CN108130731A - A kind of polyester filament spinning oil and preparation method thereof - Google Patents
A kind of polyester filament spinning oil and preparation method thereof Download PDFInfo
- Publication number
- CN108130731A CN108130731A CN201711344595.2A CN201711344595A CN108130731A CN 108130731 A CN108130731 A CN 108130731A CN 201711344595 A CN201711344595 A CN 201711344595A CN 108130731 A CN108130731 A CN 108130731A
- Authority
- CN
- China
- Prior art keywords
- parts
- polyester filament
- spinning oil
- filament spinning
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polyester filament spinning oil and preparation method thereof, the polyester filament is made of with spinning oil the raw material of following parts by weight：57 parts of lauric acid diethyl amide, 35 parts of neopelex, 5 10 parts of glycerine, 13 parts of octyl phosphate, 57 parts of nano-powder, 13 parts of dispersant, 10 20 parts of ethyl alcohol, 13 parts of sodium secondary alkyl sulfonate, 24 parts of dimethyl silicone polymer, 35 parts of sorbitan fatty acid ester, 10 20 parts of deionized water.The polyester filament of the present invention is stablized with spinning oil property, safe and harmless, and preparation process is energy saving, at low cost.
Description
Technical field
The invention belongs to field of fabric producing technology, specifically relate to a kind of polyester filament spinning oil and its preparation side
Method.
Background technology
Natural fiber is the basic material of textile industry by the chemical fibre that extrusion obtains.Strand and fiber add rear
Different mechanical force and thermal stress are subjected to during work.In order to ensure fiber is injury-free in this process, squeezed out in fiber
It should oil immediately after forming.
After dacron product is by monomer polymerization in spinning process, spinning oil can be adjusted between fiber and fiber, fiber
Frictional property between metal, reduce friction coefficient, reduce because friction generate electrostatic, make fiber have good convergence,
Flatness and fiber separation meet the relevant needs of fiber post-processing.
At present, some conventional spinning oils in the market use process can occur seriously to smolder, coking, lousiness, broken end,
The problems such as polluting workshop condition.So it is urgent problem to need to find a kind of spinning oil efficiently, environmentally friendly.
Invention content
The purpose of the present invention is to provide a kind of polyester filament spinning oil and preparation method thereof, to solve above-mentioned background
The problem of being proposed in technology.
To achieve the above object, the present invention provides following technical solution：
A kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid diethyl amide 5-7
Part, 3-5 parts of neopelex, 5-10 parts of glycerine, 1-3 parts of octyl phosphate, 5-7 parts of nano-powder, dispersant 1-3
Part, 10-20 parts of ethyl alcohol, 1-3 parts of sodium secondary alkyl sulfonate, 2-4 parts of dimethyl silicone polymer, 3-5 parts of sorbitan fatty acid ester,
10-20 parts of deionized water.
Preferably, the nano-powder is one or more than one kinds of in kaolin, diatomite, sepiolite powder.
Preferably, the ethyl alcohol is absolute ethyl alcohol, rank is that analysis is pure.
Preferably, the grain size of the nano-powder is 5-50nm.
Preferably, the dispersant is one in triethanolamine, calgon, polyethylene glycol, sodium cellulose xanghate
Kind or more than one.
Preferably, the preparation method of the polyester filament spinning oil, specific steps include：
Step 1,10-20 parts of deionized water, 50-60 DEG C of oil bath heating are added in a kettle；
Step 2,5-7 parts of lauric acid diethyl amide, 3-5 parts of neopelex, 5-10 parts of glycerine, octyl group are added in
1-3 parts of phosphate, stirs 20-30 minutes by 500-1000 revs/min；
Step 3, first by 10-20 parts of 5-7 parts of nano-powder, 1-3 parts of dispersant, ethyl alcohol progress ultrasonic disperses, ultrasonic power
For 500-800W, ultrasonic time is 10-20 minutes；
Step 4, temperature is reduced to 20-30 DEG C, the solution of step 3 is poured into the solution of step 2,500-1000 revs/min
Clock stirs 20-30 minutes；
Step 5,1-3 parts of sodium secondary alkyl sulfonate of addition, 3-5 parts of sorbitan fatty acid ester, 500-1000 revs/min,
Stirring 30-40 minutes；
Step 6,2-4 parts of dimethyl silicone polymer is added in, 500-1000 revs/min, is stirred 10-20 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Compared with prior art, the beneficial effects of the invention are as follows：
1st, polyester filament of the invention is stablized with spinning oil property, safe and harmless, and preparation process is energy saving, cost
It is low.
2nd, it is equal with good spinnability, flatness, coherent after polyester filament of the invention is applied with spinning oil
Well, no lousiness, end breakage rate is low, and waste silk rate is low.
3rd, after polyester filament of the invention is applied with spinning oil in spinning process, smoke is few, noncoking carbonization, nothing
Pollution.
4th, mutual compatibility, synergistic effect between various raw materials used in polyester filament spinning oil of the invention, common group
Into the product haveing excellent performance.
5th, simplify technique, safe operation is simple, is easy to industrialized production.
6th, use of the invention can receive good economic benefit.
Example is embodied
The invention discloses a kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid two
5-7 parts of glycollic amide, 3-5 parts of neopelex, 5-10 parts of glycerine, 1-3 parts of octyl phosphate, 5-7 parts of nano-powder,
1-3 parts of dispersant, 10-20 parts of ethyl alcohol, 1-3 parts of sodium secondary alkyl sulfonate, 2-4 parts of dimethyl silicone polymer, sorbitan fatty
3-5 parts of acid esters, 10-20 parts of deionized water.
The present invention also provides a kind of preparation method of polyester filament spinning oil, specific steps include：
Step 1,10-20 parts of deionized water, 50-60 DEG C of oil bath heating are added in a kettle；
Step 2,5-7 parts of lauric acid diethyl amide, 3-5 parts of neopelex, 5-10 parts of glycerine, octyl group are added in
1-3 parts of phosphate, stirs 20-30 minutes by 500-1000 revs/min；
Step 3, first by 10-20 parts of 5-7 parts of nano-powder, 1-3 parts of dispersant, ethyl alcohol progress ultrasonic disperses, ultrasonic power
For 500-800W, ultrasonic time is 10-20 minutes；
Step 4, temperature is reduced to 20-30 DEG C, the solution of step 3 is poured into the solution of step 2,500-1000 revs/min
Clock stirs 20-30 minutes；
Step 5,1-3 parts of sodium secondary alkyl sulfonate of addition, 3-5 parts of sorbitan fatty acid ester, 500-1000 revs/min,
Stirring 30-40 minutes；
Step 6,2-4 parts of dimethyl silicone polymer is added in, 500-1000 revs/min, is stirred 10-20 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Embodiment 1
The invention discloses a kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid two
5 parts of glycollic amide, 3 parts of neopelex, 5 parts of glycerine, 1 part of octyl phosphate, 5 parts of nano-powder, 1 part of dispersant,
10 parts of ethyl alcohol, 1 part of sodium secondary alkyl sulfonate, 2 parts of dimethyl silicone polymer, 3 parts of sorbitan fatty acid ester, deionized water 10
Part.
The present invention also provides a kind of preparation method of polyester filament spinning oil, specific steps include：
Step 1,10 parts of deionized water, 50 DEG C of oil bath heating are added in a kettle；
Step 2,5 parts of lauric acid diethyl amide, 3 parts of neopelex, 5 parts of glycerine, octyl phosphate 1 are added in
Part, it 500 revs/min, stirs 20 minutes；
Step 3, first by 5 parts of nano-powder, 1 part of dispersant, 10 parts of ethyl alcohol progress ultrasonic disperses, ultrasonic power 500W,
Ultrasonic time is 10 minutes；
Step 4, temperature is reduced to 20 DEG C, the solution of step 3 is poured into the solution of step 2,500 revs/min, stirring 20
Minute；
Step 5,1 part of sodium secondary alkyl sulfonate, 3 parts of sorbitan fatty acid ester are added in, 500 revs/min, stirs 30 points
Clock；
Step 6,2 parts of dimethyl silicone polymer is added in, 500 revs/min, is stirred 10 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Embodiment 2
The invention discloses a kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid two
6 parts of glycollic amide, 4 parts of neopelex, 8 parts of glycerine, 2 parts of octyl phosphate, 6 parts of nano-powder, 2 parts of dispersant,
15 parts of ethyl alcohol, 2 parts of sodium secondary alkyl sulfonate, 3 parts of dimethyl silicone polymer, 4 parts of sorbitan fatty acid ester, deionized water 15
Part.
The present invention also provides a kind of preparation method of polyester filament spinning oil, specific steps include：
Step 1,15 parts of deionized water, 55 DEG C of oil bath heating are added in a kettle；
Step 2,6 parts of lauric acid diethyl amide, 4 parts of neopelex, 8 parts of glycerine, octyl phosphate 2 are added in
Part, it 800 revs/min, stirs 25 minutes；
Step 3, first by 6 parts of nano-powder, 2 parts of dispersant, 15 parts of ethyl alcohol progress ultrasonic disperses, ultrasonic power 700W,
Ultrasonic time is 15 minutes；
Step 4, temperature is reduced to 25 DEG C, the solution of step 3 is poured into the solution of step 2,800 revs/min, stirring 25
Minute；
Step 5,2 parts of sodium secondary alkyl sulfonate, 4 parts of sorbitan fatty acid ester are added in, 800 revs/min, stirs 35 points
Clock；
Step 6,3 parts of dimethyl silicone polymer is added in, 800 revs/min, is stirred 15 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Embodiment 3
The invention discloses a kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid two
7 parts of glycollic amide, 5 parts of neopelex, 10 parts of glycerine, 3 parts of octyl phosphate, 7 parts of nano-powder, 3 parts of dispersant,
20 parts of ethyl alcohol, 3 parts of sodium secondary alkyl sulfonate, 4 parts of dimethyl silicone polymer, 5 parts of sorbitan fatty acid ester, deionized water 20
Part.
The present invention also provides a kind of preparation method of polyester filament spinning oil, specific steps include：
Step 1,20 parts of deionized water, 60 DEG C of oil bath heating are added in a kettle；
Step 2,7 parts of lauric acid diethyl amide, 5 parts of neopelex, 10 parts of glycerine, octyl phosphate are added in
It 3 parts, 1000 revs/min, stirs 30 minutes；
Step 3, first by 7 parts of nano-powder, 3 parts of dispersant, 20 parts of ethyl alcohol progress ultrasonic disperses, ultrasonic power 800W,
Ultrasonic time is 10 minutes；
Step 4, temperature is reduced to 20 DEG C, the solution of step 3 is poured into the solution of step 2,800 revs/min, stirring 25
Minute；
Step 5,3 parts of sodium secondary alkyl sulfonate, 5 parts of sorbitan fatty acid ester are added in, 900 revs/min, stirs 30 points
Clock；
Step 6,4 parts of dimethyl silicone polymer is added in, 1000 revs/min, is stirred 10 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Embodiment 4
The invention discloses a kind of polyester filament spinning oil, according to parts by weight, including following components：Lauric acid two
7 parts of glycollic amide, 5 parts of neopelex, 8 parts of glycerine, 1 part of octyl phosphate, 7 parts of nano-powder, 3 parts of dispersant,
20 parts of ethyl alcohol, 1 part of sodium secondary alkyl sulfonate, 4 parts of dimethyl silicone polymer, 3 parts of sorbitan fatty acid ester, deionized water 20
Part.
The present invention also provides a kind of preparation method of polyester filament spinning oil, specific steps include：
Step 1,20 parts of deionized water, 55 DEG C of oil bath heating are added in a kettle；
Step 2,7 parts of lauric acid diethyl amide, 5 parts of neopelex, 8 parts of glycerine, octyl phosphate 1 are added in
Part, it 800 revs/min, stirs 20 minutes；
Step 3, first by 7 parts of nano-powder, 3 parts of dispersant, 20 parts of ethyl alcohol progress ultrasonic disperses, ultrasonic power 800W,
Ultrasonic time is 20 minutes；
Step 4, temperature is reduced to 30 DEG C, the solution of step 3 is poured into the solution of step 2,800 revs/min, stirring 25
Minute；
Step 5,1 part of sodium secondary alkyl sulfonate, 3 parts of sorbitan fatty acid ester are added in, 900 revs/min, stirs 30 points
Clock；
Step 6,4 parts of dimethyl silicone polymer is added in, 800 revs/min, is stirred 10 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation is made
Finished product.
Test case
Polyester filament is handled using the polyester filament spinning oil of embodiment 1,2,3,4, test result is as follows：
The above-mentioned various embodiments enumerated, under the premise of reconcilable, can be combined with each other implementation, those skilled in the art
It can combine above to the explanation of embodiment, as the foundation being combined to the technical characteristic in different embodiments.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding without departing from the principles and spirit of the present invention can carry out these embodiments a variety of variations, modification, replace
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of polyester filament spinning oil, it is characterised in that：The polyester filament includes following parts by weight with spinning oil
Several raw materials：5-7 parts of lauric acid diethyl amide, 3-5 parts of neopelex, 5-10 parts of glycerine, octyl phosphate 1-3
Part, 5-7 parts of nano-powder, 1-3 parts of dispersant, 10-20 parts of ethyl alcohol, 1-3 parts of sodium secondary alkyl sulfonate, dimethyl silicone polymer 2-4
Part, 3-5 parts of sorbitan fatty acid ester, 10-20 parts of deionized water.
2. polyester filament spinning oil according to claim 1, it is characterised in that：The nano-powder is kaolinite
It is one or more than one kinds of in soil, diatomite, sepiolite powder.
3. polyester filament spinning oil according to claim 1, it is characterised in that：The ethyl alcohol for absolute ethyl alcohol,
Rank is pure to analyze.
4. polyester filament spinning oil according to claim 1, it is characterised in that：The grain size of the nano-powder is
5-50nm。
5. polyester filament spinning oil according to claim 1, it is characterised in that：The dispersant is three ethyl alcohol
It is one or more than one kinds of in amine, calgon, polyethylene glycol, sodium cellulose xanghate.
6. a kind of preparation method using any one of the claims 1-5 polyester filament spinning oils, feature
It is：Specific steps include：
Step 1,10-20 parts of deionized water, 50-60 DEG C of oil bath heating are added in a kettle；
Step 2,5-7 parts of lauric acid diethyl amide, 3-5 parts of neopelex, 5-10 parts of glycerine, octylphosphonic acid are added in
1-3 parts of ester, stirs 20-30 minutes by 500-1000 revs/min；
Step 3, first by 10-20 parts of 5-7 parts of nano-powder, 1-3 parts of dispersant, ethyl alcohol progress ultrasonic disperses, ultrasonic power is
500-800W, ultrasonic time are 10-20 minutes；
Step 4, temperature is reduced to 20-30 DEG C, the solution of step 3 is poured into the solution of step 2,500-1000 revs/min, stirred
It mixes 20-30 minutes；
Step 5,1-3 parts of sodium secondary alkyl sulfonate, 3-5 parts of sorbitan fatty acid ester are added in, 500-1000 revs/min, is stirred
30-40 minutes；
Step 6,2-4 parts of dimethyl silicone polymer is added in, 500-1000 revs/min, is stirred 10-20 minutes；
Step 7, stirring is shut down, obtains prepared liquid polyester filament spinning oil；
Step 8, it stands and is cooled in reaction kettle liquid polyester filament spinning oil and is less than 20 DEG C, blowing encapsulation, finished product.