CN107930603A - A kind of dried flower protects drier used and preparation method thereof in prepared by color drying plate - Google Patents
A kind of dried flower protects drier used and preparation method thereof in prepared by color drying plate Download PDFInfo
- Publication number
- CN107930603A CN107930603A CN201711165182.8A CN201711165182A CN107930603A CN 107930603 A CN107930603 A CN 107930603A CN 201711165182 A CN201711165182 A CN 201711165182A CN 107930603 A CN107930603 A CN 107930603A
- Authority
- CN
- China
- Prior art keywords
- parts
- drier
- drying plate
- prepared
- dried flower
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of dried flower protects drier used and preparation method thereof in prepared by color drying plate, drier include 50 65 parts of iron powder, 18 parts of bamboo charcoal, 18 parts of sodium chloride, 15 parts of bentonite, 10 30 parts of quartz sand, 10 25 parts of acid solution, 17 22 parts of calcium sulfate, 39 parts of barium monoxide, 19 26 parts of sodium hydroxide, auxiliary material be 15 parts, 50 90 parts of silica, 10 50 parts of high molecule plastic.Drying plate is that paper pulp and drier are merged to a kind of cardboard produced, the component in drying plate using special drying plate at high temperature, so that pigment is stablized, and acid solution spends the acid-base value of inside as reducing agent, adjustment so that recovers original color in acid inside petal.
Description
Technical field:
The present invention relates to dried flower color-protection technique, and in particular to a kind of dried flower protect in prepared by color drying plate drier used and its
Preparation method.
Background technology:
Dry flower is to view and admire colored material by what is formed after either physically or chemically handling using natural plants material.In recent years
Due to its unique shape and graceful bearing, the characteristics of lasting is preserved, is increasingly subject to liking for people.
Also have with the improvement of people's living standards, the requirement to landscaping, interior decoration with the development of science and technology
Improved, people increasingly yearn for nature ornaments.Dried flower is got over due to becoming current with lasting ornamental value and unique glamour
Carry out more welcome ornament.It can not only beautify the environment, and make one to be in a cheerful frame of mind, while can also provide original for embossing works
Material.Embossing art is also increasingly popularized, and embossing art match is also held in the whole world, it is seen that the prospect of the international market of dried flower
It is bright and clear.
And discoloration easily occurs in the drying process for China rose, except external factor shadows such as exterior temperature humidities and pressure
Outside ringing, petal internal environmental factor is primarily due to, and moisture quickly loses in pressing process so that petal is in neutrality and color
The unstable easily discoloration purple of element, and smeared after drying with the keeping color agent prepared, metal magnesium ion and flower in keeping color agent
Blue or green element complexing forms anthocyanin so that pigment is stablized, and acid solution is spent the acid-base value of inside, made as reducing agent, adjustment
Obtain and recover original color in acid inside petal.
Existing drying means includes following several:
Spontaneously dry
Moisture is evaporated in dried medium (blotting paper) from plant material surface, but it is time-consuming longer, suitable for fibre-bearing
More, water is low, the small vegetable material of flower pattern
Heated-air drying
(hair-dryer is dry, constant temperature forced air drying):Pigment enzyme is decomposed in cell tissue in hot environment and loses work rapidly
Property and protect color.Its advantage is that the temperature and humidity of dried medium is easy to control, and can monitor colored material surface temperature in real time, prevent
Coking phenomenon, so as to improve drying quality, its equipment is simple, adaptable, and cost is low.
Micro-wave oven is dried
The polar molecule of water makes polar orientation change repeatedly in electromagnetic field of high frequency by changing the frequency of electromagnetic field, and then
Form violent molecular motion and produce heat, moisture is by thermal evaporation, so as to fulfill the drying of petal.
Silica gel Embedding drying
Silica gel is a kind of high activity sorbing material, when being embedded to Chinese rose petal, can effectively adsorb the acid in colored material
Property solution point.
The content of the invention:
The technical problems to be solved by the invention are the defects of part takes the prior art, there is provided a kind of dried flower protects color drying plate
Drier used and preparation method thereof in preparation.
The technical problems to be solved by the invention are realized using following technical scheme.
A kind of dried flower protects drier used in prepared by color drying plate, it is characterised in that:Drier include 50-65 parts of iron powder,
1-8 parts of bamboo charcoal, 1-8 parts of sodium chloride, 1-5 parts of bentonite, 10-30 parts of quartz sand, 10-25 parts of acid solution, calcium sulfate 17-22
Part, 3-9 parts of barium monoxide, 19-26 parts of sodium hydroxide, auxiliary material are 1-5 parts, 50-90 parts of silica, 10-50 parts of high molecule plastic.
The silica is selected from:One or both of pore and silochrom.
The high molecule plastic is selected from:Low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene, polystyrene, polylactic acid,
Hydroxypropyl methyl cellulose and carboxymethyl cellulose are one or more of.
The auxiliary material is:Stearate or stearic acic derivative, preferably calcium stearate or magnesium stearate.
The drier preparation method is:
Iron powder, bamboo charcoal are sequentially added into bucket, is stirred 30 minutes with 350 turns/min, adds sodium chloride, bentonite, with
400 turns/min is sufficiently stirred 30 minutes, sequentially adds quartz sand, calcium sulfate, is stirred 30 minutes, added with 500 turns/min
Barium monoxide, sodium hydroxide, with 500 turns/min stir 30 minutes, sequentially add auxiliary material be, silica, high molecule plastic, with
450 turns/min is sufficiently stirred;
Mixed with acid solution, as in reaction kettle, 300 DEG C of -320 DEG C of high-temperature stirrings, take upper strata mixture, watered after cool
Water, lid lid are put in shady place storage;Smooth china bowl can also be used, paste is scooped out and is put into clear water basin, is allowed to natural cooling;
It is sent to after cooling in unlimited head box, jet flow online, mesh is 40-60 mesh, is furnished with suction flat box under forming net,
Vacuum degree control is 0.1~0.6MPa.
A kind of drying equipment, it is in cube structure, is made of six blocks of plates of up, down, left, right, before and after;Wherein upper plate is
The double-decker fitted closely, its internal layer are iron plate or aluminium sheet, and outer layer is merged one produced for paper pulp and drier
Kind cardboard, the interior hot media channel that labyrinth shape detour is set of the cube structure, the entrance and exit difference of hot media channel
It is arranged on left and right plate.
The upper plate and supporting structure is equipped between coming off duty.
The supporting structure is spring.
The left plate, right panel, foreboard, back plate are by hinge connection in upper plate side wall.
The upper plate upper end-face edge is equipped with two parallel planks with sliding slot, and the sliding slot of two planks is opposite, cardboard
It is inserted in sliding slot.
The sliding slot is equipped with 2 layers, and cardboard is inserted in lower floor, and one piece of glass cover-plate is inserted on upper strata.
The glass cover-plate is equipped with air hole.
The internal layer is not limited to iron plate and aluminium sheet, other metallic plates with thermal conductivity.
The preparation method of the cardboard is:Drier is first prepared, then drier is mixed with beating with paper pulp and is discongested, is made
The paper making pulp of required concentration, wherein it is 10-20% that the drier, which accounts for the paper making pulp mass percent, the paper
Slurry accounts for the paper making pulp mass percent as 80~90%;The paper making pulp, which is sent into, includes the paper machine online of head box
Simultaneously copy paper is molded, obtains magma paper;After if dried layer magma paper is superimposed to certain thickness, it is sent into vacuum laminator and carries out vacuum pressure
Plate, platen temperature are 105~155 degree, and pressure is 15~20kg/cm2.
Beneficial effect:Drying plate is that paper pulp and drier are merged to a kind of cardboard produced, there is very strong suction
Outlet capacity, and can recycle many times, it is convenient for changing at the same time, petal is layered on the preferable drying plate of water absorbing properties,
It is placed in glass plate, gas permeability can be increased by boring a certain number of holes on a glass, easy to the release of steam;Done using special
Dry plate at high temperature, the component in drying plate so that pigment is stablized, and acid solution is used as reducing agent, and adjustment is spent internal
Acid-base value so that recover original color in acid inside petal.
Contrast existing intensive drying method:Advantage and disadvantage are as follows:
Brief description of the drawings:
Fig. 1 is drying plate side structure schematic diagram of the present invention;
Fig. 2 is the drying plate positive structure schematic of the present invention.
Embodiment:
In order to make the technical means, the creative features, the aims and the efficiencies achieved by the present invention easy to understand, tie below
Specific embodiment and legend are closed, the present invention is further explained.
Such as Fig. 1 and Fig. 2, a kind of drying equipment, it is in cube structure, by upper plate 1, lower plate 2, left plate 3, right panel 4, preceding
Six pieces of plate 5, back plate plate compositions;Wherein upper plate is the double-decker fitted closely, its internal layer is iron plate, and outer layer is paper pulp and drying
Agent is merged a kind of cardboard 11 produced, and the hot media channel of labyrinth shape detour, thermal medium are set in cube structure
The entrance 6 of passage and outlet are separately positioned on left and right plate.
Upper plate and come off duty between be equipped with supporting structure 7.
Supporting structure is spring.
Left plate, right panel, foreboard, back plate are connected to upper plate side wall by hinge 8.
Upper plate upper end-face edge is equipped with two parallel planks 9 with sliding slot, and the sliding slot of two planks is opposite, and cardboard is inserted in cunning
In groove.
Sliding slot is equipped with 2 layers, and cardboard is inserted in lower floor, and one piece of glass cover-plate 10 is inserted on upper strata.
Glass cover-plate is equipped with air hole.
Internal layer is not limited to iron plate and aluminium sheet, other metallic plates with thermal conductivity.
The preparation method of cardboard is:Drier is first prepared, then drier is mixed with beating with paper pulp and is discongested, required for being made
Concentration paper making pulp, wherein it is 10-20% that the drier, which accounts for the paper making pulp mass percent, the paper pulp accounts for institute
Paper making pulp mass percent is stated as 80~90%;The paper making pulp, which is sent into, includes on the paper machine of head box net forming simultaneously
Copy paper, obtains magma paper;After if dried layer magma paper is superimposed to certain thickness, it is sent into vacuum laminator and carries out vaccum pressing plate, pressure
Plate temperature is 105~155 degree, and pressure is 15~20kg/cm2.
A kind of dried flower protects drier used in prepared by color drying plate, and drier includes 50 parts of iron powder, 1 part of bamboo charcoal, sodium chloride 1
Part, 1 part of bentonite, 10 parts of quartz sand, 10 parts of acid solution, 17 parts of calcium sulfate, 3 parts of barium monoxide, 19 parts of sodium hydroxide, auxiliary material are
1 part, 50 parts of silica, 10 parts of high molecule plastic.
Drier includes 55 parts of iron powder, 5 parts of bamboo charcoal, 5 parts of sodium chloride, 3 parts of bentonite, 20 parts of quartz sand, acid solution 15
Part, 20 parts of calcium sulfate, 5 parts of barium monoxide, 23 parts of sodium hydroxide, auxiliary material are 3 parts, 70 parts of silica, 30 parts of high molecule plastic.
Drier includes 65 parts of iron powder, 8 parts of bamboo charcoal, 8 parts of sodium chloride, 5 parts of bentonite, 30 parts of quartz sand, acid solution 25
Part, 22 parts of calcium sulfate, 9 parts of barium monoxide, 26 parts of sodium hydroxide, auxiliary material are 5 parts, 90 parts of silica, 50 parts of high molecule plastic.
Silica is selected from:One or both of pore and silochrom.
High molecule plastic is selected from:Low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene, polystyrene, polylactic acid, hydroxypropyl
Ylmethyl cellulose and carboxymethyl cellulose are one or more of.
Auxiliary material is:Stearate or stearic acic derivative, preferably calcium stearate or magnesium stearate.
Drier preparation method is:
Iron powder, bamboo charcoal are sequentially added into bucket, is stirred 30 minutes with 350 turns/min, adds sodium chloride, bentonite, with
400 turns/min is sufficiently stirred 30 minutes, sequentially adds quartz sand, calcium sulfate, is stirred 30 minutes, added with 500 turns/min
Barium monoxide, sodium hydroxide, with 500 turns/min stir 30 minutes, sequentially add auxiliary material be, silica, high molecule plastic, with
450 turns/min is sufficiently stirred;
Mixed with acid solution, as in reaction kettle, 300 DEG C of -320 DEG C of high-temperature stirrings, take upper strata mixture, watered after cool
Water, lid lid are put in shady place storage;Smooth china bowl can also be used, paste is scooped out and is put into clear water basin, is allowed to natural cooling;
It is sent to after cooling in unlimited head box, jet flow online, mesh is 40-60 mesh, is furnished with suction flat box under forming net,
Vacuum degree control is 0.1~0.6MPa.
Basic principle, main feature and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (5)
1. a kind of dried flower protects drier used in prepared by color drying plate, it is characterised in that:Drier includes 50-65 parts of iron powder, bamboo
1-8 parts of charcoal, 1-8 parts of sodium chloride, 1-5 parts of bentonite, 10-30 parts of quartz sand, 10-25 parts of acid solution, 17-22 parts of calcium sulfate,
3-9 parts of barium monoxide, 19-26 parts of sodium hydroxide, auxiliary material are 1-5 parts, 50-90 parts of silica, 10-50 parts of high molecule plastic.
2. a kind of dried flower according to claim 1 protects drier used in prepared by color drying plate, it is characterised in that described
Drier preparation method is:
Iron powder, bamboo charcoal are sequentially added into bucket, is stirred 30 minutes with 350 turns/min, sodium chloride, bentonite is added, with 400
Turn/min is sufficiently stirred 30 minutes, sequentially adds quartz sand, calcium sulfate, stirred 30 minutes with 500 turns/min, add oxidation
Barium, sodium hydroxide, with 500 turns/min stir 30 minutes, sequentially add auxiliary material be, silica, high molecule plastic, with 450
Turn/min is sufficiently stirred;
Mixed with acid solution, as in reaction kettle, 300 DEG C of -320 DEG C of high-temperature stirrings, take upper strata mixture, water are watered after cool,
Lid lid is put in shady place storage;Smooth china bowl can also be used, paste is scooped out and is put into clear water basin, is allowed to natural cooling;
It is sent to after cooling in unlimited head box, jet flow online, mesh is 40-60 mesh, is furnished with suction flat box, vacuum under forming net
Degree control is 0.1~0.6MPa.
3. a kind of dried flower according to claim 1 protects drier used in prepared by color drying plate, it is characterised in that described two
Silica is selected from:One or both of pore and silochrom.
4. a kind of dried flower according to claim 1 protects drier used in prepared by color drying plate, it is characterised in that the height
Molecule plastics are selected from:Low density polyethylene (LDPE), high density polyethylene (HDPE), polypropylene, polystyrene, polylactic acid, hydroxypropyl methyl fiber
Element and carboxymethyl cellulose are one or more of.
5. a kind of dried flower according to claim 1 protects drier used in prepared by color drying plate, it is characterised in that described auxiliary
Expect be:Stearate or stearic acic derivative, preferably calcium stearate or magnesium stearate.