CN107446682A - A kind of rack high performance water-soluble lubricating oil - Google Patents
A kind of rack high performance water-soluble lubricating oil Download PDFInfo
- Publication number
- CN107446682A CN107446682A CN201710854769.3A CN201710854769A CN107446682A CN 107446682 A CN107446682 A CN 107446682A CN 201710854769 A CN201710854769 A CN 201710854769A CN 107446682 A CN107446682 A CN 107446682A
- Authority
- CN
- China
- Prior art keywords
- lubricating oil
- parts
- high performance
- performance water
- rack
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of rack high performance water-soluble lubricating oil, base oil has preferably viscosity, lubricity and viscosity temperature characteristic, high viscosity index (HVI), good rheological property;Nano kaoline and nano aluminium oxide compounding, Synergistic, greatly improve the service life of lubricating oil and recycle number, while be also prevented from lubricating oil and precipitate;Various additives compound, and can improve the various performances of lubricating oil, increase the stability and lubricant effect of lubricating oil, can be very good to prevent tooth surface of rack from the disrepair phenomenons such as abrasion, scratch occur, extend the service life of rack;Scientific formulation is reasonable, and using deionization as the water-soluble lubricating of solvent oil, environmentally friendly, environment-protecting and non-poisonous, production cost is low.
Description
Technical field
The present invention relates to technical field of lubricating oil, particularly a kind of rack high performance water-soluble lubricating oil.
Background technology
Lubricating oil is with various types of plant equipment, and to reduce the frictional force of equipment room, protection is mechanical and processes
The liquid or semisolid lubricants of part, mainly play lubrication, supplement heat rejecter, antirust, cleaning, sealing and buffering etc..
Lubricating oil is made up of base oil and additive two parts, and base oil is the main component of lubricating oil, decides lubrication
The fundamental property of oil, additive can then make up and improve the deficiency of base oil aspect of performance, assign some new performances, be lubrication
The important component of oil.The problems such as existing splash ring guaranteed cost is poor, production cost is high, can not meet requirement.
The content of the invention
Goal of the invention:In order to solve the above problems, it is an object of the invention to provide a kind of rack high performance water-soluble
Lubricating oil.
The content of the invention:A kind of rack high performance water-soluble lubricating oil, include the component of following parts by weight:Base oil 80-
100 parts, hydroxyethyl cellulose 3-5 parts, Sodium Polyacrylate 6-8 parts, ethylene glycol 8-12 parts, modified graphite powder 1-2 parts, nanometer kaolinite
Soil and nano aluminium oxide blend 3-9 parts, polyvinyl alcohol emulsions 0.3-0.5 parts, stabilizer 5-15 parts, surfactant 2-10
Part, defoamer 0.2-1 parts, deionized water 30-70 parts.
Preferably, described base oil is high viscosity index (HVI) I class base oils, is 5-8mm in 100 DEG C of kinematic viscosity2/ s, glue
Spend index and be more than 95.
Preferably, described modified graphite powder is the poly- methyl-prop obtained using cyanacrylate modified nano graphite
E pioic acid methyl ester/graphite composite.
Preferably, described nano kaoline and nano aluminium oxide blend preparation method be by triethanolamine borate and
The triethanolamine borate solution that mass concentration is 4.98% is configured to after deionized water is well mixed, then by nano kaoline
It is added to nano aluminium oxide in triethanolamine borate solution, is heated to 85 DEG C, and with 200r/min rotating speed stir process 1h,
Room temperature filtering drying is cooled to after insulation standing 30min to produce.
Preferably, described stabilizer is polypropylene glycol monobutyl ether.
Preferably, described defoamer is the special defoamer DF-668 of lubricating oil.
Preferably, described surfactant is A310 surfactants.
The beneficial effects of the present invention are:A kind of rack high performance water-soluble lubricating oil of the present invention, base oil have
Preferably viscosity, lubricity and viscosity temperature characteristic, high viscosity index (HVI), good rheological property;Nano kaoline and nano aluminium oxide compounding,
Synergistic, greatly improve the service life of lubricating oil and recycle number, while be also prevented from lubricating oil
Precipitation;Various additives compound, and can improve the various performances of lubricating oil, increase the stability and lubricant effect of lubricating oil, can
To prevent tooth surface of rack from the disrepair phenomenons such as abrasion, scratch occur well, extend the service life of rack;Scientific formulation is reasonable,
Using deionization as the water-soluble lubricating of solvent oil, environmentally friendly, environment-protecting and non-poisonous, production cost is low.
Embodiment
In order to illustrate more clearly of the embodiment of the present application or technical scheme of the prior art, letter will be made to embodiment below
Singly introduce, for those of ordinary skill in the art, on the premise of not paying creative work, can also be according to these
Embodiment obtains other embodiments.
Table 1 is the wear-resistant antiseptic and rustproof lubricating oil constituent table of antioxygen described in the embodiment of the present invention.
The wear-resistant antiseptic and rustproof lubricating oil family (unit of antioxygen described in the embodiment of table 1.:Part)
Embodiment 1
A kind of rack high performance water-soluble lubricating oil, described base oil is high viscosity index (HVI) I class base oils, 100
DEG C kinematic viscosity is 5mm2/ s, viscosity index (VI) are more than 90.
Described modified graphite powder is the poly-methyl methacrylate obtained using cyanacrylate modified nano graphite
Ester/graphite composite.
Described nano kaoline and nano aluminium oxide blend preparation method are by triethanolamine borate and deionization
The triethanolamine borate solution that mass concentration is 4.98% is configured to after water is well mixed, then by nano kaoline and nanometer
Aluminum oxide is added in triethanolamine borate solution, is heated to 85 DEG C, and quiet with 200r/min rotating speed stir process 1h, insulation
Put and be cooled to room temperature filtering drying after 30min and produce.
Described stabilizer is polypropylene glycol monobutyl ether.
Described defoamer is the special defoamer DF-668 of lubricating oil.
Described surfactant is A310 surfactants.
Embodiment 2
A kind of rack high performance water-soluble lubricating oil, described base oil is high viscosity index (HVI) I class base oils, 100
DEG C kinematic viscosity is 8mm2/ s, viscosity index (VI) are more than 90.
Described modified graphite powder is the poly-methyl methacrylate obtained using cyanacrylate modified nano graphite
Ester/graphite composite.
Described nano kaoline and nano aluminium oxide blend preparation method are by triethanolamine borate and deionization
The triethanolamine borate solution that mass concentration is 4.98% is configured to after water is well mixed, then by nano kaoline and nanometer
Aluminum oxide is added in triethanolamine borate solution, is heated to 85 DEG C, and quiet with 200r/min rotating speed stir process 1h, insulation
Put and be cooled to room temperature filtering drying after 30min and produce.
Described stabilizer is polypropylene glycol monobutyl ether.
Described defoamer is the special defoamer DF-668 of lubricating oil.
Described surfactant is A310 surfactants.
Embodiment 3
A kind of rack high performance water-soluble lubricating oil, described base oil is high viscosity index (HVI) I class base oils, 100
DEG C kinematic viscosity is 6mm2/ s, viscosity index (VI) are more than 90.
Described modified graphite powder is the poly-methyl methacrylate obtained using cyanacrylate modified nano graphite
Ester/graphite composite.
Described nano kaoline and nano aluminium oxide blend preparation method are by triethanolamine borate and deionization
The triethanolamine borate solution that mass concentration is 4.98% is configured to after water is well mixed, then by nano kaoline and nanometer
Aluminum oxide is added in triethanolamine borate solution, is heated to 85 DEG C, and quiet with 200r/min rotating speed stir process 1h, insulation
Put and be cooled to room temperature filtering drying after 30min and produce.
Described stabilizer is polypropylene glycol monobutyl ether.
Described defoamer is the special defoamer DF-668 of lubricating oil.
Described surfactant is A310 surfactants.
Above example is only illustrating the preferred technical solution of the present invention, it is noted that for the general of the art
For logical technical staff, under the premise without departing from the principles of the invention, some improvement made or equivalent substitution, this is accordingly to be regarded as
The protection domain of invention, it should cover in scope of the presently claimed invention.
Claims (7)
1. a kind of rack high performance water-soluble lubricating oil, it is characterised in that include the component of following parts by weight:Base oil 80-
100 parts, hydroxyethyl cellulose 3-5 parts, Sodium Polyacrylate 6-8 parts, ethylene glycol 8-12 parts, modified graphite powder 1-2 parts, nanometer kaolinite
Soil and nano aluminium oxide blend 3-9 parts, polyvinyl alcohol emulsions 0.3-0.5 parts, stabilizer 5-15 parts, surfactant 2-10
Part, defoamer 0.2-1 parts, deionized water 30-70 parts.
A kind of 2. rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that described base oil
It is 5-8mm in 100 DEG C of kinematic viscosity for high viscosity index (HVI) I class base oils2/ s, viscosity index (VI) are more than 95.
A kind of 3. rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that described modification stone
Ink powder is the polymethyl methacrylate/graphite composite obtained using cyanacrylate modified nano graphite.
4. a kind of rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that described nanometer is high
Ridge soil and nano aluminium oxide blend preparation method are to be configured to matter after being well mixed triethanolamine borate and deionized water
The triethanolamine borate solution that concentration is 4.98% is measured, nano kaoline and nano aluminium oxide are then added to triethanolamine
In acid ester solution, 85 DEG C are heated to, and room temperature is cooled to after standing 30min with 200r/min rotating speed stir process 1h, insulation
Filtering drying produces.
A kind of 5. rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that described stabilizer
For polypropylene glycol monobutyl ether.
A kind of 6. rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that described defoamer
For the special defoamer DF-668 of lubricating oil.
7. a kind of rack high performance water-soluble lubricating oil according to claim 1, it is characterised in that live on described surface
Property agent is A310 surfactants.