CN107556808A - A kind of environmental printing ink and preparation method thereof - Google Patents
A kind of environmental printing ink and preparation method thereof Download PDFInfo
- Publication number
- CN107556808A CN107556808A CN201710918344.4A CN201710918344A CN107556808A CN 107556808 A CN107556808 A CN 107556808A CN 201710918344 A CN201710918344 A CN 201710918344A CN 107556808 A CN107556808 A CN 107556808A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- ink
- printing ink
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environmental printing ink and preparation method thereof, the raw material of the environmental printing ink is made up of the component of following parts by weight：15 20 parts of colorant, 25 30 parts of bridging agent, 20 30 parts of diluent, 5 10 parts of anti skinning agent, 10 15 parts of filler, 5 10 parts of slip agent, 5 10 parts of counnter attack ink, 13 parts of anti-settling agent, 13 parts of defoamer, 5 10 parts of auxiliary agent, wherein auxiliary agent is Potato Porous Starch, bridging agent is made up of tricresyl phosphate, hydrogenated rosin glyceride, ethyl acetate, epoxy resin, ethanol and dibutyl tin laurate, and diluent is made up of dichloromethane, ethyl acetate, methyl ethyl ketone, ethylene glycol ethyl ether and oligomeric linseed oil.Raw material of the present invention is free of volatility toxic solvent, will not endanger the health of printing worker, prints printing using ink of the present invention, glossiness is high, and rate of drying is fast, and product quality is good, ink is not in the phenomenon for coming off, falling the effect of ink, and the printing effect of printing can persistently be kept.
Description
Technical field
The present invention relates to printing technology, and in particular to a kind of environmental printing ink and preparation method thereof.
Background technology
Ink is the important materials for packaging material printing, and it is shown pattern, word on stock by printing,
Ink includes main component and auxiliary element, and they equably mix and form a kind of sticky colloidal fluid through repeat-rolling.
It is made up of pigment, link stuff and auxiliary agent etc..For the various printings such as books and periodicals, packing and decorating, building decoration.
In recent years, with expanding economy, environmentally friendly cry is more and more high, and printing bound pair offset ink is nontoxic, pollution-free
Aspect proposes new requirement.The PAH (polycyclic aromatic hydrocarbons) contained in traditional ink composition is a kind of volatility
Solvent, it is harmful, wherein the VOC contained not only increases atmosphere pollution, also human body can be caused to hinder
Evil.Rate of drying, thixotropy, the skeleton property of ink have tremendous influence to production efficiency, product quality, and ink
Composition has an impact to human body, and how to study the ink that harm to the human body is as far as possible small, environment-friendly, cost is low turns into later print line
The developing direction of industry.
The content of the invention
It is an object of the invention to provide a kind of small, the environment-friendly environmental printing ink of harm to the human body and its preparation side
Method.
To achieve the above object, the present invention adopts the following technical scheme that：
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
Colorant 15-20 parts；Bridging agent 25-30 parts；Diluent 20-30 parts；
Anti skinning agent 5-10 part filler 10-15 parts；Slip agent 5-10 parts；
Counnter attack ink 5-10 parts；Anti-settling agent 1-3 parts；Defoamer 1-3 parts；
Auxiliary agent 5-10 parts, the auxiliary agent are Potato Porous Starch；
The bridging agent is by tricresyl phosphate, hydrogenated rosin glyceride, ethyl acetate, epoxy resin, ethanol and two bays
Sour dibutyl tin composition；
The diluent is made up of dichloromethane, ethyl acetate, methyl ethyl ketone, ethylene glycol ethyl ether and oligomeric linseed oil.
Further, the parts by weight of each component are as follows in the bridging agent：Tricresyl phosphate 15-20 parts, hydrogenated rosin are sweet
Grease 5-10 parts, ethyl acetate 3-8 parts, epoxy resin 3-8 parts, ethanol 20-30 parts, dibutyl tin laurate 3-8 parts.
The parts by weight of each component are as follows in the diluent：1 part of dichloromethane, ethyl acetate 1-3 parts, methyl ethyl ketone 1-
3 parts, ethylene glycol ethyl ether 1-3 parts, oligomerization linseed oil 2-3 parts.
The anti skinning agent is made up of the component of following parts by weight：It is 2,6 di tert butyl 4 methyl phenol 20-40 parts, big
Soya-bean oil 25-35 parts, mineral oil 25-35 parts, hydroquinones 5-10 parts.
The filler is one kind in calcene, talcum powder or aluminium-hydroxide powder.
The slip agent is high density polyethylene waxes.
The counnter attack ink is cornstarch.
The anti-settling agent is aerosil anti-settling agent.
The defoamer is one in polyether modified silicon oil, polypropylene glycerol aether or polyoxypropylene ethylene oxide glycerin ether
Kind.
The preparation method of environmental printing ink of the present invention, comprises the following steps：1）Each raw material is weighed by weight, is put successively
Enter in stirred autoclave, stir speed (S.S.) 1500-2000r/min, be first warming up to 60-70 DEG C of stirring reaction 20-25min, then
It is warming up to 80-85 DEG C and continues stirring reaction 30-35min；2）Material after stirring reaction is stood into 20-25min, then through three rollers
Machine is ground to the slurry that fineness is less than 15 μm, as described environmental printing ink.
The present invention is auxiliary agent from Potato Porous Starch, is accelerated using the excellent characterization of adsorption of Potato Porous Starch
Ink setting speed, the properties of stable printing-ink, while suction-operated of the printing machine to printing-ink can be substantially reduced,
And then improve the availability of printing-ink.
Bridging agent plays the instrumentality of dispersion color and auxiliary material, and link stuff is to the transitivity of ink, brightness, set speed
And other effects have a significant impact, therefore, it is to ensure to print one of good key to select suitable bridging agent.The present invention selects phosphoric acid
Bonding agent is made in front three phenolic ester, hydrogenated rosin glyceride, ethyl acetate, epoxy resin, ethanol and dibutyl tin laurate,
There is certain mobility, ink is formed uniform thin layer after printing, the film layer formed with some strength after drying, and to color
Material shields, and improves the tinting strength, tinting power of colorant, makes it be difficult to come off.
The effect of anti skinning agent is to suppress the rate of drying of ink, prevents ink from mechanically drying conjunctiva.The present invention's
Anti skinning agent is made up of 2,6- di-tert-butyl-4-methy phenols, soybean oil, mineral oil and hydroquinones, wherein 2,6- bis- uncles
Butyl -4- methylphenols are a kind of antioxidants of food-grade, have the function that to prevent ink skinning added in ink, it makes
Dosage can increase as needed；The oxidation resistant effect that hydroquinones has to the metal salt in ink, can prevent ink
Surface crusting.
For the present invention from by the use of cornstarch as counnter attack ink, it is to prevent printing ink layer from printing to the paper back of the body that it, which is acted on,
Face, to ensure printing quality.The present invention is with polyether modified silicon oil, polypropylene glycerol aether or polyoxypropylene ethylene oxide glycerin ether
For defoamer, there is the features such as defoaming is rapid, and the suds time is grown and is safe and non-toxic.
The present invention use above technical scheme, uses raw material as without benzene series material, will not without volatility toxic solvent
The health of printing worker is endangered, it is good to air also non-environmental-pollution, the feature of environmental protection.Printing, light are printed using ink of the present invention
Ze Dugao, wearability is good, and rate of drying is fast, and product quality is good, and ink is not in the phenomenon for coming off, falling the effect of ink, the printing of printing
Effect can persistently be kept.
Embodiment
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
Colorant 15-20 parts；Bridging agent 25-30 parts；Diluent 20-30 parts；
Anti skinning agent 5-10 part filler 10-15 parts；Slip agent 5-10 parts；
Counnter attack ink 5-10 parts；Anti-settling agent 1-3 parts；Defoamer 1-3 parts；
Auxiliary agent 5-10 parts, the auxiliary agent are Potato Porous Starch；
The bridging agent is made up of the component of following parts by weight：Tricresyl phosphate 15-20 parts, hydrogenated rosin glyceride 5-10
Part, ethyl acetate 3-8 parts, epoxy resin 3-8 parts, ethanol 20-30 parts, dibutyl tin laurate 3-8 parts.
The diluent is made up of the component of following parts by weight：1 part of dichloromethane, ethyl acetate 1-3 parts, methyl ethyl ketone
1-3 parts, ethylene glycol ethyl ether 1-3 parts, oligomerization linseed oil 2-3 parts.
The anti skinning agent is made up of the component of following parts by weight：It is 2,6 di tert butyl 4 methyl phenol 20-40 parts, big
Soya-bean oil 25-35 parts, mineral oil 25-35 parts, hydroquinones 5-10 parts.
The filler is one kind in calcene, talcum powder or aluminium-hydroxide powder.The slip agent is highly dense
Spend Tissuemat E.The counnter attack ink is cornstarch.The anti-settling agent is aerosil anti-settling agent.The defoamer is
One kind in polyether modified silicon oil, polypropylene glycerol aether or polyoxypropylene ethylene oxide glycerin ether.
The preparation method of the environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, is sequentially placed into
In stirred autoclave, stir speed (S.S.) 1500-2000r/min, 60-70 DEG C of stirring reaction 20-25min, Ran Housheng are first warming up to
Warm to 80-85 DEG C is continued stirring reaction 30-35min；2）Material after stirring reaction is stood into 20-25min, then through three-roller
It is ground to the slurry that fineness is less than 15 μm, as described environmental printing ink.
Embodiment 1
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
15 parts of colorant；25 parts of bridging agent；25 parts of diluent；
7.5 parts of anti skinning agent, 12 parts of filler；7.5 parts of slip agent；
7.5 parts of counnter attack ink；2 parts of anti-settling agent；2 parts of defoamer；
7 parts of auxiliary agent Potato Porous Starch；
Wherein, bridging agent is made up of the component of following parts by weight：15 parts of tricresyl phosphate, 5 parts of hydrogenated rosin glyceride, acetic acid
3 parts of ethyl ester, 8 parts of epoxy resin, 30 parts of ethanol, 8 parts of dibutyl tin laurate；
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 2 parts of ethyl acetate, 2 parts of methyl ethyl ketone, ethylene glycol
2 parts of ether, 2.5 parts of oligomerization linseed oil；
Anti skinning agent is made up of the component of following parts by weight：30 parts of 2,6 di tert butyl 4 methyl phenol, 30 parts of soybean oil, ore deposit
Thing oil 30 parts, 7.5 parts of hydroquinones；
Filler is calcene, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is gas phase
Silica anti-settling agent, defoamer are polyether modified silicon oil.
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, successively
It is put into stirred autoclave, stir speed (S.S.) 1500r/min, is first warming up to 65 DEG C of stirring reaction 25min, then heats to 80 DEG C
Continue stirring reaction 35min；2）Material after stirring reaction is stood into 20min, is then ground to fineness through three-roller as 15 μm
Following slurry, as described environmental printing ink.
Embodiment 2
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
20 parts of colorant；30 parts of bridging agent；20 parts of diluent；
5 parts of anti skinning agent, 10 parts of filler；5 parts of slip agent；
5 parts of counnter attack ink；1 part of anti-settling agent；1.5 parts of defoamer；
10 parts of auxiliary agent Potato Porous Starch；
Wherein, bridging agent is made up of the component of following parts by weight：15 parts of tricresyl phosphate, 10 parts of hydrogenated rosin glyceride, second
8 parts of acetoacetic ester, 8 parts of epoxy resin, 20 parts of ethanol, 3 parts of dibutyl tin laurate；
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 1 part of ethyl acetate, 1 part of methyl ethyl ketone, ethylene glycol
1 part of ether, 2 parts of oligomerization linseed oil；
Anti skinning agent is made up of the component of following parts by weight：20 parts of 2,6 di tert butyl 4 methyl phenol, 35 parts of soybean oil, ore deposit
Thing oil 25 parts, hydroquinones part；
The filler is talcum powder, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is gas phase
Silica anti-settling agent, defoamer are polypropylene glycerol aether
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, is sequentially placed into
In stirred autoclave, stir speed (S.S.) 2000r/min, 60 DEG C of stirring reaction 25min are first warming up to, then heat to 85 DEG C of continuation
Stirring reaction 30min；2）Material after stirring reaction is stood into 25min, is then ground to fineness through three-roller as less than 15 μm
Slurry, as described environmental printing ink.
Embodiment 3
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
20 parts of colorant；25 parts of bridging agent；20 parts of diluent；
10 parts of anti skinning agent, 15 parts of filler；10 parts of slip agent；
5 parts of counnter attack ink；3 parts of anti-settling agent；3 parts of defoamer；
10 parts of auxiliary agent Potato Porous Starch；
Wherein, bridging agent is made up of the component of following parts by weight：15 parts of tricresyl phosphate, 5 parts of hydrogenated rosin glyceride, acetic acid
3 parts of ethyl ester, 3 parts of epoxy resin, 25 parts of ethanol, 5 parts of dibutyl tin laurate；
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 1.5 parts of ethyl acetate, 2.5 parts of methyl ethyl ketone, second
3 parts of glycol ether, 2.5 parts of oligomerization linseed oil.
Anti skinning agent is made up of the component of following parts by weight：20 parts of 2,6 di tert butyl 4 methyl phenol, soybean oil 25
Part, 35 parts of mineral oil, 0 part of hydroquinones；
Filler is aluminium-hydroxide powder, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is gas
Aerosil anti-settling agent, defoamer are polyoxypropylene ethylene oxide glycerin ether.
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, successively
It is put into stirred autoclave, stir speed (S.S.) 1800r/min, is first warming up to 70 DEG C of stirring reaction 25min, then heats to 85 DEG C
Continue stirring reaction 30min；2）Material after stirring reaction is stood into 20min, is then ground to fineness through three-roller as 15 μm
Following slurry, as described environmental printing ink.
Embodiment 4
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
15 parts of colorant；25 parts of bridging agent；25 parts of diluent；
50 parts of anti skinning agent, 10 parts of filler；8 parts of slip agent；
5 parts of counnter attack ink；1 part of anti-settling agent；1 part of defoamer；
5 parts of auxiliary agent Potato Porous Starch；
Wherein, bridging agent is made up of the component of following parts by weight：18 parts of tricresyl phosphate, 7.5 parts of hydrogenated rosin glyceride, second
6 parts of acetoacetic ester, 6 parts of epoxy resin, 30 parts of ethanol, 3 parts of dibutyl tin laurate；
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 3 parts of ethyl acetate, 3 parts of methyl ethyl ketone, ethylene glycol
3 parts of ether, 3 parts of oligomerization linseed oil；
Anti skinning agent is made up of the component of following parts by weight：40 parts of 2,6 di tert butyl 4 methyl phenol, 35 parts of soybean oil, ore deposit
Thing oil 25 parts, hydroquinones 5- parts；
Filler is calcene, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is gas phase
Silica anti-settling agent, defoamer are polyether modified silicon oil.
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, successively
It is put into stirred autoclave, stir speed (S.S.) 1500r/min, is first warming up to 70 DEG C of stirring reaction 20min, then heats to 80 DEG C
Continue stirring reaction 35min；2）Material after stirring reaction is stood into 20min, is then ground to fineness through three-roller as 15 μm
Following slurry, as described environmental printing ink.
Embodiment 5
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
18 parts of colorant；28 parts of bridging agent；25 parts of diluent；
5 parts of anti skinning agent, 10 parts of filler；8 parts of slip agent；
5 parts of counnter attack ink；2 parts of anti-settling agent；3 parts of defoamer；
10 parts of auxiliary agent Potato Porous Starch；；
Wherein, bridging agent is made up of the component of following parts by weight：18 parts of tricresyl phosphate, 7 parts of hydrogenated rosin glyceride, acetic acid
8 parts of ethyl ester, 6 parts of epoxy resin, 25 parts of ethanol, 5 parts of dibutyl tin laurate；
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 1 part of ethyl acetate, 1 part of methyl ethyl ketone, ethylene glycol
1 part of ether, 2 parts of oligomerization linseed oil；
Anti skinning agent is made up of the component of following parts by weight：25 parts of 2,6 di tert butyl 4 methyl phenol, 35 parts of soybean oil, ore deposit
Thing oil 30 parts, 10 parts of hydroquinones.
Filler is colloid talcum powder, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is
Aerosil anti-settling agent, defoamer are polypropylene glycerol aether.
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, successively
It is put into stirred autoclave, stir speed (S.S.) 2000r/min, is first warming up to 60 DEG C of stirring reaction 20min, then heats to 85 DEG C
Continue stirring reaction 30min；2）Material after stirring reaction is stood into 25min, is then ground to fineness through three-roller as 15 μm
Following slurry, as described environmental printing ink.
Embodiment 6
A kind of environmental printing ink, its raw material are made up of the component of following parts by weight：
20 parts of colorant；30 parts of bridging agent；30 parts of diluent；
7.5 parts of anti skinning agent, 12 parts of filler；8 parts of slip agent；
7.5 parts of counnter attack ink；2 parts of anti-settling agent；1 part of defoamer；
8 parts of auxiliary agent Potato Porous Starch；
Wherein, bridging agent is made up of the component of following parts by weight：15 parts of tricresyl phosphate, 5 parts of hydrogenated rosin glyceride, acetic acid
8 parts of ethyl ester, 58 parts of epoxy resin, 20 parts of ethanol, 3 parts of dibutyl tin laurate.
Diluent is made up of the component of following parts by weight：1 part of dichloromethane, 3 parts of ethyl acetate, 1 part of methyl ethyl ketone, second
1 part of glycol ether, 3 parts of oligomerization linseed oil；
The anti skinning agent is made up of the component of following parts by weight：20 parts of 2,6 di tert butyl 4 methyl phenol, soybean oil 25
Part, 35 parts of mineral oil, 10 parts of hydroquinones；
Filler is calcene, and slip agent is high density polyethylene waxes, and counnter attack ink is cornstarch, and anti-settling agent is gas phase
Silica anti-settling agent, defoamer are polyether modified silicon oil.
The preparation method of the present embodiment environmental printing ink, comprises the following steps：1）Each raw material is weighed by weight, successively
It is put into stirred autoclave, stir speed (S.S.) 2000r/min, is first warming up to 60 DEG C of stirring reaction 25min, then heats to 80 DEG C
Continue stirring reaction 30min；2）Material after stirring reaction is stood into 25min, is then ground to fineness through three-roller as 15 μm
Following slurry, as described environmental printing ink.
Claims (10)
- A kind of 1. environmental printing ink, it is characterised in that：Its raw material is made up of the component of following parts by weight：Colorant 15-20 parts；Bridging agent 25-30 parts；Diluent 20-30 parts；Anti skinning agent 5-10 part filler 10-15 parts；Slip agent 5-10 parts；Counnter attack ink 5-10 parts；Anti-settling agent 1-3 parts；Defoamer 1-3 parts；Auxiliary agent 5-10 parts, the auxiliary agent are Potato Porous Starch；The bridging agent is by tricresyl phosphate, hydrogenated rosin glyceride, ethyl acetate, epoxy resin, ethanol and two bays Sour dibutyl tin composition；The diluent is made up of dichloromethane, ethyl acetate, methyl ethyl ketone, ethylene glycol ethyl ether and oligomeric linseed oil.
- A kind of 2. environmental printing ink according to claim 1, it is characterised in that：The weight of each component in the bridging agent Part is as follows：Tricresyl phosphate 15-20 parts, hydrogenated rosin glyceride 5-10 parts, ethyl acetate 3-8 parts, epoxy resin 3-8 parts, Ethanol 20-30 parts, dibutyl tin laurate 3-8 parts.
- A kind of 3. environmental printing ink according to claim 1, it is characterised in that：The weight of each component in the diluent Part is as follows：1 part of dichloromethane, ethyl acetate 1-3 parts, methyl ethyl ketone 1-3 parts, ethylene glycol ethyl ether 1-3 parts, oligomerization linseed oil 2-3 parts.
- A kind of 4. environmental printing ink according to claim 1, it is characterised in that：The anti skinning agent is by following parts by weight Component composition：2,6 di tert butyl 4 methyl phenol 20-40 parts, soybean oil 25-35 parts, mineral oil 25-35 parts, to benzene two Phenol 5-10 parts.
- A kind of 5. environmental printing ink according to claim 1, it is characterised in that：The filler be calcene, One kind in talcum powder or aluminium-hydroxide powder.
- A kind of 6. environmental printing ink according to claim 1, it is characterised in that：The slip agent is high density polyethylene (HDPE) Wax.
- A kind of 7. environmental printing ink according to claim 1, it is characterised in that：The counnter attack ink is cornstarch.
- A kind of 8. environmental printing ink according to claim 1, it is characterised in that：The anti-settling agent is aerosil Anti-settling agent.
- A kind of 9. environmental printing ink according to claim 1, it is characterised in that：The defoamer is polyether-modified silicon One kind in oil, polypropylene glycerol aether or polyoxypropylene ethylene oxide glycerin ether.
- A kind of 10. preparation method of environmental printing ink as described in one of claim 1-9, it is characterised in that：It include with Lower step：1）Each raw material is weighed by weight, is sequentially placed into stirred autoclave, stir speed (S.S.) 1500-2000r/min, first 60-70 DEG C of stirring reaction 20-25min is warming up to, 80-85 DEG C is then heated to and continues stirring reaction 30-35min；2）Will stirring Reacted material stands 20-25min, is then ground to the slurry that fineness is less than 15 μm, as described environmental protection through three-roller Printing-ink.