing carton, comprise the following steps：
S1：Mixed solution：20-30 parts of sodium hydroxides are dissolved in water, the sodium hydroxide solution that concentration is 30% are configured to, by this
Sodium hydroxide solution is at the uniform velocity instilled in 30min in 20-30 parts of acrylic acid, then, adds in 1-5 parts of Aragonite Style Calcium Carbonate Whiskers,
It stirs 5min and forms mixed solution；
S2：Pre-composite solution：10-20 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min,
15min is stirred to react in the environment of 25 DEG C, forms pre-composite solution；
S3：Compounded mix：By 1-10 konjaku glucomannans, 10-15 parts of rosin milks, 1-3 parts of aluminum sulfate add in pre-composite solution
In, 15min is stirred at 30 DEG C, then adds in 1-10 parts of N, N- methylene-bisacrylamides continue to stir 10min, then will
1-3 parts of sorbitan tristearates and 0.1-1 parts of potassium peroxydisulfates, are stirred to react 25min, gelatinous are obtained by filtration through non-woven fabrics
Compounded mix；
S3：Paper is filled：It chooses honeycomb and becomes the honeycomb cardboard of a length of 6-10mm, thickness into 25-40mm, draw quantitative compound fill out
Expect and in injection fillers to honeycomb hole, and honeycomb cardboard is carried out to foaming processing 1-2min in the case where microwave power is 125w, formed
Composite honeycomb cardboard；
S4：Coating process：Composite honeycomb cardboard is placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡,
The solid content of coating is 55%,
S5：Printing：Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process using Flexographic printing equipment, is being printed
Pressure is 200-250N, and coating pH value is between 8-9, viscosity 55s, latex content be 13% and anilox roll in screen density be
In the environment of 220l/CM, printing process is completed；
S6：Carton forming：The composite honeycomb cardboard being completed for printing is cut into corresponding shape, is formed and printed by manual assembly
Carton.
The production technology of the present invention is further detailed below according to embodiment：
Embodiment 1
20 parts of sodium hydroxides are dissolved in water, are configured to the sodium hydroxide solution that concentration is 30%, which is existed
It is at the uniform velocity instilled in 30min in 20 parts of acrylic acid, then, adds in 1 part of Aragonite Style Calcium Carbonate Whiskers, it is molten that stirring 5min forms mixing
Liquid；10 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min, are stirred in the environment of 25 DEG C
15min is reacted, forms pre-composite solution；By 1 konjaku glucomannan, 10 parts of rosin milks, 1 part of aluminum sulfate adds in pre-composite solution
In, 15min is stirred at 30 DEG C, then adds in 1 part of N, N- methylene-bisacrylamides continue to stir 10min, then by 1 part
Sorbitan tristearate and 0.1 part of potassium peroxydisulfate, are stirred to react 25min, are obtained by filtration through non-woven fabrics gelatinous compound
Filler；Choose the honeycomb cardboard that honeycomb becomes a length of 6mm, thickness is 40mm, draw quantitative compounded mix simultaneously injection fillers to bee
In socket bore, and honeycomb cardboard in the case where microwave power is 125w is carried out to foaming processing 1-2min, form composite honeycomb cardboard；It will be multiple
It closes honeycomb cardboard to be placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡, and the solid content of coating is 55%, profit
Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process with Flexographic printing equipment, is 215N in printing pressure, applies
Expect pH value between 8-9, viscosity 55s, latex content be 13% and anilox roll in the environment of screen density is 220l/CM, complete
Printing process；The composite honeycomb cardboard being completed for printing is cut into corresponding shape, printing carton is formed by manual assembly.
Embodiment 2
25 parts of sodium hydroxides are dissolved in water, are configured to the sodium hydroxide solution that concentration is 30%, which is existed
It is at the uniform velocity instilled in 30min in 25 parts of acrylic acid, then, adds in 3 parts of Aragonite Style Calcium Carbonate Whiskers, it is molten that stirring 5min forms mixing
Liquid；15 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min, are stirred in the environment of 25 DEG C
15min is reacted, forms pre-composite solution；By 2 konjaku glucomannans, 10 parts of rosin milks, 3 parts of aluminum sulfate add in pre-composite solution
In, 15min is stirred at 30 DEG C, then adds in 8 parts of N, N- methylene-bisacrylamides continue to stir 10min, then by 3 parts
Sorbitan tristearate and 0.2 part of potassium peroxydisulfate, are stirred to react 25min, are obtained by filtration through non-woven fabrics gelatinous compound
Filler；Choose the honeycomb cardboard that honeycomb becomes a length of 6mm, thickness is 40mm, draw quantitative compounded mix simultaneously injection fillers to bee
In socket bore, and honeycomb cardboard in the case where microwave power is 125w is carried out to foaming processing 1-2min, form composite honeycomb cardboard；It will be multiple
It closes honeycomb cardboard to be placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡, and the solid content of coating is 55%, profit
Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process with Flexographic printing equipment, is 215N in printing pressure, applies
Expect pH value between 8-9, viscosity 55s, latex content be 13% and anilox roll in the environment of screen density is 220l/CM, complete
Printing process；The composite honeycomb cardboard being completed for printing is cut into corresponding shape, printing carton is formed by manual assembly.
Embodiment 3
30 parts of sodium hydroxides are dissolved in water, are configured to the sodium hydroxide solution that concentration is 30%, which is existed
It is at the uniform velocity instilled in 30min in 30 parts of acrylic acid, then, adds in 5 parts of Aragonite Style Calcium Carbonate Whiskers, it is molten that stirring 5min forms mixing
Liquid；20 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min, are stirred in the environment of 25 DEG C
15min is reacted, forms pre-composite solution；By 10 konjaku glucomannans, 15 parts of rosin milks, 3 parts of aluminum sulfate add in pre-composite molten
In liquid, 15min is stirred at 30 DEG C, then adds in 10 parts of N, N- methylene-bisacrylamides continue to stir 10min, then by 3
Part sorbitan tristearate and 1 part of potassium peroxydisulfate, are stirred to react 25min, are obtained by filtration through non-woven fabrics gelatinous compound
Filler；Choose the honeycomb cardboard that honeycomb becomes a length of 6mm, thickness is 40mm, draw quantitative compounded mix simultaneously injection fillers to bee
In socket bore, and honeycomb cardboard in the case where microwave power is 125w is carried out to foaming processing 1-2min, form composite honeycomb cardboard；It will be multiple
It closes honeycomb cardboard to be placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡, and the solid content of coating is 55%, profit
Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process with Flexographic printing equipment, is 215N in printing pressure, applies
Expect pH value between 8-9, viscosity 55s, latex content be 13% and anilox roll in the environment of screen density is 220l/CM, complete
Printing process；The composite honeycomb cardboard being completed for printing is cut into corresponding shape, printing carton is formed by manual assembly.
According to above-described embodiment, after testing, it is as follows to obtain technical data：
| Project | Embodiment 1 | Embodiment 2 | Embodiment 3 |
| Color/grade | 4 | 5 | 5 |
| Hydroscopicity % | 51.4 | 56.8 | 53.1 |
| Moisture releasing rate % | 49.2 | 55.1 | 50.9 |
| Energy absorption（It is maximum）/E | 2.85 | 3.12 | 2.99 |
| Stress（It is maximum）/MPa | 1.92 | 2.21 | 2.19 |
| Unit volume always absorbs energy (J/cm3) | 2.45 | 2.61 | 2.55 |
It is known that the printing carton that the present invention obtains has better anti-pressure ability, elasticity and hygroscopic desiccation performance, simultaneously
Printing appearance color is more bright-coloured beautiful, and condition is more preferable, wherein optimal with the carton that embodiment 2 obtains.
Claims (6)
1. a kind of printing carton, including box body, which is characterized in that the box body top surface is provided with opening, and the box body includes bottom
Face, the first side being connected on front side of bottom surface and the second side for being connected to bottom surface back, the first side and second
Interconnection face is respectively connected at left and right sides of side, stationary plane is connected at left and right sides of the bottom surface, the box body is using multiple
It closes honeycomb cardboard to be made, the box surface is provided with printing layer.
2. a kind of printing carton according to claim 1, which is characterized in that V-shaped groove mouth is offered on the interconnection face,
The opening direction for being arranged on the V-shaped groove mouth in two interconnection faces of the same side is opposite.
3. a kind of printing carton according to claim 1, which is characterized in that in the honeycomb hole of the composite honeycomb paper intralamellar part
Filled with compounded mix, the compounded mix includes the component of following weight proportion：1-5 parts of Aragonite Style Calcium Carbonate Whiskers, 1-10
Part konjaku glucomannan, 1-10 parts of N, N- methylene-bisacrylamides, 20-30 parts of acrylic acid, 20-30 parts of sodium hydroxides, 10-20
Part acrylamide, 10-15 parts of rosin milks, 1-3 parts of aluminum sulfate, 1-3 parts of sorbitan tristearates and 0.1-1 parts of persulfuric acid
Potassium.
4. a kind of printing carton according to claim 3, which is characterized in that the compounded mix includes following weight proportion
Component：3 parts of Aragonite Style Calcium Carbonate Whiskers, 2 parts of konjaku glucomannans, 8 parts of N, N- methylene-bisacrylamides, 25 parts of acrylic acid,
25 parts of sodium hydroxides, 15 parts of acrylamides, 10 parts of rosin milks, 3 parts of aluminum sulfate, 3 parts of sorbitan tristearates and 0.2 part
Potassium peroxydisulfate.
5. a kind of production technology for printing carton, which is characterized in that comprise the following steps：
S1：Mixed solution：20-30 parts of sodium hydroxides are dissolved in water, the sodium hydroxide solution that concentration is 30% are configured to, by this
Sodium hydroxide solution is at the uniform velocity instilled in 30min in 20-30 parts of acrylic acid, then, adds in 1-5 parts of Aragonite Style Calcium Carbonate Whiskers,
It stirs 5min and forms mixed solution；
S2：Pre-composite solution：10-20 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min,
15min is stirred to react in the environment of 25 DEG C, forms pre-composite solution；
S3：Compounded mix：By 1-10 konjaku glucomannans, 10-15 parts of rosin milks, 1-3 parts of aluminum sulfate add in pre-composite solution
In, 15min is stirred at 30 DEG C, then adds in 1-10 parts of N, N- methylene-bisacrylamides continue to stir 10min, then will
1-3 parts of sorbitan tristearates and 0.1-1 parts of potassium peroxydisulfates, are stirred to react 25min, gelatinous are obtained by filtration through non-woven fabrics
Compounded mix；
S3：Paper is filled：It chooses honeycomb and becomes the honeycomb cardboard of a length of 6-10mm, thickness into 25-40mm, draw quantitative compound fill out
Expect and in injection fillers to honeycomb hole, and honeycomb cardboard is carried out to foaming processing 1-2min in the case where microwave power is 125w, formed
Composite honeycomb cardboard；
S4：Coating process：Composite honeycomb cardboard is placed on coating machine, in its surface coating paint, coating weight is 8g/ ㎡,
The solid content of coating is 55%,
S5：Printing：Surface printing is carried out to the composite honeycomb cardboard Jing Guo coating process using Flexographic printing equipment, is being printed
Pressure is 200-250N, and coating pH value is between 8-9, viscosity 55s, latex content be 13% and anilox roll in screen density be
In the environment of 220l/CM, printing process is completed；
S6：Carton forming：The composite honeycomb cardboard being completed for printing is cut into corresponding shape, is formed and printed by manual assembly
Carton.
A kind of 6. production technology for printing carton according to claim 5, which is characterized in that the production process bag of compounded mix
Include following steps：25 parts of sodium hydroxides are dissolved in water, the sodium hydroxide solution that concentration is 30% are configured to, by the sodium hydroxide
Solution is at the uniform velocity instilled in 30min in 25 parts of acrylic acid, then, adds in 3 parts of Aragonite Style Calcium Carbonate Whiskers, stirring 5min forms mixed
Close solution；15 parts of acrylamides are at the uniform velocity added in the mixed solution and are stirred in 5min, in the environment of 25 DEG C
15min is stirred to react, forms pre-composite solution；By 2 parts of konjaku glucomannans, 10 parts of rosin milks, 3 parts of aluminum sulfate add in pre- multiple
It closes in solution, 15min is stirred at 30 DEG C, then add in 8 parts of N, N- methylene-bisacrylamides continue to stir 10min, then
By 3 parts of sorbitan tristearates and 0.2 part of potassium peroxydisulfate, 25min is stirred to react, is obtained by filtration through non-woven fabrics gelatinous
Compounded mix.