CN107715364A - 一种抑烟型干粉灭火剂及其制备方法 - Google Patents

一种抑烟型干粉灭火剂及其制备方法 Download PDF

Info

Publication number
CN107715364A
CN107715364A CN201711106715.5A CN201711106715A CN107715364A CN 107715364 A CN107715364 A CN 107715364A CN 201711106715 A CN201711106715 A CN 201711106715A CN 107715364 A CN107715364 A CN 107715364A
Authority
CN
China
Prior art keywords
parts
smoke
extinguishing agent
powder extinguishing
inhibiting type
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201711106715.5A
Other languages
English (en)
Inventor
卢思迪
王伟
鲁怀宁
左振
王哲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU LONGTAI FIRE-FIGHTING Co Ltd
Original Assignee
BENGBU LONGTAI FIRE-FIGHTING Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU LONGTAI FIRE-FIGHTING Co Ltd filed Critical BENGBU LONGTAI FIRE-FIGHTING Co Ltd
Priority to CN201711106715.5A priority Critical patent/CN107715364A/zh
Publication of CN107715364A publication Critical patent/CN107715364A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵60‑70份、膨润土10‑15份、氢氧化铝12‑14份、氢氧化镁8‑9份、全氟己酮2‑4份、二磷酸吡啶核苷酸2‑3份、硝酸二羟铋2‑3份、石墨粉2‑3份、无机硅胶1‑2份。本发明还公开了上述抑烟型干粉灭火剂的制备方法。本发明的干粉灭火剂能够弥补现有干粉灭火剂灭火时烟雾量较大的缺陷。

Description

一种抑烟型干粉灭火剂及其制备方法
技术领域
本发明涉及灭火剂，尤其涉及一种抑烟型干粉灭火剂及其制备方法。
背景技术
干粉灭火剂是由灭火基料和适量润滑剂、少量防潮剂混合后共同研磨制成的细小颗粒，用二氧化碳作喷射动力。喷射出来的粉末，浓度密集，颗粒微细，盖在固体燃烧物上能够构成阻碍燃烧的隔离层，同时析出不可燃气体，使空气中的氧气浓度降低，火焰熄灭。干粉灭火剂，可以灌装于各种类型的手提式和固定式干粉灭火装置内，可与氟蛋白泡沫灭火剂、水成膜泡沫灭火剂联用，扑救油罐的初起火灾，能快速控制火焰发展，起到迅速灭火的作用。
目前市面上大部分干粉灭火剂，其性能差异较大，普遍存在灭火效能低、污染严重问题、尤其是灭火时烟雾量较大的缺陷，因此需加强对此方面的研究，进一步改善缺陷。
发明内容
基于背景技术存在的技术问题，本发明提出了一种抑烟型干粉灭火剂及其制备方法，以弥补现有干粉灭火剂灭火时烟雾量较大的缺陷。
本发明提出的一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵60-70份、膨润土10-15份、氢氧化铝12-14份、氢氧化镁8-9份、全氟己酮2-4份、二磷酸吡啶核苷酸2-3份、硝酸二羟铋2-3份、石墨粉2-3份、无机硅胶1-2份。
优选地，其原料按重量份包括：磷酸铵62-68份、膨润土12-14份、氢氧化铝12.5-13.5份、氢氧化镁8.2-8.8份、全氟己酮2.5-3.5份、二磷酸吡啶核苷酸2.3-2.9份、硝酸二羟铋2.3-2.9份、石墨粉2.3-2.9份、无机硅胶1.3-1.8份。
优选地，所述石墨粉与无机硅胶的重量比为2.5-2.6：1.5-1.7。
优选地，所述磷酸铵的粒径小于0.5mm。
优选地，所述石墨粉的粒径小于0.5mm。
本发明还提供一种所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至80-90℃，保温搅拌，真空干燥，过400-500目筛，得到抑烟型干粉灭火剂。
优选地，研磨的时间为40-50min。
优选地，搅拌的时间为1-2h。
上述真空干燥的温度和时间均不作限定，达到干燥的状态即可。
本发明的干粉灭火剂以磷酸铵作为酸源，采用石墨粉作为碳源，两者互配能在可燃物表面形成致密炭层，阻止火焰的蔓延，加入氢氧化铝和氢氧化镁，两者互配后，吸热效果优异，且能吸附在上述炭层表面，显著提高干粉灭火剂的灭火效果，同时提高干粉灭火剂的热稳定性；加入二磷酸吡啶核苷酸、硝酸二羟铋，与磷酸铵、氢氧化铝、氢氧化镁配合作用，能够大幅度降低灭火时材料表面的烟雾释放量，对于抑制烟雾的效果显著；加入全氟己酮、膨润土，两者配合作用，能够有效抑制火焰的蔓延，进一步提高干粉灭火剂的灭火效果；加入膨润土、无机硅胶，与磷酸铵互配能够提升干粉灭火剂的防潮防结块性能。
具体实施方式
下面，通过具体实施例对本发明的技术方案进行详细说明。
实施例1
一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵60份、膨润土15份、氢氧化铝12份、氢氧化镁9份、全氟己酮2份、二磷酸吡啶核苷酸3份、硝酸二羟铋2份、石墨粉3份、无机硅胶1份。
所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至90℃，保温搅拌，真空干燥，过400目筛，得到抑烟型干粉灭火剂。
实施例2
一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵70份、膨润土10份、氢氧化铝14份、氢氧化镁8份、全氟己酮4份、二磷酸吡啶核苷酸2份、硝酸二羟铋3份、石墨粉2份、无机硅胶2份；
其中，所述磷酸铵的粒径小于0.5mm；
所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至80℃，保温搅拌，真空干燥，过500目筛，得到抑烟型干粉灭火剂。
实施例3
一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵65份、膨润土13份、氢氧化铝13份、氢氧化镁8.5份、全氟己酮3份、二磷酸吡啶核苷酸2.5份、硝酸二羟铋2.5份、石墨粉2.5份、无机硅胶1.5份；
其中，所述磷酸铵的粒径小于0.5mm；
所述石墨粉的粒径小于0.5mm。
所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至85℃，保温搅拌，真空干燥，过400目筛，得到抑烟型干粉灭火剂。
实施例4
一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵62份、膨润土14份、氢氧化铝12.5份、氢氧化镁8.8份、全氟己酮2.5份、二磷酸吡啶核苷酸2.9份、硝酸二羟铋2.3份、石墨粉2.9份、无机硅胶1.3份；
其中，所述磷酸铵的粒径小于0.5mm；
所述石墨粉的粒径小于0.5mm。
所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至82℃，保温搅拌，真空干燥，过500目筛，得到抑烟型干粉灭火剂；
其中，研磨的时间为40min；
搅拌的时间为2h。
实施例5
一种抑烟型干粉灭火剂，其原料按重量份包括：磷酸铵68份、膨润土12份、氢氧化铝13.5份、氢氧化镁8.2份、全氟己酮3.5份、二磷酸吡啶核苷酸2.3份、硝酸二羟铋2.9份、石墨粉2.3份、无机硅胶1.8份；
其中，所述磷酸铵的粒径小于0.5mm；
所述石墨粉的粒径小于0.5mm。
所述抑烟型干粉灭火剂的制备方法，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至88℃，保温搅拌，真空干燥，过400目筛，得到抑烟型干粉灭火剂；
其中，研磨的时间为50min；
搅拌的时间为1h。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。

Claims (8)

1.一种抑烟型干粉灭火剂，其特征在于，其原料按重量份包括：磷酸铵60-70份、膨润土10-15份、氢氧化铝12-14份、氢氧化镁8-9份、全氟己酮2-4份、二磷酸吡啶核苷酸2-3份、硝酸二羟铋2-3份、石墨粉2-3份、无机硅胶1-2份。
2.根据权利要求1所述抑烟型干粉灭火剂，其特征在于，其原料按重量份包括：磷酸铵62-68份、膨润土12-14份、氢氧化铝12.5-13.5份、氢氧化镁8.2-8.8份、全氟己酮2.5-3.5份、二磷酸吡啶核苷酸2.3-2.9份、硝酸二羟铋2.3-2.9份、石墨粉2.3-2.9份、无机硅胶1.3-1.8份。
3.根据权利要求1或2所述抑烟型干粉灭火剂，其特征在于，所述石墨粉与无机硅胶的重量比为2.5-2.6：1.5-1.7。
4.根据权利要求1-3任一项所述抑烟型干粉灭火剂，其特征在于，所述磷酸铵的粒径小于0.5mm。
5.根据权利要求1-4任一项所述抑烟型干粉灭火剂，其特征在于，所述石墨粉的粒径小于0.5mm。
6.一种如权利要求1-5任一项所述抑烟型干粉灭火剂的制备方法，其特征在于，包括如下步骤：按组成原料的重量份称取各原料，将磷酸铵、膨润土、石墨粉和无机硅胶混合，研磨，依次加入氢氧化铝、氢氧化镁、全氟己酮、二磷酸吡啶核苷酸、硝酸二羟铋，升温至80-90℃，保温搅拌，真空干燥，过400-500目筛，得到抑烟型干粉灭火剂。
7.根据权利要求6所述抑烟型干粉灭火剂的制备方法，其特征在于，研磨的时间为40-50min。
8.根据权利要求6或7所述抑烟型干粉灭火剂的制备方法，其特征在于，搅拌的时间为1-2h。
CN201711106715.5A 2017-11-10 2017-11-10 一种抑烟型干粉灭火剂及其制备方法 Withdrawn CN107715364A (zh)