CN108102342A - Plastic cement race track and preparation method - Google Patents
Plastic cement race track and preparation method Download PDFInfo
- Publication number
- CN108102342A CN108102342A CN201611049671.2A CN201611049671A CN108102342A CN 108102342 A CN108102342 A CN 108102342A CN 201611049671 A CN201611049671 A CN 201611049671A CN 108102342 A CN108102342 A CN 108102342A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- plastic cement
- race track
- cement race
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of plastic cement race track and preparation method thereof, according to parts by weight, the B component including 30 50 parts of component As and 50 70 parts, the component A is by following weight parts into being grouped into:Toluene di-isocyanate(TDI), polyether polyol;The B component is by following weight parts into being grouped into:Crosslinking agent, filler, pigment, thickener, antioxidant.The plastic cement race track of the present invention has manufacture craft simple, makes raw material and is easy to buy, has the advantages that low manufacture cost, have broad application prospects.
Description
Technical field
The present invention relates to plastic cement race track preparing technical fields more particularly to a kind of plastic cement race track and preparation method thereof.
Background technology
Polyurethane plastic has moderate, the bright in colour, anti-skid wearable of elasticity, place cleaning, easy maintenance, can effectively avoid
Sportsman's damage significantly improves the features such as sports achievement, is generally used in the sports and training of countries in the world.At me
State, with the development of sports cause, it is indispensable that laying plastic cement race track has become major small and medium-sized cities self-growth
One of hardware.
Existing polyurethane plastic complex production process, production cost are high.It is therefore desirable to propose a kind of new poly- ammonia
Ester plastic cement race track and preparation method.
The content of the invention
The object of the present invention is to provide a kind of plastic cement race track and preparation methods.
Technical scheme is as follows:
A kind of plastic cement race track, which is characterized in that according to parts by weight, the B groups including 30-50 parts of component As and 50-70 parts
Point,
The component A is by following weight parts into being grouped into:
30-40 parts of toluene di-isocyanate(TDI),
40-50 parts of polyether polyol;
The B component is by following weight parts into being grouped into:
Further, the crosslinking agent is trimethylolpropane.
Further, the filler is talcum powder or kaolin.
Further, the pigment is iron oxide.
Further, the antioxidant is antioxidant GA-80.
Further, the thickener is organobentonite HY-708.
A kind of preparation method of plastic cement race track, it is characterised in that:
S1:The preparation of component A:Polyether polyol is added in reaction kettle, stirring is warming up to 90~120 DEG C, is taken off under vacuum
It is cooled to 50 DEG C after water, adds in toluene diisocyanate, slow reaction is to being down to room temperature after 85 DEG C;
S2:The preparation of B component:Crosslinking agent, filler, filler, pigment, thickener, antioxidant are put into after mixing
Into reaction kettle, stirring is warming up to 80 degree, and is dehydrated under vacuo;
S3:By A and B component according to certain proportioning, it is poured into plastic mould, cures at room temperature, moulded after the demoulding
Glue.
According to the above aspect of the present invention, the present invention at least has the following advantages that:
The plastic cement race track of the present invention has manufacture craft simple, makes raw material and is easy to buy, has the excellent of low manufacture cost
Point, has broad application prospects.
Specific embodiment
Technical scheme is described in detail as follows with reference to embodiment.
Embodiment 1
A kind of plastic cement race track, according to parts by weight, the B component including 30-50 parts of component As and 50-70 parts,
The component A is by following weight parts into being grouped into:
40 parts of toluene di-isocyanate(TDI),
50 parts of polyether polyol;
The B component is by following weight parts into being grouped into:
Preparation method:
S1:The preparation of component A:Polyether polyol is added in reaction kettle, stirring is warming up to 90~120 DEG C, is taken off under vacuum
It is cooled to 50 DEG C after water, adds in toluene diisocyanate, slow reaction is to being down to room temperature after 85 DEG C;
S2:The preparation of B component:Trimethylolpropane, talcum powder, iron oxide, thickener, antioxidant GA-80 are mixed equal
It is put into after even in reaction kettle, stirring is warming up to 80 degree, and is dehydrated under vacuo;
S3:By A and B component according to certain proportioning, it is poured into plastic mould, cures at room temperature, moulded after the demoulding
Glue.
Embodiment 2
A kind of plastic cement race track, according to parts by weight, the B component including 30-50 parts of component As and 50-70 parts,
The component A is by following weight parts into being grouped into:
30 parts of toluene di-isocyanate(TDI),
40 parts of polyether polyol;
The B component is by following weight parts into being grouped into:
Preparation method:
S1:The preparation of component A:Polyether polyol is added in reaction kettle, stirring is warming up to 90~120 DEG C, is taken off under vacuum
It is cooled to 50 DEG C after water, adds in toluene diisocyanate, slow reaction is to being down to room temperature after 85 DEG C;
S2:The preparation of B component:Trimethylolpropane, talcum powder, iron oxide, thickener, antioxidant GA-80 are mixed equal
It is put into after even in reaction kettle, stirring is warming up to 80 degree, and is dehydrated under vacuo;
S3:By A and B component according to certain proportioning, it is poured into plastic mould, cures at room temperature, moulded after the demoulding
Glue.
Embodiment 3
A kind of plastic cement race track, according to parts by weight, the B component including 30-50 parts of component As and 50-70 parts,
The component A is by following weight parts into being grouped into:
35 parts of toluene di-isocyanate(TDI),
45 parts of polyether polyol;
The B component is by following weight parts into being grouped into:
Preparation method:
S1:The preparation of component A:Polyether polyol is added in reaction kettle, stirring is warming up to 90~120 DEG C, is taken off under vacuum
It is cooled to 50 DEG C after water, adds in toluene diisocyanate, slow reaction is to being down to room temperature after 85 DEG C;
S2:The preparation of B component:Trimethylolpropane, talcum powder, iron oxide, thickener, antioxidant GA-80 are mixed equal
It is put into after even in reaction kettle, stirring is warming up to 80 degree, and is dehydrated under vacuo;
S3:By A and B component according to certain proportioning, it is poured into plastic mould, cures at room temperature, moulded after the demoulding
Glue.
The above is only the preferred embodiment of the present invention, is not intended to limit the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (7)
1. a kind of plastic cement race track, which is characterized in that according to parts by weight, the B component including 30-50 parts of component As and 50-70 parts,
The component A is by following weight parts into being grouped into:
30-40 parts of toluene di-isocyanate(TDI),
40-50 parts of polyether polyol;
The B component is by following weight parts into being grouped into:
2. a kind of plastic cement race track according to claim 1, it is characterised in that:The crosslinking agent is trimethylolpropane.
3. a kind of plastic cement race track according to claim 1, it is characterised in that:The filler is talcum powder or kaolin.
4. a kind of plastic cement race track according to claim 1, it is characterised in that:The pigment is iron oxide.
5. a kind of plastic cement race track according to claim 1, it is characterised in that:The antioxidant is antioxidant GA-80.
6. a kind of plastic cement race track according to claim 1, it is characterised in that:The thickener is organobentonite HY-
708。
7. a kind of preparation method of plastic cement race track according to claim 1, it is characterised in that:
S1:The preparation of component A:Polyether polyol is added in reaction kettle, stirring is warming up to 90~120 DEG C, after dehydrated under vacuum
It is cooled to 50 DEG C, adds in toluene diisocyanate, slow reaction is to being down to room temperature after 85 DEG C;
S2:The preparation of B component:Crosslinking agent, filler, filler, pigment, thickener, antioxidant are put into instead after mixing
It answers in kettle, stirring is warming up to 80 degree, and is dehydrated under vacuo;
S3:By A and B component according to certain proportioning, it is poured into plastic mould, cures at room temperature, plastic cement is obtained after the demoulding.