CN107382270A - A kind of development of pearly-lustre handsel ceramic plate - Google Patents

A kind of development of pearly-lustre handsel ceramic plate Download PDF

Info

Publication number
CN107382270A
CN107382270A CN201710619047.XA CN201710619047A CN107382270A CN 107382270 A CN107382270 A CN 107382270A CN 201710619047 A CN201710619047 A CN 201710619047A CN 107382270 A CN107382270 A CN 107382270A
Authority
CN
China
Prior art keywords
ceramic plate
lustre
pearly
handsel
glaze
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710619047.XA
Other languages
Chinese (zh)
Inventor
张千里
杨勇军
张拥海
葛庆
钟侃
秦爱民
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Ruigao (zhejiang) New Environmental Mstar Technology Ltd
Original Assignee
Ruigao (zhejiang) New Environmental Mstar Technology Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ruigao (zhejiang) New Environmental Mstar Technology Ltd filed Critical Ruigao (zhejiang) New Environmental Mstar Technology Ltd
Priority to CN201710619047.XA priority Critical patent/CN107382270A/en
Publication of CN107382270A publication Critical patent/CN107382270A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of development of pearly-lustre handsel ceramic plate, it is characterised in that comprises the following steps：Natural clay, quartz, float stone and the feldspar sampling test of storage will be put in storage；Appropriate natural clay, quartz, float stone and feldspar are chosen according to the demand of making；The material configured is mixed evenly；The mixture of preparation is passed through into high pressure extrusion molding, low temperature drying, applies high-temperature glaze through 1180 degree of high-temperature firing, obtains ceramic plate base substrate；After cleaved processing, surface clean is clean, applies the pearly-lustre glaze of one layer of independent research with leaching glaze mode or glaze spraying mode in billet surface, then calcine 3 hours through 800 degree；Pearly-lustre handsel ceramic plate can be obtained after cooling；The advantage of the invention is that the color of riot of color is presented in ceramic plate surface effect under light, color gloss and textural effect are similar to shell, seem bright and glittering on decorated style, welcome by market instantly.

Description

A kind of development of pearly-lustre handsel ceramic plate
Technical field
The present invention relates to a kind of development of pearly-lustre handsel ceramic plate, belong to building decoration area.
Background technology
Ceramic plate has the characteristics that green, radiationless, color and luster is gentle, will not bring light pollution.By the ceramic plate of firing Because of the difference that can be produced in size of expanding with heat and contract with cold, market can be supplied after high-accuracy mechanical is cut, then through inspection is qualified.It is existing Ceramic plate belongs to natural clay, burns effect and is similar to natural clay quality and color, however in terms of colorful and discoloration but without Method embodies, and can not meet the needs of different crowd is to decorated style.
The content of the invention
（One）Technical problems to be solved
To solve the above problems, the present invention proposes a kind of development of pearly-lustre handsel ceramic plate.
（Two）Technical scheme
A kind of development of pearly-lustre handsel ceramic plate, it is characterised in that comprise the following steps：
（1）Natural clay, quartz, float stone and the feldspar sampling test of storage will be put in storage；
（2）Appropriate natural clay, quartz, float stone and feldspar are chosen according to the demand of making；
（3）The material configured is mixed evenly；
（4）The mixture of preparation by high pressure extrusion molding, low temperature drying and is applied into high-temperature glaze through 1180 degree of high-temperature firing, obtained To ceramic plate base substrate；
（5）After the cleaved processing of base substrate, surface clean is clean, and one layer of independent research is applied with leaching glaze mode or glaze spraying mode on surface Pearly-lustre glaze, then through 800 degree calcining 3 hours after, normal temperature cooling；
（6）Pearly-lustre handsel ceramic plate can be obtained after cooling.
As preferential technical scheme, the natural clay is kaolinite, illite/mica and montomorillonite.
As preferential technical scheme, the step（4）In extrusion molding completed by ceramic plate extruder.
（Three）Beneficial effect
Compared with prior art, it has the advantages that the present invention：The advantage of the invention is that ceramic plate surface effect exists The color of riot of color is presented under light, color gloss and textural effect are similar to shell, seem honorable on decorated style It is brilliant, welcome by market instantly.
Embodiment
The present invention is further detailed by the following examples.
The development of a kind of pearly-lustre handsel ceramic plate of the present invention, it is characterised in that comprise the following steps：
（1）Natural clay, quartz, float stone and the feldspar sampling test of storage will be put in storage；
（2）Appropriate natural clay, quartz, float stone and feldspar are chosen according to the demand of making；
（3）The material configured is mixed evenly；
（4）The mixture of preparation by high pressure extrusion molding, low temperature drying and is applied into high-temperature glaze through 1180 degree of high-temperature firing, obtained To ceramic plate base substrate；
（5）After the cleaved processing of base substrate, surface clean is clean, and one layer of independent research is applied with leaching glaze mode or glaze spraying mode on surface Pearly-lustre glaze, then through 800 degree calcining 3 hours after, normal temperature cooling；
（6）Pearly-lustre handsel ceramic plate can be obtained after cooling.
Wherein, the natural clay is kaolinite, illite/mica and montomorillonite；The step（4）In extrusion molding Completed by ceramic plate extruder.
A kind of development of pearly-lustre handsel ceramic plate of the present invention, have below beneficial to fruit：The advantage of the invention is that ceramic plate table The color of riot of color is presented in face effect under light, and color gloss and textural effect are similar to shell, on decorated style Seem bright and glittering, welcome by market instantly.
The above-described embodiments are merely illustrative of preferred embodiments of the present invention, not to the structure of the present invention Think and scope is defined.On the premise of design concept of the present invention is not departed from, technology of the ordinary people in the field to the present invention The all variations and modifications that scheme is made, all should drop into protection scope of the present invention, the claimed technology contents of the present invention, All record in detail in the claims.

Claims (3)

1. a kind of development of pearly-lustre handsel ceramic plate, it is characterised in that comprise the following steps：
（1）Natural clay, quartz, float stone and the feldspar sampling test of storage will be put in storage；
（2）Appropriate natural clay, quartz, float stone and feldspar are chosen according to the demand of making；
（3）The material configured is mixed evenly；
（4）The mixture of preparation by high pressure extrusion molding, low temperature drying and is applied into high-temperature glaze through 1180 degree of high-temperature firing, obtained To ceramic plate base substrate；
（5）After the cleaved processing of base substrate, surface clean is clean, and one layer of independent research is applied with leaching glaze mode or glaze spraying mode on surface Pearly-lustre glaze, then through 800 degree calcining 3 hours after, normal temperature cooling；
（6）Pearly-lustre handsel ceramic plate can be obtained after cooling.
2. the development of pearly-lustre handsel ceramic plate as claimed in claim 1, it is characterised in that：The natural clay is kaolinite, she Sharp stone/mica and montomorillonite.
3. the development of pearly-lustre handsel ceramic plate as claimed in claim 1, it is characterised in that：The step（4）In extrusion molding Completed by ceramic plate extruder.
CN201710619047.XA 2017-07-26 2017-07-26 A kind of development of pearly-lustre handsel ceramic plate Pending CN107382270A (en)