CN107337944A - A kind of building coating with Air purification and preparation method thereof - Google Patents
A kind of building coating with Air purification and preparation method thereof Download PDFInfo
- Publication number
- CN107337944A CN107337944A CN201710646734.0A CN201710646734A CN107337944A CN 107337944 A CN107337944 A CN 107337944A CN 201710646734 A CN201710646734 A CN 201710646734A CN 107337944 A CN107337944 A CN 107337944A
- Authority
- CN
- China
- Prior art keywords
- parts
- degrees celsius
- garlic
- air purification
- nandina
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building coating with Air purification, it is made up of following raw material according to parts by weight：6 10 parts of 15 24 parts of polystyrene, 0.5 2 parts of egg white, 36 parts of nano titanium oxide, 6 10 parts of tourmaline, 48 parts of zeolite, 13 parts of flax fiber, 30 45 parts of water silica sol, 28 parts of schmigel, 6 12 parts of phenolic resin, 5 14 parts of nano-ceramic particle, 0.5 1.2 parts of hydrophober, 24 parts of garlic, 4 10 parts of nandina and diatomite.The present invention also disclosed the preparation method of the coating.Finished product prepared by the present invention, cohesive force and water resistance are good, it is less prone to the aging phenomena such as cracking, peeling, peeling, cracking, finished product prepared by the present invention has good sterilization and suppresses action of ultraviolet radiation, more anion can be produced, pernicious gas can be adsorbed, ion exchange can also be carried out, gas is dried and purified.
Description
Technical field
The present invention relates to building coating field, specifically a kind of building coating with Air purification.
Background technology
Covering with paint, lacquer, colour wash, etc. can very well bond with matrix material in body surface and form the material of complete and tough and tensile diaphragm, referred to as apply
Material.Coating and paint are identical concepts.Paint is people's custom title used for a long time, after introducing China, is just utilized always
Building trade.The effect of coating may be summarized to be three aspects：Protective effect, decoration function, specific function effect.The one of coating
As composition：Include film forming matter, color stuffing, solvent and auxiliary agent.
The time that all one's life of people has 70% is spent indoors, and the quality of IAQ is related to the physiology of people
Health.For new interior air quality qualification rate of sprucing up less than 20%, main cause is furniture, ornament materials, materials for wall etc.
Noxious pollutant severe overweight, anion are referred to as air vitamin, have fresh air, eliminate stink and bacteriostasis, mesh
It is preceding that ventilation equipment and anion generator are mainly used to indoor air purification, by filtering, physico-chemical process to being harmful to gas
Body is adsorbed or photocatalysis Decomposition, but this mode energy consumption is big, and use cost is high, and this for people with regard to carrying out room air
Purification brings inconvenience.
The content of the invention
It is an object of the invention to provide a kind of building coating with Air purification, to solve above-mentioned background technology
The problem of middle proposition.
To achieve the above object, the present invention provides following technical scheme：
A kind of building coating with Air purification, is made up of following raw material according to parts by weight：Polystyrene 15-24
Part, egg white 0.5-2 parts, nano titanium oxide 3-6 parts, tourmaline 6-10 parts, zeolite 4-8 parts, flax fiber 1-3 parts, water-based silicon
It is colloidal sol 30-45 parts, schmigel 2-8 parts, phenolic resin 6-12 parts, nano-ceramic particle 5-14 parts, hydrophober 0.5-1.2 parts, big
Garlic 2-4 parts, nandina 4-10 parts and diatomite 6-10 parts.
As the further scheme of the present invention：Egg white uses pale blue or goose albumen.
As the further scheme of the present invention：Hydrophober uses organosilicon, and polystyrene is using discarded polystyrene.
The preparation method of the building coating with Air purification, is comprised the following steps that：
Step 1, by phenolic resin, polystyrene, flax fiber, diatomite, zeolite and tourmaline mix and ball milling,
Ball milling temperature is 40-48 degrees Celsius and crosses 150-210 mesh sieve, obtains the first mixture；
Step 2, smash into garlic to pieces mashed garlic, mashed garlic is placed on under 45-52 degrees Celsius of aerobic environment the 2-3 that ferments
Hour, fermented garlic mud is obtained, then fermented garlic mud is extracted into 4-6 hours, filtering, institute under 35-40 degrees Celsius with extractant
It is garlic extract to obtain filtrate；
Step 3, nandina is broken into the fragment of 0.8-1.5 square centimeters, is put into immersion 40-65 minutes, slow fire in water
30-40 minutes are decocted, first time decoction liquor is poured out and filtered, adds water to submerge the dregs of a decoction, big fire decocts 45-60 minutes, obtains
To second of decoction liquor, merge decoction liquor twice and carry out centrifugal treating, collect supernatant, obtain nandina extract solution；
Step 4, the first mixture, nano titanium oxide, nano-ceramic particle and water silica sol are put into tank diameter
In, side stirring just adds nandina extract solution, egg white and schmigel, in 50-62 degrees Celsius of lower insulated and stirred 5-8 hour, obtains
Suspension；
Step 5, suspension, garlic extract and hydrophober are stirred and are heated to 120-160 degrees Celsius, guarantor
Warm 2-4 hours, 60 degrees Celsius are furnace-cooled to, are incubated 1-2 hours, be again heated to 125-140 degrees Celsius, be incubated 1 hour, taken the photograph with 6
Family name's degree/hour is cooled to normal temperature, i.e. finished product.
As the further scheme of the present invention：The mixing speed of step 4 is 450-600rpm.
Compared with prior art, the beneficial effects of the invention are as follows：Raw material sources of the present invention are extensive, and equipment cost is low, this hair
The finished product of bright preparation, cohesive force and water resistance are good, are less prone to the aging phenomena such as cracking, peeling, peeling, cracking, the present invention
The finished product of preparation has good sterilization and suppresses action of ultraviolet radiation, can produce more anion, can be to pernicious gas
Adsorbed, ion exchange can also be carried out, gas can be dried and be purified, meet the use demand of people.
Embodiment
The technical scheme of this patent is described in more detail with reference to embodiment.
Embodiment 1
A kind of building coating with Air purification, is made up of following raw material according to parts by weight：15 parts of polystyrene,
0.5 part of pale blue, 3 parts of nano titanium oxide, 6 parts of tourmaline, 4 parts of zeolite, 1 part of flax fiber, 30 parts of water silica sol, corundum
6 parts of 2 parts of powder, 6 parts of phenolic resin, 5 parts of nano-ceramic particle, 0.5 part of hydrophober, 2 parts of garlic, 4 parts of nandina and diatomite.
The preparation method of the building coating with Air purification, is comprised the following steps that：
Step 1, by phenolic resin, polystyrene, flax fiber, diatomite, zeolite and tourmaline mix and ball milling,
Ball milling temperature is 42 degrees Celsius and crosses 160 mesh sieve, obtains the first mixture；
Step 2, smash into garlic to pieces mashed garlic, it is small that mashed garlic is placed on into fermentation 2.5 under 45 degrees Celsius of aerobic environment
When, fermented garlic mud is obtained, then fermented garlic mud is extracted 5 hours under 37 degrees Celsius with extractant, filtering, gained filtrate is
For garlic extract；
Step 3, nandina is broken into 0.8 square centimeter of fragment, is put into water and soaks 45 minutes, be cooked by slow fire 32
Minute, first time decoction liquor is poured out and filtered, adds water to submerge the dregs of a decoction, big fire decocts 50 minutes, obtains second of decoction
Liquid, merge decoction liquor twice and carry out centrifugal treating, collect supernatant, obtain nandina extract solution；
Step 4, the first mixture, nano titanium oxide, nano-ceramic particle and water silica sol are put into tank diameter
In, side stirring just adds nandina extract solution, pale blue and schmigel, in 52 degrees Celsius of lower insulated and stirreds 6 hours, is suspended
Liquid；
Step 5, suspension, garlic extract and hydrophober are stirred and are heated to 135 degrees Celsius, insulation 3 is small
When, 60 degrees Celsius are furnace-cooled to, is incubated 1.5 hours, is again heated to 130 degrees Celsius, is incubated 1 hour, is cooled down with 6 degrees Celsius/hour
To normal temperature, i.e. finished product.
Embodiment 2
A kind of building coating with Air purification, is made up of following raw material according to parts by weight：20 parts of polystyrene,
1.5 parts of egg white, 4.5 parts of nano titanium oxide, 8 parts of tourmaline, 6 parts of zeolite, 2 parts of flax fiber, 38 parts of water silica sol, just
Beautiful 5 parts of powder, 9 parts of phenolic resin, 10 parts of nano-ceramic particle, 0.9 part of hydrophober, 3 parts of garlic, 7 parts of nandina and diatomite 9
Part.Hydrophober uses organosilicon, and polystyrene is using discarded polystyrene.
The preparation method of the building coating with Air purification, is comprised the following steps that：
Step 1, by phenolic resin, polystyrene, flax fiber, diatomite, zeolite and tourmaline mix and ball milling,
Ball milling temperature is 45 degrees Celsius and crosses 200 mesh sieve, obtains the first mixture；
Step 2, smash into garlic to pieces mashed garlic, mashed garlic be placed under 49 degrees Celsius of aerobic environment and fermented 3 hours,
Fermented garlic mud is obtained, then fermented garlic mud is extracted 5 hours under 38 degrees Celsius with extractant, filtering, gained filtrate is
Garlic extract；
Step 3, nandina is broken into 1.2 square centimeters of fragment, is put into water and soaks 54 minutes, be cooked by slow fire 36
Minute, first time decoction liquor is poured out and filtered, adds water to submerge the dregs of a decoction, big fire decocts 54 minutes, obtains second of decoction
Liquid, merge decoction liquor twice and carry out centrifugal treating, collect supernatant, obtain nandina extract solution；
Step 4, the first mixture, nano titanium oxide, nano-ceramic particle and water silica sol are put into tank diameter
In, stirred below in 500rpm mixing speed and just add nandina extract solution, egg white and schmigel, be incubated under 58 degrees Celsius
Stirring 7 hours, obtains suspension；
Step 5, suspension, garlic extract and hydrophober are stirred and are heated to 145 degrees Celsius, insulation 3 is small
When, 60 degrees Celsius are furnace-cooled to, is incubated 1.5 hours, is again heated to 130 degrees Celsius, is incubated 1 hour, is cooled down with 6 degrees Celsius/hour
To normal temperature, i.e. finished product.
Embodiment 3
A kind of building coating with Air purification, is made up of following raw material according to parts by weight：24 parts of polystyrene,
2 parts of goose albumen, 6 parts of nano titanium oxide, 10 parts of tourmaline, 8 parts of zeolite, 3 parts of flax fiber, 42 parts of water silica sol, corundum
8 parts of powder, 12 parts of phenolic resin, 14 parts of nano-ceramic particle, 1.2 parts of hydrophober, 4 parts of garlic, 10 parts of nandina and diatomite 10
Part.Hydrophober uses organosilicon, and polystyrene is using discarded polystyrene.
The preparation method of the building coating with Air purification, is comprised the following steps that：
Step 1, by phenolic resin, polystyrene, flax fiber, diatomite, zeolite and tourmaline mix and ball milling,
Ball milling temperature is 46 degrees Celsius and crosses 200 mesh sieve, obtains the first mixture；
Step 2, smash into garlic to pieces mashed garlic, mashed garlic be placed under 50 degrees Celsius of aerobic environment and fermented 3 hours,
Fermented garlic mud is obtained, then fermented garlic mud is extracted 6 hours under 40 degrees Celsius with extractant, filtering, gained filtrate is
Garlic extract；
Step 3, nandina is broken into 1.2 square centimeters of fragment, is put into water and soaks 60 minutes, be cooked by slow fire 38
Minute, first time decoction liquor is poured out and filtered, adds water to submerge the dregs of a decoction, big fire decocts 60 minutes, obtains second of decoction
Liquid, merge decoction liquor twice and carry out centrifugal treating, collect supernatant, obtain nandina extract solution；
Step 4, the first mixture, nano titanium oxide, nano-ceramic particle and water silica sol are put into tank diameter
In, stirred below in 540rpm mixing speed and just add nandina extract solution, egg white and schmigel, be incubated at 60 c
Stirring 7 hours, obtains suspension；
Step 5, suspension, garlic extract and hydrophober are stirred and are heated to 160 degrees Celsius, insulation 4 is small
When, 60 degrees Celsius are furnace-cooled to, is incubated 2 hours, is again heated to 140 degrees Celsius, 1 hour is incubated, is cooled to 6 degrees Celsius/hour
Normal temperature, i.e. finished product.
Nano titanium oxide is safe and non-toxic, under the conditions of existing for Guang Heshui, can to the pernicious gas in air, such as
Formaldehyde, toluene etc. have good degradation, while have very strong bactericidal action, while nano titanium oxide is with very strong
Ultraviolet absorption ability, injury of the ultraviolet to furniture or decoration can be reduced, extend furniture and decoration use the longevity
Life.Tourmaline can produce more anion, have catharsis to air.Zeolite is rack-like structure, and there are many cavitys centre,
Pernicious gas can be adsorbed, ion exchange can also be carried out, gas can be dried and be purified.Flax fiber has
There is good hygroscopicity, can keep indoor dry and comfortable, there is good sterilization and suppress ultraviolet function, can be to room air
Purified.Diatomite has loose structure, can adjust the cohesive force of coating and basal plane so that coating rapid draing.Garlic
The extract solution obtained after fermentation contains allicin, has the bactericidal action of strength.Nandina extract solution, egg white and hydrophober mix
Close, can not only make it that the surface tension of matrix is good, and can be with Skien mistake hydrophobic adsorption layer, water droplet or other materials are not
It can adsorb in coating surface.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be realized in other specific forms.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each embodiment is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that those skilled in the art should for clarity
Using specification as an entirety, the technical solutions in the various embodiments may also be suitably combined, forms those skilled in the art
It is appreciated that other embodiment.
Claims (5)
1. a kind of building coating with Air purification, it is characterised in that be made up of following raw material according to parts by weight：Polyphenyl
Ethene 15-24 parts, egg white 0.5-2 parts, nano titanium oxide 3-6 parts, tourmaline 6-10 parts, zeolite 4-8 parts, flax fiber 1-3
Part, water silica sol 30-45 parts, schmigel 2-8 parts, phenolic resin 6-12 parts, nano-ceramic particle 5-14 parts, hydrophober 0.5-
1.2 parts, garlic 2-4 parts, nandina 4-10 parts and diatomite 6-10 parts.
2. the building coating according to claim 1 with Air purification, it is characterised in that the egg white uses duck
Egg white or goose albumen.
3. the building coating according to claim 1 or 2 with Air purification, it is characterised in that the hydrophober
Using organosilicon, polystyrene is using discarded polystyrene.
4. a kind of preparation method of building coating with Air purification as described in claim 1-3 is any, its feature
It is, comprises the following steps that：
Step 1, by the mixing of phenolic resin, polystyrene, flax fiber, diatomite, zeolite and tourmaline and ball milling, ball milling
Temperature is 40-48 degrees Celsius and crosses 150-210 mesh sieve, obtains the first mixture；
Step 2, smash into garlic to pieces mashed garlic, mashed garlic be placed on to fermentation 2-3 hours under 45-52 degrees Celsius of aerobic environment,
Fermented garlic mud is obtained, then fermented garlic mud is extracted into 4-6 hours, filtering, gained filtrate under 35-40 degrees Celsius with extractant
As garlic extract；
Step 3, nandina is broken into the fragment of 0.8-1.5 square centimeters, is put into immersion 40-65 minutes in water, is cooked by slow fire
30-40 minutes, first time decoction liquor is poured out and filtered, adds water to submerge the dregs of a decoction, big fire decocts 45-60 minutes, obtains the
Secondary decoction liquor, merge decoction liquor twice and carry out centrifugal treating, collect supernatant, obtain nandina extract solution；
Step 4, the first mixture, nano titanium oxide, nano-ceramic particle and water silica sol are put into tank diameter, side
Stirring just adds nandina extract solution, egg white and schmigel, in 50-62 degrees Celsius of lower insulated and stirred 5-8 hour, is suspended
Liquid；
Step 5, suspension, garlic extract and hydrophober are stirred and are heated to 120-160 degrees Celsius, insulation 2-4
Hour, be furnace-cooled to 60 degrees Celsius, be incubated 1-2 hours, be again heated to 125-140 degrees Celsius, be incubated 1 hour, with 6 degrees Celsius/it is small
When be cooled to normal temperature, i.e. finished product.
5. the preparation method of the building coating according to claim 4 with Air purification, it is characterised in that described
The mixing speed of step 4 is 450-600rpm.