CN107916728A - 一种泡沫玻璃复合保温彩钢板 - Google Patents
一种泡沫玻璃复合保温彩钢板 Download PDFInfo
- Publication number
- CN107916728A CN107916728A CN201610874380.0A CN201610874380A CN107916728A CN 107916728 A CN107916728 A CN 107916728A CN 201610874380 A CN201610874380 A CN 201610874380A CN 107916728 A CN107916728 A CN 107916728A
- Authority
- CN
- China
- Prior art keywords
- foam glass
- foam
- steel slab
- color steel
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种泡沫玻璃复合保温彩钢板,包括泡沫玻璃、粘合剂和彩钢板,所述泡沫玻璃作为夹芯设置在彩钢板内部,所述泡沫玻璃与彩钢板之间设置有粘合剂。本发明为无机非金属无机保温板材,具有A级不燃、无毒环保、无污染、防辐射、不吸水、保温性能稳定持久等特点。
Description
技术领域
本发明属于建筑材料技术领域,具体涉及一种泡沫玻璃复合保温彩钢板。
背景技术
泡沫玻璃是由碎玻璃、发泡剂、改性添加剂和发泡促进剂等,经过细粉碎和均匀混合后,再经过高温熔化,发泡、退火而制成的无机非金属玻璃材料。泡沫玻璃材料具有防潮、防火、防腐的作用,加之玻璃材料具有长期使用性能不劣化的优点,使其在绝热、深冷、地下、露天、易燃、易潮以及有化学侵蚀等苛刻环境下倍受用户青睐;被广泛用于石油、化工、机房降噪、高速公路吸音隔离墙、电力、军工产品等,被用户称之为绿色环保型绝热材料;但现有技术中,泡沫玻璃还很难直接应用到建筑墙体建设、冷库墙体建设和其他需要保温隔热的箱体房间建设,现有技术中一般采用聚氨酯保温彩钢板,应用到建筑领域。然而聚氨酯泡沫是易燃物体,未经阻燃处理。不适宜用来做外墙保温和室内装修。为有机保温板材,生产过程挥发较多的有机废气污染环境。
发明内容
本发明的目的是提供一种泡沫玻璃复合保温彩钢板,本发明为无机非金属无机保温板材,具有A级不燃、无毒环保、无污染、防辐射、不吸水、保温性能稳定持久等特点。
一种泡沫玻璃复合保温彩钢板,包括泡沫玻璃1、粘合剂2和彩钢板3,所述泡沫玻璃1作为夹芯设置在彩钢板3内部,所述泡沫玻璃1与彩钢板3之间设置有粘合剂2。
所述泡沫玻璃采用碎玻璃、发泡剂和改性添加剂而成,其配方如下:碎玻璃40-66份,发泡剂20-30份,改性添加剂5-10份。
所述发泡剂采用碳化硅、碳酸氢钠和硅酸钠的混合物,所述碳化硅、碳酸氢钠和硅酸钠的比例为3∶2∶2.
所述改性添加剂包括絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂,所述絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂的比例为2∶1∶2∶1∶1。
所述絮凝剂采用明矾、三氧化铁水合物、硫酸铝的一种或几种。
所述活化剂采用磷酸酯、聚丙烯酸、聚丙烯酸钠、纳米二氧化钛的一种或几种。
所述助熔剂采用氧化钙与氧化镁的混合物,氧化钙与氧化镁的比例是6∶4.
所述发泡促进剂为氧化铝。
所述稳泡剂为磷酸钾或磷酸氢二钠。
一种泡沫玻璃复合保温彩钢板的制备方法,其步骤如下:
(1)按要求将泡沫玻璃进行切割,得到所需规格尺寸;
(2)采用磨砂机进行边缘打磨,得到与彩钢板尺寸一样的玻璃泡沫夹芯板;
(3)将玻璃泡沫夹芯放入高压浇注机,在玻璃泡沫夹芯与彩钢板之间注入粘合剂;
(4)将设置好的注有泡沫玻璃的彩钢板进行切割,打磨成所需尺寸,得到成品。
与现有技术相比,本发明具有以下有益效果:本发明为无机非金属无机保温板材,具有A级不燃、无毒环保、无污染、防辐射、不吸水、保温性能稳定持久等特点。本发明能够直接应用到建筑墙体建设、冷库墙体建设和其他需要保温隔热的箱体房间建设。
附图说明
图1是本发明的结构示意图;
1、泡沫玻璃;2、粘合剂;3、彩钢板
具体实施方式
下面结合实施例对本发明做进一步描述:
实施例1
一种泡沫玻璃复合保温彩钢板,包括泡沫玻璃1、粘合剂2和彩钢板3,所述泡沫玻璃1作为夹芯设置在彩钢板3内部,所述泡沫玻璃1与彩钢板3之间设置有粘合剂2。
所述泡沫玻璃采用碎玻璃、发泡剂和改性添加剂而成,其配方如下:碎玻璃40份,发泡剂20份,改性添加剂5份。
所述发泡剂采用碳化硅、碳酸氢钠和硅酸钠的混合物,所述碳化硅、碳酸氢钠和硅酸钠的比例为3∶2∶2.
所述改性添加剂包括絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂,所述絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂的比例为2∶1∶2∶1∶1。
所述絮凝剂采用明矾、三氧化铁水合物、硫酸铝的一种或几种。
所述活化剂采用磷酸酯、聚丙烯酸、聚丙烯酸钠、纳米二氧化钛的一种或几种。
所述助熔剂采用氧化钙与氧化镁的混合物,氧化钙与氧化镁的比例是6∶4.
所述发泡促进剂为氧化铝。
所述稳泡剂为磷酸钾或磷酸氢二钠。
一种泡沫玻璃复合保温彩钢板的制备方法,其步骤如下:
(1)按要求将泡沫玻璃进行切割,得到所需规格尺寸;
(2)采用磨砂机进行边缘打磨,得到与彩钢板尺寸一样的玻璃泡沫夹芯板;
(3)将玻璃泡沫夹芯放入高压浇注机,在玻璃泡沫夹芯与彩钢板之间注入粘合剂;
(4)将设置好的注有泡沫玻璃的彩钢板进行切割,打磨成所需尺寸,得到成品。
实施例2
一种泡沫玻璃复合保温彩钢板,包括泡沫玻璃1、粘合剂2和彩钢板3,所述泡沫玻璃1作为夹芯设置在彩钢板3内部,所述泡沫玻璃1与彩钢板3之间设置有粘合剂2。
所述泡沫玻璃采用碎玻璃、发泡剂和改性添加剂而成,其配方如下:碎玻璃66份,发泡剂30份,改性添加剂10份。
所述发泡剂采用碳化硅、碳酸氢钠和硅酸钠的混合物,所述碳化硅、碳酸氢钠和硅酸钠的比例为3∶2∶2.
所述改性添加剂包括絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂,所述絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂的比例为2∶1∶2∶1∶1。
所述絮凝剂采用明矾、三氧化铁水合物、硫酸铝的一种或几种。
所述活化剂采用磷酸酯、聚丙烯酸、聚丙烯酸钠、纳米二氧化钛的一种或几种。
所述助熔剂采用氧化钙与氧化镁的混合物,氧化钙与氧化镁的比例是6∶4.
所述发泡促进剂为氧化铝。
所述稳泡剂为磷酸钾或磷酸氢二钠。
一种泡沫玻璃复合保温彩钢板的制备方法,其步骤如下:
(1)按要求将泡沫玻璃进行切割,得到所需规格尺寸;
(2)采用磨砂机进行边缘打磨,得到与彩钢板尺寸一样的玻璃泡沫夹芯板;
(3)将玻璃泡沫夹芯放入高压浇注机,在玻璃泡沫夹芯与彩钢板之间注入粘合剂;
(4)将设置好的注有泡沫玻璃的彩钢板进行切割,打磨成所需尺寸,得到成品。
实施例3
一种泡沫玻璃复合保温彩钢板,包括泡沫玻璃1、粘合剂2和彩钢板3,所述泡沫玻璃1作为夹芯设置在彩钢板3内部,所述泡沫玻璃1与彩钢板3之间设置有粘合剂2。
所述泡沫玻璃采用碎玻璃、发泡剂和改性添加剂而成,其配方如下:碎玻璃50份,发泡剂23份,改性添加剂7份。
所述发泡剂采用碳化硅、碳酸氢钠和硅酸钠的混合物,所述碳化硅、碳酸氢钠和硅酸钠的比例为3∶2∶2.
所述改性添加剂包括絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂,所述絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂的比例为2∶1∶2∶1∶1。
所述絮凝剂采用明矾、三氧化铁水合物、硫酸铝的一种或几种。
所述活化剂采用磷酸酯、聚丙烯酸、聚丙烯酸钠、纳米二氧化钛的一种或几种。
所述助熔剂采用氧化钙与氧化镁的混合物,氧化钙与氧化镁的比例是6∶4.
所述发泡促进剂为氧化铝。
所述稳泡剂为磷酸钾或磷酸氢二钠。
一种泡沫玻璃复合保温彩钢板的制备方法,其步骤如下:
(1)按要求将泡沫玻璃进行切割,得到所需规格尺寸;
(2)采用磨砂机进行边缘打磨,得到与彩钢板尺寸一样的玻璃泡沫夹芯板;
(3)将玻璃泡沫夹芯放入高压浇注机,在玻璃泡沫夹芯与彩钢板之间注入粘合剂;
(4)将设置好的注有泡沫玻璃的彩钢板进行切割,打磨成所需尺寸,得到成品。
实施例1-3中,泡沫玻璃保温彩钢板生产所需主要原料为碎玻璃,生产过程对环境污染小,它可以变废为宝,减少污染,利于环境保护。
泡沫玻璃保温彩钢板具有无机材料的极强耐久性,能够做到墙体保温***与整个建筑的使用寿命保持同步,从而省却了在一个建筑生命周期中反复多次更新其保温设施的麻烦,一次投入终生受益。
因为生产泡沫玻璃保温彩钢板原料主要是利用各种废弃玻璃,不造成环境污染和生态破坏,而且可为国家节约大量的土地、燃料、人力物力。并且在生产和使用过程中不会对环境产生不良影响,是一种绿色节能产品。仅一条年产20000立方米生产线每年就可为国家节约土地200亩,为建筑物节能68%,使建筑物结构减轻重量30%。
本发明填补了目前在我国无机保温防火复合板领域无泡沫玻璃保温彩钢板材料的空白,泡沫玻璃保温彩钢板为具有A级不燃性能、无毒环保、无污染、防辐射、不吸水、保温性能优良的无机保温防火材料,可为2015年底我国***确定实现建筑节能率60%的目标和防火夹心A级材料标准做出重大贡献。
以上所述仅为本发明的一实施例,并不限制本发明,凡采用等同替换或等效变换的方式所获得的技术方案,均落在本发明的保护范围内。
Claims (10)
1.一种泡沫玻璃复合保温彩钢板,其特征在于:它包括泡沫玻璃(1)、粘合剂(2)和彩钢板(3),所述泡沫玻璃(1)作为夹芯设置在彩钢板(3)内部,所述泡沫玻璃(1)与彩钢板(3)之间设置有粘合剂(2)。
2.根据权利要求书1所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述泡沫玻璃采用碎玻璃、发泡剂和改性添加剂而成,其配方如下:碎玻璃40-66份,发泡剂20-30份,改性添加剂5-10份。
3.根据权利要求书2所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述发泡剂采用碳化硅、碳酸氢钠和硅酸钠的混合物,所述碳化硅、碳酸氢钠和硅酸钠的比例为3∶2∶2。
4.根据权利要求书2所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述改性添加剂包括絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂,所述絮凝剂、活性剂、助熔剂、发泡促进剂和稳泡剂的比例为2∶1∶2∶1∶1。
5.根据权利要求书4所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述絮凝剂采用明矾、三氧化铁水合物、硫酸铝的一种或几种。
6.根据权利要求书4所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述活化剂采用磷酸酯、聚丙烯酸、聚丙烯酸钠、纳米二氧化钛的一种或几种。
7.根据权利要求书4所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述助熔剂采用氧化钙与氧化镁的混合物,氧化钙与氧化镁的比例是6∶4。
8.根据权利要求书4所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述发泡促进剂为氧化铝。
9.根据权利要求书4所述的一种泡沫玻璃复合保温彩钢板,其特征在于,所述稳泡剂为磷酸钾或磷酸氢二钠。
10.根据权利要求书1所述的一种泡沫玻璃复合保温彩钢板,其特征在于,泡沫玻璃复合保温彩钢板的制备方法,其步骤如下:
(1)按要求将泡沫玻璃进行切割,得到所需规格尺寸;
(2)采用磨砂机进行边缘打磨,得到与彩钢板尺寸一样的玻璃泡沫夹芯板;
(3)将玻璃泡沫夹芯放入高压浇注机,在玻璃泡沫夹芯与彩钢板之间注入粘合剂;
(4)将设置好的注有泡沫玻璃的彩钢板进行切割,打磨成所需尺寸,得到成品。