CN107189532A - A kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method - Google Patents
A kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method Download PDFInfo
- Publication number
- CN107189532A CN107189532A CN201710352097.6A CN201710352097A CN107189532A CN 107189532 A CN107189532 A CN 107189532A CN 201710352097 A CN201710352097 A CN 201710352097A CN 107189532 A CN107189532 A CN 107189532A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde
- graphene
- wallpaper
- wall paper
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to decorative materials technology, it is related to a kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method, this method includes:(1) prepare and remove aldehyde coating or aqueous, environmental protective ink wallpaper coating;(2) base material is subjected to the pre-heat treatment;(3) wallpaper coating is coated on the base material after preheated processing, and heats, is embossed graphene formaldehyde-removing wallpaper, wall paper is made.It is of the invention not contain the organic pollutions such as formaldehyde, benzene compared with common wallpaper, wall paper, and formaldehyde can be fundamentally removed, meanwhile, the addition of graphene can also improve the decomposing, purifying efficiency of harmful substance and the anti-wear performance of wallpaper coating.
Description
Technical field
The invention belongs to decorative materials technology, it is related to a kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method.
Background technology
Wallpaper is a kind of quite extensive house decorative material of application.Because wallpaper has, color is various, pattern is abundant, person of outstanding talent
The characteristics of a variety of other house decorative materials institutes such as magnificent style, safety and environmental protection, easy construction, affordable are incomparable, therefore
The developed countries and regions such as America and Europe, Southeast Asia, Japan obtain considerable degree of popularization.Because with certain intensity, attractive in appearance
Appearance and good clean-up performance, are widely used in house, office, interior decoration of hotel etc..
The main raw material(s) for making wallpaper or wall paper at present is fluoropolymer resin, and the inside is contained in higher formaldehyde, finishing
Also higher formaldehyde is contained in terms of the bonding of wallpaper in glue used.Therefore, there has been proposed various methods, example
Such as the sprinkling of plant absorption method, cleanser, charcoal absorption remove free formaldehyde.Although but the above method can be cleared up
Formaldehyde, but many deficiencies are still suffered from, for example, plant absorption method purification efficiency is limited, take effect too slow, DeGrain;Cleanser
Spray effect is not lasting, and some cleansers are to cover smell, can not eliminate formaldehyde;The absorption of activated carbon PARA FORMALDEHYDE PRILLS(91,95) is made
With it is obvious that still according to the of different sizes of space, the amount for placing activated carbon is also different.In addition, charcoal absorption is to one
Determine to need to be changed after degree.Although the effect of activated carbon is pretty good, can not fully erased sky as other method
Formaldehyde in gas.A kind of formaldehyde-removing wallpaper, wall paper how are made, makes itself to be free of formaldehyde, and the function with decomposing formaldehyde,
And it is significant to meet home safety, environmental protection, comfortable performance simultaneously.
The content of the invention
The problems such as present invention is for formaldehyde pollution in above-mentioned hard-cover house fitting-up and larger summer in winter indoor/outdoor temperature-difference, is carried
A kind of graphene formaldehyde-removing wallpaper, wall paper and preparation method are supplied.
In order to achieve the above object, the technical solution adopted by the present invention is,
A kind of graphene formaldehyde-removing wallpaper and wall paper, the wallpaper and wall paper are by graphene except aldehyde coating or aqueous, environmental protective oil
Coating prepared by ink is prepared from;
The graphene specifically includes following number by weight except aldehyde coating:
The anti-Formaldehyde as Additives is the mixture of graphene and nano titanium oxide, and its mass ratio is 1:10-10:1;
The aqueous, environmental protective ink specifically includes following number by weight:
Preferably, the multifunctional assistant is multifunction amine analog assistant;The dispersant is calgon and 12
Sodium alkyl sulfate is according to mass ratio 1:The mixture of 2 compositions;The waterproofing agent is organic silicon hydrophobic waterproofing agent;The defoamer is
The one or two of mineral hydrocarbon defoamer, non-ionic alkyl copolymer defoamer;The thickener is association
At least one of type alkali swollen thickener or polyurethane thickener;The water-base resin is acrylic copolymer, pure third polymerization
Any one or a few in thing, phenylpropyl alcohol, polyurethane, organosilicon, polyflon;Color stuffing slurry is titanium dioxide,
At least one of powdered whiting slurry, kaolin, talcum powder, ultra-fine calcite in powder, diatomite, barium sulfate, mica powder material
Add the slurry like material for disperseing stirring in wetting and dispersing auxiliary agent and with deionized water.
Preferably, the water-soluble resin be acrylic copolymer, pure third polymer, phenylpropyl alcohol, polyurethane, organosilicon,
One or more in polyflon;The graining paste is the one or more in yellow, red, blue, three kinds of colors, and will
It adds wetting and dispersing auxiliary agent and the slurry like material of the scattered stirring of deionized water, and the pigment that the yellow uitramarine slurry is selected is
Benzidine yellow, the pigment that red pigment slurry is selected is fuchsin, and the pigment that blue pigment slurry is selected is phthalocyanine blue;The auxiliary agent is increasing
Thick dose, surfactant, defoamer, anti-Formaldehyde as Additives by weight be 1:2:1:1 mixing composition, the anti-Formaldehyde as Additives is stone
The mixture of black alkene and nano titanium oxide, its mass ratio is 1:10-10:1.
A kind of method for preparing graphene formaldehyde-removing wallpaper and wall paper, specifically includes following steps:
(1) the wallpaper coating except aldehyde coating or aqueous, environmental protective ink is prepared;
(2) base material is subjected to the pre-heat treatment;
(3) wallpaper coating is coated on the base material after preheated processing, and heats, is embossed graphene formaldehyde-removing wallpaper is made
Or wall paper.
Preferably, the base material includes any one in paper substrate, PVC, non-woven fabrics, fabric, Bu Ji, goldleaf.
Preferably, the pre-heat treatment includes the first the pre-heat treatment and the second the pre-heat treatment successively.
Preferably, first the pre-heat treatment meets following condition:Initial temperature is 20-25 DEG C, and heating rate is 1-5
DEG C/min, the heating-up time is 1-3min;The heating rate of second the pre-heat treatment is 6-10 DEG C/min, and the heating-up time is 1-
5min。
Preferably, the heating-up temperature is 110-130 DEG C, the heat time is 30-50min.
Compared with prior art, advantages and positive effects of the present invention are,
The present invention carries out secondary preheating by first preparing except aldehyde coating and aqueous, environmental protective ink wallpaper coating, and to base material
Processing, finally wallpaper coating is coated on the base material after preheated processing, and heat, be embossed be made graphene formaldehyde-removing wallpaper,
Wall paper.In the process, the composition that the anti-Formaldehyde as Additives added in wallpaper coating contains graphene, matches somebody with somebody with traditional wallpaper coating
Side is compared, and be make use of the light transmittance of graphene, is made it as photocatalysis carrier, greatly improve the efficiency of light-catalyzed reaction.Meanwhile,
Graphene will be added in Nano titanium dioxide, add visible-light absorptivity, and improve electronics conduction efficiency.Furthermore, stone
Effectively being combined for black alkene and Nano titanium dioxide, not only improves dispersiveness of the photo-catalytic nano particle in graphenic surface,
And by reducing the compound of photo-generate electron-hole, improve the photocatalytic activity of photocatalyst.At the same time, due to energy band knot
The adjustment of structure, graphene will also play the effect of sensitising agent, the absorption region of photocatalyst is extended to visible region, effectively carries
High utilization rate of the photocatalyst to sunshine.Interaction between these molecules and carrier both increases material in air
The decomposition efficiency and detergent power of free formaldehyde, and the addition of graphene, also add the anti-wear performance of wallpaper coating.This
Outside, the pre-heat treatment that base material is carried out can be reduced or avoid that base material occurs in heating process after coating wallpaper coating should
Become, so as to improve obtained graphene formaldehyde-removing wallpaper, the mechanical property of wall paper and except aldehyde effect, and thing in a heated condition
Interaction between material can effectively improve obtained graphene formaldehyde-removing wallpaper, the toughness and tensile strength of wall paper.This method is
A kind of with low cost, mild condition, environmental protection and method simple to operate, obtained graphene formaldehyde-removing wallpaper, wall paper have
Except aldehyde, the effect of air is purified, it is and environment friendly and pollution-free.
Embodiment
In order to be more clearly understood that the above objects, features and advantages of the present invention, with reference to embodiment to this hair
It is bright to be described further.It should be noted that in the case where not conflicting, the feature in embodiments herein and embodiment can
To be mutually combined.
Many details are elaborated in the following description to facilitate a thorough understanding of the present invention, still, the present invention may be used also
To be implemented using other modes described here are different from, therefore, the present invention is not limited to the specific of specification described below
The limitation of embodiment.
Embodiment 1
(1) by 5 parts of deionized water, 0.3 part of multifunction amine auxiliary agent (AMP-95), 42.5 parts of water-based acrylic resin, face is filled out
50 parts of slurry, (calgon and lauryl sodium sulfate mass ratio are 1 to dispersant:2) 0.5 part, 0.5 part of waterproofing agent, it is non-from
0.3 part of subtype alkyl copolymer defoamer (CHE COAT DF9000), association type alkali swollen thickener (CHE COATVT-183)
0.1 part, 0.1 part of polyurethane thickener (CHE COAT VT-903), 0.5 part of bactericide (Clariant HF-1), anti-Formaldehyde as Additives
(nano TiO 2 and graphene ratio are 2:8) 0.2 part is mixed to prepare except aldehyde coating wallpaper coating;
(2) paper is heated up 3min to carry out at the first preheating under 20 DEG C of initial temperature with 2 DEG C/min heating rate
Reason;Then heat up 2min to carry out the second the pre-heat treatment with 7 DEG C/min heating rate;
(3) it will be coated on the paper after preheated processing, and heated at a temperature of 110 DEG C except aldehyde coating wallpaper coating
Graphene formaldehyde-removing wallpaper 1 is made in 35min, embossing.
Embodiment 2
(1) by 8 parts of deionized water, 0.2 part of multifunction amine auxiliary agent (AMP-95), 49.5 parts of water-based acrylic resin, face is filled out
40 parts of slurry, (calgon and lauryl sodium sulfate mass ratio are 1 to dispersant:2) 0.3 part, 0.8 part of waterproofing agent, it is non-from
0.2 part of subtype alkyl copolymer defoamer (CHE COAT DF9000), association type alkali swollen thickener (CHE COATVT-183)
0.1 part, 0.2 part of polyurethane thickener (CHE COAT VT-903), 0.5 part of bactericide (Clariant HF-1), anti-Formaldehyde as Additives
(nano TiO 2 and graphene ratio are 5:5) 0.2 part is mixed to prepare except aldehyde coating wallpaper coating;
(2) by non-woven fabrics under 25 DEG C of initial temperature it is pre- to carry out first with the 3 DEG C/min heating rate 2min that heats up
Heat treatment;Then heat up 3min to carry out the second the pre-heat treatment with 10 DEG C/min heating rate;
(3) it will be coated on the non-woven fabrics after preheated processing, and add at a temperature of 120 DEG C except aldehyde coating wallpaper coating
Graphene is made except aldehyde wall paper 2 in hot 30min, embossing.
Embodiment 3
(3) by 10.5 parts of deionized water, 45 parts of water-based acrylic resin, 42 parts of phthalocyanine blue graining paste, defoamer (CHE
COATDF9000) 0.5 part, 0.5 part of polyurethane thickener (CHE COATVT-903), 1 part of water soluble anion fluorine carbon, anti-formaldehyde
(nano TiO 2 and graphene ratio are 8 to auxiliary agent:2) 0.5 part is mixed to prepare aqueous, environmental protective ink wallpaper coating;
(2) fabric is heated up 3min to carry out the first preheating under 25 DEG C of initial temperature with 1 DEG C/min heating rate
Processing;Then heat up 5min to carry out the second the pre-heat treatment with 8 DEG C/min heating rate;
(3) aqueous, environmental protective ink wallpaper coating is coated on the fabric after preheated processing, and at a temperature of 125 DEG C
Graphene is made except aldehyde wall paper 3 in heating 40min, embossing.
The effect of graphene formaldehyde-removing wallpaper, wall paper to embodiment 1-3 offers enters detection, wherein purifying formaldehyde rate test side
Method performs JC/T1074-2008《Function of purifying indoor air coating material purification function》Defined Ι classes requirement is tested.
Table 1:The graphene formaldehyde-removing wallpaper of embodiment 1-3 offers, the testing result of wall paper:
The above described is only a preferred embodiment of the present invention, being not the limitation for making other forms to the present invention, appoint
What those skilled in the art changed or be modified as possibly also with the technology contents of the disclosure above equivalent variations etc.
Imitate embodiment and be applied to other fields, but every without departing from technical solution of the present invention content, the technical spirit according to the present invention
Any simple modification, equivalent variations and the remodeling made to above example, still fall within the protection domain of technical solution of the present invention.
Claims (8)
1. a kind of graphene formaldehyde-removing wallpaper and wall paper, it is characterised in that the wallpaper and wall paper by graphene except aldehyde coating or
Coating prepared by aqueous, environmental protective ink is prepared from;
The graphene specifically includes following number by weight except aldehyde coating:
The anti-Formaldehyde as Additives is the mixture of graphene and nano titanium oxide, and its mass ratio is 1:10-10:1;
The aqueous, environmental protective ink specifically includes following number by weight:
2. a kind of graphene formaldehyde-removing wallpaper according to claim 1 and wall paper, it is characterised in that the multifunctional assistant is
Multifunction amine analog assistant;The dispersant is calgon and lauryl sodium sulfate according to mass ratio 1:The mixing of 2 compositions
Thing;The waterproofing agent is organic silicon hydrophobic waterproofing agent;The defoamer is mineral hydrocarbon defoamer, non-ionic alkane
The one or two of base co-polymer defoamer;The thickener be in association type alkali swollen thickener or polyurethane thickener extremely
Few one kind;The water-base resin is acrylic copolymer, pure third polymer, phenylpropyl alcohol, polyurethane, organosilicon, polytetrafluoroethylene (PTFE) tree
Any one or a few in fat;The color stuffing slurry is titanium dioxide, powdered whiting slurry, kaolin, talcum powder, ultra-fine side solution
At least one of stone flour, diatomite, barium sulfate, mica powder material adds in wetting and dispersing auxiliary agent and disperses to stir with deionized water
The slurry like material mixed.
3. a kind of graphene formaldehyde-removing wallpaper according to claim 1 and wall paper, it is characterised in that the water-soluble resin is
One or more in acrylic copolymer, pure third polymer, phenylpropyl alcohol, polyurethane, organosilicon, polyflon;It is described
Graining paste is the one or more in yellow, red, blue, three kinds of colors, and it is scattered with deionized water to be added into wetting and dispersing auxiliary agent
The slurry like material of stirring, the pigment that the yellow uitramarine slurry is selected is benzidine yellow, and the pigment that red pigment slurry is selected is
Fuchsin, the pigment that blue pigment slurry is selected is phthalocyanine blue;The auxiliary agent is thickener, surfactant, defoamer, anti-formaldehyde are helped
Agent is 1 by weight:2:1:1 mixing composition, the anti-Formaldehyde as Additives is the mixture of graphene and nano titanium oxide, its matter
Amount is than being 1:10-10:1.
4. a kind of method of a kind of graphene formaldehyde-removing wallpaper prepared described in Claims 2 or 3 and wall paper, it is characterised in that
Specifically include following steps:
(1) the wallpaper coating except aldehyde coating or aqueous, environmental protective ink is prepared;
(2) base material is subjected to the pre-heat treatment;
(3) wallpaper coating is coated on the base material after preheated processing, and heats, is embossed graphene formaldehyde-removing wallpaper or wall is made
Cloth.
5. a kind of profit for preparing according to claim 4 requires a kind of graphene formaldehyde-removing wallpaper described in 2 or 3 and wall paper
Method, it is characterised in that:The base material includes any one in paper substrate, PVC, non-woven fabrics, fabric, Bu Ji, goldleaf.
6. a kind of profit for preparing according to claim 4 requires a kind of graphene formaldehyde-removing wallpaper described in 2 or 3 and wall paper
Method, it is characterised in that:The pre-heat treatment includes the first the pre-heat treatment and the second the pre-heat treatment successively.
7. a kind of profit for preparing according to claim 4 requires a kind of graphene formaldehyde-removing wallpaper described in 2 or 3 and wall paper
Method, it is characterised in that:First the pre-heat treatment meets following condition:Initial temperature is 20-25 DEG C, and heating rate is 1-5
DEG C/min, the heating-up time is 1-3min;The heating rate of second the pre-heat treatment is 6-10 DEG C/min, and the heating-up time is 1-
5min。
8. a kind of profit for preparing according to claim 4 requires a kind of graphene formaldehyde-removing wallpaper described in 2 or 3 and wall paper
Method, it is characterised in that:The heating-up temperature is 110-130 DEG C, and the heat time is 30-50min.