CN107602066A - A kind of preparation method of Buddhist public affairs pottery handicraft - Google Patents
A kind of preparation method of Buddhist public affairs pottery handicraft Download PDFInfo
- Publication number
- CN107602066A CN107602066A CN201710960866.0A CN201710960866A CN107602066A CN 107602066 A CN107602066 A CN 107602066A CN 201710960866 A CN201710960866 A CN 201710960866A CN 107602066 A CN107602066 A CN 107602066A
- Authority
- CN
- China
- Prior art keywords
- glaze
- glazing
- base substrate
- clay
- beads
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of preparation method of Buddhist public affairs pottery handicraft, including:Step 1, engraving model;Step 2, make mould;The some that step 1 is carved to shaping makes gypsum mold respectively;Step 3, choose clay;Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, then ground, its fineness of grinding is 230 250 mesh, adds ball milling after water mixing, slurry is made;Step 5, injection forming;Step 6, dry;Step 7, biscuiting;Base substrate is put into biscuit kiln, 56 hours are fired at a temperature of 900 DEG C 1000 DEG C;Step 8, glazing;Step 9, fire;By after glazing and the temperature that is put into kiln at 1280 DEG C 1300 DEG C of base substrate dried fires 12 15 hours.Glaze-body bonding performance of the present invention is good, the high yield rate of pottery, and its device shape and color can more embody the intention and artistic effect of works of the present invention.
Description
Technical field
The present invention relates to pottery technology field, more particularly to a kind of preparation method of Buddhist public affairs pottery handicraft.
Background technology
Ceramics are one of important components of Chinese culture, and pottery is one in Chinese Ceramics Culture bright bright
Pearl.Pottery rises in the Eastern Han Dynasty, is one of five big kiln porcelain of Song Dynasty, is the treasure in traditional technology in producing porcelain, with the transmutation of uniqueness
Art and be world-famous for, be known as " the valuable an ancient unit of weight average price of gold " and the good reputation of " there is ten thousand strings of cash in family, be not as a piece of as pottery ".Pottery is described as
It is the special product of China Countermeasure In Yuzhou City of Henan Province first of Chinese " five big porcelain ", it is mainly characterized by the color of porcelain and complicated, and changes
The single colour glaze development grain of ancient times porcelain, there is unique characteristics such as " enter kiln is of the same colour, kiln discharge ten thousand is color ", be other ceramic processes
What product can not be realized and compare.But when making pottery, although although present technology has had been achieved with remarkable progress,
Or some defects be present, pottery, from sorting to finished product is fired, will pass through tens of road production processes, nothing therebetween in manufacturing process
Careless slightly by which procedure, even slight mistake will also result in that all that has been achieved is spoiled, and this is also the extremely low original of pottery treasure rate
Cause, the key of pottery are enamel, and enamel chatoyance after being fired by glaze decides the value of pottery, and when firing, pottery is going out
Easily ftractureed after kiln cooling, so as to cause treasure rate low.
The content of the invention
In view of this, the present invention provides a kind of preparation method of Buddhist public affairs pottery handicraft, and glaze-body bonding performance is good, yield rate
It is high.
To achieve the above object, the present invention uses following technical scheme:
A kind of preparation method of Buddhist public affairs pottery handicraft, comprises the following steps:
Step 1, engraving model;Whole handicraft is divided into some to carve respectively, including head, hand, leg, beads and
Main body, wherein hand, which are put one's palms together devoutly, is put in front, and beads are placed at the wrist of both hands, and hand and beads are put in the robe of main body
Outside;Leg both legs are sat crosslegged, outer in the robe pendulum of main body;
Step 2, make mould;The some that step 1 is carved to shaping makes gypsum mold respectively;
Step 3, choose clay;The clay includes following components:Kaolin 65-75%, sandstone 8-15%, lead powder 8-12%, Mo Lai
Stone 8-12%, iron ore 1-2%, cobalt oxide 0.2-0.4%, dietary alkali 0.3-0.5%;
Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, then ground, it grinds carefully
Spend for 230-250 mesh, add water mix after ball milling, slurry is made;
Step 5, injection forming;Slurry is injected separately into each mould in step 2, and by multiple moulds after slip casting
The base substrate of generation is solidified, is bonded together according to design requirement, by finishing, forms overall image;
Step 6, dry;The base substrate trimmed is dried at a temperature of 25-120 DEG C, dried base substrate water content is less than
3%;
Step 7, biscuiting;Base substrate is put into biscuit kiln, 5-6 hour is fired at a temperature of 900 DEG C -1000 DEG C;
Step 8, glazing;By after biscuiting billet surface removal of impurities processing after carry out surface apply glaze material, wherein head, hand, leg,
Beads and bottom not glazing, main part using brushing glazing either glaze spraying or dip in glaze method carry out glazing;Glaze be by including
Melilite 50-60%, white feldspar 8-12%, calcite 8-11%, Copper Ores 1-3%, zinc chloride 3-5%, barium carbonate 0.1-0.4%, oxygen
Change tin 0.1-0.8%, di-iron trioxide 5-7%, potassium oxide 1-3%, sodium oxide molybdena 0.5-1%, kieselguhr 3-8% glaze is crushed,
Mixing, ball milling, it is 400-450 targeted fine powders to become fineness, adds water that glaze slip is made after being stirred ball milling;
Step 9, fire;By after glazing and the base substrate dried is put into kiln that to fire 12-15 in 1280 DEG C -1300 DEG C of temperature small
When.
Beneficial effects of the present invention are:
Potassium oxide and sodium oxide molybdena are added in the glaze of the present invention, the melting temperature and high temperature viscosity of glaze is reduced, improves the change of glaze
Stability and heat endurance to be learned, makes glaze that there is good transparency and glossiness, glaze-body bonding performance is good, while using the present invention
Clay, glaze and making step, the high yield rate of pottery, its device shape and color can more embody the intention and skill of works of the present invention
Art effect.
Brief description of the drawings
Fig. 1 is a kind of structural representation of Buddhist public affairs pottery handicraft of the present invention.
In figure:1- heads;2- hands;3- beads;4- main bodys;5- legs.
Embodiment
In order to further illustrate technical scheme, in conjunction with example, illustrate embodiment of the invention;
Embodiment 1:
As shown in figure 1, a kind of preparation method of Buddhist public affairs pottery handicraft, comprises the following steps:
Step 1, engraving model;From the model engraving process that the industry is general, whole handicraft is divided into some difference
Engraving, including head 1, hand 2, leg 5, beads 3 and main body 4, wherein hand 2, which is put one's palms together devoutly, is put in front, and beads 3 are placed on
At the wrist of both hands, hand 2 and beads 3 are outer in the robe pendulum of main body;The both legs of leg 5 are sat crosslegged, outer in the robe pendulum of main body 4.
Step 2, make mould;The gypsum mold of each several part is made from the general method of the industry, step 1 is engraved as
The some of type makes gypsum mold respectively.
Step 3, choose clay;The clay includes following components:Kaolin 65%, sandstone 13%, lead powder 8%, mullite
12%, iron ore 1.5%, cobalt oxide 0.2%, dietary alkali 0.3%;
Step 4, slurrying carry out the clay of step 3 coarse crushing into sand shape or powdery first, are then ground, its fineness of grinding
For 230-250 mesh, add ball milling after water mixing, slurry is made;
Step 5, injection forming;Slurry is injected separately into each mould in step 2, and by multiple moulds after slip casting
The base substrate of generation is solidified, is bonded together according to design requirement, by finishing, forms overall image;
Step 6, dry;The base substrate trimmed is dried at a temperature of 120 DEG C, dried base substrate water content is less than 1%;
Step 7, biscuiting;Base substrate is put into biscuit kiln, 5-6 hour is fired at a temperature of 950 DEG C;
Step 8, glazing;By after biscuiting billet surface removal of impurities processing after carry out surface apply glaze material, wherein head, hand, leg,
Beads and bottom not glazing, main part using brushing glazing either glaze spraying or dip in glaze method carry out glazing;Glaze be by including
Melilite 55%, white feldspar 10%, calcite 10%, Copper Ores 3%, zinc chloride 5%, barium carbonate 0.1%, tin oxide 0.4%, three oxidations
Two iron 7%, potassium oxide 2%, sodium oxide molybdena 0.5%, the glaze of kieselguhr 7% are crushed, mixing, ball milling, become fineness as 450
Targeted fine powder, add water that glaze slip is made after being stirred ball milling;
Step 9, fire;By after glazing and the base substrate dried is put into kiln that to fire 12-15 in 1280 DEG C -1300 DEG C of temperature small
When, it becomes possible to obtain meeting design philosophy, and the Buddhist public affairs pottery handicraft that the present invention that can embody features above is signified.
Potassium oxide and sodium oxide molybdena are added in the glaze of invention, the melting temperature and high temperature viscosity of glaze is reduced, improves glaze
Chemical stability and heat endurance, make glaze that there is good transparency and glossiness, glaze-body bonding performance is good, while uses this hair
Bright clay, glaze and making step, the high yield rate of pottery, its device shape and color can more embody works of the present invention intention and
Artistic effect.In embodiment more than it should be noted that in main part glazing, it shall be guaranteed that the glazed thickness of glazing is little
In 1 millimeter, to ensure to reduce the cracking of glaze layer, the solemnity of this works is influenceed.The Buddhist public affairs color of the present invention burnt out is that chicken blood is red.
Embodiment 2:
As shown in figure 1, a kind of preparation method of Buddhist public affairs pottery handicraft, comprises the following steps:
Step 1, engraving model;From the model engraving process that the industry is general, whole handicraft is divided into some difference
Engraving, including head 1, hand 2, leg 5, beads 3 and main body 4, wherein hand 2, which is put one's palms together devoutly, is put in front, and beads 3 are placed on
At the wrist of both hands, hand 2 and beads 3 are outer in the robe pendulum of main body;The both legs of leg 5 are sat crosslegged, outer in the robe pendulum of main body 4.
Step 2, make mould;The gypsum mold of each several part is made from the general method of the industry, step 1 is engraved as
The some of type makes gypsum mold respectively.
Step 3, choose clay;The clay includes following components:Kaolin 70%, sandstone 10%, lead powder 8%, mullite
10%, iron ore 1.5%, cobalt oxide 0.2%, dietary alkali 0.3%.
Step 4, slurrying carry out the clay of step 3 coarse crushing into sand shape or powdery first, are then ground, it grinds
Fineness is 230-250 mesh, adds ball milling after water mixing, slurry is made.
Step 5, injection forming;Slurry is injected separately into each mould in step 2, and note will be passed through in multiple moulds
The base substrate of generation is solidified after slurry, is bonded together according to design requirement, by finishing, forms overall image.
Step 6, dry;The base substrate trimmed is dried at a temperature of 120 DEG C, dried base substrate water content is less than
1%。
Step 7, biscuiting;Base substrate is put into biscuit kiln, 5-6 hour is fired at a temperature of 950 DEG C.
Step 8, glazing;By after biscuiting billet surface removal of impurities processing after carry out surface apply glaze material, wherein head, hand,
Leg, beads and bottom not glazing, main part using brushing glazing either glaze spraying or dip in glaze method carry out glazing;Glaze be by
Including melilite 60%, white feldspar 9%, calcite 8%, Copper Ores 2%, zinc chloride 5%, barium carbonate 0.1%, tin oxide 0.4%, three oxygen
Change two iron 7%, potassium oxide 3%, sodium oxide molybdena 0.5%, the glaze of kieselguhr 5% crushed, mixed, ball milling, becoming fineness is
450 targeted fine powders, add water that glaze slip is made after being stirred ball milling.
Step 9, fire;By after glazing and dry base substrate be put into kiln 1280 DEG C -1300 DEG C temperature fire 12-15
Individual hour, it becomes possible to obtain meeting design philosophy, and the Buddhist public affairs pottery handicraft that the present invention that can embody features above is signified.
In embodiment more than it should be noted that in main part glazing, it shall be guaranteed that the glazed thickness of glazing is little
In 1 millimeter, to ensure to reduce the cracking of glaze layer, the solemnity of this works is influenceed.
The foregoing is only presently preferred embodiments of the present invention, be not intended to limit the invention, it is all the present invention spirit and
Within principle, any modification, equivalent substitution and improvements made etc., it should be included in the scope of the protection.
Claims (1)
- A kind of 1. preparation method of Buddhist public affairs pottery handicraft, it is characterised in that:Comprise the following steps:Step 1, engraving model;Whole handicraft is divided into some to carve respectively, including head, hand, leg, beads and Main body, wherein hand, which are put one's palms together devoutly, is put in front, and beads are placed at the wrist of both hands, and hand and beads are put in the robe of main body Outside;Leg both legs are sat crosslegged, outer in the robe pendulum of main body;Step 2, make mould;The some that step 1 is carved to shaping makes gypsum mold respectively;Step 3, choose clay;The clay includes following components:Kaolin 65-75%, sandstone 8-15%, lead powder 8-12%, Mo Lai Stone 8-12%, iron ore 1-2%, cobalt oxide 0.2-0.4%, dietary alkali 0.3-0.5%;Step 4, slurrying;The clay of step 3 is carried out to coarse crushing first into sand shape or powdery, then ground, it grinds carefully Spend for 230-250 mesh, add water mix after ball milling, slurry is made;Step 5, injection forming;Slurry is injected separately into each mould in step 2, and by multiple moulds after slip casting The base substrate of generation is solidified, is bonded together according to design requirement, by finishing, forms overall image;Step 6, dry;The base substrate trimmed is dried at a temperature of 25-120 DEG C, dried base substrate water content is less than 3%;Step 7, biscuiting;Base substrate is put into biscuit kiln, 5-6 hour is fired at a temperature of 900 DEG C -1000 DEG C;Step 8, glazing;By after biscuiting billet surface removal of impurities processing after carry out surface apply glaze material, wherein head, hand, leg, Beads and bottom not glazing, main part using brushing glazing either glaze spraying or dip in glaze method carry out glazing;Glaze be by including Melilite 50-60%, white feldspar 8-12%, calcite 8-11%, Copper Ores 1-3%, zinc chloride 3-5%, barium carbonate 0.1-0.4%, oxygen Change tin 0.1-0.8%, di-iron trioxide 5-7%, potassium oxide 1-3%, sodium oxide molybdena 0.5-1%, kieselguhr 3-8% glaze is crushed, Mixing, ball milling, it is 400-450 targeted fine powders to become fineness, adds water that glaze slip is made after being stirred ball milling;Step 9, fire;By after glazing and the base substrate dried is put into kiln that to fire 12-15 in 1280 DEG C -1300 DEG C of temperature small When.