CN106120150A - A kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof - Google Patents
A kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof Download PDFInfo
- Publication number
- CN106120150A CN106120150A CN201610709449.4A CN201610709449A CN106120150A CN 106120150 A CN106120150 A CN 106120150A CN 201610709449 A CN201610709449 A CN 201610709449A CN 106120150 A CN106120150 A CN 106120150A
- Authority
- CN
- China
- Prior art keywords
- woven fabrics
- powder
- bamboo filament
- filament fibre
- oxygen ion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof, it is characterised in that be made up of the raw material of following weight portion: bamboo filament fibre powder 37, nano-tourmaline powder 48, PAMAM solution 49, polylactic acid 5 10, polyethylene glycol 200 12, activated carbon 35, Mint Essence 48, sodium periodate solution 10 15, isotactic polypropylene 50 70, kieselguhr 36, dodecyl sodium sulfate 12, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；In non-woven fabrics, add nano-tourmaline powder, the effect of continuous releasing negative oxygen ion can be reached, when being applied to clothing liner, there is calmness, analgesia, antitussive, antipruritic, increasing appetite, the effect of blood pressure lowering, Mint Essence of arranging in pairs or groups, people's spirit and QI cleaning, resisting fatigue can be made.
Description
Technical field
The present invention relates to a kind of non-woven fabrics and preparation method thereof, be specifically related to a kind of can continuously releasing negative oxygen ion containing bamboo
Silk fiber non-woven fabrics and preparation method thereof.
Background technology
Non-woven fabrics is a kind of non-weaving cloth, and it is to directly utilize high polymer section, chopped fiber or long filament fiber is passed through gas
Stream or machinery become net, are then passed through spun lacing, acupuncture, or hot rolling and reinforce, and eventually pass the cloth without braiding that Final finishing is formed.Tool
Having softness, the ventilative and tencel goods of planar structure, advantage is not produce Soft flocks, tough, durable, silkiness is soft, and
And the sensation of also cotton, have been widely used for garment industry.Along with people's constantly chasing after " ecological, healthy, environmental protection " theory
Ask, together with textile has been closely connected with fashion, health environment-friendly, what this fashion reflected the is mankind to the love of self and
Concern to living environment, simultaneously because the popularization that ecological textile concept is in the world, and people pursue natural relaxing
Suitable, back to nature, the psychology recovered one's original simplicity, Green Textiles has become as the main trend of following textile development.
Jiang Yinggang, in " containing the preparation of bamboo charcoal powder liner cloth and Study on adsorption properties ", utilizes bamboo charcoal powder and non-weaving cloth, logical
Cross coating, the method such as pad, make multiple containing bamboo charcoal powder nonwoven interlining.But, there is also and be not provided that negative oxygen ion, no
Refrigerant fragrance of refreshing oneself can be discharged and wait healthy, the weak point of resisting fatigue of refreshing oneself being conducive to people.
Summary of the invention
Comprehensive above consideration, the present invention provides a kind of non-woven fabrics and formula thereof, it is therefore intended that solve when non-woven fabrics is applied
When automotive trim, it is impossible to releasing negative oxygen ion continuously, it is provided that the preferably defect of interior space.
For achieving the above object, technical scheme is as follows:
A kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics, it is characterised in that by the raw material system of following weight portion
Become:
Bamboo filament fibre powder 3-7, nano-tourmaline powder 4-8, PAMAM solution 4-9, polylactic acid 5-10, polyethylene glycol 200 1-2, live
Property charcoal 3-5, Mint Essence 4-8, sodium periodate solution 10-15, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfonate
Sodium 1-2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
Described a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof, its feature exists
In, it is made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake
Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, after being uniformly dispersed
Proceed to stand under vacuumized conditions 3-5h, obtain being loaded with the activated carbon powder of Mint Essence by centrifugal, dry, milled processed；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake
Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85
DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained the load activated carbon powder of Mint Essence, step c gained
PAMAM grafting bamboo filament fibre powder adds screw extruder to and melts, then prepares nonwoven after spinning, drawing-off, one-tenth net, hot rolling
Cloth；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into supersonic oscillations
Ultrasonic 5-10min in device, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence is used padder mangle, soaked again
Not yet, then with after padder mangle, put into baker, bakee 2-5min, take out.
Described a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof, its feature exists
In, curer stoving temperature described in step b is 70-110 DEG C.
The invention has the beneficial effects as follows: in non-woven fabrics, add nano-tourmaline powder, can reach to discharge continuously negative oxygen from
The effect of son, when being applied to clothing liner, has calmness, analgesia, antitussive, antipruritic, increasing appetite, the effect of blood pressure lowering, Herba Menthae of arranging in pairs or groups
Essence, can make people's spirit and QI cleaning, resisting fatigue；Utilize polylactic acid to wrap up nano-tourmaline powder, not only prevent nanometer electric
Stone powder broken and coming off, and the appearance promoting tourmaline powder and polypropylene substrate closes and dispersion, and polylactic acid has excellent simultaneously
Good breathability, oxygen permeability, and antibacterial and anti-mildew characteristic, improve the fungus resistance of non-woven fabrics, extends service life；By activity
Charcoal loads Mint Essence, adds loading and the air contact area of Mint Essence, reaches more lasting releasing effect,
It is simultaneously introduced the characterization of adsorption of activated carbon, increases the function of non-woven fabrics absorption abnormal flavour；Bamboo filament fibre after sodium periodate oxidation,
The oh group on its surface is oxidized to aldehyde radical even carboxyl, crosslinks reaction with the amino on PAMAM surface, thus will
PAMAM is grafted on bamboo filament fibre, is possible not only to make bamboo filament fibre more soft fluffy, and enhance bamboo filament fibre with etc.
The fusion of isotactic polypropylene substrate.
Detailed description of the invention
Below in conjunction with embodiment, the detailed description of the invention of the present invention is further described.
Embodiment
A kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics, it is characterised in that former by following weight portion
Material is made:
Bamboo filament fibre powder 7, nano-tourmaline powder 8, PAMAM solution 9, polylactic acid 10, polyethylene glycol 200 2, activated carbon 5, Herba Menthae
Essence 8, sodium periodate solution 15, isotactic polypropylene 70, kieselguhr 6, dodecyl sodium sulfate 2, Carboxymethyl cellulose sodium is appropriate,
Water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
Described a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof, its feature exists
In, it is made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake
Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, after being uniformly dispersed
Proceed to stand under vacuumized conditions 3-5h, obtain being loaded with the activated carbon powder of Mint Essence by centrifugal, dry, milled processed；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake
Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85
DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained the load activated carbon powder of Mint Essence, step c gained
PAMAM grafting bamboo filament fibre powder adds screw extruder to and melts, then prepares nonwoven after spinning, drawing-off, one-tenth net, hot rolling
Cloth；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into supersonic oscillations
Ultrasonic 5-10min in device, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence is used padder mangle, soaked again
Not yet, then with after padder mangle, put into baker, bakee 2-5min, take out.
Described a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation method thereof, its feature exists
In, curer stoving temperature described in step b is 70-110 DEG C.
The technical parameter of the present invention is:
Formaldehyde absorbing rate >=11.09% of Unit Weight non-woven fabrics, benzene adsorption rate >=14.83%, TVOC adsorption rate >=13.42%.
Claims (3)
1. one kind can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics, it is characterised in that by the raw material of following weight portion
Make:
Bamboo filament fibre powder 3-7, nano-tourmaline powder 4-8, PAMAM solution 4-9, polylactic acid 5-10, polyethylene glycol 200 1-2, live
Property charcoal 3-5, Mint Essence 4-8, sodium periodate solution 10-15, isotactic polypropylene 50-70, kieselguhr 3-6, dodecyl sodium sulfonate
Sodium 1-2, Carboxymethyl cellulose sodium is appropriate, and water is appropriate；
The concentration of described sodium periodate solution is 0.1-10g/L；PAMAM solution concentration is 1-10g/L.
The most according to claim 1 a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation side thereof
Method, it is characterised in that be made up of following steps:
A., at 150-200 DEG C, nano-tourmaline powder is joined in polylactic acid, adds polyethylene glycol 200, stir,
Make nano-tourmaline powder evenly spread in polylactic acid, and make polylactic acid be wrapped in nano-tourmaline powder surface, form microsphere, mistake
Filter and dry；
B. activated carbon is added in water and be uniformly dispersed, be then added to Mint Essence, continue dispersion, after being uniformly dispersed
Proceed to stand under vacuumized conditions 3-5h, obtain being loaded with the activated carbon powder of Mint Essence by centrifugal, dry, milled processed；
C. bamboo filament fibre powder being placed in lucifuge oxidation reaction 3-5h in sodium periodate solution, reaction temperature is 40-110 DEG C, mistake
Filter, wash, dry, obtain aoxidizing bamboo fibre；Oxidation bamboo fibre is immersed in 3-6h in PAMAM solution, reaction temperature 25-85
DEG C, filtering drying also grinds, and obtains PAMAM and is grafted bamboo filament fibre powder；
D. by isotactic polypropylene, step a thus obtained microsphere, step b gained the load activated carbon powder of Mint Essence, step c gained
PAMAM grafting bamboo filament fibre powder adds screw extruder to and melts, then prepares nonwoven after spinning, drawing-off, one-tenth net, hot rolling
Cloth；
E. kieselguhr is added to the water, is stirring evenly and then adding into dodecyl sodium sulfate, be stirring evenly and then adding into methylol fine
Dimension element sodium, adjusts modest viscosity, prepares serosity；Step d gained non-woven fabrics is totally submerged in serosity, and puts into supersonic oscillations
Ultrasonic 5-10min in device, takes out, the method using " two leachings two are rolled ", and i.e. fully submergence is used padder mangle, soaked again
Not yet, then with after padder mangle, put into baker, bakee 2-5min, take out.
The most according to claim 2 a kind of can continuously releasing negative oxygen ion containing bamboo filament fibre non-woven fabrics and preparation side thereof
Method, it is characterised in that curer stoving temperature described in step b is 70-110 DEG C.