CN107815152A - A kind of high temperature resistant heat insulation is resistance to burn metallic paint and preparation method thereof - Google Patents
A kind of high temperature resistant heat insulation is resistance to burn metallic paint and preparation method thereof Download PDFInfo
- Publication number
- CN107815152A CN107815152A CN201711184025.1A CN201711184025A CN107815152A CN 107815152 A CN107815152 A CN 107815152A CN 201711184025 A CN201711184025 A CN 201711184025A CN 107815152 A CN107815152 A CN 107815152A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistance
- high temperature
- metallic paint
- temperature resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to surface functional material field, especially a kind of high temperature resistant heat insulation is resistance to burn metallic paint and preparation method thereof.The composition that it includes following parts by weight is made:Heat-resisting 20 50 parts of solid solution, boron nitride are 5 15 parts, α AL2O3 are 5 15 parts, 5 15 parts of mica powder, 20 50 parts of binding agent, 9 15 parts of coating additive.It has the characteristics that heatproof it is high, it is heat-insulated it is good, have concurrently corrosion-resistant, wear-resisting, have the resistance to burning protective effect of good high temperature to metal, can form one layer on coated object surface has higher volume resistivity, can bear strong electric without breakdown ceramic coating;Coating is fine and close, and hardness is high, is adapted to brushing to form the layer of resistance to burning on various metals;The coating has higher mechanical strength and good chemical stability, can be ageing-resistant, water-fast, resistant to chemical etching;Coating, as filler, the homogeneous system through being formed with component grindings such as binding agent and coating additives, is more effectively met the needs of people, solves problems of the prior art using heat-resisting good solid solution.
Description
Technical field:
The present invention relates to protective coating field, especially a kind of high temperature resistant heat insulation is resistance to burn metallic paint and preparation method thereof.
Background technology:
Metallic paint is the coating for having metal-like, and majority needs to carry out some form of pretreatment to metal surface,
Improve surface appearance, in favor of improving the adhesive force of coating, enhancing is acted on the anti-corrosion protection of metal base, generally by sky
Gas blowout applies what is realized.Metallic paint is separated metal surface and extraneous medium are tight, protects metal not corroded by the external world.Will
Ask metallic paint to keep stable in contact medium, while require that metallic paint can form continuous non-porous film, airtight,
It is waterproof, have firm adhesive force to metal surface, have certain mechanical strength and elasticity, it is acidproof under special circumstances, alkaline-resisting
Deng.
Its used metal material is frequently necessary in some require use condition more strict industry can be resistant to
By higher temperature and there can be certain anti-corrosion function, therefore in industry generally can all be smeared now in metal surface
Layer of metal coating.Although existing metallic paint can meet the requirement of conventional environment, however similar to metal smelt,
During application under metal heat treatmet, metal welding and metallic high temperature environment, it is necessary to which quality is high, and the protective coating of great thermotolerance solves
The problems such as certainly corresponding high temperature ablation, oxidation, corrosion, existing metallic paint leads to when being used in the environment of above-mentioned high temperature ablation
Often occur surface split, local shedding the problems such as, protection effect it is poor.Obviously, existing coating can not more effectively meet people
Demand.
The content of the invention:
The present invention is in order to make up the deficiency of existing metallic paint, there is provided a kind of high temperature resistant heat insulation is resistance to burn metallic paint and its
Preparation method, it have the characteristics that heatproof it is high, it is heat-insulated it is good, have concurrently it is corrosion-resistant, wear-resisting, have to metal good high temperature it is resistance to burn protection
Effect;Coating is fine and close, and hardness is high, is adapted to brushing to form the layer of resistance to burning on various metals;The demand of people is more effectively met,
Solve problems of the prior art.
The present invention is that technical scheme is used by solving above-mentioned technical problem:A kind of resistance to metal that burns of high temperature resistant heat insulation applies
Material, including the composition of following parts by weight are made:
Heat-resisting solid solution 20-50 parts, boron nitride are 5-15 parts, α-AL2O3For 5-15 parts, mica powder 5-15 parts, binding agent
20-50 parts, coating additive 9-15 parts.
Preferably, heat-resisting 37 parts of solid solution, boron nitride are 10 parts, α-AL2O3For 10 parts, 10 parts of mica powder, binding agent 40
Part, 7 parts of coating additive.
Preferably, the heat-resisting solid solution includes the composition of following parts by weight:Kaolin 5-20 parts, cordierite 7-15
Part, vermiculite 3-10 parts, silica 3-10 parts.
Preferably, the heat-resisting solid solution includes the composition of following parts by weight:10 parts of kaolin, 10 parts of cordierite, leech
5 parts of stone, 6 parts of silica.
Preferably, the heat-resisting solid solution also includes the composition of following parts by weight:Nepheline 2-10 parts.
Preferably, composition of the binding agent including following parts by weight is made:Silicic acid glue solution 10-25 parts, three oxygen
Change two chromium micro mist 10-25 parts.
Preferably, the silicic acid glue solution concentration is 20%.
Preferably, composition of the coating additive including following parts by weight is made:Dispersant 2-4 parts, thickener 3-6
Part, pH value conditioning agent 3-6 parts, bactericide 1-3 parts.
Preferably, the dispersant is calgon, thickener is hydroxypropyl methylcellulose, pH value conditioning agent is Organic Alcohol
Amine CP-802, bactericide are C-15 bactericide.
A kind of resistance to preparation method for burning metallic paint of high temperature resistant heat insulation, it is characterised in that:Comprise the following steps:
S1:By 1300 DEG C of fusings after kaolin, cordierite, vermiculite, silica, nepheline mixing;
S2:Water quenching, drying;
S3:325 mesh sieve, and obtain a kind of primary solid solution filler porous, Heat-resistant stable is good;
S4:The micro mist of the primary solid solution filler and the zirconium oxide that particle mean size is 1 μ is calcined to 1850 DEG C again,
Heat-resisting solid solution needed for obtaining;
S5:20% silicic acid glue solution mixes with chrome green micro mist to be ground 10 hours by 320r/ bulb separations, obtained molten
Gluey binding agent;
S6:Calgon, hydroxypropyl methylcellulose, organic alcohol amine CP-802, C-15 bactericide are mixed to prepare coating and helped
Agent;
S7:By coating additive, boron nitride, α made from binding agent made from obtained heat-resisting solid solution in S4, S5, S6-
AL2O3, mica powder mixed grinding, mixture is obtained this high temperature resistant heat insulation metallic paint of resistance to burning in homogeneous system.
Beneficial effect is possessed by the present invention:It has the characteristics that heatproof it is high, it is heat-insulated it is good, have concurrently it is corrosion-resistant, wear-resisting, it is right
Metal has the resistance to burning protective effect of good high temperature, and can form one layer on coated object surface has higher volume resistivity, can hold
By strong electric without breakdown ceramic coating;Coating is fine and close, and hardness is high, is adapted to brushing to form resistance to burning on various metals
Layer;The coating has higher mechanical strength and good chemical stability, can be ageing-resistant, water-fast, resistant to chemical etching;Also simultaneously
Can continuously it be worked under corresponding operating temperature with mechanical resistant impact and thermal shock resistance properties, the coating;Coating is using heat-resisting good
Good solid solution is as filler, the homogeneous system through being formed with component grindings such as binding agent and coating additives.Coating has resistance to
Wen Gao, it is heat-insulated good, have the good characteristic such as corrosion-resistant, wear-resisting concurrently, have the resistance to burning protective effect of good high temperature to metal, more effectively
Meets the needs of people.
Embodiment:
Further clearly to illustrate the technical characterstic of this programme, below by embodiment, the present invention is carried out
Elaborate, but the present invention is not limited to this.
Embodiment 1:Composition including following parts by weight is made:
Heat-resisting 37 parts of solid solution is mainly by 6 parts of 10 parts of kaolin, 10 parts of cordierite, 5 parts of vermiculite, 6 parts of silica, nepheline groups
Into;Boron nitride is 10 parts, α-AL2O3For 10 parts, 10 parts of mica powder, 40 parts of binding agent be mainly that 20% silicic acid glue is molten by concentration
20 parts of 20 parts of liquid, chrome green micro mist compositions;12 parts of coating additive is mainly 3 parts of calgon, thickener by dispersant
For 4 parts of hydroxypropyl methylcellulose, pH value conditioning agent be organic alcohol amine CP-802 be 4 parts, bactericide be that C-15 bactericide is 2 parts of groups
Into.
The resistance to preparation method for burning metallic paint of the high temperature resistant heat insulation, using following steps:
S1:By 1300 DEG C of fusings after 6 parts of 14 parts of kaolin, 11 parts of cordierite, 6 parts of vermiculite, 6 parts of silica, nepheline mixing;
S2:Water quenching, drying;
S3:325 mesh sieve, and obtain a kind of primary solid solution filler porous, Heat-resistant stable is good;
S4:The micro mist of the primary solid solution filler and the zirconium oxide that particle mean size is 1 μ is calcined to 1850 DEG C again,
Heat-resisting solid solution needed for obtaining, the filler temperature in use may be up to more than 1800 DEG C, to metal welding, high-temperature heat treatment and
Protection under other hot environments has good effect;
S5:20% silicic acid glue solution mixes with chrome green micro mist to be ground 10 hours by 320r/ bulb separations, obtained molten
Gluey binding agent;
S6:Calgon, hydroxypropyl methylcellulose, organic alcohol amine CP-802, C-15 bactericide are mixed to prepare coating and helped
Agent;
S7:By coating additive, boron nitride, α made from binding agent made from obtained heat-resisting solid solution in S4, S5, S6-
AL2O3, mica powder mixed grinding, mixture is obtained this high temperature resistant heat insulation metallic paint of resistance to burning in homogeneous system.
Embodiment 2:Composition including following parts by weight is made:
Heat-resisting 20 parts of solid solution is mainly made up of 5 parts of kaolin, 7 parts of cordierite, 3 parts of vermiculite, 3 parts of silica, 2 parts of nepheline;
Boron nitride is 5 parts, α-AL2O3For 5 parts, 5 parts of mica powder, 20 parts of binding agent mainly by concentration be 10 parts of 20% silicic acid glue solution,
10 parts of compositions of chrome green micro mist;9 parts of coating additive is mainly 2 parts of calgon by dispersant, thickener is hydroxypropyl first
3 parts of cellulose, pH value conditioning agent be organic alcohol amine CP-802 be 3 parts, bactericide be C-15 bactericide be 1 part composition.
Preparation method is the same as embodiment 1.
Embodiment 3:Composition including following parts by weight is made:
Heat-resisting 50 parts of solid solution is mainly by 6 parts of 15 parts of kaolin, 15 parts of cordierite, 7 parts of vermiculite, 7 parts of silica, nepheline groups
Into;Boron nitride is 15 parts, α-AL2O3For 15 parts, 15 parts of mica powder, 50 parts of binding agent be mainly that 20% silicic acid glue is molten by concentration
25 parts of 25 parts of liquid, chrome green micro mist compositions;15 parts of coating additive is mainly 4 parts of calgon, thickener by dispersant
For 5 parts of hydroxypropyl methylcellulose, pH value conditioning agent be organic alcohol amine CP-802 be 3 parts, bactericide be that C-15 bactericide is 3 parts of groups
Into.
Preparation method is the same as embodiment 1.
Embodiment 4:Composition including following parts by weight is made:
Heat-resisting 30 parts of solid solution is mainly made up of 6 parts of kaolin, 9 parts of cordierite, 5 parts of vermiculite, 4 parts of silica, 4 parts of nepheline;
Boron nitride is 8 parts, α-AL2O3For 9 parts, 8 parts of mica powder, 30 parts of binding agent mainly by concentration be 15 parts of 20% silicic acid glue solution,
15 parts of compositions of chrome green micro mist;10 parts of coating additive is mainly 2 parts of calgon by dispersant, thickener is hydroxypropyl first
4 parts of cellulose, pH value conditioning agent be organic alcohol amine CP-802 be 3 parts, bactericide be C-15 bactericide be 1 part composition.
Preparation method is the same as embodiment 1.
Embodiment 5:Composition including following parts by weight is made:
Heat-resisting 47 parts of solid solution is mainly by 8 parts of 15 parts of kaolin, 11 parts of cordierite, 6 parts of vermiculite, 7 parts of silica, nepheline groups
Into;Boron nitride is 12 parts, α-AL2O3For 13 parts, 12 parts of mica powder, 40 parts of binding agent be mainly that 20% silicic acid glue is molten by concentration
20 parts of 20 parts of liquid, chrome green micro mist compositions;14 parts of coating additive is mainly 3 parts of calgon, thickener by dispersant
For 4 parts of hydroxypropyl methylcellulose, pH value conditioning agent be organic alcohol amine CP-802 be 4 parts, bactericide be that C-15 bactericide is 3 parts of groups
Into.
Preparation method is the same as embodiment 1.
Such as obtained primary solid solution filler, the preparation method after high temperature melting in the S3 of preparation method in embodiment 1
S1 in the structural form of each composition can change, respective rigid can be improved after each composition water quenching, and pass through
It is unified particulate matter that size can be obtained after sieve, and primary solid solution filler now is on material property than nature shape
There are larger lifting and improvement under state;The micro mist of primary solid solution filler and zirconium oxide is calcined at a high temperature of 1850 DEG C, can
To convert or remove unwanted material contained therein, such as volatile impurities such as chemical bonding water, CO2, NOx, while wait and enough have
The mechanical strength of the raising material of effect;20% silicic acid glue solution and chrome green micro mist mixing and ball milling can be ensured to obtain
The binding agent of colloidal sol shape its internal each composition is well mixed, caking property is good;Through calgon, hydroxypropyl methylcellulose, organic
Hydramine CP-802, C-15 bactericide is mixed to prepare the coating storage stabilization that coating additive can keep the later stage to obtain, can be effective
Improvement execution conditions, improve product quality;The chemical resistance of concrete ability of coating can be effectively improved after addition boron nitride, is made
It is not by inorganic acid and water erosion;It is not easy to be oxidized in the environment of applied at elevated temperature, makes coating that there is high-wearing feature, improves painting
Expect overall resistivity, in the state of applied at elevated temperature without flash-point, burning-point;Because of α-AL2O3Even particle size distribution, purity it is high, high
Disperse, there is resistant to elevated temperatures inertia, adding α-AL2O3Can make coating with higher resistivity, with good insulating properties
Can, so as to have good protective action in the working environment of high-temperature heat-resistance;Mica powder can play auxiliary to coating property
Effect, allow coating that there is good elasticity, toughness;It is insulating properties, high temperature resistant, acid and alkali-resistance, corrosion-resistant, while can strengthen attached
Force characteristic, ensures the adhesive capacity after brushing.
Test example 1:The resistance to service check for burning metallic paint of high temperature resistant heat insulation
In Shandong, coating Co., Ltd prepares the resistance to burning of 100KG high temperature resistant heat insulations using the method for the embodiment of the present invention 1
Metallic paint, and the mark of the resistance to average behavior parameter and prior art products for burning metallic paint of the high temperature resistant heat insulation made of inspection institute
Quasi- performance requirement contrasts situation, record such as table 1 below:
Product various performance parameters obtained by the embodiment 1 of table 1 and the contrast table of standard performance requirement
Parameter index | Standard performance requirement | This coating property |
Visible reflectance | > 85% | 95% |
Drying time | ≤1.5h | 1h |
PH value | > 8.5 | 9 |
Thermal conductivity factor | ≤0.09W/(m·K) | 0.05W/(m·K) |
Hardness | > 6.5HB | 7.5HB |
Adhesive force | > 15Mpa | 20Mpa |
Fire-protection rating | A levels | A levels |
Test example 2:The resistance to service check for burning metallic paint of high temperature resistant heat insulation
In Shandong, coating Co., Ltd prepares the resistance to burning of 100KG high temperature resistant heat insulations using the method for the embodiment of the present invention 2
Metallic paint, and the mark of the resistance to average behavior parameter and prior art products for burning metallic paint of the high temperature resistant heat insulation made of inspection institute
Quasi- performance requirement contrasts situation, record such as table 2 below:
Test example 3:The resistance to service check for burning metallic paint of high temperature resistant heat insulation
In Shandong, coating Co., Ltd prepares the resistance to burning of 100KG high temperature resistant heat insulations using the method for the embodiment of the present invention 3
Metallic paint, and the mark of the resistance to average behavior parameter and prior art products for burning metallic paint of the high temperature resistant heat insulation made of inspection institute
Quasi- performance requirement contrasts situation, record such as table 3 below:
Parameter index | Standard performance requirement | This coating property |
Visible reflectance | > 85% | 89% |
Drying time | ≤1.5h | 1.25h |
PH value | > 8.5 | 8.7 |
Thermal conductivity factor | ≤0.09W/(m·K) | 0.07W/(m·K) |
Hardness | > 6.5HB | 6.8HB |
Adhesive force | > 15Mpa | 16Mpa |
Fire-protection rating | A levels | A levels |
Test example 4:The resistance to service check for burning metallic paint of high temperature resistant heat insulation
In Shandong, coating Co., Ltd prepares the resistance to burning of 100KG high temperature resistant heat insulations using the method for the embodiment of the present invention 4
Metallic paint, and the mark of the resistance to average behavior parameter and prior art products for burning metallic paint of the high temperature resistant heat insulation made of inspection institute
Quasi- performance requirement contrasts situation, record such as table 4 below:
Test example 5:The resistance to service check for burning metallic paint of high temperature resistant heat insulation
In Shandong, coating Co., Ltd prepares the resistance to burning of 100KG high temperature resistant heat insulations using the method for the embodiment of the present invention 5
Metallic paint, and the mark of the resistance to average behavior parameter and prior art products for burning metallic paint of the high temperature resistant heat insulation made of inspection institute
Quasi- performance requirement contrasts situation, record such as table 5 below:
Parameter index | Standard performance requirement | This coating property |
Visible reflectance | > 85% | 87% |
Drying time | ≤1.5h | 1.6h |
PH value | > 8.5 | 8.7 |
Thermal conductivity factor | ≤0.09W/(m·K) | 0.08W/(m·K) |
Hardness | > 6.5HB | 6.6HB |
Adhesive force | > 15Mpa | 18Mpa |
Fire-protection rating | A levels | A levels |
This metallic paint can be seen that compared with the standard performance of prior art products by above-mentioned test example, visible
Light reflectivity, drying time, thermal conductivity factor, hardness, adhesive force various aspects of performance have certain improvement.This coating has resistance to
Wen Gao, it is heat-insulated it is good, have the features such as corrosion-resistant, wear-resisting concurrently, have the resistance to burning protective effect of good high temperature to metal, can be in coated object
Surface, which forms one layer, has higher volume resistivity, can bear strong electric without breakdown ceramic coating;Coating is fine and close, firmly
Degree is high, is adapted to brushing to form the layer of resistance to burning on various metals;The coating has higher mechanical strength and good chemically stable
Property, can be ageing-resistant, it is water-fast, it is resistant to chemical etching;Also have mechanical resistant impact and thermal shock resistance properties, the coating can be corresponding simultaneously
Continuously worked under operating temperature;Coating using heat-resisting good solid solution as filler, through with binding agent and coating additive etc.
The homogeneous system that component grinding forms.Coating has heatproof height, heat-insulated good, the good characteristic such as corrosion-resistant, wear-resisting is had concurrently, to metal
There is the resistance to burning protective effect of good high temperature, more effectively meet the needs of people.
Above-mentioned embodiment cannot function as limiting the scope of the invention, for the technology people of the art
For member, any alternate modification or conversion made to embodiment of the present invention are all fallen within protection scope of the present invention.
Part is not described in detail by the present invention, is the known technology of those skilled in the art of the present technique.
Claims (10)
- A kind of 1. high temperature resistant heat insulation metallic paint of resistance to burning, it is characterised in that:Composition including following parts by weight is made:Resistance to thermosetting Melt 20-50 parts, boron nitride are 5-15 parts, α-AL2O3For 5-15 parts, mica powder 5-15 parts, binding agent 20-50 parts, coating additive 9-15 parts.
- A kind of 2. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 1, it is characterised in that:Heat-resisting solid solution 37 Part, boron nitride are 10 parts, α-AL2O3For 10 parts, 10 parts of mica powder, 40 parts of binding agent, 7 parts of coating additive.
- A kind of 3. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 1 or 2, it is characterised in that:The resistance to thermosetting Melt includes the composition of following parts by weight:Kaolin 5-20 parts, cordierite 7-15 parts, vermiculite 3-10 parts, silica 3-10 parts.
- A kind of 4. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 3, it is characterised in that:The heat-resisting solid solution Include the composition of following parts by weight:10 parts of kaolin, 10 parts of cordierite, 5 parts of vermiculite, 6 parts of silica.
- A kind of 5. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 4, it is characterised in that:The resistance to thermosetting Melt also includes the composition of following parts by weight:Nepheline 2-10 parts.
- A kind of 6. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 5, it is characterised in that:The binding agent includes The composition of following parts by weight is made:Silicic acid glue solution 10-25 parts, chrome green micro mist 10-25 parts.
- A kind of 7. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 6, it is characterised in that:The silicic acid glue is molten Liquid concentration is 20%.
- A kind of 8. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 7, it is characterised in that:The coating additive bag The composition for including following parts by weight is made:Dispersant 2-4 parts, thickener 3-6 parts, PH value conditioning agent 3-6 parts, bactericide 1-3 Part.
- A kind of 9. high temperature resistant heat insulation metallic paint of resistance to burning according to claim 8, it is characterised in that:The dispersant is six Sodium metaphosphate, thickener are hydroxypropyl methylcellulose, pH value conditioning agent is organic alcohol amine CP-802, bactericide is C-15 bactericide.
- 10. the resistance to preparation method for burning metallic paint of a kind of high temperature resistant heat insulation according to any one in claim 1-9, its It is characterised by:Comprise the following steps:S1:By 1300 DEG C of fusings after kaolin, cordierite, vermiculite, silica, nepheline mixing;S2:Water quenching, drying;S3:325 mesh sieve, and obtain a kind of primary solid solution filler porous, Heat-resistant stable is good;S4:The micro mist of the primary solid solution filler and the zirconium oxide that particle mean size is 1 μ is calcined to 1850 DEG C again, obtains Required heat-resisting solid solution;S5:20% silicic acid glue solution mixes with chrome green micro mist to be ground 10 hours by 320r/ bulb separations, obtained colloidal sol shape Binding agent;S6:Calgon, hydroxypropyl methylcellulose, organic alcohol amine CP-802, C-15 bactericide are mixed to prepare coating additive;S7:By coating additive, boron nitride, α-AL made from binding agent made from obtained heat-resisting solid solution in S4, S5, S62O3、 Mica powder mixed grinding, mixture is set to obtain this high temperature resistant heat insulation metallic paint of resistance to burning in homogeneous system.