CN107298562A - The grey slime paint of the powdered art veins texture inner-outer wall of high durable tear-proof - Google Patents
The grey slime paint of the powdered art veins texture inner-outer wall of high durable tear-proof Download PDFInfo
- Publication number
- CN107298562A CN107298562A CN201710644557.2A CN201710644557A CN107298562A CN 107298562 A CN107298562 A CN 107298562A CN 201710644557 A CN201710644557 A CN 201710644557A CN 107298562 A CN107298562 A CN 107298562A
- Authority
- CN
- China
- Prior art keywords
- wall
- grey
- powdered
- tetrasulfide
- double
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The grey slime paint of the powdered art veins texture inner-outer wall of high durable tear-proof, its raw material includes hydroxypropyl cellulose, wood fibre, redispersible resin-oatmeal, white cement, calcite in powder, quartz sand, titanium dioxide, toner, be especially added with it is double（γ triethoxysilanes propyl group) tetrasulfide, the method have the advantages that：It is not aqueous in this coating, cost of transportation is reduced, transport capacity resource is saved.It is packaged as renewable paper bag, recoverable with low cost.Spy's addition is double（γ triethoxysilanes propyl group) tetrasulfide, improves the physical and mechanical properties of plaster, greatly service life of the extension plaster under exterior wall critical conditions.
Description
Technical field
The present invention relates to paint field, and in particular to powdery art veins texture inner-outer wall ash slime paint and its weatherability.
Background technology
Existing coating for internal and external wall is liquid coating or paste coating.It is disadvantageous in that：
1. aqueous percent 40-60 in coating, and water to be low value be easy to get and it is universal it is pure material, it is unnecessary thus to increase
Logistics transportation cost, causes huge transport power and wastes.
2. due to the presence of moisture, causing the requirement of material package to improve, generally plastics or container made of iron are plus sealing
Inner membrance, with high costs, recovery is difficult, it is impossible to which realization is recycled.
3. because coating exists for liquid, in order to ensure that its stable state need to add a large amount of organic thickening agents, easily grow
Bacterium causes the corruption failure of coating and produces harm to environment and the person.
4. liquid coating is affected by environment big, winter day cold easy freeze thawing, summer easy swell.
5th, coating for wall surface is generally that physics is mixed and stirred, and the attachment force deficiency between dissimilar substances often results in coating shedding.
The content of the invention
The purpose of the present invention is liquid coating or paste coating and bonding force aiming at existing existing coating for internal and external wall
Problem etc., and provide a kind of powdered texture inner-outer wall of high durable grey slime paint.
Its of the invention raw material include hydroxypropyl cellulose, wood fibre, redispersible resin-oatmeal, white cement, dry powder,
Quartz sand, titanium dioxide, converted starch, double-（γ-triethoxysilane propyl group)-tetrasulfide its weight is:
Its weight is:
Hydroxypropyl cellulose 8-12kg wood fibres 1-2kg
Redispersible resin-oatmeal 5-10kg white cements 280-360kg
Calcite in powder 200-400kg quartz sands 180-420kg
Titanium dioxide 0-10kg toners are appropriate
Converted starch 1-2kg
Double-（γ-triethoxysilane propyl group)-tetrasulfide 0.5-10kg.
The method have the advantages that：
1. it is not aqueous in a coating, cost of transportation is reduced, transport capacity resource is saved.
2. a coating packing is renewable paper bag, recoverable with low cost.
3. a coating is difficult to go mouldy, long-acting not bring reliably environment and health of human body to injure.
4. a coating requires low, strong applicability to Conservation environment.
5. a coating application is simple and convenient, effect is attractive in appearance, texture class likelihood mineral varnish, and solidness is higher than true mineral varnish.
6th, spies addition it is double-（γ-triethoxysilane propyl group)-tetrasulfide, this thing is powdered silane coupler, side
Just be added in powder material and be well mixed, add water mixing when, " molecule bridge joint " can be hydrolyzed to form and both enhance powdex
Bond strength between powder filler, is also strengthened, the adhesive force between coating and base material, at the same improve coating water resistance and
Tearing toughness.So as to improve the physical and mechanical properties of plaster, greatly service life of the extension plaster under exterior wall critical conditions.
This formula with the addition of quartz sand, enhance the wear-resistant and crack-resistant function of coating.
The quartz sand of this formula is distributed for different mesh numbers, and random scratch, similar day can be formed when scraping construction by criticizing
Right stone material skin texture lines, and different grain effects can be built by the collocation of quartz sand mesh number, artistic feeling is strong.
Embodiment
It is by following proportioning production technology：
Hydroxypropyl cellulose 8kg wood fibres 1kg
Redispersible resin-oatmeal 10kg white cements 300kg
Calcite in powder 350kg quartz sands 350kg
Titanium dioxide 2kg converted starches 1.5KG
Toner 1kg
Double-（γ-triethoxysilane propyl group)-tetrasulfide 1.2kg.
Raw material is put into mixing and blending machine successively according to formula order, the packaging that can discharge for one hour is at the uniform velocity stirred.
Use example：On December 18th, 2015, inventor produces 15 tons of products by above-mentioned dispensing, for Jingmen BMW vapour
The exterior wall application in car ssss shops, form of construction work is that this product is placed in container in engineering site and adds proper amount of clear water, with hand-held
Formula electric drill stirs into paste homogeneous mixture, and then with batch scraper, uniform drape over one's shoulders is scraped on exterior wall, and curing of coatings after 24 hours is formed
Hard smooth outer wall coating attractive in appearance.By the time check of 2 years, the grey slime paint of this new texture was bright in colour as before, without bright
Aobvious crackle and stripping, hence it is evident that better than the true mineral varnish and the quality of other class coating products of simultaneous construction, be not added with it is double-（γ-three
Ethoxysilane propyl group)-tetrasulfide compared with formula stucco product, its color and luster keep more bright-coloured, peel strength
Significantly improve.Because the invention new product is not only without national standard but also without professional standard, but it is produced with the existing true mineral varnish class in market
Product have something in common in indexs such as use occasion, quality requirements, therefore are pressed by Hubei Province's coating products quality monitoring testing station
True mineral varnish product quality requires detection, meets JG/T24-2000 professional standards.
Claims (1)
1. the grey slime paint of the powdered art veins texture inner-outer wall of high durable tear-proof, it is characterised in that its raw material include it is double-
（γ-triethoxysilane propyl group)-tetrasulfide, hydroxypropyl cellulose, wood fibre, redispersible resin-oatmeal, white cement,
Calcite in powder, quartz sand, titanium dioxide, toner, converted starch,
Its weight is:
Hydroxypropyl cellulose 8-12kg wood fibres 1-2kg
Redispersible resin-oatmeal 5-10kg white cements 280-360kg
Calcite in powder 200-400kg quartz sands 180-420kg
Titanium dioxide 0-10kg converted starches 1-2kg
Double-（γ-triethoxysilane propyl group)-tetrasulfide 1-10 kg
Appropriate toner.