CN107234362A - 一种钢铝异种金属用焊料及其连接工艺 - Google Patents

一种钢铝异种金属用焊料及其连接工艺 Download PDF

Info

Publication number
CN107234362A
CN107234362A CN201710563900.0A CN201710563900A CN107234362A CN 107234362 A CN107234362 A CN 107234362A CN 201710563900 A CN201710563900 A CN 201710563900A CN 107234362 A CN107234362 A CN 107234362A
Authority
CN
China
Prior art keywords
parts
steel
solder
dissimilar metal
metal solder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710563900.0A
Other languages
English (en)
Inventor
胥锴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Technical College of Mechanical and Electrical Engineering
Original Assignee
Anhui Technical College of Mechanical and Electrical Engineering
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Technical College of Mechanical and Electrical Engineering filed Critical Anhui Technical College of Mechanical and Electrical Engineering
Priority to CN201710563900.0A priority Critical patent/CN107234362A/zh
Publication of CN107234362A publication Critical patent/CN107234362A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡5‑15份，铜1‑7份，硅2‑8份，锑1‑5份，铟3‑11份，银1‑7份。本发明具有成本低、操作简单以及加工效果好等优点，且具有焊缝均匀连续，无气孔以及无裂纹缺陷等优点，方便人们的使用。

Description

一种钢铝异种金属用焊料及其连接工艺
技术领域
本发明涉及焊接领域，尤其涉及一种钢铝异种金属用焊料及其连接工艺。
背景技术
目前，随着科学技术的发展，轻量化是汽车车身制造未来发展的必然趋势，钢-铝异种金属连接能发挥两种材料各自的优势，减轻重量，在汽车、航空工业等具有良好的应用前景，然而异种金属的优质高效连接是制约钢-铝复合结构件在工程中推广应用的最大技术瓶颈，人们急需解决这个问题。
发明内容
为了克服上述现有技术的缺陷，本发明的目的是提供一种钢铝异种金属用焊料及其连接工艺。
本发明是采取以下技术方案来实现的：一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡5-15份，铜1-7份，硅2-8份，锑1-5份，铟3-11份，银1-7份。
上述的一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡5-12份，铜1-6份，硅2-6份，锑1-4份，铟3-9份，银1-6份。
上述的一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡10份，铜4份，硅5份，锑3份，铟7份，银4份。
上述的一种钢铝异种金属用焊料的连接工艺，由以下步骤组成：
（1）搭建钢-铝连接工装平台，采用钢铝搭接接头形式，钢板在上，铝板在下，在铝板和钢板之间加入焊料；
（2）在激光功率为1650w，焊接速度为35m/s，离焦量+3.0mm，Ar为保护气体，且Ar流量为20L/min的工艺条件下，对钢板和铝板进行焊接处理。
综上所述本发明具有以下有益效果：本发明具有成本低、操作简单以及加工效果好等优点，且具有焊缝均匀连续，无气孔以及无裂纹缺陷等优点，方便人们的使用。
具体实施方式
一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡5-15份，铜1-7份，硅2-8份，锑1-5份，铟3-11份，银1-7份。
上述的一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡5-12份，铜1-6份，硅2-6份，锑1-4份，铟3-9份，银1-6份。
上述的一种钢铝异种金属用焊料，焊料中各物料的重量份数为：锡10份，铜4份，硅5份，锑3份，铟7份，银4份。
上述的一种钢铝异种金属用焊料的连接工艺，由以下步骤组成：
（1）搭建钢-铝连接工装平台，采用钢铝搭接接头形式，钢板在上，铝板在下，在铝板和钢板之间加入焊料；
（2）在激光功率为1650w，焊接速度为35m/s，离焦量+3.0mm，Ar为保护气体，且Ar流量为20L/min的工艺条件下，对钢板和铝板进行焊接处理。
本发明具有成本低、操作简单以及加工效果好等优点，且具有焊缝均匀连续，无气孔以及无裂纹缺陷等优点，方便人们的使用。
以上所述是本发明的实施例，故凡依本发明申请范围所述的构造、特征及原理所做的等效变化或修饰，均包括于本发明专利申请范围内。

Claims (4)

1.一种钢铝异种金属用焊料，其特征在于，焊料中各物料的重量份数为：锡5-15份，铜1-7份，硅2-8份，锑1-5份，铟3-11份，银1-7份。
2.根据权利要求1所述的一种钢铝异种金属用焊料，其特征在于，焊料中各物料的重量份数为：锡5-12份，铜1-6份，硅2-6份，锑1-4份，铟3-9份，银1-6份。
3.根据权利要求1所述的一种钢铝异种金属用焊料，其特征在于，焊料中各物料的重量份数为：锡10份，铜4份，硅5份，锑3份，铟7份，银4份。
4.根据权利要求1所述的一种钢铝异种金属用焊料的连接工艺，其特征在于，由以下步骤组成：
（1）搭建钢-铝连接工装平台，采用钢铝搭接接头形式，钢板在上，铝板在下，在铝板和钢板之间加入焊料；
（2）在激光功率为1650w，焊接速度为35m/s，离焦量+3.0mm，Ar为保护气体，且Ar流量为20L/min的工艺条件下，对钢板和铝板进行焊接处理。
CN201710563900.0A 2017-07-12 2017-07-12 一种钢铝异种金属用焊料及其连接工艺 Pending CN107234362A (zh)