CN107686755A - A kind of cast moulding coal tar and preparation method thereof - Google Patents
A kind of cast moulding coal tar and preparation method thereof Download PDFInfo
- Publication number
- CN107686755A CN107686755A CN201710781733.7A CN201710781733A CN107686755A CN 107686755 A CN107686755 A CN 107686755A CN 201710781733 A CN201710781733 A CN 201710781733A CN 107686755 A CN107686755 A CN 107686755A
- Authority
- CN
- China
- Prior art keywords
- anthracite
- coal tar
- cast moulding
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of cast moulding coal tar and preparation method thereof, belong to casting molded coal field；Technical scheme is to include 60 70 parts of anthracite, 20 30 parts of coke powder, 5 10 parts of adhesive；Preparation method includes：Anthracite and coke powder are dried respectively, drying temperature is 270 300 DEG C；Filter out the anthracite that granularity is 3 5mm；Adhesive is added, the shaping that stirs, dries, 30 40min is sintered at 700 800 DEG C, the end for reaching tunnel cave afterwards cools down, cleans 10 15min, obtains finished product；Described cast moulding coal tar caloric value reaches 7300 7600J, falls index and reaches 98 100%, has the characteristics that low ash, low-sulfur, high fixed carbon, high intensity, lumpiness uniformity, crushing strength is good, the porosity is low, is a kind of new material of casting smelting.
Description
Technical field
The invention belongs to casting molded coal field, it is more particularly related to a kind of cast moulding coal tar and its preparation side
Method.
Background technology
Exploitation coke substitute technology is that solve high-quality caking coal shortage, meets the industry STRENGTH ON COKEs such as metallurgy, machinery, chemical industry
Needs and mitigate environmental pollution effective way.Therefore, countries in the world put into a large amount of human and material resources one after another develops such skill
Art, have been achieved with being in progress well.China lacks the good coking coal resource of low ash, low-sulfur, caking property, with steel and iron industry and machine
Tool industrial expansion, coking coal resource day is becoming tight to rise steadily with price, forces people to go to study coke substitute production skill
Art.Casting molded coal is the ideal substitute of foundry coke.Clean coal technology is control pollution, saves the energy and improve coal money
The important technology of source utilization rate.One of main path of China's development Filter Tuber For Clean Coal is exactly to greatly develop shaped coal technology.By fine coal into
Type produces moulded coal or formed coke, and the raw material or fuel of cleaning are provided for industry, coal resources can be not only saved, also with significant ring
Protect benefit.
Coke substitute shaped coal technology is developed, can not only meet the needs of the industry STRENGTH ON COKE such as metallurgy, machinery, chemical industry,
Coking coal resource can also be expanded, the overstocked problem of fine coal is solved and significantly mitigate environmental pollution.Casting type is produced using anthracite
Coal technology, it is coal deep processing frontier.This technology is succeeded in developing, and can not only extend enterprise's industrial chain, improves enterprise
Economic benefit, and meet Filter Tuber For Clean Coal developing direction and state coal Industry Policy, there are wide market prospects.
The content of the invention
Overcome the deficiencies in the prior art of the present invention, it is therefore an objective to which a kind of cast moulding coal tar and preparation method thereof is provided.Described
Cast moulding coal tar has low ash, low-sulfur, high fixed carbon, high intensity, lumpiness uniformity, the spy such as crushing strength is good, the porosity is low
Point.The present invention can sufficiently utilize resource, and anthracite and coke powder are allocated according to the cast moulding pit ash formed in component
Usage amount, it ensure that the stability of the indices of product.
To achieve the above object, the technical solution adopted in the present invention is：A kind of cast moulding coal tar is provided, included smokeless
Coal 60-70 parts, coke powder 20-30 parts, adhesive 5-10 parts.
The anthracite is content of ashes 8-10wt%, sulphur content content 0.8-1.2wt%.
Described coke fines size ＜ 0.3mm.
A kind of preparation method of described cast moulding coal tar comprises the following steps：
a）Anthracite and coke powder are dried respectively, drying temperature is 270-300 DEG C；
b）Filter out the anthracite that granularity is 3-5mm；
c）Adhesive is added, and is stirred, is delivered to forming machine shaping；
d）Dried after shaping, 30-40min is sintered at 700-800 DEG C, the end for reaching tunnel cave afterwards cools down；
e）After cooling, 10-15min is cleaned, obtains finished product.
The present invention can make full use of resource, and anthracite and coke powder can be replaced mutually in component, according to different product index
It is required that or add deduct.Because anthracite and coke powder are low-sulfur, low-volatile mineral raw material, product physical index compares phase
Closely, anthracite can be substituted with high-quality coke powder, and coke powder can be adjusted with anthracite.
Compared with prior art the invention has the advantages that：Cast moulding coal tar caloric value of the present invention reaches 7300-
7600J, 7-10% is higher by than like product；Fall index and reach 98-100%, 8-10% is higher by than like product；Coke throws stove rate
12%-13% is improved, coke 25%-35% can be saved.The present invention sinters the technology effect for the sintering that just reaches a high temperature at 700-800 DEG C
Fruit, exactly raw material proportioning bring, and cast moulding coal tar has low ash, low-sulfur, high fixed carbon, high intensity, lumpiness uniformity, anti-
The features such as broken intensity is good, the porosity is low, in fusion process, air quantity, blast wandering scope are small, furnace temperature is stable, and molten iron temperature is high,
It is a kind of new material of casting smelting.
Embodiment
Technical scheme is described in detail with reference to embodiment, but protection domain is not limited by this.
Embodiment 1
Weigh content of ashes 8wt%, sulphur content content 0.8wt% anthracite 60kg, the coke powder 20kg that granularity is 0.2mm, bonding
Agent 5kg.
Prepared according to following steps：
Anthracite and coke powder are dried respectively, drying temperature is 270 DEG C；Filter out the anthracite that granularity is 3mm；Add viscous
Mixture, and stir, it is delivered to forming machine shaping；Dried after shaping, 30min is sintered at 700 DEG C, reaches tunnel afterwards
The end of road kiln cools down；After cooling, 10min is cleaned, obtains finished product.
Embodiment 2
Weigh content of ashes 10wt%, sulphur content content 1.2wt% anthracite 70kg, the coke powder 30kg that granularity is 0.1mm, bonding
Agent 10kg.
Prepared according to following steps：
Anthracite and coke powder are dried respectively, drying temperature is 300 DEG C；Filter out the anthracite that granularity is 5mm；Add viscous
Mixture, and stir, it is delivered to forming machine shaping；Dried after shaping, 40min is sintered at 800 DEG C, reaches tunnel afterwards
The end of road kiln cools down；After cooling, 15min is cleaned, obtains finished product.
Embodiment 3
Weigh content of ashes 9wt%, sulphur content content 1wt% anthracite 65kg, coke powder 25kg, the adhesive that granularity is 0.2mm
7kg。
Prepared according to following steps：
Anthracite and coke powder are dried respectively, drying temperature is 290 DEG C；Filter out the anthracite that granularity is 4mm；Add viscous
Mixture, and stir, it is delivered to forming machine shaping；Dried after shaping, 35min is sintered at 750 DEG C, reaches tunnel afterwards
The end of road kiln cools down；After cooling, 13min is cleaned, obtains finished product.
Embodiment 4
Weigh content of ashes 10wt%, sulphur content content 1wt% anthracite 65kg, coke powder 24kg, the adhesive that granularity is 0.2mm
6kg。
Preparation method is the same as embodiment 2.
Embodiment 5
Weigh content of ashes 8wt%, sulphur content content 0.9wt% anthracite 67kg, the coke powder 22kg that granularity is 0.2mm, bonding
Agent 7kg.
Preparation method is the same as embodiment 2.
Embodiment 6
Weigh content of ashes 9wt%, sulphur content content 1.2wt% anthracite 63kg, the coke powder 26kg that granularity is 0.1mm, bonding
Agent 6kg.
Preparation method is the same as embodiment 2.
Embodiment 7
Weigh content of ashes 8wt%, sulphur content content 0.9wt% anthracite 69kg, the coke powder 20kg that granularity is 0.2mm, bonding
Agent 8kg.
Preparation method is the same as embodiment 2.
Above content is to combine the further description that specific preferred embodiment is done to the present invention, it is impossible to is assert
The embodiment of the present invention is only limitted to this, for general technical staff of the technical field of the invention, is not taking off
On the premise of from the present invention, some simple deduction or replace can also be made, should all be considered as belonging to the present invention by being submitted
Claims determine scope of patent protection.
Claims (4)
- A kind of 1. cast moulding coal tar, it is characterised in that：Include anthracite 60-70 parts, coke powder 20-30 parts, adhesive 5-10 parts.
- 2. a kind of cast moulding coal tar according to claim 1, it is characterised in that the anthracite is content of ashes 8- 10wt%, sulphur content content 0.8-1.2wt%.
- A kind of 3. cast moulding coal tar according to claim 1, it is characterised in that described coke fines size ＜ 0.3mm.
- A kind of 4. preparation method of cast moulding coal tar, it is characterised in that：Comprise the following steps：a）Anthracite and coke powder are dried respectively, drying temperature is 270-300 DEG C；b）Filter out the anthracite that granularity is 3-5mm；c）Adhesive is added, and is stirred, is delivered to forming machine shaping；d）Dried after shaping, 30-40min is sintered at 700-800 DEG C, the end for reaching tunnel cave afterwards cools down；e）After cooling, 10-15min is cleaned, obtains finished product.