CN107447594A - A kind of 3D wallpapers and its manufacture method - Google Patents
A kind of 3D wallpapers and its manufacture method Download PDFInfo
- Publication number
- CN107447594A CN107447594A CN201710700812.0A CN201710700812A CN107447594A CN 107447594 A CN107447594 A CN 107447594A CN 201710700812 A CN201710700812 A CN 201710700812A CN 107447594 A CN107447594 A CN 107447594A
- Authority
- CN
- China
- Prior art keywords
- layer
- dimensional pattern
- wallpapers
- pattern layer
- patterned
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
3D wallpapers disclosed by the invention include substrate layer, patterned layer and three-dimensional pattern layer, the patterned layer is covered in the upper surface of the substrate layer, the formation solid pattern layer of the surface selectivity of the patterned layer, the three-dimensional pattern layer through-thickness is in height fluctuations.Pattern form uncovered in the shape and patterned layer of three-dimensional pattern layer is formed into an entirety, highlights the 3D effect of three-dimensional pattern layer, is in again height fluctuations using three-dimensional pattern layer through-thickness so that the three-dimensional pattern layer can have any shape.Present invention also offers a kind of manufacture method of 3D wallpapers, manufactured using 3D printing technique, print one-shot forming stereochemical structure, process is simple, can make the effect better than relief grain, reduces the technological process of production, improves production efficiency, saves production cost.
Description
Technical field
The present invention relates to house decorative material technical field, relates more specifically to a kind of 3D wallpapers and its manufacture method.
Background technology
Wallpaper is a kind of ornament materials of paper on metope.It has rich in color, exquisite in texture, pattern magnificent, green
The characteristics such as colour circle guarantor, easy for construction, affordable, and the features such as decorative effect meets rich and varied, different demands, therefore,
Increasingly favored by people, be widely used in the interior decoration of the buildings such as house, office and hotel.
With the improvement of living standards, requirement more and more higher of the people to the visual effect of wallpaper, although common wallpaper
Pattern is rich and varied, luxurious style, but draw or the pattern that is printed in base fabric it is single, it is static, lack third dimension, Hen Duoshi
Time can not give a kind of visual impact of people.At present, also there are some to use and coating is integrally coated in base fabric, then rolled
Flower-shape into embossing pattern wallpaper, although the wallpaper have third dimension it is strong, save dosage the features such as, foaming due to
The defects of with loose structure, cause degree of adhesion between embossing pattern and wallpaper relatively low, when people encounter wallpaper or enter to wallpaper
When row is cleaned, these patterns will drop breakage, influence flower pattern effect.In addition, most PVC wallpapers on the market are all logical
To cross embossing roll-in line (also referred to as embossment) and just have the grain effect of different levels, embossment makes product have modelling effect, its
Technological process is substantially：Coating, printing, embossing, this technique process is cumbersome, is unfavorable for improving operating efficiency, and cost is higher.
And use conventional cylinder to print, whether PVC slurries or aqueous medium, its printing effect are all more smooth or only had
The effect of one level, multiple nets are needed to carry out double exposure if needing many levels, and because slurry thixotropic index is relatively low, it is static
Under state, mobility is still relatively strong, and pattern edge when cylinder prints can become rounder and more smooth because of the mobility of slurry.In order to
Anaglyptic wallpaper is obtained, method main at present is that relief shape is carried out after full width coating, and this manufacture method can be produced
Texture is fine and smooth, clear, and level enriches, the stronger anaglyptic wallpaper of texture；But full width coating sizing-agent can not be brought more to embossment
Add prominent stereoeffect, cause the waste of raw material resources on the contrary, be unfavorable for environmental protection, and due to by printing equipment or
The thickness of the limitation of person's foaming machine, 3D layers or embossed layer causes third dimension not strong no more than 3 mm.
Therefore, it is badly in need of providing a kind of new 3D wallpapers and its manufacture method, to solve the above problems.
The content of the invention
It is an object of the invention to provide a kind of 3D wallpapers, and the 3D wallpaper third dimensions are strong, and plane pattern is mutually tied with three-dimensional pattern
Close, space pattern level highlights, life-like, great visual effect and aesthetic property, has stronger practicality.
To achieve the above object, the invention provides a kind of 3D wallpapers, including substrate layer, the surface of the substrate layer to form
Patterned layer, the formation solid pattern layer of the surface selectivity of the patterned layer, the three-dimensional pattern layer through-thickness is in height
Fluctuations.
Compared with prior art, 3D wallpapers of the invention, it sets gradually patterned layer and stereogram on the surface of substrate layer
Type layer, and the three-dimensional pattern layer of one layer of covering of the upper surface selectivity of patterned layer, utilize the patterning in patterned layer, selectivity
Needs patterned surfaces cover one layer of three-dimensional pattern layer so that the remaining pattern of patterned layer with formation three-dimensional pattern layer enter
Row is organically combined so that plane pattern is combined with three-dimensional pattern, life-like, can highlight 3D stereoeffects, third dimension
By force, pattern form uncovered in the shape and patterned layer of three-dimensional pattern layer is formed into an entirety, highlights three-dimensional pattern
The 3D effect of layer, it is in again height fluctuations using three-dimensional pattern layer through-thickness so that the three-dimensional pattern layer can be to appoint
Meaning shape, can cover the pattern of arbitrary shape, and use range is wide, and its stereoeffect is strengthened, and realize the 3D of the present invention
Wallpaper has real 3D structures, and its 3D stereoeffect is that conventional wall paper matrix intends the incomparable of 3D effect, therefore, this Shen
Its 3D stereoeffect of 3D wallpapers please is more notable and prominent, great visual effect and aesthetic property, has stronger practicality.
It is preferred that the 3D wallpapers also include interspersing layer, the layer of interspersing is covered on the surface of the three-dimensional pattern layer,
The shape of three-dimensional pattern layer is further interspersed by interspersing layer, the pattern form of acquisition is vivider, further increases 3D wallpapers
Third dimension and the sense of reality.
It is preferred that the interlayer of interspersing breaks or/and is continuously covered on the surface of the three-dimensional pattern layer.
It is preferred that the thickness range of the three-dimensional pattern layer is between 0.01~200mm.
It is preferred that the thickness range of the three-dimensional pattern layer is between 3~200mm, three-dimensional pattern layer of the invention
Thickness can be more than 3mm, increase third dimension, breach 3D layers in the prior art or the thickness of embossed layer lacks no more than 3mm
Fall into, such as, the thickness of three-dimensional pattern layer is between 0.01mm-1mm, 0.1 mm-50mm, 1mm-30mm, 3mm-20mm, 3mm-
60mm, between 3mm-100mm, 5-40 mm, 5-100mm or 10-200mm.
It is preferred that the 3D wallpapers also include priming coat, the priming coat be located at the substrate layer and the patterned layer it
Between, priming coat is advantageous to improve substrate layer and patterned layer or the adhesion of three-dimensional pattern layer, improves its adhesive force.
Present invention also offers a kind of method for manufacturing above-mentioned 3D wallpapers, the manufacture method comprises the following steps：
1) substrate layer is provided, patterned layer is formed in the surface of the substrate layer；
2) in the formation solid pattern layer of the surface of patterned layer selectivity, three-dimensional pattern layer through-thickness is in height
Fluctuations.
It is preferred that in the step 2), by described in formation of the 3D printer in the surface of patterned layer selectivity
Three-dimensional pattern layer, one-shot forming stereochemical structure is printed, process is simple, and the multiple processes of traditional needs are superimposed to be formed.
It is preferred that the manufacture method also includes step 3), there is provided layer is interspersed, on the basis of step 2), using described
Intersperse layer to reprocess the shape of the three-dimensional pattern layer, the surface interspersed layer and be covered in the three-dimensional pattern layer
On.Wherein, intersperse layer and can be interrupted and be covered on the surface of three-dimensional pattern layer, can also continuously be covered in the table of three-dimensional pattern layer
On face, the part-structure interruption that can also intersperse layer is covered on the surface of three-dimensional pattern layer, and remaining part-structure continuously covers
It is placed on the surface of three-dimensional pattern layer.
It is preferred that by 3D printer in the surface of the three-dimensional pattern layer produce it is described intersperse layer, using the point
Sew layer to reprocess the pattern form of the three-dimensional pattern layer.
It is preferred that in step 1), priming coat is also provided, the priming coat is formed in the base material layer surface, in described
The surface of priming coat forms the patterned layer.
It is preferred that the substrate layer is answered selected from wood pulp paper, pure paper, non-woven paper, non-woven fabrics, flat fabric, coated paper, paper and cloth
Close any one in the Compound Fabric formed.
It is preferred that the three-dimensional pattern layer choosing is from any one in thermoplastic resin, light-cured resin, diatom ooze or extremely
Few two kinds mixture.
It is preferred that the mixture of any one or two kind of the priming coat in thermoplastic resin, diatom ooze.
It is preferred that the thermoplastic resin is selected from polyethylene, polyvinyl chloride, polystyrene, polyamide, polyformaldehyde, poly- carbon
It is acid esters, polyphenylene oxide, polysulfones, polyvinyl acetate, polyamide, polymethyl methacrylate, polyester, vinyl acetate resin, poly-
Any one in vinyl alcohol, polyvinyl acetal, ABS resin, PLA.
It is preferred that the light-cured resin is selected from acrylate, carbamate types acrylate, the acryloyl of polyalcohol
Amine, epoxy acrylate, polyester acrylate, the unsaturated polyester (UP) of polybasic carboxylic acid, monomer, double fat with acetylenic unsaturated group
Any one in ring epoxide, vinyl ethers, the organic silicon acrylic ester oligomer containing acryloxy.
3D wallpapers provided by the invention have the advantages that：
1) the uncovered structure of patterned layer is organically combined with the structure of three-dimensional pattern layer, increases third dimension, touches sense
Enhancing.
2) structure of three-dimensional pattern layer is arbitrary shape, such as plane, three-dimensional, solid, hollow, hollow out
, rectangular cross-section, section be del etc..
3) utilization intersperses layer and the second patterning of three-dimensional pattern layer is processed further, the pattern form more shape of acquisition
As the further third dimension and the sense of reality for increasing 3D wallpapers.
4) priming coat is added so that the firmness between substrate layer and patterned layer improves, while improves whole 3D walls
Paper cube sense.
5) three-dimensional pattern layer is manufactured by 3D printing technique, prints one-shot forming stereochemical structure, process is simple, and traditional need
Want multiple processes to be superimposed to be formed, the effect better than relief grain can be made, there is superpower third dimension, simplify technique, it is existing
The coating of technology, printing, three step production technologies of embossing are simplified to step completion, reduce the technological process of production, improve production effect
Rate, save production cost.
6) there can be higher jail by the three-dimensional pattern layer and substrate layer and patterned layer that are manufactured into by 3D printing technique
Soundness, conventional collision friction will not cause coming off for sizing material, and flower pattern effect is lasting, and it is high to clean fastness.
It will be become more fully apparent by following description and with reference to accompanying drawing, the present invention, these accompanying drawings are used to explain the present invention
Embodiment.
Brief description of the drawings
Fig. 1 is the structural representation of the first embodiment of the 3D wallpapers of the present invention.
Fig. 2 is the structural representation of the second embodiment of the 3D wallpapers of the present invention.
Fig. 3 is the structural representation of the 3rd embodiment of the 3D wallpapers of the present invention.
Embodiment
Embodiments of the invention are described with reference now to accompanying drawing, similar element numbers represent similar element in accompanying drawing.
Embodiment 1
Fig. 1 is refer to, a kind of 3D wallpapers 100 provided by the invention include substrate layer 10, patterned layer 30 and three-dimensional pattern layer
40, patterned layer 30 is covered in the upper surface of substrate layer 10, the three-dimensional pattern layer of one layer of covering of the upper surface selectivity of patterned layer 30
40, the three-dimensional through-thickness of pattern layer 40 is in height fluctuations.
Substrate layer 10 is the matrix of 3D wallpapers, and it is the conventional wallpaper base material in this area, in the present embodiment, base
Material layer 10 is wood pulp paper, and substrate layer 10 can be selected from pure paper, non-woven paper, non-woven fabrics, plain weave in other embodiments of the invention
Any one in the Compound Fabric that cloth, coated paper or paper and cloth are combined.
The surface of substrate layer 10 is completely covered in patterned layer 30, and patterned layer 30 is the pattern form formed in substrate layer 10, its
In, the formation for patterned layer 30 is not particularly limited, for example according to method well-known in the art, is led on stationery base material
Cross the modes such as wire mark, convex print, gravure, digital printing, Freehandhand-drawing, scribble and produce pattern, also for example pass through net on dry goods base material
Print, convex print, gravure, dye cloth, digital printing, air brushing, embroidery, the mode such as jacquard weave produce pattern, but not limited to this.More specifically
Ground, such as, in this embodiment, go out one with leafed flower motif structure by digital printing on the surface of wood pulp paper,
This is patterned layer 30 with leafed flower motif structure.
The position of three-dimensional pattern layer 40, according to being actually needed, in the formation solid pattern of the surface of patterned layer 30 selectivity
Layer 40, in the methods of the invention, the method for forming three-dimensional pattern layer 40 is not particularly limited, for example, method known to using carries
For substrate layer, while it is incorporated in a manner of spraying in above-mentioned substrate sheets, and solid is formed by dry, aging or curing process
Pattern layer 40, or 3D printing equipment is connected by resin-bonded in above-mentioned substrate sheets, and by dry, aging or curing process
Form three-dimensional pattern layer 40, in the present invention, after above-mentioned operation is carried out, be dried, the condition of aging or curing process not
It is particularly limited, it can be considered that the composition of used material is suitably selected.The present embodiment is by 3D printer by resin
Stereochemical structure is printed as, the stereochemical structure is three-dimensional pattern layer 40, and the stereochemical structure for three-dimensional pattern layer 40 can be to appoint
Anticipate shape, for example three-dimensional, solid, hollow, hollow out, rectangular cross-section, section is del etc., can be adopted
Such as square, cuboid and cylinder etc., can be not the characteristics of in order to protrude Visual Aesthetics with the stereochemical structure of rule
The stereochemical structure of rule, for example, containing convex-concave structure, containing wave structure etc., more specifically, for example, in the present embodiment, choosing
The flower that solid is formed by 3D printer on the surface of flower in patterned layer 30 of selecting property, the three-dimensional flower is solid
Pattern layer 40, the three-dimensional pattern layer 40 are organically combined with the leaf in patterned layer 30, are formed and are carried leaf with stereoeffect
The 3D wallpapers of the flower of son.Wherein, the thickness change of three-dimensional pattern layer 40 differs, height rises and falls so that level protrudes, solid effect
Fruit is obvious, suitable for arbitrary shape, has a wide range of application, specifically, the thickness range of three-dimensional pattern layer 40 can between 0.01mm~
200mm, better way be between 3mm~200mm, such as, the thickness of three-dimensional pattern layer 40 between 0.01mm-1mm,
0.1mm-50mm, 1mm -30mm, 3mm-20mm, 3mm-60mm, 3mm-100mm, 5-40mm, 5-100mm or 10-200mm it
Between, in this embodiment, between 3mm-50mm, space pattern level highlights the thickness of three-dimensional pattern layer 40, touches sense and increases
By force, 3D layers in the prior art or the thickness of embossed layer are breached no more than 3mm defects, effectively increases third dimension.Wherein,
Three-dimensional pattern layer 40 is formed from thermoplastic resin material, and in some embodiments, three-dimensional pattern layer 40 is also selected from thermoplastic
In property resin, light-cured resin, diatom ooze any one or at least two mixture.Specifically, thermoplastic resin is selected from
Polyethylene, polyvinyl chloride, polystyrene, polyamide, polyformaldehyde, makrolon, polyphenylene oxide, polysulfones, polyvinyl acetate, polyamides
Amine, polymethyl methacrylate, polyester, vinyl acetate resin, polyvinyl alcohol, polyvinyl acetal, ABS resin, poly- breast
Any one in acid；The light-cured resin is selected from acrylate, carbamate types acrylate, the epoxy third of polyalcohol
Olefin(e) acid ester, polyester acrylate, acrylamide, the unsaturated polyester (UP) of polybasic carboxylic acid, monomer, double fat with acetylenic unsaturated group
Any one in ring epoxide, vinyl ethers, the organic silicon acrylic ester oligomer containing acryloxy.
Embodiment 2
The 3D wallpapers 100a and the structure of embodiment 1 of the embodiment are essentially identical, and distinctive points are as follows：
Fig. 2 is refer to, in the present embodiment, 3D wallpapers 100a also includes interspersing layer 50, intersperses layer 50 and is covered in stereogram
On the surface of type layer 40, further interspersed by the pattern shape for interspersing the three-dimensional pattern layer 40 of 50 pairs of layer, the pattern more shape of acquisition
As the further third dimension and the sense of reality for increasing 3D wallpapers.Wherein, intersperse layer 50 and can be interrupted and be covered in three-dimensional pattern layer 40
It on surface, can also continuously be covered on the surface of three-dimensional pattern layer 40, can also be that the part-structure interruption for interspersing layer 50 is covered
It is placed on the surface of three-dimensional pattern layer 40, remaining part-structure is continuously covered on the surface of three-dimensional pattern layer 40, this implementation
It is covered in example using interruption on the surface of three-dimensional pattern layer 40.Furthermore by 3D printer in three-dimensional pattern layer 40
Surface, which produces, intersperses layer 50, and the shape for interspersing layer 50 does not limit, and can have any shape, using interspersing 50 pairs of stereogram of layer
The pattern shape of type layer 40 is reprocessed, and makes stereoeffect stronger, intersperses pattern form of the layer 50 in three-dimensional pattern layer 40
Anywhere it is processed, specific Working position is not limited, such as, in the present embodiment, by 3D printer in stereogram
The surface of type layer 40 produces the shape of droplet, and the droplet is to intersperse layer 50, this intersperse interlayer it is disconnected be covered in implementation
On flower (i.e. three-dimensional pattern layer 40) in example 1, the flower with droplet is formed, with more third dimension and the sense of reality.
It is other identical with embodiment 1 in addition to above-mentioned difference, therefore will not be repeated here.
Embodiment 3
The 3D wallpapers 100b and the structure of embodiment 2 of the embodiment are essentially identical, and distinctive points are as follows：
Fig. 3 is refer to, the 3D wallpapers 100b of the present embodiment also includes priming coat 20, and priming coat 20 is located at substrate layer 10 and figure
Between pattern layer 30, priming coat 20 is advantageous to improve the adhesion between substrate layer 10 and patterned layer 30, improves its adhesive force, moreover it is possible to
To the third dimension for improving whole 3D wallpapers, in this embodiment, priming coat 20 selects diatom ooze, can be with certain other embodiment
From any one in thermoplastic resin, diatom ooze or two kinds of mixture.
It is other identical with embodiment 2 in addition to above-mentioned difference, therefore will not be repeated here.
Embodiment 4
The embodiment further illustrates specific manufacture method to manufacture the 3D wallpapers of embodiment 1, but is not limited to embodiment
1, the manufacture method of other embodiments can also use the manufacture method of the embodiment to obtain, and manufacture method includes step：
1) substrate layer 10 is provided, patterned layer 30 is formed in the surface of substrate layer 10；
2) in the formation solid pattern layer 40 of the surface of patterned layer 30 selectivity, the three-dimensional pattern layer 40 of formation is along thickness
Direction is in height fluctuations.
Specifically, such as, there is provided wood pulp paper is substrate layer 10, and going out one by digital printing on the surface of wood pulp paper carries
The flower motif structure of leaf, this is patterned layer 30 with leafed flower motif structure, then selective in patterned layer 30
The flower that solid is formed by 3D printer on the surface of middle flower, the three-dimensional flower is three-dimensional pattern layer 40, the solid
Pattern layer 40 is organically combined with the leaf in patterned layer, forms the 3D wallpapers of the leafed flower of band with stereoeffect,
High infraversion malposition, third dimension are strengthened.
Embodiment 5
The method of the manufacture method and embodiment 4 of the 3D wallpapers of the embodiment is essentially identical, and distinctive points are as follows：
In the present embodiment, manufacture method also includes step 3), there is provided intersperses layer 50, on the basis of step 3), adopts
Reprocessed with the shape for interspersing the three-dimensional pattern layer 40 of 50 pairs of layer, intersperse layer 50 and cover on the surface of three-dimensional pattern layer 40, obtain
The 3D wallpapers that must be processed further, actually intersperse layer 50 and can be interrupted and be covered on the surface of three-dimensional pattern layer 40, can also
Continuously it is covered on the surface of three-dimensional pattern layer 40, can also be that the part-structure interruption for interspersing layer 50 is covered in three-dimensional pattern layer
On 40 surface, remaining part-structure is continuously covered on the surface of three-dimensional pattern layer 40, in the present embodiment, is beaten by 3D
Print machine produces droplet in the surface of three-dimensional pattern layer 40, and the shape of droplet is to intersperse layer 50, intersperses the interruption of layer 50
It is covered on the petal of flower, forms the flower with droplet.
It is other identical with embodiment 4 in addition to above-mentioned difference, therefore will not be repeated here.
Embodiment 6
The method of the manufacture method and embodiment 4 of the 3D wallpapers of the embodiment is essentially identical, and distinctive points are as follows：
In the present embodiment, manufacture method also includes providing priming coat 20, and priming coat 20 selects diatom ooze, by priming coat 20
Coated in the surface of substrate layer 10, priming coat 20 is advantageous to the adhesion of substrate layer 10 and patterned layer 30, improves its adhesive force, and can
To cause the stereoscopic level of 3D wallpapers to highlight, sense enhancing is touched.
It is other identical with embodiment 4 in addition to above-mentioned difference, therefore will not be repeated here.
Above in association with most preferred embodiment, invention has been described, but the invention is not limited in implementation disclosed above
Example, and modification, equivalent combinations that the various essence according to the present invention are carried out should be covered.
Claims (10)
- A kind of 1. 3D wallpapers, it is characterised in that the 3D wallpapers include substrate layer, and the surface of the substrate layer forms patterned layer, The formation solid pattern layer of the surface selectivity of the patterned layer, the three-dimensional pattern layer through-thickness rises and falls in height to be become Change.
- 2. 3D wallpapers according to claim 1, it is characterised in that the 3D wallpapers also include interspersing layer, described to intersperse layer It is covered on the surface of the three-dimensional pattern layer.
- 3. 3D wallpapers according to claim 1, it is characterised in that the thickness range of the three-dimensional pattern layer is between 0.01mm Between~200mm.
- 4. 3D wallpapers according to claim 1, it is characterised in that the 3D wallpapers also include priming coat, the priming coat Between the substrate layer and the patterned layer.
- 5. the method for the 3D wallpapers any one of a kind of manufacturing claims 1-4, it is characterised in that methods described is included such as Lower step：1) substrate layer is provided, patterned layer is formed in the surface of the substrate layer；2) in the formation solid pattern layer of the surface of patterned layer selectivity, the three-dimensional pattern layer through-thickness is in height Fluctuations.
- 6. the manufacture method of 3D wallpapers according to claim 5, it is characterised in that in the step 2), beaten by 3D The formation three-dimensional pattern layer of the print machine in the surface of patterned layer selectivity.
- 7. the manufacture method of 3D wallpapers according to claim 5, it is characterised in that the manufacture method also includes step 3), there is provided intersperse layer, on the basis of step 2), the shape of the three-dimensional pattern layer again add using the layer of interspersing Work, the layer of interspersing are covered on the surface of the three-dimensional pattern layer.
- 8. the manufacture method of 3D wallpapers according to claim 7, it is characterised in that by 3D printer in the stereogram Layer is interspersed described in producing in the surface of type layer.
- 9. the manufacture method of 3D wallpapers according to claim 5, it is characterised in that in step 1), priming coat is also provided, The priming coat is formed in the base material layer surface, the patterned layer is formed in the surface of the priming coat.
- 10. the manufacture method of 3D wallpapers according to claim 5, it is characterised in that the three-dimensional pattern layer choosing is from thermoplastic In property resin, light-cured resin, diatom ooze any one or at least two mixture.