CN107891064A - 一种改善不锈钢表面质量的生产方法 - Google Patents
一种改善不锈钢表面质量的生产方法 Download PDFInfo
- Publication number
- CN107891064A CN107891064A CN201710990532.8A CN201710990532A CN107891064A CN 107891064 A CN107891064 A CN 107891064A CN 201710990532 A CN201710990532 A CN 201710990532A CN 107891064 A CN107891064 A CN 107891064A
- Authority
- CN
- China
- Prior art keywords
- roughness
- mill speed
- rolling
- pony
- rolled
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及不锈钢轧制技术领域。一种改善不锈钢表面质量的生产方法,轧制总变形量60‑80%;首道次轧制使用粗糙度为3.0‑3.5μm工作辊轧制,变形量为23%,轧制速度为80‑100mpm;成品道次轧制使用粗糙度为0.2μm的工作辊轧制,轧制速度为120‑‑150mpm;中间道次轧制变形量为15‑20%,每次轧制使用粗糙度为0.3‑0.9μm的工作辊轧制,变形量为15‑20%,轧制速度为200‑600mpm,中间道次有多个道次组成,轧制使用的工作辊粗糙度依照道次依次减少,轧制速度依照道次依次增加。
Description
技术领域
本发明涉及不锈钢轧制技术领域。
背景技术
表面粗糙条纹是不锈钢非常常见的缺陷,随着合金成份的升高,表面条纹也呈现加重趋势。表面粗糙条纹影响不锈钢表面均匀一致性,使其在高端行业的应用受到制约。
发明内容
本发明所要解决的技术问题是:如何花费更小的成本来改善不锈钢表面质量。
本发明所采用的技术方案是:一种改善不锈钢表面质量的生产方法,轧制总变形量60-80%;首道次轧制使用粗糙度为3.0-3.5μm工作辊轧制,变形量为23%,轧制速度为80-100mpm;成品道次轧制使用粗糙度为0.2μm的工作辊轧制,轧制速度为120--150mpm;中间道次轧制变形量为15-20%,每次轧制使用粗糙度为0.3-0.9μm的工作辊轧制,变形量为15-20%,轧制速度为200-600mpm,中间道次有多个道次组成,轧制使用的工作辊粗糙度依照道次依次减少,轧制速度依照道次依次增加。
作为一种优选方式:中间道次由三个道次组成,第一中间道次的轧制使用粗糙度为0.7-0.9μm的工作辊轧制,变形量为15-20%,轧制速度为200-400mpm;第二中间道次的轧制使用粗糙度为0.5-0.7μm的工作辊轧制,变形量为15-20%,轧制速度为300-500mpm;第三中间道次的轧制使用粗糙度为0.3-0.5μm的工作辊轧制,变形量为15-20%,轧制速度为400-600mpm。
本发明的有益效果是:本发明中,高粗糙度大变形量轧制首道次,使得轧辊与钢带表面有极大的摩擦力,利用极大摩擦力消除表面条纹,使表面均匀一致,第二道次开始使用低粗糙度的轧辊轧制,降低首道次轧制形成的粗糙表面。成品道次使用粗糙度更低的轧辊轧制,尽一步降低表面粗糙度,使表面均匀、细腻。
具体实施方式
本实施例在二十辊可逆轧机上,通过多道次轧制实现。本发明的主要操作要点如下:
1、轧制前变形量设计:轧制整体总变形量不超过60-80%。
2、轧制前检查设备:二十辊辊系相互匹配,检查刮油辊、板型辊表面正常,测厚仪显示准确,轧制油清澈无杂质等。
3、首道次轧制:变形量为23%,轧机工作辊粗糙度使用3.0-3.5μm,油量2800-3000L/min,轧制速度为80-100mpm(单位:米每分钟)。高粗糙度大变形量轧制首道次,使得轧辊与钢带表面有极大的摩擦力,利用极大摩擦力消除表面条纹,使不锈钢表面均匀一致,同时采用较小的
4、第一中间道次:变形量15-20%,轧机工作辊使用粗磨辊(粗糙度0.7-0.9μm),油量2800-3300L/min,轧制速度200-400mpm。
5、第二中间道次:变形量15-20%,轧机工作辊使用精磨辊(粗糙度0.5-0.7μm),油量2100-3000L/min,轧制速度300-500mpm。
6、第三中间道次:变形量15-20%,轧机工作辊使用新的精磨辊(粗糙度0.3-0.5μm),油量2500-3800L/min,轧制速度400-600mpm。
三个中间道次通过采用逐渐变小的粗糙度,使不锈钢表面的条纹逐渐消除,同时采用逐渐增大的速度,能够更易消除不锈钢表面条纹。
7、成品道次:变形量15-18%,轧机工作辊使用粗糙度0.2μm的轧辊,成品道次轧制使用油量3300-3800L/min,成品道次轧制速度120--150mpm。成本道次采用最小粗糙度工作辊轧制,同时采用较小的速度轧制,保证了成品表面的光滑性。
Claims (2)
1.一种改善不锈钢表面质量的生产方法,其特征在于:轧制总变形量60-80%;首道次轧制使用粗糙度为3.0-3.5μm工作辊轧制,变形量为23%,轧制速度为80-100mpm;成品道次轧制使用粗糙度为0.2μm的工作辊轧制,轧制速度为120--150mpm;中间道次轧制变形量为15-20%,每次轧制使用粗糙度为0.3-0.9μm的工作辊轧制,变形量为15-20%,轧制速度为200-600mpm,中间道次有多个道次组成,轧制使用的工作辊粗糙度依照道次依次减少,轧制速度依照道次依次增加。
2.根据权利要求1所述的一种改善不锈钢表面质量的生产方法,其特征在于:中间道次由三个道次组成,第一中间道次的轧制使用粗糙度为0.7-0.9μm的工作辊轧制,变形量为15-20%,轧制速度为200-400mpm;第二中间道次的轧制使用粗糙度为0.5-0.7μm的工作辊轧制,变形量为15-20%,轧制速度为300-500mpm;第三中间道次的轧制使用粗糙度为0.3-0.5μm的工作辊轧制,变形量为15-20%,轧制速度为400-600mpm。