CN107556879A - A kind of heat-insulating nano composite coating and preparation method thereof - Google Patents
A kind of heat-insulating nano composite coating and preparation method thereof Download PDFInfo
- Publication number
- CN107556879A CN107556879A CN201710961848.4A CN201710961848A CN107556879A CN 107556879 A CN107556879 A CN 107556879A CN 201710961848 A CN201710961848 A CN 201710961848A CN 107556879 A CN107556879 A CN 107556879A
- Authority
- CN
- China
- Prior art keywords
- heat
- water
- composite coating
- parts
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (4)
- A kind of 1. heat-insulating nano composite coating, it is characterised in that the heat-insulating nano composite coating by following parts by weight raw material Composition:25-50 part waterborne curing agents, the mother liquor of 50-100 part water-base epoxy composite coatings, the water-base epoxy composite coating Mother liquor, as filler, is obtained by gadolinium zirconate nano-powder and cellulose aerogels after adding the mixed liquor of water and aqueous epoxy resins Arrive.
- 2. according to claim 1 heat-insulating nano composite coating, it is characterised in that described waterborne curing agent be Aq419 or H228B or W651 or W650.
- 3. a kind of preparation method of heat-insulating nano composite coating as claimed in claim 1, it is characterised in that this method is included such as Lower step:A. prepared by coprecipitation gadolinium zirconate powder:Take 5-10 part gadolinium oxides (Gd203), 8-17 part zirconium oxychlorides (ZrOCl2· 8H2O), ZrOCl2.8H20 is dissolved in 20-30 part ammoniacal liquor, fully reaction obtain white flock precipitate thing, with absolute ethyl alcohol and go from Sub- water cleans 5-10 times, is then substantially soluble in 20-30 parts HN03In, obtain solution one, i.e. ZrO (N03)2Solution;By Gd203It is dissolved in In the nitric acid of 5-10 parts, solution two, i.e. Gd (N0 is made3)3Solution;Resulting solution one and solution two are hybridly prepared into cation Concentration is 0.05mol/L-0.07mol/L female salting liquid, is instilled into the ammoniacal liquor that concentration is concentration 22-25% and is sunk Starch, filter after timeliness 24h-48h, be placed in 50 DEG C of -70 DEG C of baking ovens and dry, ground sieving after in Muffle furnace in 500- 1000 DEG C of calcining 4-6h, obtain Gd2Zr2O7Nano-powder;B. prepared by cellulose aerogels:In beaker containing 10g-151.4%-1.6% cellulose fento suspension, adjusted with hydrochloric acid PH value is 4-5, is 500-600rpm in rotating speed, temperature stirs 2h-4h, sample freeze-drying, prepared under the conditions of being 25 DEG C -27 DEG C Go out cellulose aerogels;C. the gadolinium zirconate nano-powder prepared and cellulose aerogels, ultrasonic vibration 2h-4h are taken, concussion frequency is 100Hz- 200Hz, 60 DEG C -80 DEG C of vacuum drying chamber, 30min-60min are removed and placed in, obtains heat insulation nano composite material;Take 10-40 Part above-mentioned heat-insulation composite material is added in the mixed liquor of 100-200 parts water and 100-200 part water-base resins as filler, Disperse 1-2h in ball mill, produce the mother liquor of water-base epoxy composite coating;D. take 25-50 parts waterborne curing agent be well mixed with 50-100 part water after again the mother liquor with water-base epoxy composite coating by 1: 3-4 ratio mixing.
- 4. the preparation method of heat-insulating nano composite coating according to claim 3, it is characterised in that step described in this method Aqueous epoxy resins in c are Ar555 epoxy resin or H228A epoxy resin or E44 epoxy emulsions or E51 epoxy emulsions, Or E20 epoxy emulsions.