CN108060598A - A kind of pulping agents used in paper for daily use processing - Google Patents
A kind of pulping agents used in paper for daily use processing Download PDFInfo
- Publication number
- CN108060598A CN108060598A CN201711309903.8A CN201711309903A CN108060598A CN 108060598 A CN108060598 A CN 108060598A CN 201711309903 A CN201711309903 A CN 201711309903A CN 108060598 A CN108060598 A CN 108060598A
- Authority
- CN
- China
- Prior art keywords
- accounts
- paper
- sodium
- parts
- daily use
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to pulp technology for making paper, disclose the pulping agents used in a kind of paper for daily use processing, contain digesting assistant, antifoaming agent, softening agents, preservative and antiseptic, process obtained digesting assistant, by the reaction for participating in removing lignin, increase the selectivity of reaction, capture the oxygen in cooking liquor, prevent damage of the air in high temperature and strongly basic medium to fiber in cooker, inhibit the degradation of cellulose, with other promoter effects, with very strong sequestering power, it is scattered, compatibilization ability, reduce surface tension, improve the whiteness and homogeneity of paper, use the pulping agents of the present invention, cooking schedule can be reduced, accelerate cooking speed, slurry yield can either be improved, the quality of paper can be significantly improved again.
Description
Technical field
The invention belongs to pulp technology for making paper, and in particular to the pulping agents used in a kind of paper for daily use processing.
Background technology
Paper is most common article in our daily lifes, no matter reads, reads newspaper or writes, draws a picture, and all obtains and paper connects
It touches.In industry, agricultural and national defense industry production, paper is also be unable to do without.Today, if without paper, that is just not imaginable.
Paper rap off, transmission of culture, develop science and technology and production in terms of, be a kind of strong instrument and material.Review is gone through
History, this important substance are exactly Ancient Times in China working people invention.Papermaking technology and compass, gunpowder, the art of printing are simultaneously known as me
The four inventions of state's Ancient Science and technolog are our peoples to the outstanding contribution made by World Science cultural development.
Paper for daily use is used mainly for people's life daily hygiene, so paper for daily use is usually in paper industry colleague's term,
It is one of paper kind indispensable in people's lives.Its shape has individual square, this to be shawl paper or face tissue,
Have and be rolled into roller barrel shape, it is this to be roll paper.They are usually manufactured by cotton pulp, wood pulp, straw pulp, secondary stock, the measured health of matter
Paper is all made of Original Pulp, its manufacturing process of paper with is similar, and simply requirement is manufactured into very thin extremely brittle weak, so
Purpose be that will rot when running into water, achieve the purpose that environmental protection.
The key of paper technology is pulping stage, and the physical and chemical performance for being related to paper for daily use is changed in getting well for paper pulp, and
Using for the pulping agents used in pulping stage in paper for daily use processing is particularly significant.
The content of the invention
The purpose of the present invention is being directed to the problem of existing, the pulping agents used in a kind of paper for daily use processing are provided,
Slurry yield can either be improved, and can significantly improve the quality of paper.
The present invention is achieved by the following technical solutions:
The pulping agents used in a kind of paper for daily use processing, consist of the following compositions in parts by weight:Digesting assistant 30-35
Part, 3.5-4.5 parts of antifoaming agent, 2.5-3.5 parts of softening agents, 2.0-2.5 parts of preservative, 1.5-2.0 parts of antiseptic, wherein the steaming
The preparation method for boiling auxiliary agent comprises the following steps:
(1)Prepare following raw material according to mass percent meter:2- hydroxy-anthraquiones account for 10-12%, sodium sulfite accounts for 4.5-5.5%, three
Polyphosphate sodium accounts for 3.5-4.0%, sulfamic acid sodium accounts for 2.0-3.0%, sodium sulfite accounts for 1.3-1.5%, sodium metasilicate accounts for 1.0-
1.2%th, sodium carboxymethylcellulose accounts for 0.4-0.6%, ethyl alcohol accounts for 15-20%, remaining as water;
(2)2- hydroxy-anthraquiones with water are mixed, under 200-300 revs/min of stirring, add sodium carboxymethylcellulose, ammonia successively
Base sodium sulfonate, sodium tripolyphosphate persistently stir 40-50 minutes, 60-70 DEG C are heated to after stirring, divide 3 times by sodium sulfite
It is added to sodium sulfite in heated solution, stirring and dissolving;
(3)Sodium metasilicate is added in ethanol solution, when curing 2-3 is small at 40-50 DEG C, is placed at 230-240 DEG C and calcines 10-
12 it is small when, product is added to step(3)In solution in, be heated to reflux at 100-110 DEG C 1-2 it is small when, obtain product
It is dry to carry out washing.
It is further described as to said program, the antifoaming agent contains following component according to mass percent meter:Turpentine oil
Account for 20-30%, dihydric alcohol accounts for 15-20%, triethylamine accounts for 10-15%, lauric acid accounts for 5-10%, remaining as silicone oil.
It is further described as to said program, the preservative contains following component according to mass percent meter:It is sub-
Methyl thiocyanates account for 30-35%, dithiocyanogen base formic acid accounts for 20-25%, chitosan accounts for 15-20%, remaining as nitropropane.
It is further described as to said program, the preparation method of the antiseptic is:By silver nitrate, copper sulphate, chlorine
Change zinc powder abrasive lapping to 200-240 mesh, add in the water of 3-4 times of volume, when at 600-700 revs/min plus stirring 2-3 is small, then
Add in mass fraction and account for the zeolite powder of mixing system 15-20%, continue to stir 1-2 it is small when, filtration drying to obtain the final product.
The present invention has the following advantages compared with prior art:In order to solve auxiliary agent of the existing paper for daily use in slurrying processing
Unreasonable problem is selected, the pulping agents used in being processed the present invention provides a kind of paper for daily use contain digesting assistant, disappear
Infusion, softening agents, preservative and antiseptic, the digesting assistant processed by participating in the reaction of removing lignin, increase reaction
Selectivity, capture the oxygen in cooking liquor, prevent damage of the air in high temperature and strongly basic medium to fiber in cooker,
Inhibit the degradation of cellulose, with other promoter effects, there is very strong sequestering power, scattered, compatibilization ability, reduce surface
Power improves the whiteness and homogeneity of paper, using the pulping agents of the present invention, can reduce cooking schedule, accelerate boiling
Speed can either improve slurry yield, and can significantly improve the quality of paper.
Specific embodiment
With reference to specific embodiment, the invention will be further described.
Embodiment 1
The pulping agents used in a kind of paper for daily use processing, consist of the following compositions in parts by weight:30 parts of digesting assistant,
3.5 parts of antifoaming agent, 2.5 parts of softening agents, 2.0 parts of preservative, 1.5 parts of antiseptic, wherein the preparation method bag of the digesting assistant
Include following steps:
(1)Prepare following raw material according to mass percent meter:2- hydroxy-anthraquiones account for 10%, sodium sulfite and account for 4.5%, sodium tripolyphosphate
It accounts for 3.5%, sulfamic acid sodium and accounts for 2.0%, sodium sulfite and account for 1.3%, sodium metasilicate and account for 1.0%, sodium carboxymethylcellulose and account for 0.4%, second
Alcohol accounts for 15%, remaining as water;
(2)2- hydroxy-anthraquiones with water are mixed, under 200 revs/min of stirrings, add sodium carboxymethylcellulose, amino sulphur successively
Sour sodium, sodium tripolyphosphate persistently stir 40 minutes, 60 DEG C are heated to after stirring, divide 3 times by sodium sulfite and two sulfurous acid
Sodium is added in heated solution, stirring and dissolving;
(3)Sodium metasilicate is added in ethanol solution, cure at 40 DEG C 2 it is small when, be placed at 230 DEG C calcining 10 it is small when, will produce
Object is added to step(3)In solution in, be heated to reflux at 100 DEG C 1 it is small when, obtaining product, to carry out washing dry.
It is further described as to said program, the antifoaming agent contains following component according to mass percent meter:Turpentine oil
It accounts for 20%, dihydric alcohol and accounts for 15%, triethylamine and account for 10%, lauric acid and account for 5%, remaining as silicone oil.
It is further described as to said program, the preservative contains following component according to mass percent meter:It is sub-
Methyl thiocyanates, which account for 30%, dithiocyanogen base formic acid and account for 20%, chitosan, accounts for 15%, remaining as nitropropane.
It is further described as to said program, the preparation method of the antiseptic is:By silver nitrate, copper sulphate, chlorine
Change zinc powder abrasive lapping to 200 mesh, add in the water of 3 times of volumes, when at 600 revs/min plus stirring 2 is small, then add in mass fraction
Account for the zeolite powder of mixing system 15%, continue stirring 1 it is small when, filtration drying to obtain the final product.
Embodiment 2
The pulping agents used in a kind of paper for daily use processing, consist of the following compositions in parts by weight:33 parts of digesting assistant,
4.0 parts of antifoaming agent, 3.0 parts of softening agents, 2.2 parts of preservative, 1.8 parts of antiseptic, wherein the preparation method bag of the digesting assistant
Include following steps:
(1)Prepare following raw material according to mass percent meter:2- hydroxy-anthraquiones account for 11%, sodium sulfite and account for 5.0%, sodium tripolyphosphate
It accounts for 3.8%, sulfamic acid sodium and accounts for 2.5%, sodium sulfite and account for 1.4%, sodium metasilicate and account for 1.1%, sodium carboxymethylcellulose and account for 0.5%, second
Alcohol accounts for 18%, remaining as water;
(2)2- hydroxy-anthraquiones with water are mixed, under 250 revs/min of stirrings, add sodium carboxymethylcellulose, amino sulphur successively
Sour sodium, sodium tripolyphosphate persistently stir 45 minutes, 65 DEG C are heated to after stirring, divide 3 times by sodium sulfite and two sulfurous acid
Sodium is added in heated solution, stirring and dissolving;
(3)Sodium metasilicate is added in ethanol solution, cure at 45 DEG C 2.5 it is small when, be placed at 235 DEG C calcining 11 it is small when, will
Product is added to step(3)In solution in, be heated to reflux at 105 DEG C 1.5 it is small when, obtaining product, to carry out washing dry i.e.
It can.
It is further described as to said program, the antifoaming agent contains following component according to mass percent meter:Turpentine oil
It accounts for 25%, dihydric alcohol and accounts for 18%, triethylamine and account for 12%, lauric acid and account for 8%, remaining as silicone oil.
It is further described as to said program, the preservative contains following component according to mass percent meter:It is sub-
Methyl thiocyanates, which account for 33%, dithiocyanogen base formic acid and account for 22%, chitosan, accounts for 18%, remaining as nitropropane.
It is further described as to said program, the preparation method of the antiseptic is:By silver nitrate, copper sulphate, chlorine
Change zinc powder abrasive lapping to 220 mesh, add in the water of 3.5 times of volumes, when at 650 revs/min plus stirring 2.5 is small, then add in quality
Fraction accounts for the zeolite powder of mixing system 18%, continue stirring 1.5 it is small when, filtration drying to obtain the final product.
Embodiment 3
The pulping agents used in a kind of paper for daily use processing, consist of the following compositions in parts by weight:Digesting assistant 35
Part, 4.5 parts of antifoaming agent, 3.5 parts of softening agents, 2.5 parts of preservative, 2.0 parts of antiseptic, wherein the preparation method of the digesting assistant
Comprise the following steps:
(1)Prepare following raw material according to mass percent meter:2- hydroxy-anthraquiones account for 12%, sodium sulfite and account for 5.5%, sodium tripolyphosphate
It accounts for 4.0%, sulfamic acid sodium and accounts for 3.0%, sodium sulfite and account for 1.5%, sodium metasilicate and account for 1.2%, sodium carboxymethylcellulose and account for 0.6%, second
Alcohol accounts for 20%, remaining as water;
(2)2- hydroxy-anthraquiones with water are mixed, under 300 revs/min of stirrings, add sodium carboxymethylcellulose, amino sulphur successively
Sour sodium, sodium tripolyphosphate persistently stir 50 minutes, 70 DEG C are heated to after stirring, divide 3 times by sodium sulfite and two sulfurous acid
Sodium is added in heated solution, stirring and dissolving;
(3)Sodium metasilicate is added in ethanol solution, cure at 50 DEG C 3 it is small when, be placed at 240 DEG C calcining 12 it is small when, will produce
Object is added to step(3)In solution in, be heated to reflux at 110 DEG C 2 it is small when, obtaining product, to carry out washing dry.
It is further described as to said program, the antifoaming agent contains following component according to mass percent meter:Turpentine oil
It accounts for 30%, dihydric alcohol and accounts for 20%, triethylamine and account for 15%, lauric acid and account for 10%, remaining as silicone oil.
It is further described as to said program, the preservative contains following component according to mass percent meter:It is sub-
Methyl thiocyanates, which account for 35%, dithiocyanogen base formic acid and account for 25%, chitosan, accounts for 20%, remaining as nitropropane.
It is further described as to said program, the preparation method of the antiseptic is:By silver nitrate, copper sulphate, chlorine
Change zinc powder abrasive lapping to 240 mesh, add in the water of 4 times of volumes, when at 700 revs/min plus stirring 3 is small, then add in mass fraction
Account for the zeolite powder of mixing system 20%, continue stirring 2 it is small when, filtration drying to obtain the final product.
Claims (4)
1. the pulping agents used in a kind of paper for daily use processing, which is characterized in that consist of the following compositions in parts by weight:
30-35 parts of digesting assistant, 3.5-4.5 parts of antifoaming agent, 2.5-3.5 parts of softening agents, 2.0-2.5 parts of preservative, antiseptic 1.5-2.0
Part, wherein the preparation method of the digesting assistant comprises the following steps:
(1)Prepare following raw material according to mass percent meter:2- hydroxy-anthraquiones account for 10-12%, sodium sulfite accounts for 4.5-5.5%, three
Polyphosphate sodium accounts for 3.5-4.0%, sulfamic acid sodium accounts for 2.0-3.0%, sodium sulfite accounts for 1.3-1.5%, sodium metasilicate accounts for 1.0-
1.2%th, sodium carboxymethylcellulose accounts for 0.4-0.6%, ethyl alcohol accounts for 15-20%, remaining as water;
(2)2- hydroxy-anthraquiones with water are mixed, under 200-300 revs/min of stirring, add sodium carboxymethylcellulose, ammonia successively
Base sodium sulfonate, sodium tripolyphosphate persistently stir 40-50 minutes, 60-70 DEG C are heated to after stirring, divide 3 times by sodium sulfite
It is added to sodium sulfite in heated solution, stirring and dissolving;
(3)Sodium metasilicate is added in ethanol solution, when curing 2-3 is small at 40-50 DEG C, is placed at 230-240 DEG C and calcines 10-
12 it is small when, product is added to step(3)In solution in, be heated to reflux at 100-110 DEG C 1-2 it is small when, obtain product
It is dry to carry out washing.
2. the pulping agents used as described in claim 1 in a kind of paper for daily use processing, which is characterized in that the antifoaming agent is pressed
Contain following component according to mass percent meter:Turpentine oil accounts for 20-30%, dihydric alcohol accounts for 15-20%, triethylamine accounts for 10-15%, bay
Acid accounts for 5-10%, remaining as silicone oil.
3. the pulping agents used as described in claim 1 in a kind of paper for daily use processing, which is characterized in that the preservative is pressed
Contain following component according to mass percent meter:Sulfonium methylide cyanate accounts for 30-35%, dithiocyanogen base formic acid accounts for 20-25%, shell gathers
Sugar accounts for 15-20%, remaining as nitropropane.
4. the pulping agents used as described in claim 1 in a kind of paper for daily use processing, which is characterized in that the antiseptic
Preparation method is:Silver nitrate, copper sulphate, zinc chloride powder are ground to 200-240 mesh, the water of 3-4 times of volume is added in, in 600-
At 700 revs/min plus stirring 2-3 small, the zeolite powder that mass fraction accounts for mixing system 15-20% is then added in, continues to stir
Mix 1-2 it is small when, filtration drying to obtain the final product.