CN107696651A - Packaging tube composite and preparation method thereof and packaging tube - Google Patents
Packaging tube composite and preparation method thereof and packaging tube Download PDFInfo
- Publication number
- CN107696651A CN107696651A CN201710885780.6A CN201710885780A CN107696651A CN 107696651 A CN107696651 A CN 107696651A CN 201710885780 A CN201710885780 A CN 201710885780A CN 107696651 A CN107696651 A CN 107696651A
- Authority
- CN
- China
- Prior art keywords
- composite
- films
- packaging tube
- film
- vinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a kind of packaging tube composite and preparation method thereof and packaging tube, is related to chemical product packaging material field, and the theca interna of the packaging tube composite includes PE films and ethylene-vinyl alcohol copolymer film.The technical problem of existing daily chemical product packaging tube resistance to corrosion difference can be alleviated using above-mentioned composite, improve the resistance to corrosion of packaging tube composite.
Description
Technical field
The present invention relates to chemical product field of packaging material, more particularly, to a kind of packaging tube composite and its
Preparation method and packaging tube.
Background technology
With the development of science and technology, the research and development of the daily use chemicals nursing product such as toothpaste and cosmetics are a hundred flowers contend in beauty, and new formula is not
Disconnected application, whitening, maintenance, beauty treatment, face cleaning and other effects have qualitative leap.Accordingly, the active component in various daily chemical products
Also increase therewith.Therefore, the material of external packaging tube proposes new test.
At present, existing packaging tube is typically combined with composite by multilayer material, and its concrete structure is generally:
Polyethylene/tack coat/barrier layer/tack coat/polyethylene, polyethylene (Polyethylene, abbreviation PE).Nursed in face of daily use chemicals
During the active all the more bioactive molecule of product, its packaging function seems awkward, or even when packing some lotions, PE is straight with lotion
Contacting, the active component in lotion penetrates the corrosion that PE layers reach tack coat and barrier layer can cause tack coat and barrier layer,
Cause packaging material layering or adhesion strength step-down, have impact on the security of packaging.
In view of this, it is special to propose the present invention.
The content of the invention
The first object of the present invention is to provide a kind of packaging tube composite, to alleviate existing daily chemical product bag
Fill the technical problem of flexible pipe resistance to corrosion difference.
Second object of the present invention is to provide a kind of preparation method of packaging tube composite, this method preparation
Technique is simple, is adapted to industrialized production.
The third object of the present invention is to provide a kind of packaging tube, and the packaging tube has excellent resistance to corrosion,
The security of packaging is higher.
In order to realize the above-mentioned purpose of the present invention, spy uses following technical scheme:
A kind of packaging tube composite, the theca interna of the composite include PE films and ethylene vinyl alcohol copolymer
Thing film.
Further, in the theca interna, the percentage thickness of the PE films is 70%-80%, the ethylene-vinyl alcohol
The percentage thickness of co-polymer membrane is 20%-30%.
Further, the structure of the theca interna is PE films/ethylene vinyl alcohol copolymer film/PE films.
Further, the theca interna of the composite also includes nylon membrane.
Further, in the theca interna, the percentage thickness of the PE films is 70%-84%, the ethylene-vinyl alcohol
The percentage thickness of co-polymer membrane is 8%-15%;The percentage thickness of the nylon membrane is 8%-15%.
Further, the structure of the theca interna is PE films/ethylene vinyl alcohol copolymer film/nylon membrane/PE films.
Further, the composite is followed successively by from outside to inside:PE layers/tack coat/barrier layer/tack coat/PE films with
The composite film or PE films of ethylene vinyl alcohol copolymer film, the composite film of ethylene vinyl alcohol copolymer film and nylon membrane.
Further, the barrier layer includes aluminium foil layer, evoh layer, pet layer, PVDC layers or plating silicon
Any of material or at least two combination.
Further, the binding agent is ethylene acrylic acid co polymer, polyvinyl resin, anticorrosive glue or at least two
Combination.
A kind of preparation method of above-mentioned packaging tube composite, including by PE and ethylene-vinyl alcohol copolymer and
Optionally nylon composite membrane-forming the step of.
Further, the preparation method of above-mentioned packaging tube composite comprises the following steps:By PE and ethylene-vinyl
It is compound using binding agent and barrier layer after alcohol copolymer and optionally nylon composite membrane-forming, binding agent and outer layer are recycled afterwards
PE layers bonding is compound, obtains the packaging tube composite.
Further, the step of composite membrane-forming includes the preparation technology of multi-layer co-extruded shaping.
Further, the preparation method of above-mentioned packaging tube composite comprises the following steps:
Step a):With ter-polymer resin by PE and ethylene-vinyl alcohol copolymer and optionally nylon inflation film manufacturing machine
Coextrusion mold obtains composite film;The technological parameter of extrusion is:220-320 DEG C of processing temperature, unwinding tension 15-25kg,
Winding tension 20-35kg, composite pressure 4-6kg;
Step b):The composite film obtained in step a) and barrier layer are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:220-320 DEG C of processing temperature, unwinding tension 15-
25kg, winding tension 20-35kg, composite pressure 4-6kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And obtain the packaging tube composite using extrusion composite technology;Extrusion composite technology parameter is:Processing temperature 220-
320 DEG C, unwinding tension 15-25kg, winding tension 20-35kg, composite pressure 4-6kg.
A kind of packaging tube, it is prepared by above-mentioned composite.
Compared with the prior art, the present invention has the advantages that:
Packaging tube composite provided by the invention, its theca interna include PE films and ethylene vinyl alcohol copolymer film,
By the combination of both films, the active component in chemical product can be effectively prevented to pass through theca interna corrosion barrier and inner membrance
Tack coat between layer and barrier layer, and then strengthen the corrosion resistance of composite.
Embodiment
Embodiment of the present invention is described in detail below in conjunction with embodiment, but those skilled in the art will
Understand, the following example is merely to illustrate the present invention, and is not construed as limiting the scope of the present invention.It is unreceipted specific in embodiment
Condition person, the condition suggested according to normal condition or manufacturer are carried out.Agents useful for same or the unreceipted production firm person of instrument, it is
The conventional products that can be obtained by commercially available purchase.
One aspect of the present invention provides a kind of packaging tube composite, and the theca interna of the composite includes
PE films and ethylene vinyl alcohol copolymer film.
Packaging tube composite provided by the invention, its theca interna include PE films and ethylene vinyl alcohol copolymer film,
By the combination of both films, the active component in chemical product can be effectively prevented to pass through theca interna corrosion barrier and inner membrance
Tack coat between layer and barrier layer, and then strengthen the corrosion resistance of composite.The present invention is intended to provide a variety of new formulas
Erosion-resisting composite, to provide security requirement of the daily use chemicals nursing product to packaging.
Polyethylene (Polyethylene, abbreviation PE) is a kind of aggregated obtained thermoplastic resin of ethene.Industrially,
Also the copolymer of ethene and a small amount of alpha-olefin is included.Polyethylene is odorless, nontoxic, feel ceraceous, has excellent resistance to low temperature
(minimum reachable -100~-70 DEG C of temperature in use), chemical stability is good, is resistant to the erosion of most of soda acids, but intolerant to
The acid of oxidizing property.
Ethylene-vinyl alcohol copolymer, abbreviation EVOH, it is the barrier by polyvinyl processability and vinyl alcohol polymer
Effect is combined, and ethylene-vinyl alcohol copolymer not only shows fabulous processing characteristics, and to gas, smell, spices,
Solvent etc. shows excellent blocking effect.
It is used as the inner layer material of chemical product packaging tube composite by the way that PE is combined with EVOH in the present invention, can shows
Write and improve its corrosion resistance, and there is preferable stability.
As the preferred embodiment of the present invention, in the theca interna, the percentage thickness of the PE films is 70%-
80%, the percentage thickness of the ethylene vinyl alcohol copolymer film is 20%-30%.By optimizing answering for PE films and EVOH films
The decay resistance of packaging tube composite can be further enhanced by closing thickness proportion.
In the above-mentioned preferred embodiment of the present invention, the typical but non-limiting percentage thickness of PE films is such as:70%th,
71%th, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79% or 80%.
In the above-mentioned preferred embodiment of the present invention, the typical but non-limiting part by weight of EVOH films is such as:20%th,
21%th, 22%, 23%, 24%, 25%, 26%, 27%, 28%, 29% or 30%.
As the preferred embodiment of the present invention, the structure of the theca interna for PE films/ethylene vinyl alcohol copolymer film/
PE films.Using two layers of PE membrane structure, it can preferably protect EVOH injury-free, bioactive molecule passes through after preventing EVOH impaired
EVOH causes to corrode.
As the preferred embodiment of the present invention, the theca interna of the composite also includes nylon membrane.
Nylon has a good combination property, including mechanical property, heat resistance, wear resistance, chemical proofing and from
Lubricity, and coefficient of friction is low, there is certain anti-flammability, it is easy to process.
It is used as chemical product packaging tube composite wood by the way that PE is combined with EVOH and nylon in above-mentioned preferred embodiment
The inner layer material of material, its corrosion resistance is remarkably improved, and there is preferable stability.
As the preferred embodiment of the present invention, in the theca interna, the percentage thickness of the PE films is 70%-
84%, the percentage thickness of the ethylene vinyl alcohol copolymer film is 8%-15%;The percentage thickness of the nylon membrane is
8%-15%.
In the above-mentioned preferred embodiment of the present invention, the typical but non-limiting percentage thickness of PE films is such as:70%th,
71%th, 72%, 73%, 74%, 75%, 76%, 77%, 78%, 79%, 80%, 81%, 82%, 83% or 84%.
In the above-mentioned preferred embodiment of the present invention, the typical but non-limiting part by weight of EVOH films is such as:8%th,
9%th, 10%, 11%, 12%, 13%, 14% or 15%.
In the above-mentioned preferred embodiment of the present invention, the typical but non-limiting part by weight of nylon membrane is such as:8%th,
9%th, 10%, 11%, 12%, 13%, 14% or 15%.
By optimizing the composite thickness ratio of PE films and EVOH films and nylon membrane, packaging tube use can be further enhanced
The decay resistance of composite.
As the preferred embodiment of the present invention, the structure of the theca interna for PE films/ethylene vinyl alcohol copolymer film/
Nylon membrane/PE films.The addition of nylon membrane can further increase the stability and corrosion resistance of theca interna.
As the preferred embodiment of the present invention, the composite is followed successively by from outside to inside:PE layers/tack coat/barrier
Layer/tack coat/PE films and the composite film or PE films of ethylene vinyl alcohol copolymer film, ethylene vinyl alcohol copolymer film and nylon
The composite film of film.
Outer layer PE layers in composite, for providing printing functionality;Middle barrier layer provides barrier property, avoids cream
Internal moisture, smell distribute, to extend its shelf-life;Theca interna be PE films and ethylene vinyl alcohol copolymer film or PE films,
The composite film of ethylene vinyl alcohol copolymer film and nylon membrane, it is directly contacted with the material in chemical product, is prevented in chemical product
Active component to composite inner permeate, there is provided anticorrosive effect.Wherein, the barrier layer includes aluminium foil layer, ethene-second
Enol copolymer layer, polyethylene terephthalate (Polyethylene terephthalate, abbreviation PET) layer, gather partially
Dichloroethylene (Polyvinylidene Chloride, abbreviation PVDC) layer or plating any of silicon materials or at least two
Combination.
As the preferred embodiment of the present invention, the binding agent is ethylene acrylic acid co polymer, polyvinyl resin, anti-corruption
Lose glue or at least two combination.
(such as ethylene acrylic acid co polymer) adds polyvinyl resin or anticorrosive glue as binding agent in conventional glue,
The cohesive force between aluminium foil layer and theca interna can further be increased, and play the effect of impermeable, so as to further increase
The decay resistance of composite.
Anticorrosive glue in above-mentioned preferred embodiment includes polyolefin emulsion adhesive.
The second aspect of the invention provides a kind of preparation method of above-mentioned packaging tube composite, including by PE
With ethylene-vinyl alcohol copolymer and optionally nylon composite membrane-forming the step of.
As the preferred embodiment of the present invention, the preparation method of above-mentioned packaging tube composite includes following step
Suddenly:PE is compound using binding agent and aluminium foil layer with ethylene-vinyl alcohol copolymer and optionally after nylon composite membrane-forming, afterwards
Recycle binding agent to be bonded with outer layer PE layers compound, obtain the packaging tube composite.Preferably, the composite membrane-forming
The step of include the preparation technology of multi-layer co-extruded shaping.
As the preferred embodiment of the present invention, the preparation method of above-mentioned packaging tube composite includes following step
Suddenly:
Step a):With ter-polymer resin by PE and ethylene-vinyl alcohol copolymer and optionally nylon inflation film manufacturing machine
Coextrusion mold obtains composite film;The technological parameter of forming process is:220-320 DEG C of processing temperature, unwinding tension 15-25kg,
Winding tension 20-35kg, composite pressure 4-6kg;
Step b):The composite film obtained in step a) and barrier layer are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:220-320 DEG C of processing temperature, unwinding tension 15-
25kg, winding tension 20-35kg, composite pressure 4-6kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And obtain the packaging tube composite using extrusion composite technology;Extrusion composite technology parameter is:Processing temperature 220-
320 DEG C, unwinding tension 15-25kg, winding tension 20-35kg, composite pressure 4-6kg.
The third aspect of the invention provides a kind of packaging tube, is prepared by above-mentioned composite.
Below in conjunction with embodiment and comparative example, the present invention will be further described in detail.
Embodiment 1
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/aluminium foil layer/viscous
Tie the composite film of layer/PE films and ethylene vinyl alcohol copolymer film, wherein, PE films and ethylene vinyl alcohol copolymer film it is compound
The structure of film layer is PE films/ethylene vinyl alcohol copolymer film/PE films, and every layer of percentage thickness is respectively:35%th, 30% and
35%, tack coat is polyvinyl resin.
Embodiment 2
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/pet layer/viscous
Tie the composite film of layer/PE films and ethylene vinyl alcohol copolymer film, wherein, PE films and ethylene vinyl alcohol copolymer film it is compound
The structure of film layer is PE films/ethylene vinyl alcohol copolymer film/PE films, and every layer of percentage thickness is respectively:37%th, 25% and
38%, tack coat is ethylene acrylic acid co polymer.
Embodiment 3
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/PVDC layers/viscous
Tie the composite film of layer/PE films and ethylene vinyl alcohol copolymer film, wherein, PE films and ethylene vinyl alcohol copolymer film it is compound
The structure of film layer is PE films/ethylene vinyl alcohol copolymer film/PE films, and every layer of percentage thickness is respectively:40%th, 20% and
40%, tack coat is polyolefin emulsion adhesive.
Embodiment 4
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/aluminium foil layer/viscous
Tie the composite film of layer/PE films and ethylene vinyl alcohol copolymer film, wherein, PE films and ethylene vinyl alcohol copolymer film it is compound
The structure of film layer is PE films/ethylene vinyl alcohol copolymer film/PE films, and every layer of percentage thickness is respectively:37%th, 25% and
38%, tack coat is the mixture of ethylene acrylic acid co polymer and polyolefin emulsion adhesive.
Embodiment 5
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/PVDC layers/viscous
Tie the composite film of layer/PE films and ethylene vinyl alcohol copolymer film, wherein, PE films and ethylene vinyl alcohol copolymer film it is compound
The structure of film layer is PE films/ethylene vinyl alcohol copolymer film/PE films, and every layer of percentage thickness is respectively:37%th, 25% and
38%, tack coat is the mixture of polyvinyl resin and polyolefin emulsion adhesive.
Embodiment 6
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/aluminium foil layer/viscous
Tie the composite film of layer/PE films, ethylene vinyl alcohol copolymer film and nylon membrane.
Wherein, the structure of the composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane is PE films/ethylene-vinyl
Alcohol copolymer film/nylon membrane/PE films, every layer of percentage thickness are respectively:35%th, 8%, 15% and 42%, tack coat is poly-
Vinyl.
Embodiment 7
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/pet layer/viscous
Tie the composite film of layer/PE films, ethylene vinyl alcohol copolymer film and nylon membrane.
Wherein, the structure of the composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane is PE films/ethylene-vinyl
Alcohol copolymer film/nylon membrane/PE films, every layer of percentage thickness are respectively:40%th, 10%, 10% and 40%, tack coat is poly-
Olefin-based emulsion adhesive.
Embodiment 8
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/PVDC layers/viscous
Tie the composite film of layer/PE films, ethylene vinyl alcohol copolymer film and nylon membrane.
Wherein, the structure of the composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane is PE films/ethylene-vinyl
Alcohol copolymer film/nylon membrane/PE films, every layer of percentage thickness are respectively:37%th, 12%, 13% and 38%, tack coat is poly-
Olefin-based emulsion adhesive.
Embodiment 9
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/aluminium foil layer/viscous
Tie the composite film of layer/PE films, ethylene vinyl alcohol copolymer film and nylon membrane.
Wherein, the structure of the composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane is PE films/ethylene-vinyl
Alcohol copolymer film/nylon membrane/PE films, every layer of percentage thickness are respectively:37%th, 12%, 13% and 38%, tack coat is second
The mixture of alkene acrylic copolymer and polyolefin emulsion adhesive.
Embodiment 10
The present embodiment is a kind of packaging tube composite, is followed successively by from outside to inside:PE layers/tack coat/aluminium foil layer/viscous
Tie the composite film of layer/PE films, ethylene vinyl alcohol copolymer film and nylon membrane.
Wherein, the structure of the composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane is PE films/ethylene-vinyl
Alcohol copolymer film/nylon membrane/PE films, every layer of percentage thickness are respectively:37%th, 12%, 13% and 38%, tack coat is poly-
The mixture of vinyl and polyolefin emulsion adhesive.
Comparative example 1
This comparative example is a kind of packaging tube composite, is followed successively by from outside to inside:PE outer layers/tack coat/aluminium foil layer/
Tack coat/PE internal layers, tack coat are ethylene acrylic acid co polymer.
Comparative example 2
This comparative example is a kind of packaging tube composite, is followed successively by from outside to inside:PE outer layers/tack coat/aluminium foil layer/
Tack coat/EVOH internal layers, tack coat are polyvinyl resin.
Comparative example 3
This comparative example is a kind of packaging tube composite, is followed successively by from outside to inside:PE outer layers/tack coat/aluminium foil layer/
Tack coat/nylon inner layer, tack coat are polyolefin emulsion adhesive.
Respectively the specific examination of corrosion-resistant experiment is done with the packaging tube that embodiment 1-10 and comparative example 1-3 is provided with composite
It is as follows to test process:Chemical product lotion agent is applied to the packaging tube composite that embodiment 1-10 and comparative example 1-3 provide
Inner layer material surface, degradation is carried out at a temperature of being subsequently placed in 50 DEG C, interlaminar strength is carried out during experiment
Tracking and testing, test result is listed in table 1, and surface topography observes and records result and is listed in table 2.
The main component for the chemical product lotion used in experiment includes:Clear glycerine, Silicon dioxide, hydrate, water, sorbierite,
Calcium pyrophosphate, silica, rilanit special APEO, titanium dioxide, lauroyl paddy, propylhomoserin sodium, sodium chloride, carragheen
Spices, ethanol, ethylene glycol tetraacetic disodium, aminocaproic acid, dipotassium glycyrrhizinate salt, allantoin, angelica extract, Chinese herbaceous peony extraction
Thing, aluctyl, hydroxy methacrylate, propylparaben, soapberry extract, Hinokitiol, yellow 4 and yellow 1.
The interlaminar strength test data of 1 different embodiments of table and comparative example
Sequence number | Initial stage | 3 days | 7 days | 14 days | 30 days |
Embodiment 1 | 9.27 | 8.14 | 8.07 | 7.63 | 7.96 |
Embodiment 2 | 8.47 | 8.42 | 8.02 | 7.61 | 7.1 |
Embodiment 3 | 8.93 | 8.91 | 8.11 | 7.42 | 7.2 |
Embodiment 4 | 10.24 | 9.85 | 9.18 | 8.79 | 8.51 |
Embodiment 5 | 9.61 | 9.52 | 8.97 | 8.86 | 8.05 |
Embodiment 6 | 12.9 | 11.62 | 10.08 | 9.98 | 8.72 |
Embodiment 7 | 13.46 | 11.64 | 11.35 | 10.41 | 9.12 |
Embodiment 8 | 12.23 | 11.81 | 10.73 | 9.41 | 8.62 |
Embodiment 9 | 14.65 | 12.35 | 12.32 | 10.16 | 9.42 |
Embodiment 10 | 14.29 | 13.76 | 12.13 | 10.98 | 9.51 |
Comparative example 1 | 9.56 | 9.24 | 8.10 | 7.84 | 6.32 |
Comparative example 2 | 9.32 | 9.12 | 8.03 | 7.71 | 6.15 |
Comparative example 3 | 9.89 | 9.54 | 8.11 | 7.01 | 6.74 |
The surface topography of table 2
As it can be seen from table 1 the interlaminar strength for the composite that embodiment 1-10 is provided is higher than in comparative example 1-3
Peel strength, and with the lengthening of ageing time, the peel strength value changes in comparative example 1-3 are more obvious.Wherein implement
Compared with mutually isostructural composite, its interlaminar strength is higher, illustrates in binding agent for example 4 and 5 and embodiment 9 and 10
Its bond effect is more preferable after adding anticorrosion glue, and is less likely to occur to permeate, and interlaminar strength is kept high value.
From table 2 it can be seen that the appearance that composite in comparative example 1-3 is all different degrees of when experiment proceeds to 30 days
The phenomenon of layering and bubble, and the composite in embodiment 1-10 does not occur the above situation, illustrate its anticorrosion ability
It is more excellent.
Embodiment 11
The present embodiment is that a kind of preparation method of packaging tube composite comprises the following steps:
Step a):With ter-polymer resin by PE and ethylene-vinyl alcohol copolymer inflation film manufacturing machine using multi-layer co-extruded
Processing method film extrusion obtains composite film;The technological parameter of forming process is:250 DEG C, unwinding tension 17kg of processing temperature,
Winding tension 21kg, composite pressure 4kg;
Step b):The composite film obtained in step a) and aluminium foil are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:250 DEG C of processing temperature processing temperature, unwinding tension
17kg, winding tension 21kg, composite pressure 4kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And the packaging tube composite is obtained using extrusion composite technology, extrusion composite technology parameter is:Processing temperature 250
DEG C, unwinding tension 17kg, winding tension 21kg, composite pressure 4kg.
Embodiment 12
The present embodiment is that a kind of preparation method of packaging tube composite comprises the following steps:
Step a):With ter-polymer resin by PE and ethylene-vinyl alcohol copolymer inflation film manufacturing machine using multi-layer co-extruded
Processing method film extrusion obtains composite film;The technological parameter of forming process is:300 DEG C, unwinding tension 22kg of processing temperature,
Winding tension 30kg, composite pressure 5kg;
Step b):The composite film obtained in step a) and aluminium foil are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:280 DEG C, unwinding tension 22kg of processing temperature, winding
Tension force 32kg, composite pressure 6kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And the packaging tube composite is obtained using extrusion composite technology, extrusion composite technology parameter is:Processing temperature 320
DEG C, unwinding tension 24kg, winding tension 30kg, composite pressure 6kg.
Embodiment 13
The present embodiment is that a kind of preparation method of packaging tube composite comprises the following steps:
Step a):It is with ter-polymer resin that the use of PE, ethylene-vinyl alcohol copolymer and nylon membrane inflation film manufacturing machine is more
The processing method film extrusion of layer co-extrusion obtains composite film;The technological parameter of forming process is:300 DEG C of processing temperature, is unreeled
Tension force 22kg, winding tension 24kg, composite pressure 5kg;
Step b):The composite film obtained in step a) and aluminium foil are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:310 DEG C, unwinding tension 24kg of processing temperature, winding
Tension force 30kg, composite pressure 6kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And the packaging tube composite is obtained using extrusion composite technology, extrusion composite technology parameter is:Processing temperature 320
DEG C, unwinding tension 25kg, winding tension 33kg, composite pressure 6kg.
Embodiment 14
The present embodiment is that a kind of preparation method of packaging tube composite comprises the following steps:
Step a):PE, ethylene-vinyl alcohol copolymer and nylon inflation film manufacturing machine are used into multilayer with ter-polymer resin
The processing method film extrusion of co-extrusion obtains composite film;The technological parameter of forming process is:290 DEG C of processing temperature, unreel and open
Power 23kg, winding tension 31kg, composite pressure 4kg;
Step b):The composite film obtained in step a) and aluminium foil are pasted simultaneously with polyvinyl resin or anticorrosive glue
Semi-finished product are obtained using extrusion composite technology, extrusion composite technology parameter is:300 DEG C, unwinding tension 24kg of processing temperature, winding
Tension force 33kg, composite pressure 5kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted with polyvinyl resin or anticorrosive glue
And the packaging tube composite is obtained using extrusion composite technology, extrusion composite technology parameter is:Processing temperature 310
DEG C, unwinding tension 25kg, winding tension 34kg, composite pressure 6kg.
Although illustrate and describing the present invention with specific embodiment, but will be appreciated that without departing substantially from the present invention's
Many other change and modification can be made in the case of spirit and scope.It is, therefore, intended that in the following claims
Including belonging to all such changes and modifications in the scope of the invention.
Claims (10)
1. a kind of packaging tube composite, it is characterised in that the theca interna of the composite includes PE films and ethene-second
Enol co-polymer membrane.
2. packaging tube composite according to claim 1, it is characterised in that in the theca interna, the PE films
Percentage thickness be 70%-80%, the percentage thickness of the ethylene vinyl alcohol copolymer film is 20%-30%;
Preferably, the structure of the theca interna is PE films/ethylene vinyl alcohol copolymer film/PE films.
3. packaging tube composite according to claim 1, it is characterised in that the theca interna of the composite is also
Including nylon membrane.
4. packaging tube composite according to claim 3, it is characterised in that in the theca interna, the PE films
Percentage thickness be 70%-84%, the percentage thickness of the ethylene vinyl alcohol copolymer film is 8%-15%;The Buddhist nun
The percentage thickness of imperial film is 8%-15%;
Preferably, the structure of the theca interna is PE films/ethylene vinyl alcohol copolymer film/nylon membrane/PE films.
5. according to the packaging tube composite described in claim any one of 1-4, it is characterised in that the composite by
It is outer to be followed successively by interior:The composite film of PE layers/tack coat/barrier layer/tack coat/PE films and ethylene vinyl alcohol copolymer film or
The composite film of PE films, ethylene vinyl alcohol copolymer film and nylon membrane;
Preferably, the barrier layer is included in aluminium foil layer, evoh layer, pet layer, PVDC layers or plating silicon materials
It is any or at least two combination.
6. packaging tube composite according to claim 5, it is characterised in that the binding agent is ethylene acrylic
Copolymer, polyvinyl resin or anticorrosive glue.
A kind of 7. preparation method of the packaging tube composite described in any one of claim 1-6, it is characterised in that including
By PE and ethylene-vinyl alcohol copolymer and optionally nylon composite membrane-forming the step of.
8. preparation method according to claim 7, it is characterised in that comprise the following steps:PE and ethylene-vinyl alcohol are total to
It is compound using binding agent and barrier layer after polymers and optionally nylon composite membrane-forming, binding agent and outer layer PE layers are recycled afterwards
Bonding is compound, obtains the packaging tube composite;
Preferably, the step of composite membrane-forming includes the preparation technology of multi-layer co-extruded shaping.
9. preparation method according to claim 8, it is characterised in that comprise the following steps:
Step a):With ter-polymer resin by PE and ethylene-vinyl alcohol copolymer and optionally nylon inflation film manufacturing machine co-extrusion
Film forming obtains composite film;The technological parameter of extrusion is:220-320 DEG C of processing temperature, unwinding tension 15-25kg, winding
Tension force 20-35kg, pressure 4-6kg;
Step b):The composite film obtained in step a) is pasted and utilized with barrier layer with polyvinyl resin or anticorrosive glue
Extrusion composite technology obtains semi-finished product, and extrusion composite technology parameter is:220-320 DEG C of processing temperature, unwinding tension 15-25kg,
Winding tension 20-35kg, composite pressure 4-6kg;
Step layer c):The semi-finished product obtained in step b) and outer layer PE layers are pasted into simultaneously profit with polyvinyl resin or anticorrosive glue
The packaging tube composite is obtained with extrusion composite technology;Extrusion composite technology parameter is:Processing temperature 220-320
DEG C, unwinding tension 15-25kg, winding tension 20-35kg, composite pressure 4-6kg.
10. a kind of packaging tube, it is characterised in that be prepared by the composite described in claim any one of 1-6.