CN108049167A - A kind of anti-chiseling down pin hole must close the production technology of coating fabric - Google Patents

A kind of anti-chiseling down pin hole must close the production technology of coating fabric Download PDF

Info

Publication number
CN108049167A
CN108049167A CN201711334484.3A CN201711334484A CN108049167A CN 108049167 A CN108049167 A CN 108049167A CN 201711334484 A CN201711334484 A CN 201711334484A CN 108049167 A CN108049167 A CN 108049167A
Authority
CN
China
Prior art keywords
pin hole
production technology
close
weights
chiseling down
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201711334484.3A
Other languages
Chinese (zh)
Inventor
秦峰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Suzhou Jingfei Textile Technology Co Ltd
Original Assignee
Suzhou Jingfei Textile Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Suzhou Jingfei Textile Technology Co Ltd filed Critical Suzhou Jingfei Textile Technology Co Ltd
Priority to CN201711334484.3A priority Critical patent/CN108049167A/en
Publication of CN108049167A publication Critical patent/CN108049167A/en
Pending legal-status Critical Current

Abstract

The present invention, which discloses a kind of anti-chiseling down pin hole, must close the production technology of coating fabric, belong to field of textile.The fabric of the production technology not only has excellent anti-chiseling down performance, while solves and suede is bored at pin hole, through the mode of padding（Pin hole, which returns, compiles auxiliary agent）Seam slippage it is bad, without courage eiderdown shell fabric it is not water-fastness the problem of, further improve the anti-suede effect of whole shell fabric.

Description

A kind of anti-chiseling down pin hole must close the production technology of coating fabric
Technical field
Patent of the present invention is related to the production technology of textile fabric, and more particularly to a kind of anti-chiseling down pin hole must close coating fabric Production technology.
Background technology
Today's society, filling class textile have become popular, down products (including down jackets, eiderdown quilt etc.) even more into For daily necessities indispensable in people's daily life, the features such as its soft comfortable, warmth retention property are good, light, is liked deeply by masses Love, but at present, after finished product is made in fabric, natural feather easily bores suede at sewing, not only affects whole appearance, but also drills out Staple disorderly fly to give people uncomfortable sensation.
The content of the invention
It is an object of the invention to overcome the deficiencies of the prior art and provide the lifes that a kind of anti-chiseling down pin hole must close coating fabric Production. art, by the process to fabric, fabric not only has excellent anti-chiseling down performance, while solves and bored at pin hole The problem of suede, while solve through the mode of padding（Pin hole, which returns, compiles auxiliary agent）Seam slippage it is bad, not water-fast without courage eiderdown shell fabric The problem of washing.
In view of the deficiencies of the prior art, the technical problems to be solved by the invention must close painting to provide a kind of anti-chiseling down pin hole The production technology of shell fabric, using following scheme：A kind of anti-chiseling down pin hole must close the production technology of coating fabric, press as flowed down Cheng Jinhang：400T nylon openpore → cold dome → open width washing → friendship refining → dye gigging dyeing → waterproof sizing → press polish（Base pressure）→ apply Layer → washing → finished product.
Further, the cold batching process, component parts by weights are：Alkali（30% soda ash）：160g/L-180g/L；Profit Humectant JFC：60g/L-68g/L；Chelating agent：25g/L-28g/L.
Preferably, the cold batching process, the time is for 24 hours, running speed is controlled in 20m/min.
Further, the open-width desizing, component parts by weights are：Aoxidize desizing agent 6g/L-8g/L；H2O2：2g/ L-4g/L；30% soda ash：100g/L.
Preferably, in the open-width desizing desizing, 65-70 DEG C of swelling bath temperature degree；Refine 85-90 DEG C of bath temperature degree；Go out Sink：75-80℃；Drying tube temperature：80-90℃；Speed is controlled in 50m/min.
Further, the friendship sweetening process, component parts by weights are：Soda ash：15-20g/L；Squama acid trisodium 1-2g/ L。
Further, the dyeing, component parts by weights are：Acid dyes：X；HAL：1g/L；Acidity dye Material：190（dwf).
Preferably, in the dyeing, fixation component parts by weights is：Color fixing agent NBS：180-190；HAC： 1g/L；Temperature is controlled at 80 DEG C；Speed is controlled in 20m/min.
Further, the waterproof sizing, temperature are controlled at 150-160 DEG C；Speed is controlled in 50m/min；
Wherein+4 overfeedings.
Further, the press polish（Base pressure）Technique, single-wheel single side is once；Select space nation machine；80 tons of pressure.
Preferably, the press polish（Base pressure）Technique, temperature are controlled at 120 DEG C；Speed is controlled in 25m/min.
Further, the coating process, component parts by weights are：FS-811:100%；Bridging agent：1.5-2g/L； Accelerating agent：3-5g/L；TOL：X.
Preferably, the coating process：Technique presses 1.6 ten thousand cps*0.3R blade type；Speed is controlled in 25m/min.
Further, the washing process, component parts by weights are：Softening agent：100%；.
Preferably, speed control is in 25m/min.
Beneficial to benefit：
Beneficial effects of the present invention：The present invention relates to the production technology that a kind of anti-chiseling down pin hole must close coating fabric, the production works The fabric 1 of skill not only has an excellent anti-chiseling down performance, and 2, solve the problems, such as to bore suede at pin hole, 3, solve through padding Mode（Pin hole, which returns, compiles auxiliary agent）Seam slippage it is bad the problem of.4th, without courage eiderdown shell fabric it is not water-fastness the problem of.5th, washing In technique, speed is controlled in 25m/min, and pin hole is in retracted state, further improves the anti-suede effect of whole shell fabric Fruit.
Specific embodiment
Clear, complete description is carried out to the technical solution in the embodiment of the present invention below, it is clear that described embodiment Only it is the part of the embodiment rather than whole embodiments of the present invention.Based on the embodiment of the present invention, ordinary skill people Member's all other embodiments obtained without making creative work, belong to the scope of protection of the invention.
Embodiment 1
A kind of anti-chiseling down pin hole must close the production technology of coating fabric, be carried out by following flow：400T nylon openpore → cold dome → open width washing → friendship refining → dye gigging dyeing → waterproof sizing → press polish（Base pressure）→ coating → washing → finished product.
Further, the cold batching process, component parts by weights are：Alkali（30% soda ash）：160g/L；Wetting agent JFC：60g/L；Chelating agent：25g/L.
Preferably, the cold batching process, the time is for 24 hours, running speed is controlled in 20m/min.
Further, the open-width desizing, component parts by weights are：Aoxidize desizing agent 6g/L；H2O2：2g/L；30% Soda ash：100g/L.
Preferably, in the open-width desizing desizing, swelling bath temperature degree 65；Refine bath temperature degree 85；Effluent trough：75；It dries Cylinder temperature：80；Speed is controlled in 50m/min.
Further, the friendship sweetening process, component parts by weights are：Soda ash：15g/L；Squama acid trisodium 1g/L.
Further, the dyeing, component parts by weights are：Acid dyes：X；HAL：1g/L；Acidity dye Material：190（dwf).
Preferably, in the dyeing, fixation component parts by weights is：Color fixing agent NBS：180；HAC：1g/L； Temperature is controlled at 80 DEG C；Speed is controlled in 20m/min.
Further, the waterproof sizing, temperature are controlled at 150 DEG C；Speed is controlled in 50m/min；
Wherein+4 overfeedings.
Further, the press polish（Base pressure）Technique, single-wheel single side is once；Select space nation machine；80 tons of pressure.
Preferably, the press polish（Base pressure）Technique, temperature are controlled at 120 DEG C；Speed is controlled in 25m/min.
Further, the coating process, component parts by weights are：FS-811:100%；Bridging agent：1.5g/L；Promote Into agent：3g/L；TOL：X.
Preferably, the coating process：Technique presses 1.6 ten thousand cps*0.3R blade type；Speed is controlled in 25m/min.
Further, the washing process, component parts by weights are：Softening agent：100%；.
Preferably, speed control is in 25m/min.
Embodiment 2
A kind of anti-chiseling down pin hole must close the production technology of coating fabric, be carried out by following flow：400T nylon openpore → cold dome → open width washing → friendship refining → dye gigging dyeing → waterproof sizing → press polish（Base pressure）→ coating → washing → finished product.
Further, the cold batching process, component parts by weights are：Alkali（30% soda ash）：170g/L；Wetting agent JFC：65g/L；Chelating agent：26g/L.
Preferably, the cold batching process, the time is for 24 hours, running speed is controlled in 20m/min.
Further, the open-width desizing, component parts by weights are：Aoxidize desizing agent 7g/L；H2O2：3g/L；30% Soda ash：100g/L.
Preferably, in the open-width desizing desizing, 68 DEG C of swelling bath temperature degree；Refine 85-90 DEG C of bath temperature degree；Water outlet Slot：78℃；Drying tube temperature：85℃；Speed is controlled in 50m/min.
Further, the friendship sweetening process, component parts by weights are：Soda ash：17g/L；Squama acid trisodium 1.5g/L.
Further, the dyeing, component parts by weights are：Acid dyes：X；HAL：1g/L；Acidity dye Material：190（dwf).
Preferably, in the dyeing, fixation component parts by weights is：Color fixing agent NBS：185；HAC：1g/L； Temperature is controlled at 80 DEG C；Speed is controlled in 20m/min.
Further, the waterproof sizing, temperature are controlled at 155 DEG C；Speed is controlled in 50m/min；
Wherein+4 overfeedings.
Further, the press polish（Base pressure）Technique, single-wheel single side is once；Select space nation machine；80 tons of pressure.
Preferably, the press polish（Base pressure）Technique, temperature are controlled at 120 DEG C；Speed is controlled in 25m/min.
Further, the coating process, component parts by weights are：FS-811:100%；Bridging agent：1.7g/L；Promote Into agent：4g/L；TOL：X.
Preferably, the coating process：Technique presses 1.6 ten thousand cps*0.3R blade type；Speed is controlled in 25m/min.
Further, the washing process, component parts by weights are：Softening agent：100%；.
Preferably, speed control is in 25m/min.
Embodiment 3：
A kind of anti-chiseling down pin hole must close the production technology of coating fabric, be carried out by following flow：400T nylon openpore → cold dome → open width washing → friendship refining → dye gigging dyeing → waterproof sizing → press polish（Base pressure）→ coating → washing → finished product.
Further, the cold batching process, component parts by weights are：Alkali（30% soda ash）：180g/L；Wetting agent JFC：68g/L；Chelating agent：28g/L.
Preferably, the cold batching process, the time is for 24 hours, running speed is controlled in 20m/min.
Further, the open-width desizing, component parts by weights are：Aoxidize desizing agent 8g/L；H2O2：4g/L；30% Soda ash：100g/L.
Preferably, in the open-width desizing desizing, swelling slot temperature 70 C；Refine 90 DEG C of bath temperature degree；Effluent trough：80 ℃；Drying tube temperature：90℃；Speed is controlled in 50m/min.
Further, the friendship sweetening process, component parts by weights are：Soda ash：20g/L；Squama acid trisodium 2g/L.
Further, the dyeing, component parts by weights are：Acid dyes：X；HAL：1g/L；Acidity dye Material：190（dwf).
Preferably, in the dyeing, fixation component parts by weights is：Color fixing agent NBS：190；HAC：1g/L； Temperature is controlled at 80 DEG C；Speed is controlled in 20m/min.
Further, the waterproof sizing, temperature are controlled at 160 DEG C；Speed is controlled in 50m/min；
Wherein+4 overfeedings.
Further, the press polish（Base pressure）Technique, single-wheel single side is once；Select space nation machine；80 tons of pressure.
Preferably, the press polish（Base pressure）Technique, temperature are controlled at 120 DEG C；Speed is controlled in 25m/min.
Further, the coating process, component parts by weights are：FS-811:100%；Bridging agent：2g/L；Promote Agent：3-5g/L；TOL：X.
Preferably, the coating process：Technique presses 1.6 ten thousand cps*0.3R blade type；Speed is controlled in 25m/min.
Further, the washing process, component parts by weights are：Softening agent：100%；.
Preferably, speed control is in 25m/min.
The present invention relates to the production technology that a kind of anti-chiseling down pin hole must close coating fabric, the fabric 1 of the production technology, not only With excellent anti-chiseling down performance, 2, solve the problems, such as to bore suede at pin hole, 3, solve through the mode of padding（Pin hole is returned to compile and helped Agent）Seam slippage it is bad the problem of.4th, without courage eiderdown shell fabric it is not water-fastness the problem of.5th, in washing process, speed control In 25m/min, pin hole is in retracted state, further improves the anti-suede effect of whole shell fabric.
The foregoing is merely the embodiment of the present invention, not thereby limit the scope of the invention, every to utilize this hair The equivalent structure or equivalent flow shift that bright description is made directly or indirectly is used in other relevant technology necks Domain is included within the scope of the present invention.

Claims (6)

1. a kind of anti-chiseling down pin hole must close the production technology of coating fabric, it is characterised in that the technological process of production by as follows into Row：400T nylon openpore → cold dome → open width washing → friendship refining → dye gigging dyeing → waterproof sizing → press polish（Base pressure）→ coating → Washing → finished product.
2. a kind of anti-chiseling down pin hole according to claim 1 must close the production technology of coating fabric, it is characterised in that described Cold batching process, component parts by weights are：Alkali（30% soda ash）：160g/L-180g/L；Wetting agent jfc：60g/L-68g/L； Chelating agent：25g/L-28g/L.
3. a kind of anti-chiseling down pin hole according to claim 2 must close the production technology of coating fabric, it is characterised in that described Open-width desizing, component parts by weights are：Aoxidize desizing agent 6g/L-8g/L；H2O2：2g/L-4g/L；30% soda ash：100g/ L。
4. a kind of anti-chiseling down pin hole according to claim 3 must close the production technology of coating fabric, it is characterised in that described Dyeing, component parts by weights are：Acid dyes：X；HAL：1g/L；Acid dyes：190（dwf).
A kind of anti-chiseling down pin hole according to claim 4 must close the production technology of coating fabric, it is characterised in that the pressure Light（Base pressure）Technique, single-wheel single side is once；Select space nation machine；80 tons of pressure.
5. a kind of anti-chiseling down pin hole according to claim 5 must close the production technology of coating fabric, it is characterised in that described Coating process, component parts by weights are：FS-811:100%；Bridging agent：1.5-2g/L；Accelerating agent：3-5g/L；TOL：X.
6. a kind of anti-chiseling down pin hole according to claim 6 must close the production technology of coating fabric, it is characterized in that described The washing process, component parts by weights are：Softening agent：100%；Speed is controlled in 25m/min.
CN201711334484.3A 2017-12-14 2017-12-14 A kind of anti-chiseling down pin hole must close the production technology of coating fabric Pending CN108049167A (en)