CN1072159A - 一种低温煅烧水泥熟料工艺 - Google Patents

一种低温煅烧水泥熟料工艺 Download PDF

Info

Publication number
CN1072159A
CN1072159A CN92111987A CN92111987A CN1072159A CN 1072159 A CN1072159 A CN 1072159A CN 92111987 A CN92111987 A CN 92111987A CN 92111987 A CN92111987 A CN 92111987A CN 1072159 A CN1072159 A CN 1072159A
Authority
CN
China
Prior art keywords
low
slag
calcining
temperature
cement clinker
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN92111987A
Other languages
English (en)
Other versions
CN1041195C (zh
Inventor
方荣利
卢中远
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SICHUAN BUILDING MATERIAL INDUSTRY COLLEGE
Original Assignee
SICHUAN BUILDING MATERIAL INDUSTRY COLLEGE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SICHUAN BUILDING MATERIAL INDUSTRY COLLEGE filed Critical SICHUAN BUILDING MATERIAL INDUSTRY COLLEGE
Priority to CN92111987A priority Critical patent/CN1041195C/zh
Publication of CN1072159A publication Critical patent/CN1072159A/zh
Application granted granted Critical
Publication of CN1041195C publication Critical patent/CN1041195C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

一种低温煅烧水泥熟料工艺，包括将20—60％ 石灰石，30—71％粉煤灰、煤矸石、钢渣，4—7％铬渣 和1—3％磷石膏或3—10％黄磷渣，以及适量煤混 合磨细；在沸腾炉等水泥煅烧设备中，于940— 1100℃温度下煅烧20—40分钟。本发明以工业废 渣为主要原料，使难处理的铬渣得到利用且毒性大大 降低，能耗低并可将热能综合利用，生产成本低，具有 显著的社会效益和经济效益。

Description

本发明涉及一种水泥的制造，特别涉及一种以工业废渣为主要原料的低温煅烧水泥熟料工艺。
现有的煅烧硅酸盐水泥熟料一般是以粘土、石灰石为主要原料，以石膏和萤石为复合矿化剂，煅烧温度为1350-1450℃，煅烧设备采用回转窑或立窑;典型的水泥熟料化学组成如附表1所示，主要矿物为C3S、C2S、C3A、C4AF等。由于煅烧温度高，消耗热能多，产品成本高。
本发明的目的是提供一种以工业废渣为主要原料、成本低廉、产品质量好的低温煅烧水泥熟料工艺。
本发明的内容是：一种低温煅烧水泥熟料工艺，其特征是包括：
a、将（重量%）20-60%石灰石，
30-71%粉煤灰、煤矸石、钢渣、劣质煤中的一种或多种的混合物，
4-7%铬渣和1-3%磷石膏或3-10%黄磷渣组成的复合矿化剂，
以及适量煤混合磨细;
b、在沸腾炉、流化床或其他水泥煅烧设备中，在温度为940-1100℃下煅烧20-40分钟;
c、冷却。
本发明内容中所述的煅烧温度较佳的是980-1100℃。
本发明内容中所述的复合矿化剂的较佳组成为：5%铬渣和1.5%磷石膏或7%黄磷渣。
与现有技术相比，本发明具有下列特点：
（1）不用粘土，使用难以处理的工业废渣-粉煤灰，煤矸石、钢渣等为主要原材料，工业废渣用量大，有利于保护环境，社会经济效益显著;
（2）采用铬渣和磷石膏或黄磷渣作为复合矿化剂，铬渣掺入量可达7%，煅烧过程中铬被还原（Cr+6→Cr+3），毒性大大降低，除毒彻底，为难处理的铬渣的利用开辟了广阔的道路，具有十分显著的环境社会效益和经济效益;
（3）煅烧温度低，仅为940-1100℃，能耗显著降低，生产成本低;
（4）使用沸腾炉作为煅烧设备，可以同时发电或供热，热能得到充分利用;
（5）本发明生产的水泥熟料，主要矿物为活性的β-C2S、C4AF、C12A7、CA等，其28天强度可超过325＃水泥标号;该水泥可广泛用于建筑工程、水泥制品、农村水利建设中。
下面通过实施例对本发明作进一步说明：
实施例1：一种低温煅烧水泥熟料工艺，将重量组成为37.6%粉煤灰、57%石灰石、4%铬渣、1.4%磷石膏的各组份，加入适量煤，混合磨细至过0.08mm筛筛余不大于10%，吹入沸腾炉内燃烧，热态流化速度为3.1米/钞，流化床温度控制1050℃，生料在炉内煅烧时间不小于20分钟，将煅烧好的熟料迅速冷却，磨细至通过0.08mm筛筛余小于6%，并按标准方法对煅烧样品进行物理力学性能测定。煅烧好的低温水泥熟热料安定性合格，抗蚀等性能好，28天抗压强度达到37.8MPa。
实施例2：一种低温煅烧水泥熟料工艺。将重量组成为41.8%煤矸石，52.5%石灰石、4.7%铬渣、1.0%磷石膏的各组份称量，加入适量煤，混合磨细至通过0.08mm筛筛余不大于10%，吹入沸腾炉内燃烧，热态流化速度为2.9米/钞，流化床温度控制1020℃，生料在炉内煅烧时间不小于20分钟，将煅烧好的熟料迅速冷却，磨细至通过0.08mm筛筛余小于6%，并按标准方法进行物理力学性能测定。煅烧好的低温水泥熟料安定性合格，抗蚀等性能好，28天抗压强度可达到36.8MPa。
实施例3：一种低温煅烧水泥熟料工艺。将重量组成为50%钢渣、20.5%煤矸石、23%石灰石、5%铬渣、1.5%磷石膏的各组份称量，加入适量煤，混合磨细至通过0.08mm筛筛余不大于10%，吹入沸腾炉内燃烧，热态流化速度为3.2米/钞，流化床温度控制980℃，生料在炉内煅烧不小于20分钟，将煅烧好的熟料迅速冷却，磨细至通过0.08mm筛筛余小于6%，并按标准方法进行物理力学性能测定。煅烧好的低温水泥熟料安定性合格，抗蚀等性能好，28天抗压强度可达到36.4MPa。
实施例4：一种低温煅烧水泥熟料工艺。取重量组成为39.5%煤矸石、49.5石灰石、5%铬渣、6%黄磷渣的各组份，加入适量煤，混合磨细至通过0.08mm筛筛余不大于10%，吹入沸腾炉内燃烧，热态流化速度为3.1米/钞，流化床温度控制在960℃，生料在炉内煅烧不少于20分钟，将煅烧好的熟料迅速冷却，磨细至通过0.08mm筛筛余小于6%，并按标准方法进行物理力学性能测定。煅烧好的低温水泥熟料安定性合格，抗蚀等性能好，28天抗压强度可达到35.4MPa。
附表1：典型的硅酸盐水泥熟料化学组成
试样 SiO2 CaO Al2O3 Fe2O3 MgO SO3 烧失量
C 19.90 63.38 6.36 4.37 1.93 2.20 1.31
D 21.29 63.63 5.92 3.82 1.29 1.75 1.32
附表2：本发明低温水泥熟料化学组成
试样 SiO2 CaO Al2O3 Fe2O3 MgO SO3 烧失量
A 28.1 50.9 8.5 3.4 3.3 3.1 1.41
B 29.7 49.8 9.1 3.2 3.9 2.3 1.52

Claims (3)

1、一种低温煅烧水泥熟料工艺，其特征是包括：
a、将(重量%)20-60%石灰石，
30-71%粉煤灰、煤矸石、钢渣、劣质煤中的一种或多种的混合物。
4-7%铬渣和1-3%磷石膏或3-10%黄磷渣组成的复合矿化剂。
以及适量煤混合磨细；
b、在沸腾炉、流化床或其他水泥煅烧设备中，在温度为940-1100℃下煅烧20-40分钟；
c、冷却。
2、按权利要求1所述的低温煅烧水泥熟料工艺，其特征是较佳的煅烧温度为980-1100℃。
3、按权利要求1或2所述的低温煅烧水泥熟料工艺，其特征是复合矿化剂的较佳组成为：5%铬渣和1.5%磷石膏或7%黄磷渣。
CN92111987A 1992-11-15 1992-11-15 一种低温煅烧水泥熟料工艺 Expired - Fee Related CN1041195C (zh)