CN107476048A - A kind of antibacterial ribbon preparation method based on original position - Google Patents

A kind of antibacterial ribbon preparation method based on original position Download PDF

Info

Publication number
CN107476048A
CN107476048A CN201710591367.9A CN201710591367A CN107476048A CN 107476048 A CN107476048 A CN 107476048A CN 201710591367 A CN201710591367 A CN 201710591367A CN 107476048 A CN107476048 A CN 107476048A
Authority
CN
China
Prior art keywords
cotton fiber
antibacterial
ribbon
original position
method based
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710591367.9A
Other languages
Chinese (zh)
Inventor
何平
李笑
陈小玲
黄科
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Gold Autumn Elastic Fabric Co Ltd
Original Assignee
Jiangsu Gold Autumn Elastic Fabric Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangsu Gold Autumn Elastic Fabric Co Ltd filed Critical Jiangsu Gold Autumn Elastic Fabric Co Ltd
Priority to CN201710591367.9A priority Critical patent/CN107476048A/en
Priority to PCT/CN2017/095526 priority patent/WO2019014968A1/en
Publication of CN107476048A publication Critical patent/CN107476048A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of antibacterial ribbon preparation method based on original position, including following content, cotton fiber is entered in sodium metaperiodate oxidized cotton fiber is prepared, polyethyleneimine is immersed again, and grafting polyethylene imine cotton fiber is prepared, enter back into and antibiotic cotton fiber is prepared in silver nitrate, then carrying out ribbon, normally intertexture forms antibacterial ribbon.The antibacterial shoulder belt that the inventive method is prepared, there is the antibiotic property of good resistance to degree of soaping and high-efficient and lasting, after 30 washings, sterilizing rate can still reach 95 100%, and the self structure of ribbon will not be destroyed, be widely used, and preparation technology is simple.

Description

A kind of antibacterial ribbon preparation method based on original position
Technical field
Patent of the present invention is related to a kind of ribbon, and in particular to a kind of antibacterial ribbon preparation method based on original position.
Background technology
Ribbon is that narrow web fabric or tubing is made as raw material using various yarns and elastic core wire, is widely used in clothes In each industrial field such as decorations, footwear material, case and bag, industry, agricultural, military supplies and communications and transportation, in garment industry, ribbon mainly as Bra shoulder harness or underpants elastic band use, and generally it is direct and skin contact, therefore requires the ribbon of garment industry to have Flexibility, the requirement of gas permeability, and the soft moisture pick-up properties of cotton fiber causes its most frequently used fiber as ribbon.
But cotton goods prepared by cotton fiber are although comfortable and easy to wear, but it has larger specific surface area and stronger moisture absorption Ability, cause cotton products easily attached microbial, and created conditions for its breeding and propagation, so as to cause the damage of fiber strength Wound, breed bacteria, or even transmission of disease is caused, influence the health of human body.
In recent years, nanometer technology fast development, some nano inorganic antimicrobial agents because possessing significant broad spectrum antibacterial performance and Textile garment field is applied to, the antibiotic finish of ribbon at present mainly uses finishing method, because technology is simple, easily implements, And be widely used, but finishing method usually occurs because the combination of Nano Silver is insecure, and make it that ribbon resists after arranging Bacterium effect is not lasting enough, and washability is poor.
The content of the invention
The purpose of invention：It is an object of the invention to provide a kind of antibacterial ribbon preparation method based on original position, using original Cotton fiber is first carried out antimicrobial treatment by liquid spin processes, forms antibiotic cotton fiber, is carrying out the weaving of ribbon, the ribbon antibacterial of formation Performance lasting good, repeatedly anti-microbial property is not from excessive influence after washing.
The technical solution adopted by the present invention：A kind of antibacterial ribbon preparation method based on original position, specifically comprises the following steps：
A, cotton fiber is placed in lucifuge oxidation reaction 30-300min in certain density sodium periodate solution, reaction temperature 30- 100 DEG C, bath raio 1:50, obtain oxidized cotton fiber；
B, oxidized cotton fiber is immersed in certain density poly- acetimide solution, 30-90 DEG C of reaction temperature, bath raio 1:50, Obtain poly- acetimide crafted cotton fibers；
C, by the poly- acetimide crafted cotton fibers obtained after step process with 1：It is 0.05-0.25 that 60 bath raio, which is immersed in concentration, In mol/L silver nitrate aqueous solution, at 25~35 DEG C, react 1~24 hour, forming Nano silver grain on cotton fiber surface bears Carry, washed 3 times with deionized water and absolute ethyl alcohol successively, at 40 DEG C, be dried in vacuo 6~10 hours, obtain antibiotic cotton fiber；
D, using warping machine, it is high-elastic that the 66 high-elastic nylon of ＇ 40D/12F*2, antibiotic cotton fiber, and twisting 40D/12F will be twisted respectively Nylon is whole on coiled hair；
E, open jacquard and carry out germ band intertexture, wherein twisting the high-elastic nylon of 66 ＇ 40D/12F*2 and cotton fiber blending as warp Line, for the twisting high-elastic nylon of 40D/12F as parallel, it is 700 ~ 800r/min to control jacquard speed；
F, the germ band to have interweaved is immersed in the dye liquor with environmental-friendly type emulsion shape modification acrylate auxiliary agent and carries out dyeing processing, Water temperature is to soak 5min at 30 DEG C, and 5min is washed at 80 DEG C, then washes 5min at 115 DEG C；
G, packaging arranges.
Preferably, in the step a, the concentration 0.1-10g/L of the sodium metaperiodate.
Preferably, in the step b, the concentration of the poly- acetimide solution is 1-10g/L.
Preferably, in the step e, the blending rate of the high-elastic nylon of 66 ＇ 40D/12F*2 of twisting and antibiotic cotton fiber For 1:2.
Beneficial effect：A kind of disclosed antibacterial ribbon preparation method based on original position, is first carried out cotton fiber Antimicrobial treatment, cotton fiber is after sodium periodate oxidation, and the oh group on its surface is oxidized to aldehyde radical even carboxyl, with poly- acetyl The amino on imines surface crosslinks reaction, generates poly- acetimide crafted cotton fibers, relative to traditional impregnation, poly- second Binding strength of the acid imide with cotton fiber between the two greatly improves, while poly- acetimide and Nano Silver can realize that collaboration is anti- Bacterium.
The antibacterial shoulder belt that the inventive method is prepared, there is the antibiotic property of good resistance to degree of soaping and high-efficient and lasting, warp After 30 washings, sterilizing rate can still reach 95-100%, and the self structure of ribbon will not be destroyed, be widely used, and prepare Technique is simple.
Embodiment
The specific embodiment of the invention is described in detail with reference to specific embodiment：
Embodiment 1
A kind of disclosed antibacterial ribbon preparation method based on original position, it comprises the following steps：
A, cotton fiber is placed in lucifuge oxidation reaction 200min in the sodium periodate solution that concentration is 0.1g/L, reaction temperature 80 DEG C, bath raio 1:50, obtain oxidized cotton fiber；
B, oxidized cotton fiber is immersed in the poly- acetimide solution that concentration is 6g/L, 60 DEG C of reaction temperature, bath raio 1:50, obtain To poly- acetimide crafted cotton fibers；
C, by the poly- acetimide crafted cotton fibers obtained after step process with 1：It is 0.15 mol/ that 60 bath raio, which is immersed in concentration, In L silver nitrate aqueous solution, at 35 DEG C, react 14 hours, Nano silver grain load is formed on cotton fiber surface, is used successively Deionized water and absolute ethyl alcohol wash 3 times, at 40 DEG C, are dried in vacuo 6 hours, obtain antibiotic cotton fiber；
D, using warping machine, it is high-elastic that the 66 high-elastic nylon of ＇ 40D/12F*2, antibiotic cotton fiber, and twisting 40D/12F will be twisted respectively Nylon is whole on coiled hair；
E, open jacquard and carry out germ band intertexture, wherein twisting the high-elastic nylon of 66 ＇ 40D/12F*2 and cotton fiber blending as warp Line, blending rate 1:2, for the twisting high-elastic nylon of 40D/12F as parallel, it is 700r/min to control jacquard speed；
F, the germ band to have interweaved is immersed in the dye liquor with environmental-friendly type emulsion shape modification acrylate auxiliary agent and carries out dyeing processing, Water temperature is to soak 5min at 30 DEG C, and 5min is washed at 80 DEG C, then washes 5min at 115 DEG C；
G, packaging arranges.
Embodiment 2
A kind of disclosed antibacterial ribbon preparation method based on original position, it comprises the following steps：
A, cotton fiber is placed in concentration as lucifuge oxidation reaction 300min in 8g/L sodium periodate solution, 100 DEG C of reaction temperature, Bath raio 1:50, obtain oxidized cotton fiber；
B, oxidized cotton fiber is immersed in the poly- acetimide solution that concentration is 2g/L, 90 DEG C of reaction temperature, bath raio 1:50, obtain To poly- acetimide crafted cotton fibers；
C, by the poly- acetimide crafted cotton fibers obtained after step process with 1：It is 0.05-0.25 that 60 bath raio, which is immersed in concentration, In mol/L silver nitrate aqueous solution, at 20 DEG C, react 20 hours, Nano silver grain load is formed on cotton fiber surface, according to It is secondary to be washed 3 times with deionized water and absolute ethyl alcohol, at 40 DEG C, it is dried in vacuo 9 hours, obtains antibiotic cotton fiber；
D, using warping machine, it is high-elastic that the 66 high-elastic nylon of ＇ 40D/12F*2, antibiotic cotton fiber, and twisting 40D/12F will be twisted respectively Nylon is whole on coiled hair；
E, open jacquard and carry out germ band intertexture, wherein twisting the high-elastic nylon of 66 ＇ 40D/12F*2 and cotton fiber blending as warp Line, blending rate 1:2, for the twisting high-elastic nylon of 40D/12F as parallel, it is 780r/min to control jacquard speed；
F, the germ band to have interweaved is immersed in the dye liquor with environmental-friendly type emulsion shape modification acrylate auxiliary agent and carries out dyeing processing, Water temperature is to soak 5min at 30 DEG C, and 5min is washed at 80 DEG C, then washes 5min at 115 DEG C；
G, packaging arranges.
Embodiment 3
A kind of disclosed antibacterial ribbon preparation method based on original position, it comprises the following steps：
A, cotton fiber is placed in concentration as lucifuge oxidation reaction 60min in 10g/L sodium periodate solution, 30 DEG C of reaction temperature, Bath raio 1:50, obtain oxidized cotton fiber；
B, oxidized cotton fiber is immersed in the poly- acetimide solution that concentration is 1g/L, 30 DEG C of reaction temperature, bath raio 1:50, obtain To poly- acetimide crafted cotton fibers；
C, by the poly- acetimide crafted cotton fibers obtained after step process with 1：It is 0.05 mol/ that 60 bath raio, which is immersed in concentration, In L silver nitrate aqueous solution, at 25 DEG C, react 3 hours, Nano silver grain load is formed on cotton fiber surface, is spent successively Ionized water and absolute ethyl alcohol wash 3 times, at 40 DEG C, are dried in vacuo 6 hours, obtain antibiotic cotton fiber；
D, using warping machine, it is high-elastic that the 66 high-elastic nylon of ＇ 40D/12F*2, antibiotic cotton fiber, and twisting 40D/12F will be twisted respectively Nylon is whole on coiled hair；
E, open jacquard and carry out germ band intertexture, wherein twisting the high-elastic nylon of 66 ＇ 40D/12F*2 and cotton fiber blending as warp Line, blending rate 1:2, for the twisting high-elastic nylon of 40D/12F as parallel, it is 700r/min to control jacquard speed；
F, the germ band to have interweaved is immersed in the dye liquor with environmental-friendly type emulsion shape modification acrylate auxiliary agent and carries out dyeing processing, Water temperature is to soak 5min at 30 DEG C, and 5min is washed at 80 DEG C, then washes 5min at 115 DEG C；
G, packaging arranges.
Described above is only the preferred embodiment of the present invention, it should be pointed out that：For the ordinary skill people of the art For member, under the premise without departing from the principles of the invention, some improvements and modifications can also be made, these improvements and modifications also should It is considered as protection scope of the present invention.

Claims (4)

  1. A kind of 1. antibacterial ribbon preparation method based on original position, it is characterised in that：Specifically comprise the following steps：
    A, cotton fiber is placed in lucifuge oxidation reaction 30-300min in certain density sodium periodate solution, reaction temperature 30- 100 DEG C, bath raio 1:50, obtain oxidized cotton fiber；
    B, oxidized cotton fiber is immersed in certain density poly- acetimide solution, 30-90 DEG C of reaction temperature, bath raio 1:50, Obtain poly- acetimide crafted cotton fibers；
    C, by the poly- acetimide crafted cotton fibers obtained after step process with 1：It is 0.05-0.25 that 60 bath raio, which is immersed in concentration, In mol/L silver nitrate aqueous solution, at 25~35 DEG C, react 1~24 hour, forming Nano silver grain on cotton fiber surface bears Carry, washed 3 times with deionized water and absolute ethyl alcohol successively, at 40 DEG C, be dried in vacuo 6~10 hours, obtain antibiotic cotton fiber；
    D, using warping machine, it is high-elastic that the 66 high-elastic nylon of ＇ 40D/12F*2, antibiotic cotton fiber, and twisting 40D/12F will be twisted respectively Nylon is whole on coiled hair；
    E, open jacquard and carry out germ band intertexture, wherein twisting the high-elastic nylon of 66 ＇ 40D/12F*2 and cotton fiber blending as warp Line, for the twisting high-elastic nylon of 40D/12F as parallel, it is 700 ~ 800r/min to control jacquard speed；
    F, the germ band to have interweaved is immersed in the dye liquor with environmental-friendly type emulsion shape modification acrylate auxiliary agent and carries out dyeing processing, Water temperature is to soak 5min at 30 DEG C, and 5min is washed at 80 DEG C, then washes 5min at 115 DEG C；
    G, packaging arranges.
  2. A kind of 2. antibacterial ribbon preparation method based on original position according to claim 1, it is characterised in that：In the step In a, the concentration 0.1-10g/L of the sodium metaperiodate.
  3. A kind of 3. antibacterial ribbon preparation method based on original position according to claim 1, it is characterised in that：In the step In b, the concentration of the poly- acetimide solution is 1-10g/L.
  4. A kind of 4. antibacterial ribbon preparation method based on original position according to claim 1, it is characterised in that：In the step In e, the blending rate of the high-elastic nylon of 66 ＇ 40D/12F*2 of twisting and antibiotic cotton fiber is 1:2.
CN201710591367.9A 2017-07-19 2017-07-19 A kind of antibacterial ribbon preparation method based on original position Pending CN107476048A (en)