CN107981842B - A kind of laminating adhesive external member and its application method and application for transcribing dermatoglyph - Google Patents
A kind of laminating adhesive external member and its application method and application for transcribing dermatoglyph Download PDFInfo
- Publication number
- CN107981842B CN107981842B CN201711154728.XA CN201711154728A CN107981842B CN 107981842 B CN107981842 B CN 107981842B CN 201711154728 A CN201711154728 A CN 201711154728A CN 107981842 B CN107981842 B CN 107981842B
- Authority
- CN
- China
- Prior art keywords
- laminating adhesive
- skin
- external member
- frame
- dermatoglyph
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The laminating adhesive external member and its application method and application that the invention discloses a kind of for transcribing dermatoglyph, which is characterized in that including laminating adhesive frame, laminating adhesive, laminating adhesive patch, cubing, wherein being equipped with a hole among the laminating adhesive frame；The laminating adhesive is that dry solidification is formed after coating laminating adhesive composition on the skin；Laminating adhesive external member sampling is simple and convenient, quick, easy to operate, consumer can Self-operating, can be used for judging dermatoglyph, pore and sebum index, and pass through overall target assessment skin aging state.
Description
Technical field
The invention belongs to Skin Detection field more particularly to a kind of laminating adhesive external member for transcribing dermatoglyph and its
Application method and application.
Background technique
Dermatoglyph refers to the texture graphics that human skin surface occurs, also known as dermatoglyph, and the skin of the mankind is by epidermis and very
Skin is constituted.Papilla is raised to epidermis, forms many marshallings, parallel mammillary line, this line is also known as ridge line.Have on ridge line
The opening of many sweat glands.The ridge line of protrusion mutually forms the ditch of recess again.These concave-convex textures just constitute the skin of human body
Texture.The existing individual of the dermatoglyph of human body to the opposite sex, and have the stability of height.
With age, skin gradually aging, the depth down of dermatoglyph, therewith because of aging or overexposure or flesh
Wrinkle will occur in meat repeating motion.Dermatoglyph is transcribed by skin laminating adhesive, the pore, sebum and elasticity of skin can be observed
Etc. indexs, to assess the health status of skin.
Currently, dermatoglyph test method on the market is usually the skin for using silica gel laminating adhesive to prepare dermatoglyph sample or profession
Skin outline detector.Prepare that dermatoglyph sample is long there are drying time, observation index is few using silica gel laminating adhesive (as only observe texture,
And the sulci of skin depth) the disadvantages of；Dermatoglyph data are acquired by external image capture device using contoured skin detector
It is transmitted to computer to analyze it, the stable image capture device figure of profession is big, it has not been convenient to carry, although and mobile terminal
(smart phone) takes pictures conveniently, but for light, photographic quality equistability poor repeatability.
Therefore, it is necessary to a kind of quick and convenient, and the detection method of low-cost detection dermatoglyph, consumer stay at home
Dermatological specimens can be voluntarily acquired, by analyzing the dermatological specimens that consumer acquires, realize precisely amount skin.
Summary of the invention
In view of the problems of the existing technology, the object of the present invention is to provide a kind of for being transferred to the laminating adhesive set of dermatoglyph
Part and its application method and application.
To achieve the goals above, the invention adopts the following technical scheme:
It is a kind of for transcribing the laminating adhesive external member of dermatoglyph, including laminating adhesive frame, laminating adhesive, laminating adhesive patch, wherein the laminating adhesive frame
Centre is equipped with a hole.
Preferably, the laminating adhesive external member further includes cubing.
Preferably, a length of 10-30mm of the laminating adhesive frame, width 10-30mm, with a thickness of 0.1-0.5mm.
Preferably, the hole on the laminating adhesive frame is round or polygon.
It is further preferred that the size in hole is 5-25mm on the laminating adhesive frame.For example, when hole is round on laminating adhesive frame,
A diameter of 5-25mm；When hole is polygon on laminating adhesive frame, its side length is 5-25mm.
Preferably, the material of the laminating adhesive frame includes but is not limited to PE, PVC.It is further preferred that the one of the laminating adhesive frame
Side is equipped with adhesive layer, pastes laminating adhesive frame on the skin.Laminating adhesive frame is for passing through laminating adhesive when smearing laminating adhesive composition
Laminating adhesive composition is smeared in hole on frame, and it is excessive or too small can to play the laminating adhesive avoided the formation of, and influences the effect of microexamination,
And play the role of positioning.
Preferably, the laminating adhesive is to be formed by curing after coating laminating adhesive composition on the skin.
Preferably, the laminating adhesive composition is the substance that dermatoglyph can be transcribed after solidifying, such as pellosil.
It is further preferred that the laminating adhesive composition includes following components by weight percentage:
Film forming agent 6-35%,
Filler 1-20%,
Auxiliary agent 0.1-10%,
Surplus is solvent.
The laminating adhesive composition is made according to the following steps:
(1) film forming agent, filler are added sequentially in solvent, are warming up to 70-90 DEG C, stirred evenly；
(2) it is cooled to room temperature, auxiliary agent is added, stirs evenly.
Preferably, the auxiliary agent is selected from grease, thickener, emulsifier, anti-sensitizer and at least one of the preservatives.
Preferably, described for obtain the laminating adhesive composition of skin physiology state to include following group by weight percentage
Point:
Preferably, the film forming agent is selected from polyvinyl alcohol, polyvinylpyrrolidone, acrylic acid (ester) analog copolymer, propylene
Sour (ester) class/ethylhexy acrylate copolymer, styrene/acrylic (ester) analog copolymer, at least one in polyurethane -35
Kind.
Preferably, the filler is selected from titanium dioxide, kaolin, zinc oxide, talcum powder, diatomite, mica powder, silica, two
Silica, bamboo charcoal powder, silica flour, Attagel, bentonite, organobentonite, volcanic ash, hot spring soil, mud, atlapulgite, water
At least one of pyroxene powder, magnesium carbonate, montmorillonite.
Preferably, the thickener in cellulose, aluminium-magnesium silicate, xanthan gum, carbomer, carragheen at least one
Kind.
Preferably, the grease be selected from dormant oil, olive oil, jojoba oil, Sweet Almond Oil, caprylic/capric triglyceride,
Ethylhexyl palmitate, Nexbase 2004, isohexadecane, sunflower (HELIANTHUS ANNUUS) seed oil, palmitinic acid isopropyl
Ester, C12-15 alcohol benzoic ether, dimethyl silicone polymer, ring five dimethyl silicone polymer at least one.
Preferably, the emulsifier is selected from -3 stearate of polyglycereol, Natrulon H-10 oleate, -4 lauric acid of polyglycereol
Ester, monoglyceride, Tween-60, cocoyl Portugal glycosides, PEG-100 stearate, ceteareth -6, ceteareth -
25, at least one of Phosphoric acid monohexadecyl ester potassium.
Preferably, the anti-sensitizer is selected from least one of allantoin, dipotassium glycyrrhizinate, purslane extract.
Preferably, the preservative is selected from least one of Phenoxyethanol, imidazolidinyl urea, hydantoins.
Preferably, the solvent in water, glycerol, propylene glycol, butanediol, glycerin polyether -26, alcohol at least one
Kind.
The preparation method of the above-mentioned laminating adhesive composition for being used to obtain skin physiology state, comprising the following steps:
(1) film forming agent, thickener and filler are added sequentially in solvent, 70-90 DEG C are warming up in 10-20min, stirring
Uniformly, it is spare to obtain A phase by mixing speed 200-300r/min；
(2) grease, emulsifier mixing are warming up to 70-80 DEG C, it is spare obtains B phase；
(3) B is added to homogeneous 2 minutes in A phase, is cooled to 40-50 DEG C, it is equal that anti-sensitizer, preservative stirring and dissolving is added
It is even.
It is highly preferred that the laminating adhesive composition is paste.
Laminating adhesive is to be loaded in the form of laminating adhesive composition in a reservoir in the present invention, and the preferably described container is hose.Make
With when, by laminating adhesive composition coating on the skin, after dry solidification, formed laminating adhesive.
Preferably, the laminating adhesive composition coating thickness is 0.05-0.5mm.Laminating adhesive composition can not coat blocked up, can lead
Cause is difficult to drying, and then can not be transferred to laminating adhesive and stick；Laminating adhesive composition can not coat it is excessively thin, will lead to cannot understand transcription skin
Skin texture and sebum secretion situation cannot be shown completely.
Preferably, the laminating adhesive patch includes sequentially connected transparent thin film layer, adhesive layer and protective layer.
The safety of laminating adhesive patch, it is nontoxic, can directly contact skin.
It is further preferred that the 180 degree Bao of the adhesive layer is no more than 10N/25mm from Qiang Du≤5.0N/25mm；Bonding
The viscosity of layer is excessive, and pain is had when tearing, and damages skin；Viscosity is too small, can not paste and shift laminating adhesive, or even shifting
Make laminating adhesive damaged in journey.The material of the transparent thin film layer includes but is not limited to polyethylene, polypropylene, glassine paper, gathers to benzene two
Formic acid glycol ester, polyolefin etc..
It is further preferred that the protective layer is divided into 2 parts, laminating adhesive can be completely covered in middle section.It is further preferred that described
Protective layer is release paper, oilpaper etc..
Preferably, the cubing is equipped with a hole, wherein the hole in cubing is greater than or equal to the hole on laminating adhesive frame, with benefit
In the dermatoglyph that microexamination is transcribed into complete laminating adhesive.
It is further preferred that the long 65-90mm of the cubing, wide 15-40mm and with a thickness of 0.5-5mm.The cubing
On hole the middle and upper part of cubing is set.It is further preferred that the material of the cubing is PE, PC or PVC etc..
It is highly preferred that the tail portion of the cubing is designed to rounded corner (as shown in Figure 8), it can be used for smear overcoating and overlay on skin
On skin, avoid pollution.
The application method of the above-mentioned laminating adhesive external member for being used to transcribe dermatoglyph, comprising the following steps:
(1) it after cleaning skin, dries；
(2) laminating adhesive frame is pasted on the skin；
(3) laminating adhesive composition is smeared on the skin from the hole of laminating adhesive frame, and smeared uniform；
(4) after laminating adhesive of tearing frame, make laminating adhesive composition that original state be kept to stop 8-15min on skin, until being completely dried；
(5) laminating adhesive is taken to paste, laminating adhesive of tearing sticks the middle section of protective layer, by the adhesive layer of exposed portion and laminating adhesive pair
Standard is simultaneously pasted onto laminating adhesive, presses lightly on laminating adhesive patch, is pasted laminating adhesive with laminating adhesive and is fitted closely；
(5) it slowly tears from top to bottom and is stained with the laminating adhesive patch of laminating adhesive；
(6) laminating adhesive of tearing sticks remaining protective layer, is directed at laminating adhesive with the hole in cubing, and laminating adhesive patch is pasted onto cubing
On, amplify and is observed under 10-100 power microscope.
Preferably, make the intersection point on the left of laminating adhesive frame at middle position alignment horizontal distance canthus 5mm with nose.
It should be noted that avoid changing expression during laminating adhesive dry solidification, it otherwise will impact analysis result.
The application of above-mentioned laminating adhesive external member for transcribing dermatoglyph, and then assesses skin condition.
Sebum is secreted in sebaceous glands, and the lipid generated with horn cell and the sweat being secreted in sweat gland exist
Skin surface is combined into one layer of invisible film, is called natural cortex film or natural moisture preserving film.After the present invention passes through face cleaning
It dries moisture and coats laminating adhesive composition immediately, be coated the sebaceous glands meeting of the remaining unchanged sebum secreted at position, the place more than sebum secretion
Protrusion can be generated, so make relative to laminating adhesive at generate recess, to observe the circular hole fallen under the microscope.
Amplify evaluation criteria:
(1) amplify 10 times of observation dermatoglyphs: sulci of skin is obvious, and skin mound is arranged with neat shape (triangle), and full
Protuberance, illustrates that dermatoglyph situation is good, and skin is bright, surface is moistened has tension and elasticity, as shown in Fig. 5 (a)；Sulci of skin is shallow,
Unobvious, skin mound is misaligned, does not swell, flat situation, illustrates poor dermatoglyph, obscure, dry tack free, without tension
And elasticity, as shown in Fig. 5 (b)；
(2) in 50 times of microscopic observation pores: texture intersection point is small, unobvious, illustrates that pore is small, and quantity is few, and skin is smoothly thin
It is greasy, as shown in Fig. 6 (a)；Texture intersection point is more, obvious, illustrates that pore is big, quantity is more, then skin surface is uneven, does not open
Power is easy de- adornment, as shown in Fig. 6 (b)；
(3) 100 observation of amplification, laminating adhesive upper concave hole is more and big, illustrates that sebum secretion is vigorous, and pore is coarse, and skin is easily long
Acne, as shown in Fig. 7 (a)；Laminating adhesive upper concave hole moderate number, illustrates that sebum secretion is more moderate, and skin oil and fat is more balanced, such as schemes
Shown in 7 (b)；Laminating adhesive upper concave hole is few and small, illustrates that sebum secretion is few, dry skin, easy itch, or even has pain, such as Fig. 7 (c)
It is shown.
Beneficial effects of the present invention:
(1) the laminating adhesive external member sampling is simple and convenient, and quick, easy to operate, consumer can Self-operating；
(2) the laminating adhesive external member can be analyzed with common Stereo microscope, at low cost and easy to operate, adapt to market hair
The demand of exhibition；
(3) the laminating adhesive external member can be used for judging dermatoglyph, pore and sebum index, and assess skin by overall target
Skin aging state.
Detailed description of the invention
Fig. 1 is the top view of the laminating adhesive frame of laminating adhesive external member of the invention；
Fig. 2 is the structural schematic diagram of the laminating adhesive patch for being stained with laminating adhesive of laminating adhesive external member of the invention；
Fig. 3 is the schematic diagram of the protective layer of laminating adhesive external member of the invention；
Fig. 4 is the schematic diagram of the cubing of laminating adhesive external member of the invention；
Fig. 5 a-5b is the micrograph of dermatoglyph；
Fig. 6 a-6b is the micrograph of skin pore；
Fig. 7a-7c is the micrograph that skin sebum secretes situation；
Fig. 8 is the side view of cubing；
Fig. 9 a-9b is respectively that volunteer A and volunteer B uses the laminating adhesive micrograph before personalized product；
Figure 10 a-10b is respectively that volunteer A and volunteer B uses the laminating adhesive micrograph after personalized product.
Specific embodiment
Below in conjunction with attached drawing and example, detailed description of the preferred embodiments.It should be understood that this
Locate described specific embodiment to be merely to illustrate and explain the present invention, be not intended to restrict the invention.
Embodiment 1
It is a kind of for being transferred to the laminating adhesive composition of dermatoglyph, including following raw material by weight percentage:
Polyvinyl alcohol 8%, acrylic acid (ester) analog copolymer 15%, kaolin 13%, dormant oil 2%, cellulose 0.02% gather
- 3 stearate 2% of glycerol, anti-sensitizer 2%, preservative 0.3%, water surplus.
Preparation method: by polyvinyl alcohol, acrylic acid (ester) analog copolymer, cellulose, kaolin sequentially adds in water, stirs
78 DEG C are warming up to, homogeneous 2 minutes, is cooled to 45 DEG C, addition dormant oil, -3 stearate of polyglycereol, anti-sensitizer, preservative stirring are molten
Solution is uniform.
Embodiment 2
It is a kind of for being transferred to the laminating adhesive composition of dermatoglyph, including following raw material by weight percentage:
Polyvinyl alcohol 5%, styrene/acrylic (ester) analog copolymer 20%, titanium dioxide 20%, olive oil 4%, magnesium silicate
Aluminium 1%, -4 laurate 0.01% of polyglycereol, anti-sensitizer 4%, preservative 0.5%, water surplus.
Preparation method: polyvinyl alcohol, styrene/acrylic (ester) analog copolymer, aluminium-magnesium silicate, titanium dioxide are sequentially added
In water, stirring is warming up to 80 DEG C, homogeneous 2 minutes, is cooled to 45 DEG C, be added olive oil, -4 laurate of polyglycereol, anti-sensitizer,
Preservative stirring and dissolving is uniform.
Embodiment 3
It is a kind of for being transferred to the laminating adhesive composition of dermatoglyph, including following raw material by weight percentage:
Acrylic acid (ester) class/ethylhexy acrylate copolymer 15%, acrylic acid (ester) analog copolymer 1%, zinc oxide
1%, ethylhexyl palmitate 0.01%, xanthan gum 0.05%, -4 laurate 4% of polyglycereol, anti-sensitizer 0.1%, preservative
0.5%, glycerol surplus.
Preparation method: acrylic acid (ester) class/ethylhexy acrylate copolymer, acrylic acid (ester) analog copolymer, xanthan gum,
Zinc oxide sequentially adds in glycerol, and stirring is warming up to 75 DEG C, homogeneous 2 minutes, is cooled to 45 DEG C, be added ethylhexyl palmitate,
- 4 laurate of polyglycereol, anti-sensitizer, preservative stirring and dissolving are uniform.
Embodiment 4
It is a kind of for transcribing the laminating adhesive external member of dermatoglyph, including laminating adhesive frame 1, laminating adhesive 2, laminating adhesive patch 3, inspection referring to Fig. 1-3
Tool 4, wherein being equipped with one hole 11 among the laminating adhesive frame.Laminating adhesive frame 1 a length of 10mm, width 10mm, with a thickness of 0.1mm；
The side length in hole is 7mm on laminating adhesive frame；The material of the laminating adhesive frame is PVC；The side of the laminating adhesive frame is equipped with adhesive layer.It is described multiple
Film 2 is that the laminating adhesive composition of embodiment 2 coats on the skin, and dry solidification is formed after 15min, in hose；It is described
Laminating adhesive is with a thickness of 0.05mm.The laminating adhesive patch 3 includes sequentially connected transparent thin film layer 31, adhesive layer 32 and protective layer 33；Its
In, protective layer 33 is divided into 2 parts, and a part is middle section, and laminating adhesive can be completely covered.The 180 degree of the adhesive layer is shelled
It is 5N/25mm from intensity.The cubing 4 is equipped with a hole 41, wherein the hole in cubing is slightly larger than the hole 11 on laminating adhesive frame.Institute
State a length of 75mm of cubing 4, width 24mm, with a thickness of 1mm.
The application method of the above-mentioned laminating adhesive external member for being used to transcribe dermatoglyph, comprising the following steps:
(1) it after cleaning skin, dries；
(2) side that laminating adhesive frame is equipped with adhesive layer is pasted on the skin, keeps middle position alignment on the left of laminating adhesive frame horizontal
At canthus 5mm with the intersection point of nose；
(3) laminating adhesive composition is expressed in the hole on laminating adhesive frame, and is smeared uniformly, or taken with the tail portion of cubing
Appropriate laminating adhesive composition, uniformly coats laminating adhesive composition along the hole in laminating adhesive frame on the skin；
(4) after laminating adhesive of tearing frame, make laminating adhesive composition that original state be kept to stop 15min on skin, until being completely dried, formed multiple
Film；
(5) laminating adhesive patch 3 is taken, it is after the middle section of protective layer 33 is torn, the adhesive layer being exposed and laminating adhesive 2 is right
Standard, and be pasted onto laminating adhesive, after fitting closely the two, so that laminating adhesive is completely transferred to laminating adhesive and sticks；
(6) it slowly tears from top to bottom and is stained with the laminating adhesive patch of laminating adhesive；
(7) laminating adhesive of tearing sticks remaining protective layer, is directed at laminating adhesive with the hole in cubing, and laminating adhesive patch is pasted onto cubing
On, 10-100 times of amplification is observed.
Embodiment 5
It is a kind of for transcribing the laminating adhesive external member of dermatoglyph, including laminating adhesive frame 1, laminating adhesive 2, laminating adhesive patch 3, inspection referring to Fig. 1-3
Tool 4, wherein being equipped with a hole 11 among the laminating adhesive frame.Laminating adhesive frame 1 a length of 15mm, width 15mm, with a thickness of 0.5mm；It is multiple
The side length in hole is 11mm on film frame；The material of the laminating adhesive frame is PVC；The side of the laminating adhesive frame is equipped with adhesive layer.It is described multiple
Film 2 is that the laminating adhesive composition of embodiment 2 coats on the skin, and dry solidification is formed after 15min, in hose；It is described
Laminating adhesive is with a thickness of 0.1mm.The laminating adhesive patch 3 includes sequentially connected transparent thin film layer 31, adhesive layer 32 and protective layer 33；Its
In, protective layer 33 is divided into 2 parts, and a part is middle section, and laminating adhesive can be completely covered.The 180 degree of the adhesive layer is shelled
It is 6N/25mm from intensity.The cubing 4 is equipped with a hole 41, wherein the hole in cubing is slightly larger than the hole 11 on laminating adhesive frame.Institute
State a length of 76mm of cubing 4, width 25mm, with a thickness of 1.5mm.
The application method of the above-mentioned laminating adhesive external member for being used to transcribe dermatoglyph, comprising the following steps:
(1) it after cleaning skin, dries；
(2) side that laminating adhesive frame is equipped with adhesive layer is pasted on the skin, keeps middle position alignment on the left of laminating adhesive frame horizontal
At canthus 5mm with the intersection point of nose；
(3) laminating adhesive composition is expressed in the hole on laminating adhesive frame, and is smeared uniformly, or taken with the tail portion of cubing
Appropriate laminating adhesive composition, uniformly coats laminating adhesive composition along the hole in laminating adhesive frame on the skin；
(4) after laminating adhesive of tearing frame, make laminating adhesive composition that original state be kept to stop 15min on skin, until being completely dried, formed multiple
Film；
(5) laminating adhesive patch 3 is taken, it is after the middle section of protective layer 33 is torn, the adhesive layer being exposed and laminating adhesive 2 is right
Standard, and be pasted onto laminating adhesive, after fitting closely the two, so that laminating adhesive is completely transferred to laminating adhesive and sticks；
(6) it slowly tears from top to bottom and is stained with the laminating adhesive patch of laminating adhesive；
(7) laminating adhesive of tearing sticks remaining protective layer, is directed at laminating adhesive with the hole in cubing, and laminating adhesive patch is pasted onto cubing
On, 10-100 times of amplification is observed.
Embodiment 6
It is a kind of for transcribing the laminating adhesive external member of dermatoglyph, including laminating adhesive frame 1, laminating adhesive 2, laminating adhesive patch 3, inspection referring to Fig. 1-3
Tool 4, wherein being equipped with hole 11 among the laminating adhesive frame.Laminating adhesive frame 1 a length of 30mm, width 20mm, with a thickness of 0.25mm；Laminating adhesive
The side length in hole is 15mm on frame；The material of the laminating adhesive frame is PVC；The side of the laminating adhesive frame is equipped with adhesive layer.The laminating adhesive 2
Be embodiment 2 the coating of laminating adhesive composition on the skin, dry solidification is formed after 15min, in the hose；The laminating adhesive
With a thickness of 0.5mm.The laminating adhesive patch 3 includes sequentially connected transparent thin film layer 31, adhesive layer 32 and protective layer 33；Wherein, it protects
Sheath 33 is divided into 2 parts, and a part is middle section, and laminating adhesive can be completely covered.The 180 degree peel strength of the adhesive layer
For 8N/25mm.The cubing 4 is equipped with a hole 41, wherein the hole in cubing is slightly larger than the hole 11 on laminating adhesive frame.The cubing 4
A length of 77mm, width 26mm, with a thickness of 5mm.
The application method of the above-mentioned laminating adhesive external member for being used to transcribe dermatoglyph, comprising the following steps:
(1) it after cleaning skin, dries；
(2) side that laminating adhesive frame is equipped with adhesive layer is pasted on the skin, keeps middle position alignment on the left of laminating adhesive frame horizontal
At canthus 5mm with the intersection point of nose；
(3) laminating adhesive composition is expressed in the hole on laminating adhesive frame, and is smeared uniformly, or taken with the tail portion of cubing
Appropriate laminating adhesive composition, uniformly coats laminating adhesive composition along the hole in laminating adhesive frame on the skin；
(4) after laminating adhesive of tearing frame, make laminating adhesive composition that original state be kept to stop 15min on skin, until being completely dried, formed multiple
Film；
(5) laminating adhesive patch 3 is taken, it is after the middle section of protective layer 33 is torn, the adhesive layer being exposed and laminating adhesive 2 is right
Standard, and be pasted onto laminating adhesive, after fitting closely the two, so that laminating adhesive is completely transferred to laminating adhesive and sticks；
(6) it slowly tears from top to bottom and is stained with the laminating adhesive patch of laminating adhesive；
(7) laminating adhesive of tearing sticks remaining protective layer, is directed at laminating adhesive with the hole in cubing, and laminating adhesive patch is pasted onto cubing
On, 10-100 times of amplification is observed.
Embodiment 7
Volunteer 20 are chosen between 16-50 years old age, is sampled using 5 method of embodiment, amplifies 100 times of observations.Take it
In 2 volunteer's laminating adhesives, the laminating adhesive micrograph of volunteer A and volunteer B are respectively Fig. 9 a and Fig. 9 b:
If the laminating adhesive skin oil and fat test chart of Fig. 9 a and Fig. 9 b are it is found that the fat secretion of aspiration A is few, aspiration B grease is excessively
It is vigorous；It is directed to the skin preparation for external use of the personalized customization of volunteer A, mainly by being added to jojoba oil, hyalomitome
The moisture and oil of sour sodium enhancing skin；In addition, by adding ceramide skin water and oil balance can be made improving sebum film, increase
The self-protection function of strong skin.
It is directed to the skin preparation for external use of the personalized customization of volunteer B, mainly by adding PCA zinc oil-control composition,
Sebum secretion amount is adjusted, the activity of esterified ferment can be reduced, it is i.e. effective in the short time.In addition there are also potent moisture-keeping efficacy and suppressions
Bacterium performance.
Based on the analysis results, the following product of personalized customization is distinguished to aspiration A, volunteer B:
The formula of volunteer's A personalized customization product A is as shown in table 1:
The formula of 1 product A of table
The formula of volunteer's B personalized customization product B is as shown in table 2:
The formula of 2 product B of table
Volunteer A after B has cleaned face sooner or later daily, takes corresponding personalized customization product 5g, is respectively applied to face.
It is sampled after 28 days using 5 method of embodiment, amplifies 100 times of observations.The laminating adhesive microexamination of volunteer A and B is taken to see Figure 10 a respectively
With Figure 10 b.
By the laminating adhesive skin oil and fat test chart test result of Figure 10 a and Figure 10 b it is found that by using personalized customization skin
After skin external preparation, the skin oil and fat content of volunteer A increases, close to normally；The skin oil and fat of volunteer B, which is secreted, to be reduced, and is connect
It is close normal.
It can be seen that laminating adhesive external member of the invention, can accurately analyze the skin physiology state that obtains first, secondly it is suitble to use
It, can effectively needle by using the preparation for external application to skin of personalized customization in the skin preparation for external use of exploitation personalized customization
Personalized skin care is carried out to individual, reaches optimal skin effect.
The above are merely the preferred embodiment of the present invention, it is noted that for those of ordinary skill in the art,
Without departing from the concept of the premise of the invention, various modifications and improvements can be made, these belong to guarantor of the invention
Protect range.
Claims (8)
1. a kind of for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that pasted including laminating adhesive frame, laminating adhesive, laminating adhesive, wherein institute
It states and is equipped with a hole among laminating adhesive frame；The laminating adhesive is that dry solidification is formed after coating laminating adhesive composition on the skin；The laminating adhesive
Composition, including following components by weight percentage:
Film forming agent 6-35%,
Filler 1-20%,
Auxiliary agent 0.1-10%,
Surplus is solvent；
The auxiliary agent is selected from grease, thickener, emulsifier, anti-sensitizer and at least one of the preservatives.
2. according to claim 1 for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that the laminating adhesive external member is also
Including cubing.
3. according to claim 1 or 2 for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that the laminating adhesive frame
A length of 10-30mm, width 10-30mm, with a thickness of 0.05-0.5mm.
4. according to claim 1 or 2 for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that the laminating adhesive frame
On hole be round or polygon；The size in the hole is 5-25mm.
5. according to claim 1 or 2 for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that the laminating adhesive patch
Including sequentially connected transparent thin film layer, adhesive layer and protective layer；The protective layer is divided into 2 parts, and middle section can be complete
Cover laminating adhesive.
6. according to claim 2 for transcribing the laminating adhesive external member of dermatoglyph, which is characterized in that the cubing is equipped with
One hole, wherein the hole in cubing is greater than or equal to the hole on laminating adhesive frame.
7. the application method of laminating adhesive external member according to claim 1 to 6, which is characterized in that including following step
It is rapid:
(1) it after cleaning skin, dries；
(2) laminating adhesive frame is pasted on the skin；
(3) laminating adhesive composition is smeared on the skin by laminating adhesive frame, and smeared uniform；
(4) after laminating adhesive of tearing frame, make laminating adhesive composition that original state be kept to stop 8-15min on skin, until being completely dried；
(5) laminating adhesive is taken to paste, laminating adhesive of tearing sticks the middle section of protective layer, the adhesive layer of exposed portion is aligned simultaneously with laminating adhesive
It is pasted onto laminating adhesive, presses lightly on laminating adhesive patch, paste laminating adhesive with laminating adhesive and fit closely；
(6) it slowly tears from top to bottom and is stained with the laminating adhesive patch of laminating adhesive；
(7) laminating adhesive of tearing sticks remaining protective layer, is directed at laminating adhesive with the hole in cubing, and laminating adhesive patch is pasted onto cubing,
It is observed under amplification 10-100 power microscope.
8. the application of laminating adhesive external member according to claim 1 to 6, which is characterized in that for transcribing skin line
Reason, and then assess skin condition.