CN107938170A - A kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial - Google Patents
A kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial Download PDFInfo
- Publication number
- CN107938170A CN107938170A CN201711416525.3A CN201711416525A CN107938170A CN 107938170 A CN107938170 A CN 107938170A CN 201711416525 A CN201711416525 A CN 201711416525A CN 107938170 A CN107938170 A CN 107938170A
- Authority
- CN
- China
- Prior art keywords
- base fabric
- drying
- fabric
- group
- spun laced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial, spun laced fabric is composed of the following components and the percentage of each component is:1.67D*38 active charcoal viscose fiber:70%~90%;1.5D*38 anti-bacterial fibre:10%~30%;The 1.67D*38 activity charcoal viscose fiber and 1.5D*38 anti-bacterial fibres carry out spun lacing reinforcing after shredding, mixing, combing, lapping, superposition after drawing-off, form spun laced fabric;Activated carbon spun laced fabric that color inhales taste antibacterial is inhaled by the way that spun laced fabric is carried out cationization processing, makes spun laced fabric that there is soft, not fugitive color, crease-resistant wear-resisting;Its functional deficiency is separately directed to, by the combination of 1.67D*38 activity charcoal viscose fiber and 1.5D*38 antibacterials, it possessed extraordinary biocidal property, inhaled color, draw peculiar smell.
Description
Technical field
The present invention relates to a kind of spun laced fabric, more particularly to a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial.
Background technology
The research and development production recent two decades of the hydro-entangled non-woven fabric in China, no matter from kind, scale, quality, equipment
All increase significantly, substantially adapted to the demand of the current national economic development;The medicine that relate to of hydro-entangled non-woven fabric is defended
The ambits such as life, light industry, electronics, environmental protection, have promoted the development of domestic traditional chemical fibre and fibre in differentiation;In the same of development
When, market proposes such product the requirement of more highers;In order to meet biocidal property, suction color, suction of the client to spun laced fabric
Take the corresponding requirements of peculiar smell;Current product is because the additive amount in fiber cannot be excessive, although causing above-mentioned several functions all
Have but not comprehensively, if antibiotic property is not broad-spectrum antiseptic, also there are many deficiencies in terms of color is inhaled.
The content of the invention
The present invention mainly solves the technical problem present in the above-mentioned prior art, there is provided a kind of work inhaled color and inhale taste antibacterial
Property charcoal spun laced fabric.
The above-mentioned technical problem of the present invention is mainly what is be addressed by following technical proposals:One kind inhales color and inhales taste antibacterial
Activated carbon spun laced fabric, spun laced fabric is composed of the following components and the percentage of each component is:1.67D*38 active charcoal viscose fiber:
70%~90%;1.5D*38 anti-bacterial fibre:10%~30%;The 1.67D*38 activity charcoal viscose fiber and 1.5D*38 antibacterials
Fiber carries out spun lacing reinforcing after shredding, mixing, combing, lapping, superposition after drawing-off, form spun laced fabric.
Further, the spun laced fabric also needs to carry out cationization processing.
Further, the cationization processing is the cation cellulose ether water that spun laced fabric is immersed in 200-300g/L
Basic species are added in solution, are tuned into PH10-11,5-15 minutes in the cationics of temperature 42-48 degree.
Further, there are big carbon content active micron particles, activated carbon micron in the 1.67D*38 activity charcoal viscose fiber
Particle has the advantages that specific surface area is big, aperture is moderate, is evenly distributed, adsorption rate is fast, impurity is few;And manufactured in fiber
Because there is the presence of micron-sized powder in journey, in drafting process, fiber surface forms substantial amounts of micropore and microflute, make fiber
On the basis of the adsorption function of grain, the function of absorption is greatly improved, and adsorption effect reaches most in cation process
It is good.
Further, the stoving process for inhaling the activated carbon spun laced fabric that color inhales taste antibacterial is as follows:
A, treated cation:Base fabric passes through quetsch, under the action of the activated carbon and existing for fiber surface micropore and
Fully react and adsorb with cation under the action of microflute;
B, first group of drying:Base fabric by starching, which enters, dries bucket, and first group of drying unit is first passed around into after drying bucket,
First drying unit dries moist base fabric first;
C, second group of drying:Wetness by the base fabric dried first has declined, and then base fabric passes through second group of baking
Bucket, second group of drying unit dry moist base fabric again;
D, the 3rd group of drying:The wetness of base fabric by second of drying has declined, and then base fabric passes through the 3rd group
Bucket is dried, the 3rd group of drying unit dries moist base fabric again;
E, the 4th group of drying:The wetness for the base fabric dried three times by younger brother has declined, and then base fabric passes through the 4th group
Bucket is dried, the 4th group of drying unit dries moist base fabric again;
F, the 5th group of drying:Base fabric by the 4th drying passes through the 5th drying unit again, and the 5th drying unit is to tide
Wet basis cloth carries out the 5th group of drying, and the base fabric by the 5th drying is relatively dry;
G, the 6th group of insulation, the base fabric by the 5th group of drying enter the first attemperator, make to go out from the 5th drying unit
The base fabric come can keep certain temperature, make the further desiccation of base fabric;
H, the 7th group of insulation, enters the second attemperator by the base fabric of the first attemperator, makes from the first attemperator
Base fabric out can keep certain temperature, make the further desiccation of base fabric;
I, drying baker is gone out:From drying baker out, by the first deflecting roller and the second deflecting roller, base fabric changes transmission to base fabric
Direction, into cloth collector;
J, cloth is received:Cloth collector winds the base fabric dried, and completes the drying of base fabric.
K, film parcel is wound:The base fabric for having beaten volume is wrapped up with winding film, base fabric is kept certain temperature, soaking time
For 3-4 it is small when, so that base fabric can be dried thoroughly, and the treatment effect of cationization can be made more preferable.
Further, the first drying unit is equipped with 10 heating buckets in step B, and heating-up temperature is 130-135 DEG C, ventilation quantity
For 2 cubes of meter per seconds, make the rapid desiccation of moist base fabric.
Further, the second drying unit is equipped with 10 heating buckets in step C, and heating-up temperature is 125-130 DEG C, ventilation quantity
For 1.8 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 3rd drying unit is equipped with 10 heating buckets in step D, and heating-up temperature is 120-125 DEG C, ventilation quantity
For 1.6 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 4th drying unit is equipped with 10 heating buckets in step E, and heating-up temperature is 115-120 DEG C, ventilation quantity
For 1.4 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 5th drying unit is equipped with 10 heating buckets in step F, and heating-up temperature is 105-115 DEG C, ventilation quantity
For 1.0 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the temperature of the second attemperator in the first attemperator and step H in step G is 90 DEG C.
Further, step B, the pace of the moist base fabric in C, D, E and F is 28-30m/min, base fabric is existed
Upper enough time is stayed in the heating zone of drying unit, increases drying effect.
The beneficial fruit of the present invention is:The present invention makes spun laced fabric have hand by the way that spun laced fabric is carried out cationization processing
Sense is soft, not fugitive color, it is crease-resistant wear-resisting the features such as;Its functional deficiency is separately directed to, it is fine by 1.67D*38 activated carbons viscose glue
The combination of peacekeeping 1.5D*38 antibacterials, makes it possess extraordinary biocidal property, inhale color, draw peculiar smell.
Embodiment
Below by embodiment, the technical solutions of the present invention will be further described.
Embodiment:
A kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial, spun laced fabric is composed of the following components and the percentage of each component
For:1.67D*38 active charcoal viscose fiber:70%~90%;1.5D*38 anti-bacterial fibre:10%~30%;The 1.67D*38
Active charcoal viscose fiber and 1.5D*38 anti-bacterial fibre carries out spun lacing after shredding, mixing, combing, lapping, superposition, after drawing-off and adds
Gu form spun laced fabric.
Further, the spun laced fabric also needs to carry out cationization processing.
Further, the cationization processing is the cation cellulose ether water that spun laced fabric is immersed in 200-300g/L
Basic species are added in solution, are tuned into PH10-11,5-15 minutes in the cationics of temperature 42-48 degree
Further, there are big carbon content active micron particles, activated carbon micron in the 1.67D*38 activity charcoal viscose fiber
Particle has the advantages that specific surface area is big, aperture is moderate, is evenly distributed, adsorption rate is fast, impurity is few;And manufactured in fiber
Because there is the presence of micron-sized powder in journey, in drafting process, fiber surface forms substantial amounts of micropore and microflute, make fiber
On the basis of the adsorption function of grain, the function of absorption is greatly improved, and adsorption effect reaches most in cation process
It is good.
Further, the stoving process for inhaling the activated carbon spun laced fabric that color inhales taste antibacterial is as follows:
A, treated cation:Base fabric passes through quetsch, under the action of the activated carbon and existing for fiber surface micropore and
Fully react and adsorb with cation under the action of microflute;
B, first group of drying:Base fabric by starching, which enters, dries bucket, and first group of drying unit is first passed around into after drying bucket,
First drying unit dries moist base fabric first;
C, second group of drying:Wetness by the base fabric dried first has declined, and then base fabric passes through second group of baking
Bucket, second group of drying unit dry moist base fabric again;
D, the 3rd group of drying:The wetness of base fabric by second of drying has declined, and then base fabric passes through the 3rd group
Bucket is dried, the 3rd group of drying unit dries moist base fabric again;
E, the 4th group of drying:The wetness for the base fabric dried three times by younger brother has declined, and then base fabric passes through the 4th group
Bucket is dried, the 4th group of drying unit dries moist base fabric again;
F, the 5th group of drying:Base fabric by the 4th drying passes through the 5th drying unit again, and the 5th drying unit is to tide
Wet basis cloth carries out the 5th group of drying, and the base fabric by the 5th drying is relatively dry;
G, the 6th group of insulation, the base fabric by the 5th group of drying enter the first attemperator, make to go out from the 5th drying unit
The base fabric come can keep certain temperature, make the further desiccation of base fabric;
H, the 7th group of insulation, enters the second attemperator by the base fabric of the first attemperator, makes from the first attemperator
Base fabric out can keep certain temperature, make the further desiccation of base fabric;
I, drying baker is gone out:From drying baker out, by the first deflecting roller and the second deflecting roller, base fabric changes transmission to base fabric
Direction, into cloth collector;
J, cloth is received:Cloth collector winds the base fabric dried, and completes the drying of base fabric.
K, film parcel is wound:The base fabric for having beaten volume is wrapped up with winding film, base fabric is kept certain temperature, soaking time
For 3-4 it is small when, so that base fabric can be dried thoroughly, and the treatment effect of cationization can be made more preferable.
Further, the first drying unit is equipped with 10 heating buckets in step B, and heating-up temperature is 130-135 DEG C, ventilation quantity
For 2 cubes of meter per seconds, make the rapid desiccation of moist base fabric.
Further, the second drying unit is equipped with 10 heating buckets in step C, and heating-up temperature is 125-130 DEG C, ventilation quantity
For 1.8 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 3rd drying unit is equipped with 10 heating buckets in step D, and heating-up temperature is 120-125 DEG C, ventilation quantity
For 1.6 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 4th drying unit is equipped with 10 heating buckets in step E, and heating-up temperature is 115-120 DEG C, ventilation quantity
For 1.4 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the 5th drying unit is equipped with 10 heating buckets in step F, and heating-up temperature is 105-115 DEG C, ventilation quantity
For 1.0 cubes of meter per seconds, make the further desiccation of moist base fabric.
Further, the temperature of the second attemperator in the first attemperator and step H in step G is 90 DEG C.
Further, step B, the pace of the moist base fabric in C, D, E and F is 28-30m/min, base fabric is existed
Upper enough time is stayed in the heating zone of drying unit, increases drying effect.
Finally it is pointed out that above example is only the more representational example of the present invention.It is clear that the invention is not restricted to
Above-described embodiment, can also there is many deformations.Any letter that every technical spirit according to the present invention makees above example
Single modification, equivalent variations and modification, are considered as belonging to protection scope of the present invention.
Claims (10)
1. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial, it is characterised in that the spun laced fabric is composed of the following components and each group
Point percentage be:1.67D*38 active charcoal viscose fiber:70%~90%;1.5D*38 anti-bacterial fibre:10%~30%;Institute
1.67D*38 activity charcoal viscose fiber and 1.5D*38 anti-bacterial fibres are stated after shredding, mixing, combing, lapping, superposition, after drawing-off
Spun lacing reinforcing is carried out, forms spun laced fabric.
2. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 1, it is characterised in that the spun laced fabric is also
Need to carry out cationization processing.
A kind of 3. activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 2, it is characterised in that the cationization
Processing is to be immersed in spun laced fabric in the cation cellulose ether aqueous solution of 200-300g/L to add basic species, is tuned into PH10-11,
5-15 minutes in the cationics of temperature 42-48 degree.
A kind of 4. any activated carbon spun laced fabrics inhaled color and inhale taste antibacterial of claim 1-3, it is characterised in that the spun laced fabric
Stoving process it is as follows:
A, treated cation:Base fabric passes through quetsch, micropore and microflute under the action of activated carbon and existing for fiber surface
Under the action of fully react and adsorb with cation;
B, first group of drying:Base fabric by starching, which enters, dries bucket, and first group of drying unit is first passed around after bucket into drying, and first
Drying unit dries moist base fabric first;
C, second group of drying:Wetness by the base fabric dried first has declined, and then base fabric passes through second group of baking bucket, the
Two groups of drying units dry moist base fabric again;
D, the 3rd group of drying:The wetness of base fabric by second of drying has declined, and then base fabric passes through the 3rd group of baking bucket,
3rd group of drying unit dries moist base fabric again;
E, the 4th group of drying:The wetness for the base fabric dried three times by younger brother has declined, and then base fabric passes through the 4th group of baking bucket,
4th group of drying unit dries moist base fabric again;
F, the 5th group of drying:Base fabric by the 4th drying passes through the 5th drying unit again, and the 5th drying unit is to moist base
Cloth carries out the 5th group of drying, and the base fabric by the 5th drying is relatively dry;
G, the 6th group of insulation, the base fabric by the 5th group of drying enter the first attemperator, make what is come out from the 5th drying unit
Base fabric can keep certain temperature, make the further desiccation of base fabric;
H, the 7th group of insulation, enters the second attemperator by the base fabric of the first attemperator, makes to come out from the first attemperator
Base fabric can keep certain temperature, make the further desiccation of base fabric;
I, drying baker is gone out:From drying baker out, by the first deflecting roller and the second deflecting roller, base fabric changes transmission side to base fabric
To into cloth collector;
J, cloth is received:Cloth collector winds the base fabric dried, and completes the drying of base fabric.
K, film parcel is wound:The base fabric for having beaten volume is wrapped up with winding film, base fabric is kept certain temperature, soaking time 3-
4 it is small when, so that base fabric can be dried thoroughly, and the treatment effect of cationization can be made more preferable.
5. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the in the step B
One drying unit is equipped with 10 heating buckets, and heating-up temperature is 130-135 DEG C, and ventilation quantity is 2 cubes of meter per seconds.
6. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the in the step C
Two drying units are equipped with 10 heating buckets, and heating-up temperature is 125-130 DEG C, and ventilation quantity is 1.8 cubes of meter per seconds.
7. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the in the step D
Three drying units are equipped with 10 heating buckets, and heating-up temperature is 120-125 DEG C, and ventilation quantity is 1.6 cubes of meter per seconds.
8. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the in the step E
Four drying units are equipped with 10 heating buckets, and heating-up temperature is 115-120 DEG C, and ventilation quantity is 1.4 cubes of meter per seconds.
9. a kind of activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the in the step F
Five drying units are equipped with 10 heating buckets, and heating-up temperature is 105-115 DEG C, and ventilation quantity is 1.0 cubes of meter per seconds.
A kind of 10. activated carbon spun laced fabric inhaled color and inhale taste antibacterial according to claim 4, it is characterised in that the step B, C,
D, the pace of the moist base fabric in E and F is 28-30m/min.