CN107793773A - A kind of high-performance anti-corrosion water-proof environmental protection new material - Google Patents
A kind of high-performance anti-corrosion water-proof environmental protection new material Download PDFInfo
- Publication number
- CN107793773A CN107793773A CN201711082769.2A CN201711082769A CN107793773A CN 107793773 A CN107793773 A CN 107793773A CN 201711082769 A CN201711082769 A CN 201711082769A CN 107793773 A CN107793773 A CN 107793773A
- Authority
- CN
- China
- Prior art keywords
- parts
- new material
- water
- environmental protection
- proof environmental
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of high-performance anti-corrosion water-proof environmental protection new material, it is composed of the following raw materials by weight:35 45 parts of pitch, 15 25 parts of natural rubber powder, 25 35 parts of neoprene, 20 30 parts of Corvic, 79 parts of retinasphal, 57 parts of graphite, 69 parts of nano silicon, 46 parts of nanometer silicon carbide, 46 parts of metallocene PE, 46 parts of nano aluminium oxide, 0.4 0.6 parts of graphene, 6 10 parts of zinc oxide, 10 13 parts of light stabilizer, 10 14 parts of watery water-proofing agent.In the manner described above, several different materials are proportionally coordinated and is combined into a kind of new material, the new material composition is simple, and waterproof, antiseptic property are good, and tensile strength is high, has a good heat resistance, and market application foreground is extensive.
Description
Technical field
The present invention relates to new material technology field, more particularly to a kind of high-performance anti-corrosion water-proof environmental protection new material.
Background technology
Pitch class or high score subclass waterproof material are immersed on carcass, the waterproof material product being fabricated to is with coiled material shape
Formula provides, referred to as waterproof roll.It is different according to main composition material, it is divided into asphalt water-proof coiled material, high-polymer modified pitch waterproof
Coiled material and synthetic polymeric waterproofing material;No carcass coiled material, paper tire coiled material, glass fibre tire volume are divided into according to the difference of carcass
Material, glass cloth tire coiled material and polyethylene tire coiled material.It is mainly used for construction wall, roofing and tunnel, highway, garbage loading embeading
Etc., play and resist extraneous rainwater, a kind of rollable flexible building material product into web-like of underground water seepage, as engineering
Ne-leakage connects between basis and building, is first of barrier of whole engineering waterproofing, whole engineering is played heavy to closing
The effect wanted.Product mainly has asphalt water-proof coiled material and polymer membranes.
At present, there is the shortcomings of non-refractory, antiseptic property difference and the scope of application is small in existing waterproof roll.Due to
Present extreme weather protrudes, and the performance of existing waterproof roll has been unable to meet demand, therefore the performance for improving waterproof roll has turned into
The technical problem of urgent need to resolve.
The content of the invention
The technical problems to be solved by the invention are to provide a kind of high-performance anti-corrosion water-proof environmental protection new material, it is intended to solve
The problem of existing waterproof roll poor performance.
The technical scheme that the present invention solves above-mentioned technical problem is as follows:
A kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Pitch 35-45 parts, natural gum
Powder 15-25 parts, neoprene 25-35 parts, Corvic 20-30 parts, retinasphal 7-9 parts, graphite 5-7 parts, nanometer two
Silica 6-9 parts, nanometer silicon carbide 4-6 parts, metallocene PE 4-6 parts, nano aluminium oxide 4-6 parts, graphene 0.4-0.6
Part, zinc oxide 6-10 parts, light stabilizer 10-13 parts, watery water-proofing agent 10-14 parts.
On the basis of above-mentioned technical proposal, the present invention can also do following improvement.
Further, the new material is composed of the following raw materials by weight:38 parts of pitch, 20 parts of natural rubber powder, neoprene
30 parts, 25 parts of Corvic, 8 parts of retinasphal, 6 parts of graphite, 8 parts of nano silicon, 5 parts of nanometer silicon carbide, cyclopentadienyl gold
Belong to 5 parts of polyethylene, 5 parts of nano aluminium oxide, 0.5 part of graphene, 8 parts of zinc oxide, 12 parts of light stabilizer, 12 parts of watery water-proofing agent.
Further, the light stabilizer is titanium oxide.
Further, the waterborne preservative is PM-4700.
Further, the preparation method of described new material, comprises the following steps:Each component is mixed, mixed in kneader
Refining, 2.5-4.5 hours are handled under the conditions of 145-165 DEG C, anti-refining plasticizing, is made into sizing material, dip-coating is in non-woven fabrics on twin-roll machine
Wound, it is made after drying.
The beneficial effects of the invention are as follows:Present component is simple, and manufacture craft is simple, reduces the labor intensity of employee
And production cost, meanwhile, the new material has good waterproof, antiseptic property, and tensile strength is high, high temperature resistant, has a wide range of application
It is general.
Embodiment
The principle and feature of the present invention are described below in conjunction with specific embodiment, example is served only for explaining this
Invention, is not intended to limit the scope of the present invention.
Embodiment 1
The present embodiment provides a kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Pitch 38
Part, 20 parts of natural rubber powder, 30 parts of neoprene, 25 parts of Corvic, 8 parts of retinasphal, 6 parts of graphite, nanometer titanium dioxide
8 parts of silicon, 5 parts of nanometer silicon carbide, 5 parts of metallocene PE, 5 parts of nano aluminium oxide, 0.5 part of graphene, 8 parts of zinc oxide, light are steady
Determine 12 parts of agent, 12 parts of watery water-proofing agent.
The preparation method of above-mentioned new material is as follows:Each component is mixed, is kneaded in kneader, in 145-165 DEG C of condition
Lower processing 2.5-4.5 hours, anti-refining plasticizing, is made into sizing material on twin-roll machine, and dip-coating is hindered in non-woven fabrics, is made after drying.
Embodiment 2
The present embodiment provides a kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Pitch 36
Part, 16 parts of natural rubber powder, 26 parts of neoprene, 20 parts of Corvic, 7 parts of retinasphal, 5 parts of graphite, nanometer titanium dioxide
6 parts of silicon, 4 parts of nanometer silicon carbide, 4 parts of metallocene PE, 4 parts of nano aluminium oxide, 0.4 part of graphene, 6 parts of zinc oxide, light are steady
Determine 10 parts of agent, 11 parts of watery water-proofing agent.
The preparation method of above-mentioned new material is as follows:Each component is mixed, is kneaded in kneader, in 145-165 DEG C of condition
Lower processing 2.5-4.5 hours, anti-refining plasticizing, is made into sizing material on twin-roll machine, and dip-coating is hindered in non-woven fabrics, is made after drying.
Embodiment 3
The present embodiment provides a kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Pitch 44
Part, 24 parts of natural rubber powder, 34 parts of neoprene, 30 parts of Corvic, 9 parts of retinasphal, 7 parts of graphite, nanometer titanium dioxide
9 parts of silicon, 6 parts of nanometer silicon carbide, 6 parts of metallocene PE, 6 parts of nano aluminium oxide, 0.6 part of graphene, 10 parts of zinc oxide, light
13 parts of stabilizer, 13 parts of watery water-proofing agent.
The preparation method of above-mentioned new material is as follows:Each component is mixed, is kneaded in kneader, in 145-165 DEG C of condition
Lower processing 2.5-4.5 hours, anti-refining plasticizing, is made into sizing material on twin-roll machine, and dip-coating is hindered in non-woven fabrics, is made after drying.
Comparative example 1
This comparative example provides a kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Natural gum
24 parts of powder, 34 parts of neoprene, 30 parts of Corvic, 9 parts of retinasphal, 7 parts of graphite, 9 parts of nano silicon, receive
6 parts of carborundum of rice, 6 parts of metallocene PE, 6 parts of nano aluminium oxide, 0.6 part of graphene, 10 parts of zinc oxide, light stabilizer 13
Part, 13 parts of watery water-proofing agent.
The preparation method of above-mentioned new material is as follows:Each component is mixed, is kneaded in kneader, in 145-165 DEG C of condition
Lower processing 2.5-4.5 hours, anti-refining plasticizing, is made into sizing material on twin-roll machine, and dip-coating is hindered in non-woven fabrics, is made after drying.
Comparative example 2
This comparative example provides a kind of high-performance anti-corrosion water-proof environmental protection new material, is composed of the following raw materials by weight:Pitch 44
Part, 24 parts of natural rubber powder, 30 parts of Corvic, 9 parts of retinasphal, 7 parts of graphite, 9 parts of nano silicon, nano-sized carbon
6 parts of SiClx, 6 parts of metallocene PE, 6 parts of nano aluminium oxide, 0.6 part of graphene, 10 parts of zinc oxide, 13 parts of light stabilizer, water
13 parts of waterproofing agent of property.
The preparation method of above-mentioned new material is as follows:Each component is mixed, is kneaded in kneader, in 145-165 DEG C of condition
Lower processing 2.5-4.5 hours, anti-refining plasticizing, is made into sizing material on twin-roll machine, and dip-coating is hindered in non-woven fabrics, is made after drying.
It is that the anti-corrosion water-proof environmental protection material for preparing three groups of embodiments and two groups of comparative examples carries out performance test below
As a result:
Example | Embodiment 1 | Embodiment 2 | Embodiment 3 | Comparative example 1 | Comparative example 2 |
Seepage rate (%) | 0.08 | 0.05 | 0.07 | 0.15 | 0.13 |
Rate of corrosion (mm/a) | 0.07 | 0.05 | 0.06 | 0.11 | 0.14 |
Deform minimum temperature (DEG C) | 298 | 303 | 296 | 285 | 279 |
Above-mentioned measurement result shows that green wood material formula provided by the invention is reasonable, hence it is evident that improves the material waterproofing, prevents
The performances such as rotten and high temperature resistant so that the material is resistant to more dislike the weather condition of summary during use, extends
The service life of material, cost reduce, economic results in society.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (5)
1. a kind of high-performance anti-corrosion water-proof environmental protection new material, it is characterised in that be composed of the following raw materials by weight:Pitch 35-45
Part, natural rubber powder 15-25 parts, neoprene 25-35 parts, Corvic 20-30 parts, retinasphal 7-9 parts, graphite 5-7
Part, nano silicon 6-9 parts, nanometer silicon carbide 4-6 parts, metallocene PE 4-6 parts, nano aluminium oxide 4-6 parts, graphene
0.4-0.6 parts, zinc oxide 6-10 parts, light stabilizer 10-13 parts, watery water-proofing agent 10-14 parts.
2. a kind of high-performance anti-corrosion water-proof environmental protection new material according to claim 1, it is characterised in that by following parts by weight
Raw material forms:38 parts of pitch, 20 parts of natural rubber powder, 30 parts of neoprene, 25 parts of Corvic, 8 parts of retinasphal, graphite
6 parts, 8 parts of nano silicon, 5 parts of nanometer silicon carbide, 5 parts of metallocene PE, 5 parts of nano aluminium oxide, 0.5 part of graphene,
8 parts of zinc oxide, 12 parts of light stabilizer, 12 parts of watery water-proofing agent.
A kind of 3. high-performance anti-corrosion water-proof environmental protection new material according to claim 1, it is characterised in that:The light stabilizer
For titanium oxide.
A kind of 4. high-performance anti-corrosion water-proof environmental protection new material according to claim 1, it is characterised in that:The water-repellent preservation
Agent is PM-4700.
5. a kind of preparation method of new material as claimed in claim 1 or 2, it is characterised in that comprise the following steps:By each component
Mixing, is kneaded in kneader, and 2.5-4.5 hours are handled under the conditions of 145-165 DEG C, and anti-refining plasticizing, is made on twin-roll machine
Sizing material, dip-coating are hindered in non-woven fabrics, are made after drying.