CN107422410A - 具有扩散功能的增白银半透型偏光片及其制作工艺 - Google Patents
具有扩散功能的增白银半透型偏光片及其制作工艺 Download PDFInfo
- Publication number
- CN107422410A CN107422410A CN201710873992.2A CN201710873992A CN107422410A CN 107422410 A CN107422410 A CN 107422410A CN 201710873992 A CN201710873992 A CN 201710873992A CN 107422410 A CN107422410 A CN 107422410A
- Authority
- CN
- China
- Prior art keywords
- silver
- diffusant
- colored
- base material
- full impregnated
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种具有扩散功能的增白银半透型偏光片及其制作工艺，该偏光片包括银半透膜、全透偏光基材以及增强银半透膜与全透偏光基材之间牢固性的扩散剂粘着层，所述扩散剂粘着层包括原胶体以及均匀嵌入原胶体内的扩散粉颗粒，所述全透偏光基材包括TAC保护层以及离型膜，所述原胶体一面与银半透膜无缝粘合，且所述原胶体的另一面与TAC保护层无缝粘合，所述TAC保护层粘合在离型膜上。在全透偏光基材上复合扩散剂粘着层，从而使偏光片具有扩散功能，提高了光纤的均匀性，且扩散剂粘着层中的扩散剂以扩散粉颗粒的形式嵌入原胶体内，从而有效降低了偏光片的有效厚度。
Description
技术领域
本发明涉及偏光片的技术领域，尤其涉及一种具有扩散功能的增白银半透型偏光片及其制作工艺。
背景技术
偏光片的全称应该是偏振光片，学过物理的应该知道什么是偏振光，液晶显示器的成像必须依靠偏振光，所有的液晶都有前后两片偏振光片紧贴在液晶玻璃，组成总厚度1mm左右的液晶片。如果少了任何一张偏光片，液晶片都是不能显示图像的。
现有技术中偏光片的问题是，扩散粉与胶的粘附力要提高比例使偏光片与银半透膜之间要牢固，否则会出现高温高湿剥离现象。
TAC——三醋酸纤维素酯，具有亲水性，在湿热的环境中很快会变形、收缩、松弛、衰退、且强度很低，质脆易破，不便于使用和加工，因此在膜两边都复合上一层强度高、透光率高而又耐湿热的TAC膜，起保护作用。
PVA——聚乙烯醇，是一种高分子聚合物，用各类具有二向色性的有机染料染色，同时在一定的湿度和温度条件下进行延伸，使其吸收二向色性染料形成偏振性能，在脱水、烘干后形成偏光片原膜。
发明内容
针对上述技术中存在的不足之处，本发明提供一种扩散性强、光线柔和的具有扩散功能的增白银半透型偏光片及其制作工艺。
为了达到上述目的，本发明一种具有扩散功能的增白银半透型偏光片，包括银半透膜、全透偏光基材以及增强银半透膜与全透偏光基材之间牢固性的扩散剂粘着层，所述扩散剂粘着层包括原胶体以及均匀嵌入原胶体内的扩散粉颗粒，所述全透偏光基材包括TAC保护层以及离型膜，所述原胶体一面与银半透膜无缝粘合，且所述原胶体的另一面与TAC保护层无缝粘合，所述TAC保护层粘合在离型膜上。
其中，所述TAC保护层包括第一TAC保护层以及第二TAC保护层，所述第一TAC保护层与原胶体相接触，所述第二TAC保护层粘合在离型膜上。
其中，所述全透偏光基材还包括PVA偏光素子层，所述PVA偏光素子层设置在第一TAC保护层与第二TAC保护层之间，且所述第一TAC保护层与PVA偏光素子层之间通过里胶固定，所述第二TAC保护层与PVA偏光素子层之间也通过里胶固定。
其中，所述全透偏光基材还包括增强离型膜附着性能的粘合剂层，所述粘合剂层一面与第二TAC保护层粘合，且所述粘合剂层另一面与离型膜粘合。
其中，该增白银半透型偏光片还包括避免银半透膜在移动过程中受损的保护膜层，所述保护膜层覆盖在银半透膜的外表面。
本发明一种具有扩散功能的增白银半透型偏光片的制作工艺，包括以下步骤：
S1、调配扩散剂，将增白扩散粉加乙酸乙酯后打散并浸泡两小时，然后将浸泡好的增白扩散粉以及固化剂倒入原胶内搅拌形成扩散剂粘着层；
S2、形成粘着层，将调配好的扩散剂液体压入生产涂布辊上，调好产品胶厚，使扩散剂液体涂布到剥离膜上；
S3、复合到全透偏光基材，将剥离膜以及全透偏光基材均放置到烘箱中，并使剥离膜上的扩散剂液体面与全透偏光基材相接触并粘合在全透偏光基材上；
S4、复合银半透膜，将扩散剂外表面的剥离膜撕掉并将银半透膜粘贴到扩散剂的外表面，使用压辊将二者压合；
S5、生产完成，将压合成型的偏光片银半透膜表层密封一层保护膜，完成生产。
其中，在S1调配扩散剂的过程中，浸泡2h的增白扩散粉首先倒入原胶内搅拌0.5h，然后再添加固化剂搅拌1.5h，并测量粘度是否在参数标准内，直至达到标准后停止搅拌，静止消泡0.5h，得到调配好的扩散剂液体。
本发明一种具有扩散功能的增白银半透型偏光片的应用，该增白银半透型偏光片用于LCD液晶面板显示产品上，对LCD液晶面板显示具有扩散功能，提高光线的均匀性和柔和性。
本发明的有益效果是：
与现有技术相比，本发明具有扩散功能的增白银半透型偏光片，在全透偏光基材上复合扩散剂粘着层，从而使偏光片具有扩散功能，提高了光纤的均匀性，且扩散剂粘着层中的扩散剂以扩散粉颗粒的形式嵌入原胶体内，从而有效降低了偏光片的有效厚度。本发明的扩散剂粘着层设置在银半透膜与全透偏光基材之间，有效增加了全透偏光基材与银半透膜之间的牢固性，避免了偏光片在高温高湿环境下剥离现象的发生。
附图说明
图1为本发明具有扩散功能的增白银半透型偏光片的结构示意图；
图2为本发明具有扩散功能的增白银半透型偏光片的制作工艺的流程示意图。
主要元件符号说明如下：
1、银半透膜 2、全透偏光基材
3、扩散剂粘着层 4、保护膜层
31、TAC保护层 32、离型膜
33、PVA偏光素子层 34、粘合剂层
311、第一TAC保护层 312、第二TAC保护层。
具体实施方式
为了更清楚地表述本发明，下面结合附图对本发明作进一步地描述。
参阅图1，本发明一种具有扩散功能的增白银半透型偏光片，包括银半透膜、全透偏光基材以及增强银半透膜与全透偏光基材之间牢固性的扩散剂粘着层，所述扩散剂粘着层包括原胶体以及均匀嵌入原胶体内的扩散粉颗粒，所述全透偏光基材包括TAC保护层以及离型膜，所述原胶体一面与银半透膜无缝粘合，且所述原胶体的另一面与TAC保护层无缝粘合，所述TAC保护层粘合在离型膜上。
相较于现有技术，本发明具有扩散功能的增白银半透型偏光片，在全透偏光基材上复合扩散剂粘着层，从而使偏光片具有扩散功能，提高了光纤的均匀性，且扩散剂粘着层中的扩散剂以扩散粉颗粒的形式嵌入原胶体内，从而有效降低了偏光片的有效厚度。本发明的扩散剂粘着层设置在银半透膜与全透偏光基材之间，有效增加了全透偏光基材与银半透膜之间的牢固性，避免了偏光片在高温高湿环境下剥离现象的发生。
在本实施例中，所述TAC保护层包括第一TAC保护层以及第二TAC保护层，所述第一TAC保护层与原胶体相接触，所述第二TAC保护层粘合在离型膜上。
在本实施例中，所述全透偏光基材还包括PVA偏光素子层，所述PVA偏光素子层设置在第一TAC保护层与第二TAC保护层之间，且所述第一TAC保护层与PVA偏光素子层之间通过里胶固定，所述第二TAC保护层与PVA偏光素子层之间也通过里胶固定。
在本实施例中，所述全透偏光基材还包括增强离型膜附着性能的粘合剂层，所述粘合剂层一面与第二TAC保护层粘合，且所述粘合剂层另一面与离型膜粘合。
在本实施例中，该增白银半透型偏光片还包括避免银半透膜在移动过程中受损的保护膜层，所述保护膜层覆盖在银半透膜的外表面。
进一步参阅图2，本发明一种具有扩散功能的增白银半透型偏光片的制作工艺，包括以下步骤：
S1、调配扩散剂，将增白扩散粉加乙酸乙酯后打散并浸泡两小时，然后将浸泡好的增白扩散粉以及固化剂倒入原胶内搅拌形成扩散剂粘着层；
S2、形成粘着层，将调配好的扩散剂液体压入生产涂布辊上，调好产品胶厚，使扩散剂液体涂布到剥离膜上；
S3、复合到全透偏光基材，将剥离膜以及全透偏光基材均放置到烘箱中，并使剥离膜上的扩散剂液体面与全透偏光基材相接触并粘合在全透偏光基材上；
S4、复合银半透膜，将扩散剂外表面的剥离膜撕掉并将银半透膜粘贴到扩散剂的外表面，使用压辊将二者压合；
S5、生产完成，将压合成型的偏光片银半透膜表层密封一层保护膜，完成生产。
在本实施例中，在S1调配扩散剂的过程中，浸泡2h的增白扩散粉首先倒入原胶内搅拌0.5h，然后再添加固化剂搅拌1.5h，并测量粘度是否在参数标准内，直至达到标准后停止搅拌，静止消泡0.5h，得到调配好的扩散剂液体。
本发明一种具有扩散功能的增白银半透型偏光片的应用，该增白银半透型偏光片用于LCD液晶面板显示产品上，对LCD液晶面板显示具有扩散功能，提高光线的均匀性和柔和性。
本发明的增白银半透型偏光片生产完成后，检测得到的成品各项参数如下表一所示：
表一
由表一数据可得，该偏光片的色相即偏光片颜色所对应的色坐标值(NBS)a值为-1.5±1.5，b值为5±2，透过率T为4％±1％，偏光度≥95％，有效厚度为270um，有效宽幅为1000mm*500mm。
以上公开的仅为本发明的几个具体实施例，但是本发明并非局限于此，任何本领域的技术人员能思之的变化都应落入本发明的保护范围。
Claims (8)
1.一种具有扩散功能的增白银半透型偏光片，其特征在于，包括银半透膜、全透偏光基材以及增强银半透膜与全透偏光基材之间牢固性的扩散剂粘着层，所述扩散剂粘着层包括原胶体以及均匀嵌入原胶体内的扩散粉颗粒，所述全透偏光基材包括TAC保护层以及离型膜，所述原胶体一面与银半透膜无缝粘合，且所述原胶体的另一面与TAC保护层无缝粘合，所述TAC保护层粘合在离型膜上。
2.根据权利要求1所述的具有扩散功能的增白银半透型偏光片，其特征在于，所述TAC保护层包括第一TAC保护层以及第二TAC保护层，所述第一TAC保护层与原胶体相接触，所述第二TAC保护层粘合在离型膜上。
3.根据权利要求2所述的具有扩散功能的增白银半透型偏光片，其特征在于，所述全透偏光基材还包括PVA偏光素子层，所述PVA偏光素子层设置在第一TAC保护层与第二TAC保护层之间，且所述第一TAC保护层与PVA偏光素子层之间通过里胶固定，所述第二TAC保护层与PVA偏光素子层之间也通过里胶固定。
4.根据权利要求3所述的具有扩散功能的增白银半透型偏光片，其特征在于，所述全透偏光基材还包括增强离型膜附着性能的粘合剂层，所述粘合剂层一面与第二TAC保护层粘合，且所述粘合剂层另一面与离型膜粘合。
5.根据权利要求1所述的具有扩散功能的增白银半透型偏光片，其特征在于，该增白银半透型偏光片还包括避免银半透膜在移动过程中受损的保护膜层，所述保护膜层覆盖在银半透膜的外表面。
6.一种具有扩散功能的增白银半透型偏光片的制作工艺，其特征在于，包括以下步骤：
S1、调配扩散剂，将增白扩散粉加乙酸乙酯后打散并浸泡两小时，然后将浸泡好的增白扩散粉以及固化剂倒入原胶内搅拌形成扩散剂粘着层；
S2、形成粘着层，将调配好的扩散剂液体压入生产涂布辊上，调好产品胶厚，使扩散剂液体涂布到剥离膜上；
S3、复合到全透偏光基材，将剥离膜以及全透偏光基材均放置到烘箱中，并使剥离膜上的扩散剂液体面与全透偏光基材相接触并粘合在全透偏光基材上；
S4、复合银半透膜，将扩散剂外表面的剥离膜撕掉并将银半透膜粘贴到扩散剂的外表面，使用压辊将二者压合；
S5、生产完成，将压合成型的偏光片银半透膜表层密封一层保护膜，完成生产。
7.根据权利要求6所述的具有扩散功能的增白银半透型偏光片的制作工艺，其特征在于，在S1调配扩散剂的过程中，浸泡2h的增白扩散粉首先倒入原胶内搅拌0.5h，然后再添加固化剂搅拌1.5h，并测量粘度是否在参数标准内，直至达到标准后停止搅拌，静止消泡0.5h，得到调配好的扩散剂液体。
8.一种具有扩散功能的增白银半透型偏光片的应用，其特征在于，该增白银半透型偏光片用于LCD液晶面板显示产品上，对LCD液晶面板显示具有扩散功能，提高光线的均匀性和柔和性。