CN107540887A - A kind of automobile chassis suspension high temperature resistant fatigue rubber composition - Google Patents
A kind of automobile chassis suspension high temperature resistant fatigue rubber composition Download PDFInfo
- Publication number
- CN107540887A CN107540887A CN201710759290.1A CN201710759290A CN107540887A CN 107540887 A CN107540887 A CN 107540887A CN 201710759290 A CN201710759290 A CN 201710759290A CN 107540887 A CN107540887 A CN 107540887A
- Authority
- CN
- China
- Prior art keywords
- parts
- high temperature
- temperature resistant
- rubber composition
- automobile chassis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of automobile chassis suspension high temperature resistant fatigue rubber composition, it is characterised in that includes 75 90 parts of natural rubber in parts by weight;10 25 parts of butadiene rubber;2.5 3.5 parts of p phenylenediamine type antioxidant;12 parts of dihyaroquinoline class age resistor;23 parts of physical antioxidant;24 parts of plasticizer;50 54 parts of reinforcing agent;58 parts of activating agent;12 parts of stearic acid;2.5 3 parts of vulcanizing agent;1 1.5 parts of accelerator;0.5 1 parts of assistant crosslinking agent.Production process of the present invention is easy to operate, it is not necessary to which special processing technology, gained rubber have splendid high temperature resistant dynamic fatigue property.
Description
Technical field
The present invention relates to a kind of automobile chassis suspension high temperature resistant fatigue rubber composition, for making automobile chassis
Arm bush is controlled, belongs to field of rubber technology.
Background technology
Chassis suspension is that isolation road vibration transmits to in-car, is to influence vehicle to drive impression and riding comfort
Key components and parts, in the process of moving, the size of in-car vibration and noise, chassis suspension serves very important vehicle
Effect.Suspension can be housed between body of a motor car and chassis, primarily serve isolation road vibration, decay road excitation and right
Circumferential component carries out the effect of confining guard;Its critical piece is made up of control arm assembly and elastomeric bushing;Primarily serve fast
The vibration that speed decay road surface is transmitted to in-car, improve ride comfort, comfortableness and the security of running car.
For offroad vehicle because of its special traveling road conditions, the load that shock absorbing bushing is subject in use is bigger, and heat is also more
Greatly, if the high temperature resistant fatigue behaviour of rubber shock-absorbing bushing is bad, if being broken during use, potential safety hazard can be caused, and need
Whole suspension assembly is changed, adds maintenance cost;So to determine that elastomeric material will meet good resistance to for its use condition
Dynamic high temperature fatigue behaviour requirement, to meet the comfortableness and security in vehicle travel process, it is therefore desirable to ensureing to take
On the premise of comfortableness, the high temperature resistant dynamic fatigue property ever more important of existing rubber composition is improved.
The content of the invention
Problem to be solved by this invention is to provide a kind of automobile chassis suspension high temperature resistant fatigue rubber composition.
In order to solve the above problems, the technical scheme is that it is tired to provide a kind of automobile chassis suspension high temperature resistant
Labor rubber composition, it is characterised in that include component as follows in parts by weight:
Preferably, the natural rubber uses SVR3L and ENR by weight 65: 35 Blend rubber.
Preferably, the physical antioxidant uses ANTIWAX 6268.
Preferably, the reinforcing agent is using Cabot N-234 carbon blacks and nano modification kaolin NCL-302 mixture.
Preferably, the plasticizer uses environment-friendly aromatic oil VIVATEC500.
Preferably, the assistant crosslinking agent uses SV207.
The present invention has selected Vietnam's SVR3L natural rubbers and epoxidation natural gum blend, and (SVR3L and ENR are common by 65: 35
It is mixed), wherein ENR is and preparation, ring after being oxidized by the partial double bond on epoxidation modification natural rubber rubber molecular chain
Oxidation after rubber macromolecule polarity increase, intermolecular force enhancing, therefore make ENR both remained with NR basic structure and
Performance characteristics, many unique performances are generated again, are mainly had:Excellent air-tightness, excellent oil resistivity, compatibility, moisture-resistant
Good adhesive property between slip, low rolling resistance and other materials etc.;It is original excellent in NR by being blended to use with NR
On the basis of performance, the combination property of vulcanizate is improved.Heat-resisting, anti-aging property to ensure excellent have selected stability
German Chinese sage environment-friendly aromatic oil VIVATEC500 good, flash-point is high.It is to ensure sulphur from Cabot super abrasive carbon black N-234
Change the combination properties such as the excellent tensile strength of glue, tearing strength, and be to reduce life with nano modification kaolin NCL-302
Heat, so that rubber reaches balance in each side such as tensile strength, tearing strength, heat build-ups.It is anti-old from new physics
Agent ANTIWAX 6268 is used in combination with p phenylenediamine type antioxidant, plays synergy, is to ensure more excellent ozone and heat
Oxygen barrier propterty.What assistant crosslinking agent was selected is that novel and multifunctional crosslinking aid S V207 is to ensure good dynamic static modulus, drawing
Stretch intensity, tearing strength, hardness, resilience, compression, heat etc., in the sulfur cross-linking that SV207 is participated in, thermodynamics will be formed
Mixing cross-bond stable and that tool is flexible, structure is " rubber-Sx-(CH2)6-Sx- rubber " (X≤3).
Production process of the present invention is easy to operate, it is not necessary to which special processing technology, gained rubber have splendid high temperature resistant
Dynamic fatigue property.
Embodiment
To become apparent the present invention, hereby with preferred embodiment, it is described in detail below.
Natural rubber used is Vietnam's SVR3L glue and Malay epoxidation natural gum blend in embodiment 1-4;
Cis-butadiene cement used is the BR9000 of Shanghai Gaoqiao petrochemical corporation (complex) production;N- (1,3- dimethyl) butyl-N '-phenyl pair used
Phenylenediamine and 2,2,4- trimethyl -1,2- dihyaroquinoline polymer are produced by Huangyan East Zhejiang province rubber chemicals chemical plant;N used,
N '-DTPD di tolyl p phenylenediamine (mixture) is produced by Jiangsu Guoli Chemical Science Co., Ltd;Physical antioxidant used
ANTIWAX 6268 is provided by Shanghai Chang Yu Chemical Co., Ltd.s;The N-234 that carbon black used is produced by Shanghai Cabot carbon black plant;
Nano modification kaolin NCL-302 used is provided by Shanghai product victory chemical industry, and plasticizer used is German Chinese sage environment-friendly aromatic oil
VIVATEC500;99.7% zinc oxide used is provided by U.S. zinc;Stearic acid used is produced by Shanghai Yan honeybee oil chemistry factory
Conventional material;Insoluble sulfur used is by the good German STRUKTOL S80 for opening up the offer of (Shanghai) Chemical trade Co., Ltd;
Accelerant N used-oxygen di- (1,2- ethylidene) -2-[4-morpholinodithio sulfenamide is given birth to by the luxuriant woods rubber chemicals chemical plant in Puyang
Production, novel and multifunctional crosslinking aid S V207 used are provided by Shanghai long day reputation chemical industry.
Embodiment 1
A kind of automobile chassis suspension high temperature resistant fatigue rubber composition, contains component as follows in parts by weight:
Table 1
The preparation of above-mentioned composition can use mixer mixing, and its step is as follows:
Mixer mixing:Banbury temperature is risen to 90-110 DEG C, the SVR3L to plasticate on a mill and ENR is thrown
Enter kneading 60s in banburying chamber, then lift one section of fines such as floating weight addition activating agent, stearic acid and age resistor, added after 60s
Reinforcing agent, add plasticizer after 120s, the carbon black on floating weight sweeping machine and floating weight lifted after 60s, put down floating weight after
Continuous banburying 60s back glues and on a mill rolling out film, at least more than 12 hours addition sulphur, assistant crosslinking agents are parked after cooling
And accelerator, 150s back glues and thin logical on a mill and beat triangle bag 3-5 times bottom sheet or shaping, wherein banburying room temperature afterwards
≤90℃。
Embodiment 2
A kind of automobile chassis suspension high temperature resistant fatigue rubber composition, contains component as follows in parts by weight:
Table 2
Preparation method is same as Example 1.
Embodiment 3
A kind of automobile chassis suspension high temperature resistant fatigue rubber composition, contains component as follows in parts by weight:
Table 3
Raw material | Parts by weight |
NR/ENR | 80 parts |
Cis-butadiene cement BR9000 | 20 parts |
Activating agent ZnO | 6 parts |
Stearic acid | 1 part |
Antioxidant 4020 | 1.5 part |
Antioxidant D TPD | 2 parts |
Anti-aging agent RD | 1.5 part |
ANTIWAX 6268 | 2.5 part |
Cabot N-234 carbon blacks | 28 parts |
Nano modification kaolin NCL-302 | 26 parts |
Environment-friendly aromatic oil VIVATEC500 | 3 parts |
Insoluble sulfur S80 | 2.8 part |
Accelerant CZ | 1.2 part |
SV207 | 0.5 part |
Preparation method is same as Example 1.
Embodiment 4
A kind of automobile chassis suspension high temperature resistant fatigue rubber composition, contains component as follows in parts by weight:
Table 4
Raw material | Parts by weight |
NR/ENR | 75 parts |
Cis-butadiene cement BR9000 | 25 parts |
Activating agent ZnO | 8 parts |
Stearic acid | 1.5 part |
Antioxidant 4020 | 1.5 part |
Antioxidant D TPD | 1.5 part |
Anti-aging agent RD | 2 parts |
ANTIWAX 6268 | 2 parts |
Cabot N-234 carbon blacks | 24 parts |
Nano modification kaolin NCL-302 | 30 parts |
Environment-friendly aromatic oil VIVATEC500 | 3 parts |
Insoluble sulfur S80 | 3 parts |
Accelerant CZ | 1 part |
SV207 | 1 part |
Preparation method is same as Example 1.
Comparative example
A kind of rubber composition, contain component as follows in parts by weight:
Table 5
Embodiment 1-4 and comparative example are subjected to elastomeric material experiment respectively, the data obtained is as shown in table 6.
Table 6
Rubber bushing is made in embodiment 1-4 and comparative example rubber composition, carries out high temperature dynamic fatigue test, experiment
Data are as shown in table 7.
Table 7
Claims (6)
1. a kind of automobile chassis suspension high temperature resistant fatigue rubber composition, it is characterised in that comprising as follows with parts by weight
The component of meter:
2. automobile chassis suspension as claimed in claim 1 high temperature resistant fatigue rubber composition, it is characterised in that described
Natural rubber uses SVR3L and ENR by weight 65: 35 Blend rubber.
3. automobile chassis suspension as claimed in claim 1 high temperature resistant fatigue rubber composition, it is characterised in that described
Physical antioxidant uses ANTIWAX 6268.
4. automobile chassis suspension as claimed in claim 1 high temperature resistant fatigue rubber composition, it is characterised in that described
Reinforcing agent is using Cabot N-234 carbon blacks and nano modification kaolin NCL-302 mixture.
5. automobile chassis suspension as claimed in claim 1 high temperature resistant fatigue rubber composition, it is characterised in that described
Plasticizer uses environment-friendly aromatic oil VIVATEC500.
6. automobile chassis suspension as claimed in claim 1 high temperature resistant fatigue rubber composition, it is characterised in that described
Assistant crosslinking agent uses SV207.