CN108035193A - A kind of production method for vacuum aluminum-coated body paper - Google Patents
A kind of production method for vacuum aluminum-coated body paper Download PDFInfo
- Publication number
- CN108035193A CN108035193A CN201810037744.9A CN201810037744A CN108035193A CN 108035193 A CN108035193 A CN 108035193A CN 201810037744 A CN201810037744 A CN 201810037744A CN 108035193 A CN108035193 A CN 108035193A
- Authority
- CN
- China
- Prior art keywords
- pulp
- production method
- paper
- coated body
- body paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of production method for vacuum aluminum-coated body paper, first calcium nitrate, disodium hydrogen phosphate are mixed after being dissolved in hardwood pulp, softwood pulp respectively, acted on by biomimetic mineralization, hydroxyapatite is generated inside wood pulp cellulose and in surface pore, then obtained modified pulp is mixed with filler, retention agent and sizing agent and manufactures paper with pulp to obtain uncoated paper, the coating fluid for being finally mixed to get styrene-acrylic emulsion, poly-vinyl alcohol solution and Ludox uniformly coats uncoated paper surface, and paper for vacuum aluminium plating is obtained after drying.Paper for vacuum aluminium plating produced by the invention has good profile pattern, gloss and printability, is suitable for packages printing field.
Description
Technical field
The present invention relates to stationery processing technique field, more particularly to a kind of production method for vacuum aluminum-coated body paper.
Background technology
Aluminized paper is mainly made of body paper, aluminium lamination and coating, and because glossiness and smoothness are good, pliability is good, sprayed-on Al layer jail
Degree is high, beautiful environmental protection, while has good printing performance and machining property, therefore is obtained widely in packaging material field
Using.Aluminized paper is divided into direct method by its production technology(Paper is aluminized)And transfer method(Film surface is aluminized), wherein direct method is logical
Cross and paper is placed directly within vacuum aluminum-plating machine aluminizes, due to open structure of the aluminium coated along paper fiber, surface is in trickle
Hole is coarse, and obtained aluminium film surface is coarse, and smoothness is poor, its flatness can not adapt to the printing of packaging, cause it to apply model
Enclose and be restricted.Direct method production aluminized paper quality influenced be subject to body paper performance it is very big, in order to improve the use of its aluminium film
Performance, is often first coated processing before aluminizing to paper surface, to improve paper surface planarization, brightness, but it is this
Lifting of the method to aluminized paper performance is limited.In order to further improve the performance of direct method production aluminized paper, can adapt to wrap
Fill the requirement of printing material, it is necessary to which the processing method of existing paper for vacuum aluminium plating is made improvements.
The content of the invention
The defects of the object of the invention is exactly to make up prior art, there is provided a kind of that there is good profile pattern, light
Damp degree, is suitable for the production method of the paper for vacuum aluminium plating of packages printing.
The present invention is achieved by the following technical solutions:
A kind of production method for vacuum aluminum-coated body paper, comprises the following steps:
(1)It will be equivalent in the calcium nitrate addition hardwood pulp of hardwood pulp weight 0.4-0.5% dissolve completely, will be equivalent to pin
The disodium hydrogen phosphate of leaf wood pulp weight 0.15-0.25% adds the leaf wood dissolved in softwood pulp and completely, then take same weight
Slurry and softwood pulp are uniformly mixed to obtain mixing slurry, and pH first is adjusted to 9-10 and in 35-37 DEG C of heat-insulation mineralizing 24-48h, then will
PH is adjusted to neutrality, obtains modified pulp;
(2)To step(1)Filler equivalent to modified pulp oven dry stock weight 10-30%, quite is added in obtained modified pulp
Retention agent in modified pulp oven dry stock weight 0.5-1% and the sizing equivalent to modified pulp oven dry stock weight 0.05-0.1%
Agent, by manufacturing paper with pulp, obtains uncoated paper;
(3)By styrene-acrylic emulsion, the poly-vinyl alcohol solution equivalent to styrene-acrylic emulsion weight 30-50% and equivalent to styrene-acrylic emulsion weight
The Ludox of 10-15% is mixed to get coating fluid, and coating fluid then is coated uniformly on step(2)Obtained uncoated paper table
Face, paper for vacuum aluminium plating is obtained after drying.
The concentration of the softwood pulp is 5-10%, and the concentration of hardwood pulp is 5-10%.
The filler is talcum powder or calcium carbonate.
The retention agent is cationic starch.
The sizing agent is alkyl ketene dimer.
The solid content of the styrene-acrylic emulsion is 40-50%.
The mass fraction of the poly-vinyl alcohol solution is 4-8%.
The solid content of the Ludox is 30-40%.
It is an advantage of the invention that:
The present invention first mixes calcium nitrate, disodium hydrogen phosphate after being dissolved in hardwood pulp, softwood pulp respectively, makes calcium ion
Infiltration is acted in wood pulp cellulose surface and internal void by biomimetic mineralization, inside wood pulp cellulose and surface pore
Interior generation hydroxyapatite, then obtained modified pulp is mixed with filler, retention agent and sizing agent manufacture paper with pulp to obtain it is uncoated
Paper, the coating fluid for being finally mixed to get styrene-acrylic emulsion, poly-vinyl alcohol solution and Ludox uniformly coat uncoated paper table
Face, paper for vacuum aluminium plating is obtained after drying.The present invention grows hydroxyl by the method for biomimetic mineralization in the hole of paper fibre
Apatite, with reference to the microcellular structure of the filling effect of the Ludox in coating fluid, effectively reduction paper surface, so as to improve paper
Planarization and glossiness, improve aluminize after aluminium film smoothness, the performance of aluminized paper is got a promotion.It is produced by the invention
Paper for vacuum aluminium plating has good profile pattern, gloss and printability, is suitable for packages printing field.
Embodiment
A kind of production method for vacuum aluminum-coated body paper, comprises the following steps:
(1)It will be equivalent in the calcium nitrate addition hardwood pulp of hardwood pulp weight 0.4% dissolve completely, will be equivalent to needlebush
The disodium hydrogen phosphate for starching weight 0.15% adds the hardwood pulp and needle for being dissolved in softwood pulp and completely, then taking same weight
Wood pulp is uniformly mixed to obtain mixing slurry, and pH first is adjusted to 9 and in 35 DEG C of heat-insulation mineralizing 24h, pH then is adjusted to neutrality, is changed
Property paper pulp;
(2)To step(1)In obtained modified pulp add equivalent to modified pulp oven dry stock weight 10% filler, equivalent to
The retention agent of modified pulp oven dry stock weight 0.5% and the sizing agent equivalent to modified pulp oven dry stock weight 0.05%, by copying
Make, obtain uncoated paper;
(3)By styrene-acrylic emulsion, the poly-vinyl alcohol solution equivalent to styrene-acrylic emulsion weight 30% and equivalent to styrene-acrylic emulsion weight 10%
Ludox be mixed to get coating fluid, coating fluid is then coated uniformly on step(2)Obtained uncoated paper surface, drying
After obtain paper for vacuum aluminium plating.
The concentration of the softwood pulp is 5%, and the concentration of hardwood pulp is 5%.
The filler is talcum powder.
The retention agent is cationic starch.
The sizing agent is alkyl ketene dimer.
The solid content of the styrene-acrylic emulsion is 40%.
The mass fraction of the poly-vinyl alcohol solution is 4%.
The solid content of the Ludox is 30%.
Claims (8)
1. a kind of production method for vacuum aluminum-coated body paper, it is characterised in that comprise the following steps:
(1)It will be equivalent in the calcium nitrate addition hardwood pulp of hardwood pulp weight 0.4-0.5% dissolve completely, will be equivalent to pin
The disodium hydrogen phosphate of leaf wood pulp weight 0.15-0.25% adds the leaf wood dissolved in softwood pulp and completely, then take same weight
Slurry and softwood pulp are uniformly mixed to obtain mixing slurry, and pH first is adjusted to 9-10 and in 35-37 DEG C of heat-insulation mineralizing 24-48h, then will
PH is adjusted to neutrality, obtains modified pulp;
(2)To step(1)Filler equivalent to modified pulp oven dry stock weight 10-30%, quite is added in obtained modified pulp
Retention agent in modified pulp oven dry stock weight 0.5-1% and the sizing equivalent to modified pulp oven dry stock weight 0.05-0.1%
Agent, by manufacturing paper with pulp, obtains uncoated paper;
(3)By styrene-acrylic emulsion, the poly-vinyl alcohol solution equivalent to styrene-acrylic emulsion weight 30-50% and equivalent to styrene-acrylic emulsion weight
The Ludox of 10-15% is mixed to get coating fluid, and coating fluid then is coated uniformly on step(2)Obtained uncoated paper table
Face, paper for vacuum aluminium plating is obtained after drying.
A kind of 2. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the needle
The concentration of wood pulp is 5-10%, and the concentration of hardwood pulp is 5-10%.
A kind of 3. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the filler
For talcum powder or calcium carbonate.
A kind of 4. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the retention
Agent is cationic starch.
A kind of 5. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the sizing
Agent is alkyl ketene dimer.
A kind of 6. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the phenylpropyl alcohol
The solid content of lotion is 40-50%.
A kind of 7. production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the poly- second
The mass fraction of enolate solution is 4-8%.
8. a kind of production method for vacuum aluminum-coated body paper according to claim 1, it is characterised in that the silicon is molten
The solid content of glue is 30-40%.