CN107881496A - A kind of copper strips passivator and its application process - Google Patents
A kind of copper strips passivator and its application process Download PDFInfo
- Publication number
- CN107881496A CN107881496A CN201711307363.XA CN201711307363A CN107881496A CN 107881496 A CN107881496 A CN 107881496A CN 201711307363 A CN201711307363 A CN 201711307363A CN 107881496 A CN107881496 A CN 107881496A
- Authority
- CN
- China
- Prior art keywords
- passivator
- copper strips
- drying
- minutes
- drying time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of copper strips passivator and its application process, belong to field of metal surface treatment technology.The passivator includes mercaptobenzothiazoler 2 5%, Ludox 1 3%, tartaric acid 2 5%, methenamine 0.5 1%, nickel sulfate 0.4 0.8%, fluorine zirconic acid 1 3%, water surplus.The passivating film of one layer of stable corrosion resistance is formed in brass belt surface by the present invention, film-formation result is good, it is firm, fine and close, stably, corrosion resistance it is strong, film surface light is substantially colorless, and passivating film its indoor lacing film for being formed of the passivator of the present invention 200 days is non-discolouring.
Description
Technical field
The invention belongs to field of metal surface treatment technology, and in particular to a kind of copper strips passivator and its application process.
Background technology
Traditional copper material surface passivating treatment technique mainly includes BTA of inorganic chromate and organic etc..
Because chromating facture contains Cr VI, the use for belonging to high poison, high pollution therefore this technique receives strict limit
System.Most of copper material passivator are all the passivator configured based on BTA in the market, but are easy to occur
Phenomena such as macula lutea, bad resistance to corrosion.
The content of the invention
The problem of existing for prior art, it is an object of the invention to design to provide a kind of copper strips passivator and its application
The technical scheme of method.
Described a kind of copper strips passivator, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 2-5%, Ludox 1-3%, tartaric acid 2-5%, methenamine 0.5-1%, nickel sulfate 0.4-0.8%, fluorine zirconium
Sour 1-3%, water surplus.
Described a kind of copper strips passivator, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 2.5-4.5%, Ludox 1.5-2.5%, tartaric acid 2.5-4.5%, methenamine 0.6-0.8%, sulfuric acid
Nickel 0.5-0.7%, fluorine zirconic acid 1.5-2.5%, water surplus.
Described a kind of copper strips passivator, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 3-4%, Ludox 1.8-2.2%, tartaric acid 3-4%, methenamine 0.6-0.8%, nickel sulfate 0.5-
0.7%th, fluorine zirconic acid 1.8-2.2%, water surplus.
A kind of application process of described copper strips passivator, it is characterised in that:
1)At normal temperatures, the brass band cleaned up is put into passivator and carries out surface passivating treatment, soak time 15-20
Minute;
2)Brass band is put into drying tunnel and carries out heating drying, first stage drying temperature is 40-50 DEG C, 5-10 points of drying time
Clock, 50-60 DEG C of second stage, drying time 5-10 minutes, 60-100 DEG C of phase III, drying time 10-15 minutes, fourth order
100-120 DEG C of section, drying time 5-10 minutes.
The passivating film of one layer of stable corrosion resistance is formed in brass belt surface by the present invention, film-formation result is good, it is firm,
It is fine and close, stably, corrosion resistance it is strong, film surface light is substantially colorless, and it is indoor for the passivating film that is formed of the passivator of the present invention
Lacing film 200 days is non-discolouring.
Embodiment
Further illustrate the present invention with reference to embodiments.
Embodiment 1
More than mercaptobenzothiazoler 3%, Ludox 2%, tartaric acid 4%, methenamine 0.8%, nickel sulfate 0.6%, fluorine zirconic acid 2%, water
Each component is uniformly mixed by amount, obtains copper strips passivator.
Application process:
1)At normal temperatures, the brass band cleaned up is put into passivator and carries out surface passivating treatment, soak time is 15 points
Clock;
2)Brass band is put into drying tunnel and carries out heating drying, first stage drying temperature is 45 DEG C, drying time 10 minutes, the
55 DEG C of two-stage, drying time 10 minutes, 80 DEG C of phase III, drying time 10 minutes, 110 DEG C of fourth stage, drying time 5
Minute.
Embodiment 2
More than mercaptobenzothiazoler 2%, Ludox 1%, tartaric acid 2%, methenamine 0.5%, nickel sulfate 0.4%, fluorine zirconic acid 1%, water
Each component is uniformly mixed by amount, obtains copper strips passivator.
Application process:
1)At normal temperatures, the brass band cleaned up is put into passivator and carries out surface passivating treatment, soak time is 20 points
Clock;
2)Brass band is put into drying tunnel and carries out heating drying, first stage drying temperature is 40 DEG C, drying time 5 minutes, the
50 DEG C of two-stage, drying time 5 minutes, 60 DEG C of phase III, drying time 10 minutes, 100 DEG C of fourth stage, drying time 5
Minute.
Embodiment 3
By mercaptobenzothiazoler 4.5%, Ludox 2.5%, tartaric acid 4.5%, methenamine 0.8%, nickel sulfate 0.7%, fluorine zirconic acid
2.5%th, each component is uniformly mixed by water surplus, obtains copper strips passivator.
Application process:
1)At normal temperatures, the brass band cleaned up is put into passivator and carries out surface passivating treatment, soak time is 15 points
Clock;
2)Brass band is put into drying tunnel and carries out heating drying, first stage drying temperature is 50 DEG C, drying time 10 minutes, the
60 DEG C of two-stage, drying time 10 minutes, 100 DEG C of phase III, drying time 15 minutes, 120 DEG C of fourth stage, drying time
10 minutes.
Performance test:
Neutral salt spray test:Tested with reference to GB/T 10125-1997.
Test result understands that the brass band after Passivation Treatment that embodiment 1-3 is obtained carries out neutral salt spray test, warp
25-30 hour neutral salt spray tests are crossed, specimen surface is good without rust staining, glossiness.
Claims (4)
1. a kind of copper strips passivator, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 2-5%, Ludox 1-3%, tartaric acid 2-5%, methenamine 0.5-1%, nickel sulfate 0.4-0.8%, fluorine zirconium
Sour 1-3%, water surplus.
2. a kind of copper strips passivator as claimed in claim 1, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 2.5-4.5%, Ludox 1.5-2.5%, tartaric acid 2.5-4.5%, methenamine 0.6-0.8%, sulfuric acid
Nickel 0.5-0.7%, fluorine zirconic acid 1.5-2.5%, water surplus.
3. a kind of copper strips passivator as claimed in claim 1, it is characterised in that include the component of following degree:
Mercaptobenzothiazoler 3-4%, Ludox 1.8-2.2%, tartaric acid 3-4%, methenamine 0.6-0.8%, nickel sulfate 0.5-
0.7%th, fluorine zirconic acid 1.8-2.2%, water surplus.
A kind of 4. application process of copper strips passivator as described in claim 1 or 2 or 3, it is characterised in that:
1)At normal temperatures, the brass band cleaned up is put into passivator and carries out surface passivating treatment, soak time 15-20
Minute;
2)Brass band is put into drying tunnel and carries out heating drying, first stage drying temperature is 40-50 DEG C, 5-10 points of drying time
Clock, 50-60 DEG C of second stage, drying time 5-10 minutes, 60-100 DEG C of phase III, drying time 10-15 minutes, fourth order
100-120 DEG C of section, drying time 5-10 minutes.