CN107227111A - A kind of new type water burnt-in sand coating and preparation method thereof - Google Patents
A kind of new type water burnt-in sand coating and preparation method thereof Download PDFInfo
- Publication number
- CN107227111A CN107227111A CN201710593332.9A CN201710593332A CN107227111A CN 107227111 A CN107227111 A CN 107227111A CN 201710593332 A CN201710593332 A CN 201710593332A CN 107227111 A CN107227111 A CN 107227111A
- Authority
- CN
- China
- Prior art keywords
- water
- raw material
- new type
- sand coating
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of new type water burnt-in sand coating, it is made up of that part, B constitute part and C constitutes part and is made A, the A, which constitutes part, includes following raw material：Water, cellulose, aqueous promoter, color stuffing, elastic emulsion, aqueous fluoro-silicone emulsion, modified synthesis sheet silicate and complex thickener, the B, which constitutes part, includes following raw material：Water and modified synthesis sheet silicate, the C, which constitutes part, includes following raw material：Water, coalescents, antifreezing agent, preservative, PH conditioning agents, fluorine silicon class emulsion and complex thickener；This kind of water burnt-in sand coating set water-water coating fidelity and true mineral varnish texture, are mainly used in imitated bush-hammered face granite building material product, the texture both with concavo-convex similar bush-hammered face again can a spray mo(u)lding.
Description
Technical field
Present invention relates particularly to a kind of new type water burnt-in sand coating and preparation method thereof, it is mainly used in imitated bush-hammered face granite
Stone material product.
Background technology
Granite is the dalle that people like, the granite (being referred to as fired slab) especially by high temperature process,
Because the uneven, expansion of being heated of its surface is different, the texture and visual effect of a little concavo-convex similar bush-hammered face can be produced, with dress
Decorations and anti-skidding effect, are favored by many consumers, but its price is costly.Therefore, attempt to study imitated production
Product, produce the visual effect of similar fired slab using traditional water-water coating, but traditional imitative bush-hammered face granite building material,
Need first to spray true mineral varnish, then in its surface sprinkling bag water paint, construct comparatively laborious, quality and effect are all difficult to control, and
And because the granulation ingredient of water-water coating is water and superfine paint filler, make its color finally produced and texture effect not
By force, preferable texture and visual effect are not reached.And water burnt-in sand coating summarizes two kinds of products of water-water coating and true mineral varnish
Advantage, water burnt-in sand coating is compared to water-water coating, and it applies film strength more preferably, and weather resistance is more superior;Water burnt-in sand coating phase
Than in true mineral varnish, its emulsion content is higher, the fidelity of decorative pattern is more rich, full, stone material it is better true to nature.
Therefore, a kind of set water-water coating fidelity of research and development and true mineral varnish texture, are mainly used in imitated bush-hammered face flower hilllock
Rock material product, the texture both with concavo-convex similar bush-hammered face, again can a spray mo(u)lding class containing sand coloured silk point new type water
Burnt-in sand coating is highly significant.
The content of the invention
In view of this, it is an object of the present invention to provide a kind of weatherability, alkali resistance, pliability, self-cleaning and uviolresistance
Can be splendid, and gathered water-water coating fidelity and true mineral varnish texture, it is mainly used in imitated bush-hammered face granite building material product,
Both have concavo-convex similar bush-hammered face texture, again can a spray mo(u)lding class containing sand coloured silk point new type water burnt-in sand coating.
In order to solve the above technical problems, the present invention is adopted the following technical scheme that：
A kind of new type water burnt-in sand coating, is made up of that part, B constitute part and C constitutes part and is made A, and the A, which constitutes part, includes following weight
The raw material of percentage：Water 30-50%, cellulose 1%, aqueous promoter 2-4%, color stuffing 5-10%, elastic emulsion 5-10%, aqueous fluorine
Silicon emulsion 10-20%, modified synthesis sheet silicate 5-10% and complex thickener 1%, the B, which constitutes part, includes following weight hundred
Divide the raw material of ratio：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes the raw material of following percentage by weight：
Water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 60-65% and complex thickener 1%.
Further, a kind of new type water burnt-in sand coating, is made up of that part, B constitute part and C constitutes part and is made, the A A
Composition part includes the raw material of following percentage by weight：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing 5%, elastic emulsion
10%th, aqueous fluoro-silicone emulsion 10%, modified synthesis sheet silicate 9% and complex thickener 1%, the B constitute part including following heavy
Measure the raw material of percentage：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes the original of following percentage by weight
Material：Water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64%, complex thickener 1%.
Further, a kind of new type water burnt-in sand coating, is made up of that part, B constitute part and C constitutes part and is made, the A A
Composition part includes the raw material of following percentage by weight：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing 5%, elastic emulsion 5%,
Aqueous fluoro-silicone emulsion 20%, modified synthesis sheet silicate 9% and complex thickener 1%, the B, which constitutes part, includes following weight hundred
Divide the raw material of ratio：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes the raw material of following percentage by weight：
Water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64% and complex thickener 1%.
Further, the cellulose is modified hydroxyethylcellulosadsorbing ether.
Further, the aqueous promoter include high-molecular type dispersing agent, anion wetting agent, coalescents, bactericide,
Defoamer and antifreezing agent.
Further, the complex thickener is that hydroxyethyl cellulose and special gelatin press 1:1 ratio is mixed.
Further, the color stuffing is titanium dioxide and kaolin.
Further, the modified synthesis sheet silicate presses 8 by bentonite and aluminium-magnesium silicate:2 ratios are mixed.
The invention solves the problems that another technical problem to provide a kind of preparation method of new type water burnt-in sand coating, it is including following
Step：
1）The preparation of A semi-finished product：Water intaking 30-50% is put into mixer, is stirred with 100r/min speed, while adding fiber
Element 1%, with 900r/min Rate Dispersion 5min, then sequentially adds aqueous promoter 2-4% and color stuffing 5-10%, with 1200r/
Min speed disperses at a high speed 10min, adds elastic emulsion 5-10%, aqueous fluoro-silicone emulsion 10-20% and modified synthesis sheet silicon
Hydrochlorate 5-10%, stirs 5min with 200r/min speed, is eventually adding complex thickener 1% to adjust viscosity, you can obtain A half into
Product, it is standby；
2）The preparation of B semi-finished product：Water intaking 90% is put into mixer, is stirred with 100r/min speed, while adding modified synthesis
Sheet silicate 10%, with 1300r/min Rate Dispersion 50min so that modified synthesis sheet silicate is completely dissolved, you can
B semi-finished product are obtained, it is standby；
3）The preparation of C semi-finished product：Water intaking 30% is put into mixer, is stirred with 100r/min speed, while sequentially adding film forming
Auxiliary agent 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1% and fluorine silicon class emulsion 60-65%, with 1200r/min speed 10min, so
5min is stirred with 200r/min speed afterwards, complex thickener 1% is added while stirring, you can obtain C semi-finished product, it is standby；
4）The preparation of finished product：A, by step 1）Obtained A semi-finished product are according to 1-1.2:1 ratio adds sandstone, is tuned into colored base
Material, it is standby；B, the step a base-materials for mixing up color are proportionally added into step 2）In obtained B semi-finished product, then made using vacuum
Grain machine is granulated to it, is obtained color point particles mixture of the size between 1-5mm, is mixed up the base-material and B semi-finished product of color
Ratio is 4.5-5：2.5, it is standby；C, the color point particles mixture that step b is obtained is proportionally added into step 3）Obtained C half into
In product, 10-15min is stirred with 60r/min speed with stirring rod, it is 7 that coloured silk, which puts particles mixture and the ratio of C semi-finished product,:
2.5-3, you can obtain the present invention water burnt-in sand coating.
The beneficial effects of the invention are as follows：The present invention is formulated safety and environmental protection, obtained water burnt-in sand coating antiseepage using water-based
Anti-soil, weatherability, alkali resistance, pliability, self-cleaning and anti-ultraviolet property are all splendid, and have gathered water-water coating fidelity
With true mineral varnish texture, it is mainly used in imitated bush-hammered face granite building material product, the texture both with concavo-convex similar bush-hammered face again may be used
It is a kind of new type water burnt-in sand coating of the coloured silk of class containing the sand point of high emulation with a spray mo(u)lding.
Embodiment
Embodiment 1
A kind of new type water burnt-in sand coating, is made up of that part, B constitute part and C constitutes part and is made A, and the A, which constitutes part, includes following weight
The raw material of percentage：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing 5%, elastic emulsion 10%, aqueous fluoro-silicone emulsion 10%,
Modified synthesis sheet silicate 9% and complex thickener 1%, the B, which constitutes part, includes the raw material of following percentage by weight：Water 90%
With modified synthesis sheet silicate 10%, the C, which constitutes part, includes the raw material of following percentage by weight：Water 30%, coalescents 1%,
Antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64% and complex thickener 1%.
A kind of preparation method of new type water burnt-in sand coating, comprises the following steps：
1）The preparation of A semi-finished product：Water intaking 50% is put into mixer, is stirred with 100r/min speed, while adding cellulose
1%, with 900r/min Rate Dispersion 5min, aqueous promoter 4% and color stuffing 5% are then sequentially added, with 1200r/min speed
Degree disperses at a high speed 10min, adds elastic emulsion 10%, aqueous fluoro-silicone emulsion 10% and modified synthesis sheet silicate 9%, with
200r/min speed stirs 5min, is eventually adding complex thickener 1% to adjust viscosity, you can obtain A semi-finished product, standby；
2）The preparation of B semi-finished product：Water intaking 90% is put into mixer, is stirred with 100r/min speed, while adding modified synthesis
Sheet silicate 10%, with 1300r/min Rate Dispersion 50min so that modified synthesis sheet silicate is completely dissolved, you can
B semi-finished product are obtained, it is standby；
3）The preparation of C semi-finished product：Water intaking 30% is put into mixer, is stirred with 100r/min speed, while sequentially adding film forming
Auxiliary agent 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1% and fluorine silicon class emulsion 64%, with 1200r/min speed 10min, then
5min is stirred with 200r/min speed, complex thickener 1% is added while stirring, you can obtain C semi-finished product, it is standby；
4）The preparation of finished product：A, by step 1）Obtained A semi-finished product are according to 1:1 ratio adds 80-120# snow white stone sands, adjusts
It is standby into colored base-material；B, the step a base-materials for mixing up color are proportionally added into step 2）In obtained B semi-finished product, then
It is granulated using vacuum granulator, color point particle of the size between 1-5mm is obtained, mix up the base-material of color and B half into
The ratio of product is 4.5：2.5, it is standby；C, the color point particles mixture that step b is obtained is proportionally added into step 3）Obtained C half
In finished product, 10-15min is stirred with 60r/min speed with stirring rod, the proportioning of coloured silk point particles mixture and C semi-finished product is 7:
3, you can obtain the present invention water burnt-in sand coating.
The cellulose is modified hydroxyethylcellulosadsorbing ether in the present embodiment.
The aqueous promoter includes high-molecular type dispersing agent, anion wetting agent, coalescents, sterilization in the present embodiment
Agent, defoamer and antifreezing agent, the macromolecule dispersing agent are hydrophobically modified co-poly carboxylic acid salt, and the anion wetting agent is block
Anionic polymer, the coalescents are propandiol butyl ether, and the bactericide is OIT, and the defoamer is poly- two
Methylsiloxane, the antifreezing agent is（Ethylene glycol, 1,2- ethylidene glycol).
The color stuffing is titanium dioxide and kaolin in the present embodiment, and titanium dioxide is selected R706 rutile-types, kaolinite
Soil is CK-400 calcined kaolins, 1250#.
Aqueous fluoro-silicone emulsion described in the present embodiment is fluorine silicon resin emulsion.
The elastic emulsion is mixed by butyl acrylate, ETHYL CYANOACRYLATE and methyl methacrylate in the present embodiment
Form.
The complex thickener is by 1 by hydroxyethyl cellulose and special gelatin in the present embodiment:1 ratio is mixed.
The modified synthesis sheet silicate presses 8 by bentonite and aluminium-magnesium silicate in the present embodiment:2 ratios mix and
Into.
The fluorine silicon class emulsion is fluorine silicone acrylic emulsion in the present embodiment.
Embodiment 2
A kind of new type water burnt-in sand coating, is made up of that part, B constitute part and C constitutes part and is made A, and the A, which constitutes part, includes following weight
The raw material of percentage：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing 5%, elastic emulsion 5%, aqueous fluoro-silicone emulsion 20%, change
Property synthesizing flaky silicate 9% and complex thickener 1%, the B, which constitutes part, includes the raw material of following percentage by weight：The He of water 90%
Modified synthesis sheet silicate 10%, the C, which constitutes part, includes the raw material of following percentage by weight：It is water 30%, coalescents 1%, anti-
Freeze agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64% and complex thickener 1%.
A kind of preparation method of new type water burnt-in sand coating, comprises the following steps：
1）The preparation of A semi-finished product：Water intaking 50% is put into mixer, is stirred with 100r/min speed, while adding cellulose
1%, with 900r/min Rate Dispersion 5min, aqueous promoter 4% and color stuffing 5% are then sequentially added, with 1200r/min speed
Degree disperses at a high speed 10min, adds elastic emulsion 5%, aqueous fluoro-silicone emulsion 20% and modified synthesis sheet silicate 9%, with
200r/min speed stirs 5min, is eventually adding complex thickener 1% to adjust viscosity, you can obtain A semi-finished product, standby；
2）The preparation of B semi-finished product：Water intaking 90% is put into mixer, is stirred with 100r/min speed, while adding modified synthesis
Sheet silicate 10%, with 1300r/min Rate Dispersion 50min so that modified synthesis sheet silicate is completely dissolved, you can
B semi-finished product are obtained, it is standby；
3）The preparation of C semi-finished product：Water intaking 30% is put into mixer, is stirred with 100r/min speed, while sequentially adding film forming
Auxiliary agent 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1% and fluorine silicon class emulsion 64%, with 1200r/min speed 10min, then
5min is stirred with 200r/min speed, complex thickener 1% is added while stirring, you can obtain C semi-finished product, it is standby；
4）The preparation of finished product：A, by step 1）Obtained A semi-finished product are according to 1.2:1 ratio adds 80-120# snow white stone sands
Pure 100# fine sands are mixed, colored base-material is tuned into, it is standby；B, the step a base-materials for mixing up color are proportionally added into step 2）System
In the B semi-finished product obtained, then it is granulated using vacuum granulator, color point particle of the size between 1-5mm is obtained and mixes
Compound, the ratio of the base-material and B semi-finished product that mix up color is 5：2.5, it is standby；C, the color point particles mixture for obtaining step b by
Ratio adds step 3）In obtained C semi-finished product, 10-15min is stirred with 60r/min speed with stirring rod, coloured silk point particle is mixed
The proportioning of compound and C semi-finished product is 7.5:2.5, you can obtain the present invention water burnt-in sand coating.
The cellulose is modified hydroxyethylcellulosadsorbing ether in the present embodiment.
The aqueous promoter includes high-molecular type dispersing agent, anion wetting agent, coalescents, sterilization in the present embodiment
Agent, defoamer and antifreezing agent, the macromolecule dispersing agent are hydrophobically modified co-poly carboxylic acid salt, and the anion wetting agent is block
Anionic polymer, the coalescents are propandiol butyl ether, and the bactericide is OIT, and the defoamer is poly- two
Methylsiloxane, the antifreezing agent is（Ethylene glycol, 1,2- ethylidene glycol).
The color stuffing is titanium dioxide and kaolin in the present embodiment, and titanium dioxide is selected R706 rutile-types, kaolinite
Soil is CK-400 calcined kaolins, 1250#.
Aqueous fluoro-silicone emulsion described in the present embodiment is fluorine silicon resin emulsion.
The elastic emulsion is mixed by butyl acrylate, ETHYL CYANOACRYLATE and methyl methacrylate in the present embodiment
Form.
The complex thickener is by 1 by hydroxyethyl cellulose and special gelatin in the present embodiment:1 ratio is mixed.
The modified synthesis sheet silicate presses 8 by bentonite and aluminium-magnesium silicate in the present embodiment:2 ratios mix and
Into.
The fluorine silicon class emulsion is fluorine silicone acrylic emulsion in the present embodiment.
Experimental example
Experimental subjects：Water sand coating material made from water sand coating material made from the embodiment of the present invention 1 and embodiment 2.
Experimental method：With reference to HG/T4343-2012《Aqueous colorful building coating》Above-mentioned two groups of coating is tested.
Table one is the test record for two groups of water sand coating material that the embodiment of the present invention is obtained：
Table one
Pass through table one, it can be seen that weatherability, alkali resistance, pliability, self-cleaning and the uvioresistant of water sand coating material of the present invention
Performance is all splendid, passes through the contrast of Example 1 and Example 2 of the present invention, it can be seen that the fluorine silicon breast selected by water burnt-in sand coating
Liquid, binder ratio, sand mold size, directly represent the combination properties such as high durable, the resistance to soiling of final finished, present example 2
Obtained color point particle is more solid, and color point hardness is high, and can not finish.
The beneficial effects of the invention are as follows：The present invention is formulated safety and environmental protection, obtained water burnt-in sand coating antiseepage using water-based
Anti-soil, weatherability, alkali resistance, pliability, self-cleaning and anti-ultraviolet property are all splendid, and have gathered water-water coating fidelity
With true mineral varnish texture, it is mainly used in imitated bush-hammered face granite building material product, the texture both with concavo-convex similar bush-hammered face again may be used
It is a kind of new type water burnt-in sand coating of the coloured silk of class containing the sand point of high emulation with a spray mo(u)lding.
Claims (8)
1. a kind of new type water burnt-in sand coating, it is characterised in that：It is made up of that part, B constitute part and C constitutes part and is made A, the A compositions
Part includes the raw material of following percentage by weight：Water 30-50%, cellulose 1%, aqueous promoter 2-4%, color stuffing 5-10%, elasticity breast
Liquid 5-10%, aqueous fluoro-silicone emulsion 10-20%, modified synthesis sheet silicate 5-10% and complex thickener 1%, the B constitute part
Include the raw material of following percentage by weight：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes following weight
The raw material of percentage：Water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 60-65% and
Complex thickener 1%.
2. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：It is made up of that part, B constitute part and C is constituted A
Part is made, and the A, which constitutes part, includes the raw material of following percentage by weight：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing
5%th, elastic emulsion 10%, aqueous fluoro-silicone emulsion 10%, modified synthesis sheet silicate 9% and complex thickener 1%, the B constitute part
Include the raw material of following percentage by weight：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes following weight
The raw material of percentage：Water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64% and multiple
Close thickener 1%.
3. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：It is made up of that part, B constitute part and C is constituted A
Part is made, and the A, which constitutes part, includes the raw material of following percentage by weight：Water 50%, cellulose 1%, aqueous promoter 4%, color stuffing
5%th, elastic emulsion 5%, aqueous fluoro-silicone emulsion 20%, modified synthesis sheet silicate 9% and complex thickener 1%, the B constitute part
Include the raw material of following percentage by weight：Water 90% and modified synthesis sheet silicate 10%, the C, which constitutes part, includes following weight
The raw material of percentage：It is water 30%, coalescents 1%, antifreezing agent 2%, preservative 1%, PH conditioning agents 1%, fluorine silicon class emulsion 64%, compound
Thickener 1%.
4. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：The cellulose is that modified hydroxyethyl is fine
The plain ether of dimension.
5. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：The aqueous promoter includes polymer electrolyte
Dispersant, anion wetting agent, coalescents, bactericide, defoamer and antifreezing agent.
6. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：The complex thickener is that ethoxy is fine
Dimension element and special gelatin press 1:1 ratio is mixed.
7. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：The color stuffing is titanium dioxide and kaolinite
Soil.
8. a kind of new type water burnt-in sand coating as claimed in claim 1, it is characterised in that：The modified synthesis sheet silicate by
Bentonite and aluminium-magnesium silicate press 8:2 ratios are mixed.