CN107458057A - A kind of grease proofing PE preservative films - Google Patents
A kind of grease proofing PE preservative films Download PDFInfo
- Publication number
- CN107458057A CN107458057A CN201710630897.XA CN201710630897A CN107458057A CN 107458057 A CN107458057 A CN 107458057A CN 201710630897 A CN201710630897 A CN 201710630897A CN 107458057 A CN107458057 A CN 107458057A
- Authority
- CN
- China
- Prior art keywords
- density polyethylene
- low density
- ldpe
- internal layer
- middle level
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of grease proofing PE preservative films, including internal layer, middle level and the outer layer being cascading;The ratio between thickness of the internal layer, middle level and outer layer is followed successively by 1 ± 0.4:1±0.4:1±0.4:It is 5 ± 0.4 that the raw material of the internal layer, which includes weight ratio,:2±0.3:1±0.2:1±0.2:1 ± 0.2 low density polyethylene (LDPE), high density polyethylene (HDPE), LLDPE, polypropylene and metallocene linear-low density polyethylene;It is 10 ± 0.2 that the raw material in the middle level, which includes weight ratio,:10±0.2:10±0.2:2±0.1:2 ± 0.1 low density polyethylene (LDPE), medium density polyethylene, high density polyethylene (HDPE), polypropylene and metallocene linear-low density polyethylene;It is 5 ± 0.4 that the raw material of the outer layer, which includes weight ratio,:2±0.3:1 ± 0.2 low density polyethylene (LDPE), high density polyethylene (HDPE) and LLDPE;The weight ratio of low density polyethylene (LDPE) in the internal layer, middle level and outer layer is 2:1:2.Its grease proofing good penetrability, and there is aromatic odor.
Description
Technical field
The invention belongs to PE technical field of membrane, and in particular to a kind of grease proofing PE preservative films.
Background technology
PE, complete entitled Polyethylene, is the simplest macromolecular organic compound of structure, the world today is most widely used
General high polymer material.PE diaphragms are divided into high density using Special polyethylene plastic sheeting as base material, according to the difference of density and gathered
Ethene diaphragm, medium density polyethylene diaphragm and low density polyethylene (LDPE) diaphragm.PE diaphragm biggest advantages are to be protected
Product producing and processing, transport, not contaminated, burn into scratches during storage and use, and protection is original bright and clean glossy
Surface, so as to improve the quality of product and the market competitiveness.
But there is following defect in traditional PE diaphragms:
(1), grease proofing poor permeability, traditional PE diaphragms are due to the linear state of its strand, when it is as food fresh keeping
When protecting fatty foods, oil molecule is easily arrived to film outer surface by the internal layer of film, middle level and outer layer, makes food for film use
Thing mutually pollutes;
(2), protected when PE diaphragms do product packaging film in use, when being particularly the packaging of some plastic products in PE
After film is taken apart, it can emit bad smell, have a strong impact on Consumer's Experience.
The content of the invention
Based on this, in view of the above-mentioned problems, the present invention proposes a kind of grease proofing PE preservative films, its by polypropylene to membrane modifying,
And make film that there is more preferable heat sealability by metallocene linear-low density polyethylene, make modified PE membrane moleculars chain into
Space multistory configuration, increase molecular density, can not when avoiding as fresh-keeping use so as to have the function that to prevent oil molecule from permeating
The situation for effectively separating grease and then triggering food mutually to pollute;Meanwhile aromatic substance laurene is added, make film that there is aroma
Taste, and laurene can coordinate with low density polyethylene (LDPE), LLDPE, heat seal strength that will not be to PE films and fracture
Tensile strength impacts.
The technical scheme is that:A kind of grease proofing PE preservative films, including be cascading internal layer, middle level and outer
Layer;The ratio between thickness of the internal layer, middle level and outer layer is followed successively by 1 ± 0.4:1±0.4:1±0.4:
It is 5 ± 0.4 that the raw material of the internal layer, which includes weight ratio,:2±0.3:1±0.2:1±0.2:1 ± 0.2 low-density
Polyethylene, high density polyethylene (HDPE), LLDPE, polypropylene and metallocene linear-low density polyethylene;
It is 10 ± 0.2 that the raw material in the middle level, which includes weight ratio,:10±0.2:10±0.2:2±0.1:2 ± 0.1 it is low close
Spend polyethylene, medium density polyethylene, high density polyethylene (HDPE), polypropylene and metallocene linear-low density polyethylene;
It is 5 ± 0.4 that the raw material of the outer layer, which includes weight ratio,:2±0.3:1 ± 0.2 low density polyethylene (LDPE), high density are gathered
Ethene and LLDPE;
The weight ratio of low density polyethylene (LDPE) in the internal layer, middle level and outer layer is 2:1:2.
There are polypropylene and metallocene linear-low density polyethylene in the internal layer of film and middle level, by polypropylene in film
Layer and middle level are modified, and film is had more preferable heat sealability by metallocene linear-low density polyethylene, are made modified
PE membrane moleculars chain increases molecular density, so as to have the function that to prevent oil molecule from permeating, avoids conduct into space multistory configuration
The situation that grease can not effectively be separated during fresh-keeping use and then trigger food mutually to pollute.
As a further improvement on the present invention, the raw material of the internal layer also includes laurene, the laurene with internal layer
The mass percent of low density polyethylene (LDPE) is 2%-16%.
Aromatic substance laurene is added in internal layer, makes film that there is aromatic odor, and laurene can be with low density polyethylene
Alkene, LLDPE coordinate, and the heat seal strength and fracture tensile strength of PE films will not be impacted, i.e., not influenceed
Make film that there is aromatic odor in the case of film properties, when film packing plastics product, free from extraneous odour after opening, Consumer's Experience is good, more
It is competitive.
As a further improvement on the present invention, the raw material of the internal layer also includes Masterbatch, the Masterbatch with internal layer
The mass percent of low density polyethylene (LDPE) is 8%-12%.
Masterbatch is showed signs of anger as colouring agent for film inner layer, and Masterbatch and low density polyethylene (LDPE), high density polyethylene (HDPE) and line
Property low density polyethylene (LDPE) has good intermiscibility, does not interfere with the performances such as heat seal strength and the fracture tensile strength of film.
As a further improvement on the present invention, the raw material of the internal layer also includes slipping agent, the slipping agent with internal layer
The mass percent of low density polyethylene (LDPE) is 1.2%-1.8%.
As a further improvement on the present invention, the raw material of the internal layer also includes Water fixing agent, the Water fixing agent with internal layer
The mass percent of low density polyethylene (LDPE) is 5%-10%.
The main component of Water fixing agent in the present invention in internal layer is polyacrylamide, can quickly absorb water and slowly discharge, when
When film protects the water content such as veterinary antibiotics more food as preservative film, the steam of food release can be quickly absorbed, avoids film
Interior formation condensation, internal layer slowly discharge after absorbing steam, make to be in moist environment, the water that appropriate supplement loses in film all the time
Point, fresh-keeping effect is very good.
As a further improvement on the present invention, the raw material in the middle level also includes laurene, the laurene with middle level
The mass percent of low density polyethylene (LDPE) is 2%-16%.
Aromatic substance laurene is added in middle level, makes film that there is aromatic odor, and laurene can be with low density polyethylene
Alkene coordinates, and the heat seal strength and fracture tensile strength of PE films will not be impacted, i.e., made in the case where not influenceing film properties
Film has aromatic odor, and when film packing plastics product, free from extraneous odour after opening, Consumer's Experience is good, more competitive.
As a further improvement on the present invention, the raw material in the middle level also includes bloom Masterbatch, the bloom Masterbatch with
The mass percent of low density polyethylene (LDPE) in mesonexine is 30%-40%.
Masterbatch is that film middle level is showed signs of anger as colouring agent, and Masterbatch gathers with the low density polyethylene (LDPE) in middle level, Midst density
Ethene and high density polyethylene (HDPE) have good intermiscibility, do not interfere with the performances such as heat seal strength and the fracture tensile strength of film.
As a further improvement on the present invention, the raw material in the middle level also includes Water fixing agent, the Water fixing agent with middle level
The mass percent of low density polyethylene (LDPE) is 5%-10%.
The main component of Water fixing agent in the present invention in middle level is polyacrylamide, can quickly absorb water and slowly discharge, when
When film protects the water content such as veterinary antibiotics more food as preservative film, the steam of food release can be quickly absorbed, avoids film
Interior formation condensation, internal layer are further absorbed after absorbing steam by middle level, increase water absorption, and internal layer steam is first slowly released after water suction
Put, middle level steam slowly discharges again afterwards, makes to be in moist environment in film all the time, the moisture that appropriate supplement loses is fresh-keeping
Effect is very good.
As a further improvement on the present invention, the raw material of the outer layer also includes Masterbatch, the Masterbatch with outer layer
The mass percent of low density polyethylene (LDPE) is 8%-12%.
Masterbatch is that film outer layer is showed signs of anger as colouring agent, and Masterbatch gathers with the low density polyethylene (LDPE) in outer layer, high density
Ethene and LLDPE have good intermiscibility, do not interfere with the property such as heat seal strength and fracture tensile strength of film
Energy.
As a further improvement on the present invention, the raw material of the outer layer also includes slipping agent, the slipping agent with outer layer
The mass percent of low density polyethylene (LDPE) is 0.8%-1.6%.
The beneficial effects of the invention are as follows:
(1) there are polypropylene and metallocene linear-low density polyethylene in the internal layer of film and middle level, pass through polypropylene pair
Film inner layer and middle level are modified, and film is had more preferable heat sealability by metallocene linear-low density polyethylene, make modification
PE membrane moleculars chain afterwards increases molecular density, so as to have the function that to prevent oil molecule from permeating, avoided into space multistory configuration
The situation that grease can not effectively be separated during as fresh-keeping use and then trigger food mutually to pollute.
(2) aromatic substance laurene is added in internal layer and middle level, makes film that there is aromatic odor, and laurene can with it is low
Density polyethylene, LLDPE coordinate, and the heat seal strength and fracture tensile strength of PE films will not be impacted, i.e.,
Make film that there is aromatic odor in the case where not influenceing film properties, when film packing plastics product, free from extraneous odour after opening, user's body
Test, it is more competitive.
(3) composition of raw materials is rationally designed, the heat seal strength and fracture tensile strength for making film obtain larger lifting.
(4) Water fixing agent is added in internal layer and middle level, film is quickly absorbed water and slowly discharge, protected when as preservative film
During the more food of the water content such as veterinary antibiotics, the steam of food release can be quickly absorbed, avoids forming condensation, internal layer in film
Further absorbed after absorbing steam by middle level, increase water absorption, internal layer steam first slowly release after water suction, middle level steam is again afterwards
Slowly release, makes to be in moist environment in film all the time, the moisture that appropriate supplement loses, fresh-keeping effect is very good.
Brief description of the drawings
Fig. 1 is the structural representation of grease proofing PE preservative films described in embodiment;
Description of reference numerals:
10 internal layers, 20 middle levels, 30 outer layers.
Embodiment
Embodiments of the invention are described in detail below in conjunction with the accompanying drawings.
Embodiment:
As shown in figure 1, a kind of grease proofing PE preservative films, including internal layer 10, middle level 20 and the outer layer 30 being cascading;Institute
State the ratio between thickness of internal layer 10, middle level 20 and outer layer 30 and be followed successively by 1:1:1, or 0.6:1.4:0.6 or 1.4:0.6:
1.4。
It is 5 that the raw material of the internal layer 10, which includes weight ratio,:2:1:1:It is 1 low density polyethylene (LDPE), high density polyethylene (HDPE), linear
Low density polyethylene (LDPE), high density in low density polyethylene (LDPE), polypropylene and metallocene linear-low density polyethylene, wherein internal layer 10
Polyethylene, LLDPE, the weight ratio of polypropylene and metallocene linear-low density polyethylene are alternatively 4.6:1.7:
0.8:0.8:0.8 or 5.4:2.3:1.2:1.2:1.2.
It is 10 that the raw material in the middle level 20, which includes weight ratio,:10:10:2:2 low density polyethylene (LDPE), medium density polyethylene,
High density polyethylene (HDPE), polypropylene and metallocene linear-low density polyethylene, wherein, low density polyethylene (LDPE) in middle level 20, in it is close
The weight ratio for spending polyethylene, high density polyethylene (HDPE), polypropylene and metallocene linear-low density polyethylene is alternatively 10.2:10.2:
10.2:2.1:2.1 or 0.8:0.8:0.8:1.9:1.9.
It is 5 that the raw material of the outer layer 30, which includes weight ratio,:2:1 low density polyethylene (LDPE), high density polyethylene (HDPE) and linear low
Density polyethylene, wherein, the weight ratio of low density polyethylene (LDPE), high density polyethylene (HDPE) and LLDPE in outer layer 30
Or 5.4:2.3:1.2 or 4.6:1.7:0.8.
The weight ratio of the internal layer 10, middle level 20 and the low density polyethylene (LDPE) in outer layer 30 is 2:1:2.
There are polypropylene and metallocene linear-low density polyethylene in the internal layer 10 of film and middle level 20, pass through polypropylene pair
Film inner layer 10 and middle level 20 are modified, and film is had more preferable heat sealability by metallocene linear-low density polyethylene, are made
Modified PE membrane moleculars chain increases molecular density into space multistory configuration, so as to have the function that to prevent oil molecule from permeating,
Avoid the situation that can not effectively separate grease during as fresh-keeping use and then trigger food mutually to pollute.
In another embodiment, the raw material of the internal layer 10 also includes laurene, and the laurene is low with internal layer 10
The mass percent of density polyethylene is 2%, or 9% or 16%.
Aromatic substance laurene is added in internal layer 10, makes film that there is aromatic odor, and laurene can gather with low-density
Ethene, LLDPE coordinate, and the heat seal strength and fracture tensile strength of PE films will not be impacted, i.e., in not shadow
Make film that there is aromatic odor in the case of ringing film properties, when film packing plastics product, free from extraneous odour after opening, Consumer's Experience is good,
It is more competitive.
In another embodiment, the raw material of the internal layer 10 also includes Masterbatch, and the Masterbatch is low with internal layer 10
The mass percent of density polyethylene is 8%, or 10% or 12%.
Masterbatch is that film inner layer 10 is showed signs of anger as colouring agent, and Masterbatch and low density polyethylene (LDPE), high density polyethylene (HDPE) and
LLDPE has good intermiscibility, does not interfere with the performances such as heat seal strength and the fracture tensile strength of film.
In another embodiment, the raw material of the internal layer 10 also includes slipping agent, and the slipping agent is low with internal layer 10
The mass percent of density polyethylene is 1.2%, or 1.5% or 1.8%.
In another embodiment, the raw material of the internal layer 10 also includes Water fixing agent, and the Water fixing agent is low with internal layer 10
The mass percent of density polyethylene is 5%, or 7.5% or 10%.
The main component of Water fixing agent in the present invention in internal layer 10 is polyacrylamide, can quickly absorb water and slowly discharge,
When the film food more as water content such as preservative film protection veterinary antibiotics, the steam of food release can be quickly absorbed, is avoided
Condensation is formed in film, internal layer 10 slowly discharges after absorbing steam, makes to be in moist environment in film all the time, appropriate supplement loses
Moisture, fresh-keeping effect is very good.
In another embodiment, the raw material in the middle level 20 also includes laurene, and the laurene is low with middle level 20
The mass percent of density polyethylene is 2%, or 9% or 16%.
Aromatic substance laurene is added in middle level 20, makes film that there is aromatic odor, and laurene can gather with low-density
Ethene coordinates, and the heat seal strength and fracture tensile strength of PE films will not be impacted, i.e., in the case where not influenceing film properties
Make film that there is aromatic odor, when film packing plastics product, free from extraneous odour after opening, Consumer's Experience is good, more competitive.
In another embodiment, the raw material in the middle level 20 also includes bloom Masterbatch, the bloom Masterbatch with it is interior in
The mass percent of low density polyethylene (LDPE) in layer 20 is 30%, or 35% or 40%.
Masterbatch is that film middle level 20 is showed signs of anger as colouring agent, and Masterbatch and the low density polyethylene (LDPE) in middle level 20, in it is close
Degree polyethylene and high density polyethylene (HDPE) have good intermiscibility, do not interfere with the property such as heat seal strength and fracture tensile strength of film
Energy.
In another embodiment, the raw material in the middle level 20 also includes Water fixing agent, and the Water fixing agent is low with middle level 20
The mass percent of density polyethylene is 5%, or 7.5% or 10%.
The main component of Water fixing agent in the present invention in middle level 20 is polyacrylamide, can quickly absorb water and slowly discharge,
When the film food more as water content such as preservative film protection veterinary antibiotics, the steam of food release can be quickly absorbed, is avoided
Condensation is formed in film, internal layer 10 is further absorbed after absorbing steam by middle level 20, increases water absorption, and the steam of internal layer 10 is first after water suction
Slowly release, the steam of middle level 20 slowly discharges again afterwards, makes to be in moist environment, the water that appropriate supplement loses in film all the time
Point, fresh-keeping effect is very good.
In another embodiment, the raw material of the outer layer 30 also includes Masterbatch, and the Masterbatch is low with outer layer 30
The mass percent of density polyethylene is 8%, or 10% or 12%.
Masterbatch is that film outer layer 30 is showed signs of anger as colouring agent, and Masterbatch and the low density polyethylene (LDPE) in outer layer 30, highly dense
Degree polyethylene and LLDPE have good intermiscibility, do not interfere with the heat seal strength and fracture tensile strength of film
Etc. performance.
In another embodiment, the raw material of the outer layer 30 also includes slipping agent, and the slipping agent is low with outer layer 30
The mass percent of density polyethylene is 0.8%, or 1.2% or 1.6%.
Embodiment described above only expresses the embodiment of the present invention, and its description is more specific and detailed, but simultaneously
Therefore the limitation to the scope of the claims of the present invention can not be interpreted as.It should be pointed out that for one of ordinary skill in the art
For, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to the guarantor of the present invention
Protect scope.
Claims (10)
- A kind of 1. grease proofing PE preservative films, it is characterised in that:Including internal layer, middle level and the outer layer being cascading;The internal layer, The ratio between thickness of middle level and outer layer is followed successively by 1 ± 0.4:1±0.4:1±0.4:It is 5 ± 0.4 that the raw material of the internal layer, which includes weight ratio,:2±0.3:1±0.2:1±0.2:1 ± 0.2 low density polyethylene Alkene, high density polyethylene (HDPE), LLDPE, polypropylene and metallocene linear-low density polyethylene;It is 10 ± 0.2 that the raw material in the middle level, which includes weight ratio,:10±0.2:10±0.2:2±0.1:2 ± 0.1 low-density is gathered Ethene, medium density polyethylene, high density polyethylene (HDPE), polypropylene and metallocene linear-low density polyethylene;It is 5 ± 0.4 that the raw material of the outer layer, which includes weight ratio,:2±0.3:1 ± 0.2 low density polyethylene (LDPE), high density polyethylene (HDPE) And LLDPE;The weight ratio of low density polyethylene (LDPE) in the internal layer, middle level and outer layer is 2:1:2.
- 2. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the internal layer also includes laurene, The mass percent of the laurene and the low density polyethylene (LDPE) in internal layer is 2%-16%.
- 3. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the internal layer also includes Masterbatch, The mass percent of the Masterbatch and the low density polyethylene (LDPE) in internal layer is 8%-12%.
- 4. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the internal layer also includes slipping agent, The mass percent of the slipping agent and the low density polyethylene (LDPE) in internal layer is 1.2%-1.8%.
- 5. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the internal layer also includes Water fixing agent, The mass percent of the Water fixing agent and the low density polyethylene (LDPE) in internal layer is 5%-10%.
- 6. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material in the middle level also includes laurene, The mass percent of the laurene and the low density polyethylene (LDPE) in middle level is 2%-16%.
- 7. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material in the middle level also includes bloom color masterbatch Grain, the mass percent of the bloom Masterbatch and the low density polyethylene (LDPE) in mesonexine is 30%-40%.
- 8. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material in the middle level also includes Water fixing agent, The mass percent of the Water fixing agent and the low density polyethylene (LDPE) in middle level is 5%-10%.
- 9. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the outer layer also includes Masterbatch, The mass percent of the Masterbatch and the low density polyethylene (LDPE) in outer layer is 8%-12%.
- 10. grease proofing PE preservative films according to claim 1, it is characterised in that:The raw material of the outer layer also includes slipping agent, The mass percent of the slipping agent and the low density polyethylene (LDPE) in outer layer is 0.8%-1.6%.