CN107381731A - 水及处理水的方法及应用 - Google Patents

水及处理水的方法及应用 Download PDF

Info

Publication number
CN107381731A
CN107381731A CN201710669945.6A CN201710669945A CN107381731A CN 107381731 A CN107381731 A CN 107381731A CN 201710669945 A CN201710669945 A CN 201710669945A CN 107381731 A CN107381731 A CN 107381731A
Authority
CN
China
Prior art keywords
water
quantum
ceramics
health products
processing water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710669945.6A
Other languages
English (en)
Inventor
雷永泉
汪兴江
杜艳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201710669945.6A priority Critical patent/CN107381731A/zh
Publication of CN107381731A publication Critical patent/CN107381731A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种水及处理水的方法及应用，涉及材料技术领域。该处理水的方法为将水置于设有量子陶瓷的容器中至少10min所得；其中，量子陶瓷为按配方将原料混合后，于氮气气氛下，烧结后冷却所得，配方包括：电气石，陨石，砭石，麦饭石，锗石，二氧化硅，二氧化钛，氧化钙，高岭土，三氧化二铁，氧化锌，钕，硼和氧化镁，有效净化水质，同时将缩小水分子团，提高水的渗透力，增加水中的矿物质含量。由上述处理水的方法制得的水，其富含矿物质，渗透率佳。上述水在保健品中的应用，有效提高保健品的保健性能。

Description

水及处理水的方法及应用
技术领域
本发明涉及材料技术领域，且特别涉及一种水及处理水的方法及应用。
背景技术
水不仅是生命存在的基本条件，也是生命结构的基本构本，人类与水资源密不可分。随着人类社会的进步和城市的发展，水被分为饮用水和生活用水，然而不管是饮用水还是生活用水，在其为人类服务的同时，每时每刻也被人类所污染，并且污染程度日趋严重，污染物质的种类日趋增多，以至于威胁到人类的健康和生命。目前，人们普遍认为，饮用水是有害物质的侵入方式，实际上，淋浴时人的呼吸和皮肤吸收也可能使人吸收这些有害物质，恰恰是生活用水更加贯穿于我们日常生活的各个方面，例如，沐浴用水、厨房用水，衣服清洗用水，卫生盥洗用水。特别是沐浴用水，由于直接与人体的毛发和肌肤接触，其净化问题应当引起人们的重视。
近年来，市场上已出现了许多净化水的技术和产品，包括化学药品处理技术和产品、活性炭类过滤净化处理技术和产品、离子交换树脂处理技术和产品、麦饭石类净化处理技术和产品等。但实践证明上述各种技术和产品，如化学药品处理技术和产品因刺激性或发生化学反应而被淘汰，而其它几种处理技术和产品大都效果单一或不完善，也不具备或不完全具备释放负离子、杀菌、抗菌、除氯的效果。
发明内容
本发明的目的在于提供一种处理水的方法，有效净化水质，同时将缩小水分子团，提高水的渗透力，增加水中的矿物质含量。
本发明的另一目的在于提供一种由上述处理水的方法制得的水，其富含矿物质，渗透率佳。
本发明的另一目的在于提供上述水在保健品中的应用，有效提高保健品的保健性能。
本发明解决其技术问题是采用以下技术方案来实现的。
本发明提出一种处理水的方法，将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合后，于氮气气氛下，烧结后冷却所得。
配方按照质量百分比计，包括：电气石25％～36％，陨石1％～3％，砭石7％～14％，麦饭石7％～25％，锗石5％～10％，二氧化硅6％～13％，二氧化钛0.5％～3.5％，氧化钙1～5％，高岭土7％～12％，三氧化二铁0.5％～3％，氧化锌0.5％～3％，钕0.5％～3％，硼0.5％～3％，以及氧化镁6％～12％。本发明提出一种由上述处理水的方法制得的水。
本发明提出一种上述水在保健品中的应用。
本发明实施例的水及处理水的方法及应用的有益效果是：
通过以电气石为主，其他原料为辅的配方，配比合理，有效提高得到的量子陶瓷的性能，使其可以持久的产生2高斯的磁力和6～14微米的红外线，具有优异的保健功效。使用该量子陶瓷对水进行物理处理，该量子陶瓷向水中释放负氢粒子，使水中的负氢粒子由0PPM/L提高到1.2PPM/L以上，同时，通过高频磁化波的振荡原理，把原来的由13～16个水分子组成的大分子团水，迅速改变为6～9个水分子组成小分子团水，同时，由于其富含矿物质，有效使水的pH值提高至pH为7.5～8.8，使水呈弱碱性，同时把把ORP(电位)值由原来的+180～250改变为-100～220之间；使经处理后的水具有更高的活性，更便于吸收以及保健效果佳。
同时，将该量子陶瓷运用于保健品，可以有效增强其保健性能。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
下面对本发明实施例的水及处理水的方法及应用进行具体说明。
本发明提供一种处理水的方法，将水置于设有量子陶瓷的容器中至少10min所得。通过量子陶瓷有效去除水中的不良因素，同时，该量子陶瓷对水进行物理处理，该量子陶瓷向水中释放负氢粒子，使水中的负氢粒子由0PPM/L提高到1.2PPM/L以上，同时，通过高频磁化波的振荡原理，把原来的由13～16个水分子组成的大分子团水，迅速改变为6～9个水分子组成小分子团水，同时，由于其富含矿物质，有效使水的pH值提高至pH为7.5～8.5，使水呈弱碱性，同时把把ORP(电位)值由原来的+180～250改变为-100～220之间。该处理方法简单便捷，有效净化水质，同时将缩小水分子团，提高水的渗透力，增加水中的矿物质含量。
其中，容器例如可以为被子、对水的进化处理器等等，在此不作具体限定，本领域本工作人员可根据实际情况进行选择。
本发明中，量子陶瓷为按配方将原料混合后，于氮气气氛下，烧结后冷却所得；其中，配方按照质量百分比计，包括：
电气石25％～36％，陨石1％～3％，砭石7％～14％，麦饭石7％～25％，锗石5％～10％，二氧化硅6％～13％，二氧化钛0.5％～3.5％，氧化钙1～5％，高岭土7％～12％，三氧化二铁0.5％～3％，氧化锌0.5％～3％，钕0.5％～3％，硼0.5％～3％，以及氧化镁6％～12％。
更优选地，在本发明较佳的实施例中，量子陶瓷的配方，按质量百分比计，包括：电气石26％～36％，陨石1％～3％，砭石9％～10％，麦饭石8％～22％，锗石7％～8％，二氧化硅8％～11％，二氧化钛1％～2％，氧化钙2～3％，高岭土9％～10％，三氧化二铁1％～3％，氧化锌1％～3％，钕1％～3％，硼1％～3％，以及氧化镁8％～10％。
通过上述各原料的合理配比，有效提高最终得到的量子陶瓷的性能，使其长久的释放较佳的释放微磁和红外光波，具有优异的保健功效，有效激活人体细胞、增加血液循环、调整人体微循环的功能。
同时该陶瓷材料可以吸附水中的纳米铜、锌、银合金，因为合金金属簇能够有效的去除水中的余氯、可溶性的重金属离子、硝酸盐、氟化物、碳酸盐和硫酸盐等有害物质，并可控制水中的细菌和藻类的生长繁殖及阻止硬垢的累积，同时可去除因钢铁材料制成的输水管件腐蚀时形成的氧化亚铁胶体，从而达到净化水质的效果。
其中，电气石，晶体属三方晶系的一族环状结构硅酸盐矿物的总称。
电气石可以产生负离子，具有调整人体离子平衡，除臭，活化细胞，提高自然治愈力等作用，并能抑制身体的氧化或老化。其还可以电解水以及缩小水分子团，有效去除氨或不纯物，同时提高水的渗透力。同时电气石还可以放射远红外线，其能渗透到身体深层部位，温暖细胞，促进血液循环，使新陈代谢顺畅，同时电气石含有各种天然矿物质，其中有很多与人类必需的矿物质相同。借着微弱电流作用，矿物质容易被吸收，是极佳的矿物质来源。
本发明采用以电气石为主要配料，以陨石，砭石，麦饭石，锗石，二氧化硅，二氧化钛，高岭土等作为配料，有效增强其磁性以及保健效果。同时增加三氧化二铁，钕，硼等，进一步有效增强制得的量子陶瓷的磁性。
本发明提供一种量子陶瓷的制作方法，按上述配方将原料混合后，于氮气气氛下，烧结后冷却，得到量子陶瓷的成品，该成品可以为球、块、或者不规则几何形状，或者得到后进一步对其形状进行加工成规则品，均可，在此不做具体限定。
由于烧结过程中，涉及各原料之间的氧化还原反应，为避免影响最终的成份受到影响，因此优选在于氮气气氛下进行烧结、冷却。
优选地，在本发明较佳的实施例中，于烧结前，将原料粉碎至410～480目，有效增大各原料之间的接触面积，促进反应，有效提高反应效率。
优选地，在本发明较佳的实施例中，于烧结前在640～660℃保温0.3～0.7h，使各原料预热，同时使个原料之间进行固相反应。需要说明的是，本发明中，当在640～660℃保温0.3～0.7h后，直接进行烧结，期间，在室温至640～660℃也以烧结的第一阶段的升温速率进行，即先以2～3℃/min的速度升温至640～660℃，保证各原料匀速受热，保证其性质的稳定性。
优选地，在本发明较佳的实施例中，烧结包括第一阶段与第二阶段，第一阶段为：先以2～3℃/min的速度升温至1000℃，再以0.5～1℃/min的速度升温至1450℃～1500℃。有效提高量子陶瓷的磁性。
第二阶段为在1450℃～1500℃，保温0.5～1.5h，有效增大饱和磁感应强度，同时使个原料充分进行氧化还原反应，提高产品的成品率。在本发明较佳的实施例中，冷却至20～35℃。
更优选地，在本发明较佳的实施例中，冷却包括：
先以1～2℃/min的速度降温至1000℃，然后再以3～5℃/min的速度降温，有效提高产品的磁稳定性，使其可以持久的发射较佳的磁力。
本发明提出一种量子陶瓷，其由上述制作方法制得，其可以持久的产生2高斯的磁力和6～14微米的红外线，有效提高其保健能力。
本发明提出由上述处理水的方法制得的水，其富含负氢粒子，能够中和人体内的代谢产物以及感染所产生的氧自由基；其中，氧自由基是一种极不稳定的物质，当被负离子***所带的多余电子中和后，氧自由基的种种危害得以消除，如破坏细胞膜，加速动脉硬化，抑制免疫功能，使人体器宫衰老等。从而有效提高人体免疫力，同时，把原来的由13～16个水分子组成的大分子团水，迅速改变为6～9个水分子组成小分子团水，并且由于其富含矿物质，有效使水的pH值提高至pH为7.5～8.8，使水呈弱碱性，同时把把ORP(电位)值由原来的+180～250改变为-100～220之间；使经处理后的水具有更高的活性，更便于吸收以及保健效果佳。
本发明还提供上述水水在保健品中的应用。
具体地，保健品为治疗风湿性关节炎的保健品、治疗痛风病的保健品或治疗Ⅱ型糖尿病的保健品。可有效提高其保健功效，有效提高其商业价值。
以下结合实施例对本发明的特征和性能作进一步的详细描述。
实施例1
一种水，由以下处理水的方法制得：
将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合，粉碎至440目后，于氮气气氛下，于室温先以2.5℃/min的速度升温至1000℃，再以1℃/min的速度升温至1450℃，在1450℃保温1h后，再以1.6℃/min的速度降温至1000℃，然后再以4℃/min的速度降温至25℃，即得。
其中，配方按质量百分比计，包括：
电气石27％，陨石2％，砭石8％，麦饭石17％，锗石8％，二氧化硅7％，二氧化钛2％，氧化钙3％，高岭土10％，三氧化二铁2％，氧化锌2％，钕2％，硼2％，以及氧化镁8％。
实施例2
一种水，由以下处理水的方法制得：
将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合，粉碎至410目后，于氮气气氛下，先以2.5℃/min的速度升温至660℃，在660℃保温0.7h后，接着以2.5℃/min的速度升温至1000℃，再以0.7℃/min的速度升温至1500℃，在1500℃保温0.7h后，再以2℃/min的速度降温至1000℃，然后再以4℃/min的速度降温至20℃，即得。
其中，配方按质量百分比计，包括：
电气石36％，陨石3％，砭石14％，麦饭石7％％，锗石8％，二氧化硅8％，二氧化钛1％，氧化钙4％，高岭土8％，三氧化二铁1％，氧化锌1％，钕1％，硼1％，以及氧化镁7％。
实施例3
一种水，由以下处理水的方法制得：
将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合，粉碎至460目后，于氮气气氛下，先以2℃/min的速度升温至650℃，在650℃保温0.5h后，接着以2℃/min的速度升温至1000℃，再以1℃/min的速度升温至1470℃，在1470℃保温1.2h后，再以1℃/min的速度降温至1000℃，然后再以3℃/min的速度降温至25℃，即得。
其中，配方按质量百分比计，包括：
电气石26％，陨石1％，砭石10％，麦饭石22％，锗石6％，二氧化硅6％，二氧化钛2％，氧化钙2.5％，高岭土9％，三氧化二铁1.5％，氧化锌1％，钕1.5％，硼1.5％，以及氧化镁10％。
实施例4
一种水，由以下处理水的方法制得：
将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合，粉碎至470目后，于氮气气氛下，先以2.7℃/min的速度升温至645℃，在645℃保温0.6h后，接着以2.7℃/min的速度升温至1000℃，再以1℃/min的速度升温至1460℃，在1460℃保温1h后，再以1.8℃/min的速度降温至1000℃，然后再以3.5℃/min的速度降温至30℃，即得。
其中，配方按质量百分比计，包括：
电气石30％，陨石1.5％，砭石9％，麦饭石15％，锗石10％，二氧化硅12.5％，二氧化钛1％，氧化钙3％，高岭土8％，三氧化二铁1％，氧化锌1％，钕1％，硼1％，以及氧化镁6％。
实施例5
一种水，由以下处理水的方法制得：
将水置于设有量子陶瓷的容器中至少10min所得。
量子陶瓷为按配方将原料混合，粉碎至470目后，于氮气气氛下，先以3℃/min的速度升温至650℃，在650℃保温0.5h后，接着以3℃/min的速度升温至1000℃，再以1℃/min的速度升温至1450℃，在1450℃保温1.5h后，再以1.5℃/min的速度降温至1000℃，然后再以4℃/min的速度降温至25℃，即得。
其中，配方按质量百分比计，包括：
电气石25％，陨石2％，砭石7％，麦饭石18％，锗石6％，二氧化硅10％，二氧化钛0.5％，氧化钙2.5％，高岭土11％，三氧化二铁2.5％，氧化锌2.5％，钕2.5％，硼2.5％，以及氧化镁8％。
实施例6
一种水，由实施例1～5中任意一个实施例制得。
实施例7
一种治疗风湿性关节炎的保健品，包括实施例6提供的水。
实施例8
一种治疗痛风病的保健品，包括实施例6提供的水。
实施例9
一种治疗Ⅱ型糖尿病的保健品，包括实施例6提供的水。
试验例1
采用本发明提供的处理水的方法，将待处理的水浸泡设有量子陶瓷的容器中20min进行处理，对待处理的水以及处理后的水，分别核磁共振仪检测水的分子团，采用高斯计检测量子陶瓷的磁性，采用氢元素检测仪检测水的氢气含量，采用红外线扫描仪检测量子陶瓷的红外线，采用ORP值检测仪检测水的负电位，以及采用pH值试剂检测水的pH值。
结果如下：
该量子陶瓷可以持久的产生2高斯的磁力和6～14微米的红外线。使用该量子陶瓷对水进行物理处理，使水中的负氢粒子由0PPM/L提高到1.2PPM/L以上，同时，把原来的由13～16个水分子组成的大分子团水，迅速改变为6～9个水分子组成小分子团水，有效使水的pH值提高至pH为7.5～8.8，使水呈弱碱性，同时把把ORP(电位)值由原来的+180～250改变为-100～220之间，使经处理后的水具有更高的活性，更便于吸收以及保健效果佳。
试验例2
张某某，男，58岁。
患痛风病10年有余，在每天饮用三次本发明提供的经量子陶瓷处理后的水，同时按照之前的服药习惯以及***习惯进行服药、***，一个月以后，病情有所好转，同时减少服药量以及***量，连续饮用三个月以后停止用药，有效缓解症状，饮用半年后痊愈，至今没有复发。
王某，女，39岁。
患风湿性关节炎6年有余。在每天喝三次本发明提供的经量子陶瓷处理后的水，同时按照之前的服药习惯以及***习惯进行服药、***，饮用二个月以后，病情有所好转，减少服药量以及***量，连续饮用三个月，停止服药以及***，连续饮用五个月以后有效缓解，连续饮用8个月以后痊愈，至今没有复发。
杨某某，男，48岁。
患Ⅱ型糖尿病10年有余，患病期间不断服用降糖药。
在每天饮用三次本发明提供的经量子陶瓷处理后的水，同时服用之前服用的降糖药的基础上，病情有所好转，第一个月后降糖药的服用量逐步减少，连续饮用两个月以后，停止服药，连续使用三个月后，有效缓解，饮用一年后血糖恢复正常，至今没有复发。
王某，女，36岁。
患Ⅱ型糖尿病5年有余。期间不断服用降糖药。
在每天喝三次本发明提供的经量子陶瓷处理后的水，同时服用之前服用的降糖药的基础上，病情有所好转，服药15天后降糖药停止服用降糖药，连续饮用两个月以后，病情有所好转，连续饮用9个月以后血糖恢复正常，至今没有复发。
以上所描述的实施例是本发明一部分实施例，而不是全部的实施例。本发明的实施例的详细描述并非旨在限制要求保护的本发明的范围，而是仅仅表示本发明的选定实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。

Claims (10)

1.一种处理水的方法，其特征在于，将水置于设有量子陶瓷的容器中至少10min所得；
所述量子陶瓷为按配方将原料混合后，于氮气气氛下，烧结后冷却所得；
所述配方按照质量百分比计，包括：电气石25％～36％，陨石1％～3％，砭石7％～14％，麦饭石7％～25％，锗石5％～10％，二氧化硅6％～13％，二氧化钛0.5％～3.5％，氧化钙1～5％，高岭土7％～12％，三氧化二铁0.5％～3％，氧化锌0.5％～3％，钕0.5％～3％，硼0.5％～3％，以及氧化镁6％～12％。
2.根据权利要求1所述的处理水的方法，其特征在于，所述配方按照质量百分比计，包括：所述电气石26％～36％，所述陨石1％～3％，所述砭石9％～10％，所述麦饭石8％～22％，所述锗石7％～8％，所述二氧化硅8％～11％，所述二氧化钛1％～2％，所述氧化钙2～3％，所述高岭土9％～10％，所述三氧化二铁1％～3％，所述氧化锌1％～3％，所述钕1％～3％，所述硼1％～3％，以及所述氧化镁8％～10％。
3.根据权利要求1所述的处理水的方法，其特征在于，于烧结前在640～660℃保温0.3～0.7h。
4.根据权利要求3所述的处理水的方法，其特征在于，烧结包括第一阶段与第二阶段，第一阶段为：先以2～3℃/min的速度升温至1000℃，再以0.5～1℃/min的速度升温至1450℃～1500℃。
5.根据权利要求4所述的处理水的方法，其特征在于，第二阶段为在1450℃～1500℃，保温0.5～1.5h。
6.根据权利要求1所述的处理水的方法，其特征在于，冷却包括：先以1～2℃/min的速度降温至1000℃，然后再以3～5℃/min的速度降温至20～35℃。
7.根据权利要求1所述的处理水的方法，其特征在于，于烧结前将所述原料粉碎至410～480目。
8.如权利要求1～7任意一项所述的处理水的方法制得的水。
9.如权利要求8所述的水在保健品中的应用。
10.根据权利要求9所述的应用，所述保健品为治疗风湿性关节炎的保健品、治疗痛风病的保健品或治疗Ⅱ型糖尿病的保健品。
CN201710669945.6A 2017-08-08 2017-08-08 水及处理水的方法及应用 Pending CN107381731A (zh)