CN107841232A - A kind of water-repellent paint - Google Patents
A kind of water-repellent paint Download PDFInfo
- Publication number
- CN107841232A CN107841232A CN201711147597.2A CN201711147597A CN107841232A CN 107841232 A CN107841232 A CN 107841232A CN 201711147597 A CN201711147597 A CN 201711147597A CN 107841232 A CN107841232 A CN 107841232A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- repellent paint
- glycerine
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-repellent paint, it is prepared from the following raw materials in parts by weight：20 30 parts of acrylic emulsion, 5 10 parts of clay, 15 25 parts of quartz sand, 25 parts of titanium dioxide, 59 parts of calcium carbonate, 37 parts of wooden fine fiber, 13 parts of glycerine, 39 parts of sodium chloride, 7 12 parts of pentaerythrite, 5 15 parts of organic siliconresin, 25 35 parts of 20 epoxy resin of E, 24 32 parts of water.The coating water-proof function admirable of the present invention, intensity is higher, and adhesion strength, tensile strength are higher, has good pliability and elongation percentage.
Description
Technical field
The invention belongs to technical field of buildings, and in particular to a kind of water-repellent paint.
Background technology
It is in the viscous liquid high molecular synthetic material without solid shape at normal temperatures that water-repellent paint, which is,.After coated, pass through
The general name of the material of tough and tensile waterproof membrane is formed after the volatilization of solvent or the evaporation of moisture or reaction solidification on basic unit face..Mesh
The flexibility that waterproof material used in preceding building trade is generally divided into including waterproof roll, water-repellent paint, sealing cement etc. is prevented
Water material and based on cement matrix, addition waterproofing agent and other auxiliary agents rigidity water-proofing material.It is existing although species is abundant
Various reinforcing agents, filler, macromolecular elastomer are made it by some water-repellent paint water resistances, weatherability, loss of properties on aging, hardly possible
It is dispersed in colloid, the phenomenon of seepage or bonding loosely easily occurs in product, simultaneously because the ring that coating soaks for a long time
Border, existing coating flexibility is bad, and elongation percentage is poor, is easily broken off.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of water resistance, weatherability, the preferable water-repellent paint of resistance to ag(e)ing,
There is good pliability and elongation percentage simultaneously.
The present invention adopts the technical scheme that：
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：Acrylic emulsion 20-30 parts, clay 5-10 parts, stone
Sand 15-25 parts, titanium dioxide 2-5 parts, calcium carbonate 5-9 parts, wooden fine fiber 3-7 parts, glycerine 1-3 parts, sodium chloride 3-9 parts, season
Penta tetrol 7-12 parts, organic siliconresin 5-15 parts, E-20 epoxy resin 25-35 parts, water 24-32 parts.
Preferably, described water-repellent paint, is prepared from the following raw materials in parts by weight：25 parts of acrylic emulsion, clay 7.5
Part, 20 parts of quartz sand, 3.5 parts of titanium dioxide, 7 parts of calcium carbonate, 5 parts of wooden fine fiber, 2 parts of glycerine, 6 parts of sodium chloride, pentaerythrite
9.5 parts, 10 parts of organic siliconresin, 30 parts of E-20 epoxy resin, 28 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, in 80-
Heat 10-15min under the conditions of 100 DEG C, during do not stop to stir, obtain water-repellent paint.
It is an advantage of the invention that：The present invention coating water-proof function admirable, intensity is higher, adhesion strength, tensile strength compared with
Height, there is good pliability and elongation percentage.
Embodiment
Presently preferred embodiments of the present invention is described in detail below so that advantages and features of the invention can be easier to by
It will be appreciated by those skilled in the art that apparent clearly defined so as to be made to protection scope of the present invention.
Embodiment 1
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：20 parts of acrylic emulsion, 5 parts of clay, quartz sand 15
Part, 2 parts of titanium dioxide, 5 parts of calcium carbonate, 3 parts of wooden fine fiber, 1 part of glycerine, 3 parts of sodium chloride, 7 parts of pentaerythrite, organic siliconresin
5 parts, 25 parts of E-20 epoxy resin, 24 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, 80
10min is heated under the conditions of DEG C, during do not stop to stir, obtain water-repellent paint.
Embodiment 2
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：23 parts of acrylic emulsion, 6 parts of clay, quartz sand 18
Part, 3 parts of titanium dioxide, 6 parts of calcium carbonate, 4 parts of wooden fine fiber, 1.5 parts of glycerine, 5 parts of sodium chloride, 8 parts of pentaerythrite, organosilicon tree
7 parts of fat, 28 parts of E-20 epoxy resin, 26 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, 85
12min is heated under the conditions of DEG C, during do not stop to stir, obtain water-repellent paint.
Embodiment 3
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：25 parts of acrylic emulsion, 7.5 parts of clay, quartz sand
20 parts, it is 3.5 parts of titanium dioxide, 7 parts of calcium carbonate, 5 parts of wooden fine fiber, 2 parts of glycerine, 6 parts of sodium chloride, 9.5 parts of pentaerythrite, organic
10 parts of silicones, 30 parts of E-20 epoxy resin, 28 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, 90
13min is heated under the conditions of DEG C, during do not stop to stir, obtain water-repellent paint.
Embodiment 4
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：28 parts of acrylic emulsion, 9 parts of clay, quartz sand 22
Part, 4 parts of titanium dioxide, 8 parts of calcium carbonate, 6 parts of wooden fine fiber, 2.5 parts of glycerine, 8 parts of sodium chloride, 11 parts of pentaerythrite, organosilicon
12 parts of resin, 32 parts of E-20 epoxy resin, 30 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, 95
14min is heated under the conditions of DEG C, during do not stop to stir, obtain water-repellent paint.
Embodiment 5
A kind of water-repellent paint, is prepared from the following raw materials in parts by weight：30 parts of acrylic emulsion, 10 parts of clay, quartz sand
25 parts, 5 parts of titanium dioxide, 9 parts of calcium carbonate, 7 parts of wooden fine fiber, 3 parts of glycerine, 9 parts of sodium chloride, 12 parts of pentaerythrite, organosilicon
15 parts of resin, 35 parts of E-20 epoxy resin, 32 parts of water.
The preparation method of above-mentioned water-repellent paint, comprises the following steps：Each component is proportionally added into, is well mixed, 100
15min is heated under the conditions of DEG C, during do not stop to stir, obtain water-repellent paint.
Claims (3)
1. a kind of water-repellent paint, it is characterised in that be prepared from the following raw materials in parts by weight：Acrylic emulsion 20-30 parts, clay
5-10 parts, quartz sand 15-25 parts, titanium dioxide 2-5 parts, calcium carbonate 5-9 parts, wooden fine fiber 3-7 parts, glycerine 1-3 parts, sodium chloride
3-9 parts, pentaerythrite 7-12 parts, organic siliconresin 5-15 parts, E-20 epoxy resin 25-35 parts, water 24-32 parts.
2. water-repellent paint according to claim 1, it is characterised in that be prepared from the following raw materials in parts by weight：Propylene yogurt
25 parts of liquid, 7.5 parts of clay, 20 parts of quartz sand, 3.5 parts of titanium dioxide, 7 parts of calcium carbonate, 5 parts of wooden fine fiber, 2 parts of glycerine, chlorination
6 parts of sodium, 9.5 parts of pentaerythrite, 10 parts of organic siliconresin, 30 parts of E-20 epoxy resin, 28 parts of water.
3. the preparation method of water-repellent paint according to claim 1 or 2, it is characterised in that comprise the following steps：By each group
Point be proportionally added into, be well mixed, 10-15min is heated under the conditions of 80-100 DEG C, during do not stop to stir, obtain waterproof painting
Material.