CN107599551A - It is a kind of to tear wear-resisting wool spinning fabric with resistance to - Google Patents
It is a kind of to tear wear-resisting wool spinning fabric with resistance to Download PDFInfo
- Publication number
- CN107599551A CN107599551A CN201710873826.2A CN201710873826A CN107599551A CN 107599551 A CN107599551 A CN 107599551A CN 201710873826 A CN201710873826 A CN 201710873826A CN 107599551 A CN107599551 A CN 107599551A
- Authority
- CN
- China
- Prior art keywords
- fiber
- fabric
- wear
- resistance
- wool spinning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting wool spinning fabric is torn with resistance to,Including superpower wear-resistant nylon fiber and silk fiber,The top viscose of superpower wear-resistant nylon fiber is bonded with radiation proof groups of metal filaments,Degerming cilium is closely fitted with below superpower wear-resistant nylon fiber,This kind has that resistance to tear wear-resisting wool spinning fabric rational in infrastructure,It is provided with micro fiber leather,It is a kind of superfine fibre enhancing leather,Its thickness is 0.3CM,By its exclusive toughness material characteristic,Addition increases its tamper-proof resistance to ability of tearing in fabric,Fabric is set not to be destroyed easily in being torn by external force,Radiation proof groups of metal filaments employs metal tantalum material manufacture and formed,Machining accuracy reaches ± 0.1CM,When fabric is attacked by micro- radiation, metal tantalum material can play an absorption bonding to it and be acted on,Prevent from penetrating into inside fabric,Cause further to destroy,600D oxfords coincide with chrysotile asbestos fibre appearance and size.
Description
Technical field
It is specially a kind of to tear wear-resisting wool spinning fabric with resistance to the present invention relates to wool spinning fabric technical field.
Background technology
Wool spinning fabric, it is the spinning process process for wool fibre being processed into yarn, wool fibre is based on wool, also including mountain
The special animal hair fibers such as wool, the rabbit hair, mohair yarn, yak hair, wool spinning process can also be used for wool type chemical fiber and tie up pure spinning, with wanting for technique
Ask, existing wool spinning fabric is difficult to the extraordinary demand for meeting various crowd, be nowadays badly in need of it is a kind of have resistance to tear wear-resisting wool spinning
Fabric, but existing pure wool textile fabric safe class is not high enough, can not meet the basic functions such as radioresistance, fire resisting, and it is wear-resisting,
Prevent that effect is smaller in terms of tearing shock resistance, and it is ventilative not perfect enough, it is single using function, nowadays popular need can not be catered to
Ask.
So how to design it is a kind of have it is resistance to tear wear-resisting wool spinning fabric, turning into us will currently solve the problems, such as.
The content of the invention
Wear-resisting wool spinning fabric is torn with resistance to it is an object of the invention to provide a kind of, to solve to carry in above-mentioned background technology
The problem of going out.
To achieve the above object, the present invention provides following technical scheme;It is a kind of have it is resistance to tear wear-resisting wool spinning fabric, including
Superpower wear-resistant nylon fiber and silk fiber, the top viscose of the superpower wear-resistant nylon fiber are bonded with radiation proof wire
Group, degerming cilium is closely fitted with below the superpower wear-resistant nylon fiber, the bottom viscose of the degerming cilium is bonded with
Elastomer, moisture permeable membrane has been sewed and connected below the elastomer, the bottom of the moisture permeable membrane is closely fitted with mesh layer,
The medial surface of the mesh layer has been sewed and connected 600D oxfords, and the lower section viscose of the 600D oxfords is bonded with micro fiber leather,
The medial surface of the micro fiber leather is closely fitted with polyester fiber fabric, and the bottom of the polyester fiber fabric has been sewed and connected secondary carbon
Fiber hair, the lower section viscose of the secondary carbon fiber hair are bonded with silicone rubber coating glass fibre, the silicone rubber coating glass fibers
The medial surface of dimension is closely fitted with super-hydrophobic layer, and the bottom of the silk fiber has been sewed and connected chrysotile asbestos fibre, the fire stons
The lower section of cotton fiber is closely connected with spider silk fiber, and the medial surface viscose of the spider silk fiber is bonded with bamboo-carbon fibre, institute
The bottom for stating bamboo-carbon fibre is closely fitted with main carbon fiber hair.
Preferably, the micro fiber leather is a kind of superfine fibre enhancing leather, and its thickness is 0.3CM.
Preferably, the radiation proof groups of metal filaments employs metal tantalum material manufacture and formed, and machining accuracy reaches ±
0.1CM。
Preferably, the 600D oxfords coincide with the chrysotile asbestos fibre appearance and size, and the 600D oxfords with
The chrysotile asbestos fibre is network structure.
Preferably, the position of the superpower wear-resistant nylon fiber and the spider silk fiber is corresponding, and described superpower resistance to
The position of mill nylon fiber and the spider silk fiber is located on same vertical line.
Preferably, the mesh layer is coincide with the silk fiber appearance and size, and the mesh layer and the silk fibroin
Dimension is network structure.
Compared with prior art, the beneficial effects of the invention are as follows:This kind have it is resistance to tear wear-resisting wool spinning fabric rational in infrastructure,
Micro fiber leather is provided with, is a kind of superfine fibre enhancing leather, its thickness is 0.3CM, by its exclusive toughness material characteristic, makes face
Material increases its tamper-proof resistance to ability torn, and allows fabric not to be destroyed easily in being torn by external force, radiation proof groups of metal filaments is adopted
Formed with metal tantalum material manufacture, machining accuracy reaches ± 0.1CM, the metal tantalum material meeting when fabric is attacked by micro- radiation
The effect of an absorption bonding is played to it, prevents from penetrating into inside fabric, causes further to destroy, 600D oxfords and temperature
Asbestos fibre appearance and size is coincide, and 600D oxfords and chrysotile asbestos fibre are network structure, two kinds of high-temperature flame-proof composite woods
Material, when fabric is toasted by external high temperature naked light, play a part of a temperature isolation to it, and it is distinctive not by its material
Combustibility, one can be played a part of to naked light and extinguished naturally, the position of superpower wear-resistant nylon fiber and spider silk fiber is relative
Should, and the position of superpower wear-resistant nylon fiber and spider silk fiber is located on same vertical line, in the external world by abrasion extruding
During stress, one can be played a part of to it and offset resistance, different from traditional fabric, substantially increase wearability, greatly
Demand of the fabric to wear-resisting aspect is met, mesh layer is coincide with silk fiber appearance and size, and mesh layer and silk fiber are equal
For network structure, improve the ventilative gas permeability of fabric, meet the diversification of fabric function when in use, increase use it is extensive
Property.
Brief description of the drawings
Fig. 1 is the overall structure diagram of the present invention;
Fig. 2 is the micro fiber leather structural representation of the present invention;
Fig. 3 is the chrysotile asbestos fibre structural representation of the present invention.
In figure:1st, superpower wear-resistant nylon fiber, 101, radiation proof groups of metal filaments, 102, degerming cilium, 2, elastomer,
201st, moisture permeable membrane, 3, mesh layer, 301,600D oxfords, 302, micro fiber leather, 4, polyester fiber fabric, 401, secondary carbon fiber hair,
402nd, silicone rubber coating glass fibre, 403, super-hydrophobic coat, 5, silk fiber, 501, chrysotile asbestos fibre, 502, spider silk it is fine
Dimension, 6, bamboo-carbon fibre, 601, main carbon fiber hair.
Embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation describes, it is clear that described embodiment is only part of the embodiment of the present invention, rather than whole embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made
Embodiment, belong to the scope of protection of the invention.
Fig. 1-3 are referred to, the present invention provides a kind of technical scheme;It is a kind of to tear wear-resisting wool spinning fabric with resistance to, including 1 surpass
Strong wear resistant nylon fiber, 101 radiation proof groups of metal filaments, 102 degerming ciliums, 2 elastomers, 201 moisture permeable membranes, 3 mesh layers,
301600D oxfords, 302 micro fiber leathers, 4 polyester fiber fabrics, 401 secondary carbon fiber hairs, 402 silicone rubber coating glass fibres, 403
Super-hydrophobic coat, 5 silk fibers, 501 chrysotile asbestos fibres, 502 spider silk fibers, 6 bamboo-carbon fibres, 601 main carbon fiber hairs are superpower
The top viscose of wear resistant nylon fiber 1 is bonded with radiation proof groups of metal filaments 101, and the lower section of superpower wear-resistant nylon fiber 1 is closely pasted
Conjunction has degerming cilium 102, and the bottom viscose of degerming cilium 2 is bonded with elastomer 2, and the lower section of elastomer 2 has been sewed and connected
Moisture permeable membrane 201, the bottom of moisture permeable membrane 201 are closely fitted with mesh layer 3, and the medial surface of mesh layer 3 has been sewed and connected 600D Oxfords
Cloth 301, the lower section viscose of 600D oxfords 301 are bonded with micro fiber leather 302, and the medial surface of micro fiber leather 302 is closely fitted with polyester
Fabric lining 4, the bottom of polyester fiber fabric 4 have been sewed and connected secondary carbon fiber hair 401, the lower section viscose of secondary carbon fiber hair 401
Silicone rubber coating glass fibre 402 is bonded with, the medial surface of silicone rubber coating glass fibre 402 is closely fitted with super-hydrophobic layer
403, the bottom of silk fiber 5 has been sewed and connected chrysotile asbestos fibre 501, and the lower section of chrysotile asbestos fibre 501 is closely connected with spider
Silk fiber 502, the medial surface viscose of spider silk fiber 502 are bonded with bamboo-carbon fibre 6, and the bottom of bamboo-carbon fibre 6 is closely fitted with
Main carbon fiber hair 601.
Further, radiation proof groups of metal filaments 101 employs metal tantalum material manufacture and formed, and machining accuracy reaches ±
0.1CM, tantalum metal material can play the effect of an absorption bonding to micro- radiation, prevent from penetrating into inside fabric.
Further, 600D oxfords 301 coincide with the appearance and size of chrysotile asbestos fibre 501, and 600D oxfords 301 and temperature
Asbestos fibre 501 is network structure, and when fabric is toasted by external high temperature naked light, the work of a temperature isolation is played to it
With.
Further, the position of superpower wear-resistant nylon fiber 1 and spider silk fiber 502 is corresponding, and superpower wear-resistant nylon
The position of fiber 1 and spider silk fiber 502 is located on same vertical line, can be to it in the extraneous stress by abrasion extruding
Play a part of one and offset resistance.
Further, mesh layer 3 is coincide with the appearance and size of silk fiber 5, and mesh layer 3 and silk fiber 5 are netted
Structure, the ventilative gas permeability of fabric is improved, meets the diversification of fabric function when in use, increases the popularity used.
Operation principle:First, fabric is devoted oneself to work use, the radiation proof groups of metal filaments 101 on fabric most top layer is by air
In it is micro absorb and be attached on metal itself with radiation emitting granular materials, prevent from penetrating into inside fabric, lower section
Superpower wear-resistant nylon fiber 1 effect of defence pioneer is served as in fabric, when fabric and external object collide friction,
The stress tear fabric prevented, it is further to destroy inside fabric, cause unnecessary loss, the 600D Oxfords in fabric
Cloth 301 plays effect with chrysotile asbestos fibre 501, two kinds of high-temperature flame-proof composites, is toasted in fabric by external high temperature naked light
When, play a part of a temperature isolation to it, and by the distinctive incombustibility of its material, one can be played to naked light and is put out naturally
The effect gone out, the micro fiber leather 302 at middle part, it is a kind of superfine fibre enhancing leather, by its exclusive toughness material characteristic, makes fabric
Increase its tamper-proof resistance to ability torn, allow fabric not to be destroyed easily in being torn by external force, main carbon fiber hair 601 and secondary carbon
Fiber hair 401 increases the softness and plasticity of fabric during fabric use, improves the comfort level used, super-hydrophobic painting
Layer 403 provides a good hydrophobicity when water is contacted for fabric, it is not attacked by the infiltration of water, keeps fabric
Drying property, mesh layer 3 improve the ventilative gas permeability of fabric with silk fiber 5, meet the diversification of fabric function when in use, increase
Add the popularity used.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of changes, modification can be carried out to these embodiments, replace without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (6)
1. a kind of tear wear-resisting wool spinning fabric, including superpower wear-resistant nylon fiber with resistance to(1)And silk fiber(5), its feature
It is:The superpower wear-resistant nylon fiber(1)Top viscose be bonded with radiation proof groups of metal filaments(101), the superpower wear-resistant
Nylon fiber(1)Lower section be closely fitted with degerming cilium(102), the degerming cilium(2)The bonding of bottom viscose it is flexible
Fiber(2), the elastomer(2)Lower section be sewed and connected moisture permeable membrane(201), the moisture permeable membrane(201)Bottom it is close
It is fitted with mesh layer(3), the mesh layer(3)Medial surface be sewed and connected 600D oxfords(301), the 600D oxfords
(301)Lower section viscose be bonded with micro fiber leather(302), the micro fiber leather(302)Medial surface be closely fitted with polyester fiber face
Material(4), the polyester fiber fabric(4)Bottom be sewed and connected secondary carbon fiber hair(401), the secondary carbon fiber hair(401)
Lower section viscose be bonded with silicone rubber coating glass fibre(402), the silicone rubber coating glass fibre(402)Medial surface it is tight
It is close to be fitted with super-hydrophobic layer(403), the silk fiber(5)Bottom be sewed and connected chrysotile asbestos fibre(501), the fire stons
Cotton fiber(501)Lower section be closely connected with spider silk fiber(502), the spider silk fiber(502)Medial surface viscose glue
Conjunction has bamboo-carbon fibre(6), the bamboo-carbon fibre(6)Bottom be closely fitted with main carbon fiber hair(601).
2. it is according to claim 1 it is a kind of have resistance to tear wear-resisting wool spinning fabric, it is characterised in that:The micro fiber leather
(302)It is a kind of superfine fibre enhancing leather, its thickness is 0.3CM.
3. it is according to claim 1 it is a kind of have resistance to tear wear-resisting wool spinning fabric, it is characterised in that:The radiation proof metal
Silk group(101)Employ metal tantalum material manufacture to form, machining accuracy reaches ± 0.1CM.
4. it is according to claim 1 it is a kind of have resistance to tear wear-resisting wool spinning fabric, it is characterised in that:The 600D oxfords
(301)With the chrysotile asbestos fibre(501)Appearance and size is coincide, and the 600D oxfords(301)With the chrysotile asbestos fibre
(501)It is network structure.
5. it is according to claim 1 it is a kind of have resistance to tear wear-resisting wool spinning fabric, it is characterised in that:The superpower wear-resistant Buddhist nun
Imperial fiber(1)With the spider silk fiber(502)Position it is corresponding, and the superpower wear-resistant nylon fiber(1)With the spider
Spider's thread fiber(502)Position be located on same vertical line.
6. it is according to claim 1 it is a kind of have resistance to tear wear-resisting wool spinning fabric, it is characterised in that:The mesh layer(3)
With the silk fiber(5)Appearance and size is coincide, and the mesh layer(3)With the silk fiber(5)It is network structure.