CN107511550A - A kind of high-frequency induction brazing device and method of aluminum bronze soldered fitting - Google Patents
A kind of high-frequency induction brazing device and method of aluminum bronze soldered fitting Download PDFInfo
- Publication number
- CN107511550A CN107511550A CN201710804490.4A CN201710804490A CN107511550A CN 107511550 A CN107511550 A CN 107511550A CN 201710804490 A CN201710804490 A CN 201710804490A CN 107511550 A CN107511550 A CN 107511550A
- Authority
- CN
- China
- Prior art keywords
- frequency induction
- heating element
- copper
- aluminium
- heating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to soldering tech, and in particular to a kind of high-frequency induction brazing device and method of aluminum bronze soldered fitting.The high-frequency induction brazing device of aluminum bronze soldered fitting of the present invention includes heating element heater, radio-frequency induction coil, workbench, base.Wherein, the workbench is arranged on base, heating element heater is arranged on workbench, and heating element heater is divided into two parts, a part is used to place heating copper tip, another part is used to place heating aluminium bar, and radio-frequency induction coil is divided into two parts, is looped around two parts that heating element heater is used to heat copper tip and aluminium bar respectively.The present invention heats heating element heater by using radio-frequency induction coil, then carries out soldering by heating element heats copper-aluminium joint, and its is simple in construction, easy to operate, and brazing quality is high, has larger practical value.
Description
Technical field
The invention belongs to soldering tech, and in particular to high-frequency induction brazing device and side to a kind of aluminum bronze soldered fitting
Method.
Background technology
High-frequency induction brazing is the soldering processes carried out using high frequency electric sensing heating, noiseless in welding process,
It is a kind of green, environmental protection, the soldering tech of safety, can be applied to the soldering of the parts such as busbar, ingot head screw, latch.Phase
For gas brazing, production noise can be reduced, improves production environment, improves operating efficiency.
But problems be present when welding copper aluminium soldering plumb joint using high-frequency induction brazing：1. due to the magnetic of copper aluminium
Coefficient of conductivity very little, high-frequency induction are slow to the firing rate of copper element in aluminium joint, so as to be difficult directly to carry out high-frequency induction brazing；
2. the magnetic conductance rate coefficient very little of bronze medal aluminium, can cause the electric current in high-frequency induction brazing equipment excessive, equipment be damaged, therefore
General high-frequency induction brazing equipment is difficult to directly apply to the soldering of copper element in aluminium joint.
The content of the invention
Goal of the invention：A kind of device and method for the high-frequency induction brazing that can realize aluminum bronze soldered fitting is provided.
Technical solution of the present invention：A kind of high-frequency induction brazing device of aluminum bronze soldered fitting, it includes heating element heater, high frequency
Induction coil, workbench, base, wherein, the workbench is arranged on base, and heating element heater is arranged on workbench
On, and heating element heater is divided into two parts, a part is used to place heating copper tip, and another part is used to place heating aluminium bar, high
Frequency induction coil is divided into two parts, is looped around two parts that heating element heater is used to heat copper tip and aluminium bar respectively.
The heating element heater is the high ferrous metal of unit permeance.
The heating element heater is iron or steel or stainless steel.
Below the heating element heater, flitch is provided with base.
Shape, the frequency of the radio-frequency induction coil are identical with electric current.
A kind of method that high-frequency induction brazing device described in carries out copper element in aluminium joint soldering, first passes through high frequency sense
Coil heats heating element heater is answered, then heats the copper tip and aluminium bar being disposed thereon in thermo-conducting manner by heating element heater,
By monitoring temperature, when temp of heating element reaches setting value, take out aluminium bar and the copper tip with presetting solder is welded
Connect, realize copper aluminium soldering.
When copper tip and aluminium bar carry out copper aluminium soldering, isothermal holding is carried out by heating element heater.
During heating element heats, the preset solder of copper tip can melt the pricker that not stopping pregnancy life impurity swims in fusing
Material above, strikes off the impurity of floating, until exposing the metallic luster of solder.
In solder solidification process, processing is carried out to the solder at copper element in aluminium joint and accomplishes groove.
Advantages of the present invention and effect：High-frequency induction brazing device and method of the present invention is simple and practical, it is easy to operate, do not increase
The financial cost of part processing, engineer applied of the high-frequency induction brazing in copper element in aluminium joint can be achieved.Between radio-frequency induction coil
Connect that the firing rate of Heated Copper element in aluminium joint is fast, the thermostatic control of brazing temperature can be realized.Go the convenient letter of deimpurity method
It is single effective, avoid impurity from polluting radio-frequency induction coil in removal process, there is certain security.Although by solder and aluminium bar
Separately heating, but the shape of induction coil, frequency are identical with electric current, the shapes of materials of heating element heater is also identical, therefore solder
There is identical temperature with aluminium bar, ensure that brazing temperature requirement.
Brief description of the drawings
Fig. 1 is the high-frequency induction brazing device heating schematic diagram of aluminum bronze soldered fitting of the present invention；
Fig. 2 is the high-frequency induction brazing view of aluminum bronze soldered fitting of the present invention；
Fig. 3 is aluminum bronze soldered fitting structural representation involved in the present invention,
Wherein, the heating element heater 8. of 1. copper tip, 2. aluminium bar, 3. soldered fitting, 4. base, 5. workbench, 6. flitch 7.
The coil 2 of coil 1 9..
Specific implementation step
The present invention is described in further detail below.
Referring to Fig. 2, the high-frequency induction brazing device of aluminum bronze soldered fitting of the present invention includes heating element heater 7, high-frequency induction
Coil, workbench 5, base 4, solder 6.Wherein, the workbench 5 is arranged on base 4, and heating element heater 7 is arranged on work
Make on platform 6.The heating element heater 4 is divided into the essentially identical two parts of profile, size, and a part is used to place Heated Copper end
Son, another part are used to place heating aluminium bar.The radio-frequency induction coil is divided into coil 1 and the two parts of coil 2, two coils
Shape, frequency and electric current are identical, are looped around two parts that heating element heater is used to heat copper tip and aluminium bar respectively.
The heating element heater is the high ferrous metal of unit permeance, such as iron or steel or stainless steel, in radio-frequency induction coil
It can be rapidly heated under effect.
In addition, below the heating element heater, flitch is provided with base, for the solder fallen under collection.
The present invention changes the mode of heating that copper element in aluminium joint is directly heated using radio-frequency induction coil, is changed into high-frequency induction
Coil first heats the high heating element heater of steel, stainless steel equimagnetic coefficient of conductivity, then again in a manner of heat transfer or heat radiation between
Connect Heated Copper element in aluminium joint.Since so, when being heated, heating element heater can be as the thermal source of soldering, when stopping
When only heating, heating element heater can be incubated to copper element in aluminium joint, so as to improve the quality of soldered fitting.
The high-frequency induction brazing method of copper element in aluminium joint of the present invention is given below, its detailed process is as follows：
Step 1: material prepares
Engineer testing sample is got in warehouse, checks whether pattern is consistent for part verification of conformity.Solder and brazing flux should have
Acceptable quality proves.
Step 2: welding preparation.
The joint edges of part should go flash removed and careful backfit.The welding region of part carries out soak cleaning or machinery is clear
Reason, ensure institute's cleaning area oxide-free, greasy dirt and other exotics.
Step 2: welding
A) copper tip is fixed on the heating element；
B) the heating position for selecting heating element heater is temperature measuring point, and heating position is heating member in the part in region 1.Laser is taken aim at
Certainly behind position, tighten and fix support；
C) high-frequency induction welder is opened, is adjusted to weld preceding use state.Cooling recirculation system is first opened, opens main electricity afterwards
Source, manual heating pattern is selected, is heated.Thermometric temperature is set as 720 DEG C；
D) brazing flux is first preset in copper tip.After floor push heated partses reach design temperature, solder HL501 is added；
E) impurity that foam-like can be constantly produced during brazing filler metal melts is swum in above the solder of fusing, with saw blade not
The disconnected impurity for striking off floating, until exposing the metallic luster of solder.Stop heating, part is carried out using the residual temperature of heating member
Insulation.Impurity plate on work top is changed into new stainless steel flitch；
F) after solder of the copper tip inner chamber full of melting, aluminium bus bar is heated with induction coil, while copper tip is entered
Row insulation, after aluminium bus bar is warming up to more than solder temperature, is immediately inserted into copper tip inner chamber；
G) solder, which is extruded, is retained on new stainless steel flitch, and the solder for preventing from being extruded scalds people.Observe welding machine temperature
Temperature and the state of solder on panel are spent, panel temperature is maintained between 300 DEG C~400 DEG C, is scraped with saw blade and smear groove, and groove will
Rounding off is sought, as shown in Fig. 2 computer heating control temperature during repairing groove；
H) after groove is fixed, part is slightly cooled down, and testpieces is taken out out of fixture, normal temperature is cooled in air；
I) pickling removes brazing flux.Part should be cleaned and dried in postwelding 6h；
J) polish.The redundant brazing filler metal of piece surface is removed with scraper or pneumatic grinding wheel.
Claims (9)
1. a kind of high-frequency induction brazing device of aluminum bronze soldered fitting, it is characterised in that including heating element heater, radio-frequency induction coil
Circle, workbench, base, wherein, the workbench is arranged on base, and heating element heater is arranged on workbench, and is added
Thermal element is divided into two parts, and a part is used to place heating copper tip, and another part is used to place heating aluminium bar, radio-frequency induction coil
Circle is divided into two parts, is looped around two parts that heating element heater is used to heat copper tip and aluminium bar respectively.
2. the high-frequency induction brazing device of aluminum bronze soldered fitting according to claim 1, it is characterised in that the heating unit
Part is the high ferrous metal of unit permeance.
3. the high-frequency induction brazing device of aluminum bronze soldered fitting according to claim 1, it is characterised in that the heating unit
Part is iron or steel or stainless steel.
4. the high-frequency induction brazing device of aluminum bronze soldered fitting according to claim 1, it is characterised in that the heating unit
Below part, flitch is provided with base.
5. the high-frequency induction brazing device of aluminum bronze soldered fitting according to claim 1, it is characterised in that the high frequency sense
Answer shape, frequency and the electric current of coil identical.
6. a kind of method that copper element in aluminium joint soldering is carried out using high-frequency induction brazing device according to claim 1,
Characterized in that, first passing through radio-frequency induction coil heating heating element heater, then heated and set in thermo-conducting manner by heating element heater
Put the copper tip and aluminium bar thereon, by monitoring temperature, when temp of heating element reaches setting value, take out aluminium bar and with it is pre-
The copper tip for being equipped with solder is welded, and realizes copper aluminium soldering.
7. copper element in aluminium joint high-frequency induction brazing method according to claim 6, it is characterised in that copper tip and aluminium bar
When carrying out copper aluminium soldering, isothermal holding is carried out by heating element heater.
8. copper element in aluminium joint high-frequency induction brazing method according to claim 6, it is characterised in that heating element heats
During, the preset solder of copper tip can melt not stopping pregnancy life impurity and swim in above the solder of fusing, strike off the miscellaneous of floating
Matter, until exposing the metallic luster of solder.
9. copper element in aluminium joint high-frequency induction brazing method according to claim 6, it is characterised in that solidified in solder
Cheng Zhong, processing is carried out to the solder at copper element in aluminium joint and accomplishes groove.