CN107460787A - 不透明环保无纺壁纸 - Google Patents
不透明环保无纺壁纸 Download PDFInfo
- Publication number
- CN107460787A CN107460787A CN201710769193.0A CN201710769193A CN107460787A CN 107460787 A CN107460787 A CN 107460787A CN 201710769193 A CN201710769193 A CN 201710769193A CN 107460787 A CN107460787 A CN 107460787A
- Authority
- CN
- China
- Prior art keywords
- nonwoven wallpaper
- wallpaper
- grams
- opaque
- environmentally friendly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种不透明环保无纺壁纸,属于无纺壁纸技术领域。所述的不透明环保无纺壁纸,由以下重量份数的原料制成:漂白针叶浆35‑45份、漂白阔叶浆40‑50份、杨木化机浆10‑20份、钛白粉3‑9份。本发明的无纺壁纸因具有不透明度高的特性,不但解决了装修时的墙面透底现象,还帮助下游客户降低了生产成本,促进了壁纸在装饰行业中的应用,定量110克的本发明的无纺壁纸(无纺纸壁纸行业最低克重),不透明度为88‑90,跟130克无纺壁纸不透明度基本一样,而普通的110克无纺壁纸不透明度一般在80‑82之间,也就是说原本客户要用130克的无纺壁纸,现在可以使用110克的无纺壁纸,大大节省了下游客户的生产成本。
Description
技术领域
本发明涉及一种不透明环保无纺壁纸,属于无纺壁纸技术领域。
背景技术
无纺壁纸是当下最流行的新型绿色环保壁纸,其制备方法是以棉、麻、木浆等天然植物纤维和涤纶纤维为原料,经湿法成型而得到的一种壁纸,产品中不含任何聚氯乙烯、聚乙烯和氯元素,完全燃烧时只产生二氧化碳和水,视觉效果和手感柔和,透气性好,此类壁纸表底一体,无纸基,采用直接印花套色的先进工艺,比织物面壁纸图案更丰富,是高贵典雅的经典花纹与简约时尚的现代设计风格的完美结合。无纺壁纸因具备以上优质特性,近年来在国内得到了快速发展,但随着下游客户需求的不断变化和意见反馈,目前的无纺壁纸因不透明度低,施工后易造成墙面透底,影响美观,而要想避免这种现象的发生,则需要提高纸张的定量,但由此也会导致生产成本大幅提高,用户的购买价格也就居高不下,且需要装修的业主也要把墙面处理的相当平整,无深色杂物才可以,这会大大影响壁纸产品在装修行业中的应用。
发明内容
本发明的目的是提供一种不透明环保无纺壁纸,解决了传统无纺壁纸不透明度低、施工后墙面透底的问题,具有耐晒度高、生产成本低、不透明度高的特点。
本发明所述的不透明环保无纺壁纸,由以下重量份数的原料制成:
优选地,由以下重量份数的原料制成:
所述的不透明环保无纺壁纸的制备流程如下:
原料称量→碎浆→磨浆→配浆→纸机流送***输送→流浆箱→压榨部→前烘干部→施胶
→后烘干部→压光机→卷取部→分切复卷包装入库
具体包括以下步骤:
(1)破碎、磨浆、配浆:
将配比量的漂白针叶浆和漂白阔叶浆同时放入碎浆机内碎解,碎解完以后放入磨前池A;将配比量的杨木化机浆同样放入碎浆机内碎解,碎解完以后放入磨前池B;
碎解好的漂白针叶浆和漂白阔叶浆采用半游离状半粘状的磨浆方式磨好备用,碎解好的杨木化机浆采用轻度疏解的磨浆方式磨好备用,将上述两者按比例送入配浆池,然后加入钛白粉,添加白水稀释到要求的浓度备用;
(2)纸张抄造:
将步骤(1)的配浆池中配制好的浆料泵送至流浆箱,经脱水形成湿纸页,将网部形成的湿纸页引至压榨部强制脱水,然后引至烘干部干燥,被烘干的纸页送入施胶机进行施胶,施胶后继续干燥,经压光整饰后由卷取部收成纸卷,最后进行分切复卷,包装好入库。
根据库贝尔卡—门柯理论,增加光散射能力或光吸收能力都能提高纸张的不透明度,其中,光散射能力主要取决于纸页结构中未结合的自由表面积和纸内组分的折射系数,改变打浆、压榨、干燥条件等都能在一定程度上改变纸的光散射系数,如在同等条件下,当纸张的紧度很高时,光散射系数就很低;光的吸收系数是表示光能转变为其他能量的程度,其主要受纸张中的原料成分影响,例如木素含量、染料、颜料等,通常情况下,增加光散射能力,也将增加光吸收能力。
本发明根据以上理论,从以下两方面进行着手研究:
(1)木素含量高的化学机械浆具有较高的不透明度和松厚度,但是容易反黄,因此,采用耐黄变相对较好的杨木化机浆(APMP),通过实验得知,添加APMP后,纸张厚度能够增加10%左右,且APMP的价位比漂白木浆价位低,吨纸成本能够节约150-300元;
(2)因矿物填料比木浆料纤维有更强的光散射能力,可用在造纸中的矿物填料也非常多,如滑石粉、高岭土、轻(重)质碳酸钙、钛白粉等。通过实验,采用钛白粉作为本发明的原料,因为钛白粉在诸多填料中的折光系数是最大的,亮度也是最高的,同时钛白粉具有非常好的耐晒性,对于提高壁纸的耐晒度很有帮助,另外,钛白粉是一种环保材料,日常化妆品的生产就使用钛白粉作为原料,钛白粉还具有很强的吸附性,对室内异味的祛除很有帮助,选择钛白粉的缺点在于,其价位比较高,因此,根据不同客户的需求,添加量控制在5-10%,吨纸成本提高约200-400元。
本发明的有益效果如下:
(1)本发明的无纺壁纸因具有不透明度高的特性,不但解决了装修时的墙面透底现象,还帮助下游客户降低了生产成本,促进了壁纸在装饰行业中的应用;
(2)耐晒度高,非常适用于现在追求高采光度的家庭装修,在长时间的光照下,本发明的无纺壁纸不会因变色而影响美观;
(3)定量110克的本发明的无纺壁纸(无纺纸壁纸行业最低克重),不透明度为88-90,跟130克无纺壁纸不透明度基本一样,而普通的110克无纺壁纸不透明度一般在80-82之间,也就是说原本客户要用130克的无纺壁纸,现在可以使用110克的无纺壁纸,大大节省了下游客户的生产成本。
具体实施方式
以下结合实施例对本发明做进一步描述。
实施例1
所述的不透明环保无纺壁纸,由以下重量份数的原料制成:
制备方法包括以下步骤:
(1)破碎、磨浆、配浆:
将配比量的漂白针叶浆和漂白阔叶浆同时放入碎浆机内碎解,碎解完以后放入磨前池A;将配比量的杨木化机浆同样放入碎浆机内碎解,碎解完以后放入磨前池B;
碎解好的漂白针叶浆和漂白阔叶浆采用半游离状半粘状的磨浆方式磨好备用,碎解好的杨木化机浆采用轻度疏解的磨浆方式磨好备用,将上述两者按比例送入配浆池,然后加入钛白粉,添加白水稀释到要求的浓度备用;
(2)纸张抄造:
将配制好的浆料泵送至流浆箱,经脱水形成湿纸页,将网部形成的湿纸页引至压榨部强制脱水,然后引至烘干部干燥,被烘干的纸页送入施胶机进行施胶,施胶后继续干燥,经压光整饰后由卷取部收成纸卷,最后进行分切复卷,包装好入库。
经检测,定量110克的本实施例得到的无纺壁纸,不透明度为86-88。
实施例2
所述的不透明环保无纺壁纸,由以下重量份数的原料制成:
制备方法同实施例1。
经检测,定量110克的本实施例得到的无纺壁纸,不透明度为90-92。
实施例3
所述的不透明环保无纺壁纸,由以下重量份数的原料制成:
制备方法同实施例1。
经检测,定量110克的本实施例得到的无纺壁纸,不透明度为88-90。
Claims (3)
1.一种不透明环保无纺壁纸,其特征在于:由以下重量份数的原料制成:
2.根据权利要求1所述的不透明环保无纺壁纸,其特征在于:由以下重量份数的原料制成:
3.根据权利要求1所述的不透明环保无纺壁纸,其特征在于:制备方法包括以下步骤:
(1)破碎、磨浆、配浆:
将配比量的漂白针叶浆和漂白阔叶浆同时放入碎浆机内碎解,碎解完以后放入磨前池A;将配比量的杨木化机浆同样放入碎浆机内碎解,碎解完以后放入磨前池B;
碎解好的漂白针叶浆和漂白阔叶浆采用半游离状半粘状的磨浆方式磨好备用,碎解好的杨木化机浆采用轻度疏解的磨浆方式磨好备用,将上述两者按比例送入配浆池,然后加入钛白粉,添加白水稀释到要求的浓度备用;
(2)纸张抄造:
将步骤(1)的配浆池中配制好的浆料泵送至流浆箱,经脱水形成湿纸页,将网部形成的湿纸页引至压榨部强制脱水,然后引至烘干部干燥,被烘干的纸页送入施胶机进行施胶,施胶后继续干燥,经压光整饰后由卷取部收成纸卷,最后进行分切复卷,包装好入库。