CN107573873A - A kind of High-Speed Automatic mounting box glue of low smell - Google Patents
A kind of High-Speed Automatic mounting box glue of low smell Download PDFInfo
- Publication number
- CN107573873A CN107573873A CN201710880772.2A CN201710880772A CN107573873A CN 107573873 A CN107573873 A CN 107573873A CN 201710880772 A CN201710880772 A CN 201710880772A CN 107573873 A CN107573873 A CN 107573873A
- Authority
- CN
- China
- Prior art keywords
- parts
- mounting box
- speed automatic
- automatic mounting
- box glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low High-Speed Automatic mounting box glue of smell.The mounting box glue is made up of the raw material of following mass parts:370~410 parts of acrylic acid ester emulsion;90~130 parts of vinyl acetate ethylene copolymer emulsion;360~400 parts of rosin milk;100~140 parts of silicon powder;1~3 part of defoamer.The present invention adds the water-based silicon powder of solid using environmentally friendly water-based rosin resin emulsion, improves the solids content of glue, adds rate of drying, is operated suitable for machine.
Description
Technical field
The present invention relates to a kind of low High-Speed Automatic mounting box glue of smell.
Background technology
Existing mounting box glue adds the organic solvents such as benzene class, not only pollutes environment, can also endanger the health of direct labor.When
When the product of these packagings is largely deposited, it can make to diffuse dense or even insufferable toxic organic solvents smell in warehouse, have
Smell even packed article absorb and pollute packing material.And current mounting box is essentially manual operations, mounting box glue is dried
Slowly, low production efficiency.At present, it is low to need a kind of smell of exploitation badly, fast drying, the environmental protection mounting box glue available for high-speed automation.
The content of the invention
It is an object of the invention to provide a kind of low High-Speed Automatic mounting box glue of smell.
The technical solution used in the present invention is:
A kind of High-Speed Automatic mounting box glue of low smell, is made up of the raw material of following mass parts:
Preferably, the High-Speed Automatic mounting box glue of a kind of low smell, is made up of the raw material of following mass parts:
The solid content of acrylic acid ester emulsion is 55wt%~65wt%.
The solid content of vinyl acetate-ethylene copolymerization emulsions is 50wt%~60wt%.
The solid content of rosin milk is 45wt%~55wt%.
The particle size range of silicon powder is 1~5 μm.
Defoamer is organic silicon defoamer.
The beneficial effects of the invention are as follows:
The present invention adds the water-based silicon powder of solid using environmentally friendly water-based rosin resin emulsion, improves glue
Solids content, add rate of drying, suitable for machine operate.
Embodiment
A kind of High-Speed Automatic mounting box glue of low smell, is made up of the raw material of following mass parts:
Preferably, the High-Speed Automatic mounting box glue of a kind of low smell, is made up of the raw material of following mass parts:
Preferably, the solid content of acrylic acid ester emulsion is 55wt%~65wt%;Acrylic acid ester emulsion is viscous at 23 DEG C
Spend for (30~300) mPas.
It is further preferred that acrylic acid ester emulsion is the acrylic acid ester emulsion V206 of BASF.
Preferably, the solid content of vinyl acetate-ethylene copolymerization emulsions is 50wt%~60wt%;Vinyl acetate-ethylene is total to
Viscosity of the poly- emulsion at 25 DEG C is (2500~3700) mPas;PH of the vinyl acetate-ethylene copolymerization emulsions at 20 DEG C be
4.5~6.5.
It is further preferred that vinyl acetate-ethylene copolymerization emulsions are the VAE emulsions DA102 of Dalian chemistry.
Preferably, the solid content of rosin milk is 45wt%~55wt%;Viscosity of the rosin milk at 20 DEG C is (100
~800) mPas;PH of the rosin milk at 20 DEG C is 6~8.5;The softening point of rosin milk is 40~96 DEG C;Rosin milk
Particle size range be 180~240nm.
It is further preferred that rosin milk is the water-based rosin milks of French DRT.
Preferably, the particle size range of silicon powder is 1~5 μm.
Preferably, defoamer is organic silicon defoamer.
It is further preferred that defoamer is the defoamer BYK-024 of Bi Ke chemistry.
Present disclosure is described in further detail below by way of specific embodiment.
Embodiment:
The raw material composition and performance indications of embodiment 1~3 are listed in Table 1 below.In embodiment 1~3, acrylic acid ester emulsion is
The acrylic acid ester emulsion V206 of BASF, vinyl acetate-ethylene copolymerization emulsions are the VAE emulsion DA102 of Dalian chemistry, and rosin is newborn
Liquid is the water-based rosin milks of French DRT, and silicon powder is the silicon powder that commercially available particle size range is 1~5 μm, defoamer Bi Kehua
Defoamer BYK-024.The High-Speed Automatic mounting box glue preparation method of low smell of the present invention is mixed to weigh various raw materials in proportion
After closing stirring.Performance test methods in table 1 are performed by national standard.
The High-Speed Automatic mounting box glue composition of low smell and performance of the embodiment of table 1
Claims (7)
- A kind of 1. High-Speed Automatic mounting box glue of low smell, it is characterised in that:It is made up of the raw material of following mass parts:370~410 parts of acrylic acid ester emulsion;90~130 parts of vinyl acetate-ethylene copolymerization emulsions;360~400 parts of rosin milk;100~140 parts of silicon powder;1~3 part of defoamer.
- A kind of 2. low High-Speed Automatic mounting box glue of smell according to claim 1, it is characterised in that:By the original of following mass parts Material composition:380~400 parts of acrylic acid ester emulsion;100~120 parts of vinyl acetate-ethylene copolymerization emulsions;370~380 parts of rosin milk;110~120 parts of silicon powder;1~2 part of defoamer.
- A kind of 3. low High-Speed Automatic mounting box glue of smell according to claim 1 or 2, it is characterised in that:Acrylic acid ester emulsion Solid content be 55wt%~65wt%.
- A kind of 4. low High-Speed Automatic mounting box glue of smell according to claim 1 or 2, it is characterised in that:Vinyl acetate-ethylene The solid content of copolymer emulsion is 50wt%~60wt%.
- A kind of 5. low High-Speed Automatic mounting box glue of smell according to claim 1 or 2, it is characterised in that:Rosin milk is consolidated Content is 45wt%~55wt%.
- A kind of 6. low High-Speed Automatic mounting box glue of smell according to claim 1 or 2, it is characterised in that:The particle diameter of silicon powder Scope is 1~5 μm.
- A kind of 7. low High-Speed Automatic mounting box glue of smell according to claim 1 or 2, it is characterised in that:Defoamer is organic Silicon defoaming agent.