CN107141927A - 一种供水管道防腐涂料及其制备方法 - Google Patents
一种供水管道防腐涂料及其制备方法 Download PDFInfo
- Publication number
- CN107141927A CN107141927A CN201710543282.3A CN201710543282A CN107141927A CN 107141927 A CN107141927 A CN 107141927A CN 201710543282 A CN201710543282 A CN 201710543282A CN 107141927 A CN107141927 A CN 107141927A
- Authority
- CN
- China
- Prior art keywords
- parts
- water supply
- anticorrosive paint
- supply line
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种供水管道防腐涂料及其制备方法,涉及水管防腐技术领域,包括以下份计的原料:丙烯酸乳液60~65份、松香脂50~52份、白炭黑35~40份、竹醋液30~33份、石墨粉28~29份、抗菌剂22~25份、改性硫酸钙晶须19~21份、深海扇贝贝壳15~17份、纳米粒子11~13份、助剂10~11份和水65~70份。本发明有抗菌抑菌作用,施工方便,防腐性能、抗菌性能优异。
Description
技术领域
本发明涉及水管防腐技术领域,具体涉及一种供水管道防腐涂料及其制备方法。
背景技术
为了防止空气、水及土壤对金属的腐蚀,地下水管网外部使用涂料来防腐蚀,随着我国经济的高速发展,人们对自己居所的要求也越来越高,目前,我国地下水管网所用的涂料大多为只起到了对阀门、管件、管道的防腐作用,但是在长时间的使用过程中会产生致病微生物,没有抗菌作用。
发明内容
本发明的目的是提供一种供水管道防腐涂料及其制备方法,具有抗菌抑菌作用,施工方便,防腐性能、抗菌性能优异。
本发明提供了如下的技术方案:一种供水管道防腐涂料,包括以下份计的原料:丙烯酸乳液60~65份、松香脂50~52份、白炭黑35~40份、竹醋液30~33份、石墨粉28~29份、抗菌剂22~25份、改性硫酸钙晶须19~21份、深海扇贝贝壳15~17份、纳米粒子11~13份、助剂10~11份和水65~70份;
所述助剂包括以下份计的原料:分散剂4~6份、成膜助剂3~4份、增塑剂2~3份和增稠剂1~2份。
其中,所述抗菌剂包括以下份计的原料:氧化银11~13份、氧化锌9~10份、植物精油8~9份和珍珠岩5~7份。
其中,所述植物精油以木香、丁香、肉桂、银杏叶和野菊花为原料制备得到。
其中,所述抗菌剂的制备方法为:按照配比称取氧化银、氧化锌和珍珠岩,充分混合均匀在400~500摄氏度高温下灼烧2~3h,冷却后过200~300目筛,与植物精油混合均匀,得到所述抗菌剂。
其中,所述改性硫酸钙晶须的制备方法为:将直径10~20微米的硫酸钙晶须和硅烷偶联剂加入到高速混合机中,以500~600r/min的转速混合15~20min,即得所述改性硫酸钙晶须,所述硫酸钙晶须和偶联剂的质量比为6~7:1。
其中,所述纳米粒子为纳米氧化铝、纳米氧化硅和纳米二氧化锰中的一种或几种。
其中,所述分散剂为三聚磷酸钠、四聚磷酸钠或六偏磷酸钠中的一种或几种,所述成膜助剂为乙二醇***、乙二醇丁醚、乙二醇和丙二醇中的一种或几种,所述增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸辛酯,所述增稠剂为水性膨润土。
本发明提供一种供水管道防腐涂料的制备方法,包括如下步骤:
(1)、制备改性贝壳粉
称取深海扇贝贝壳,放入煅烧炉,在300~450摄氏度高温下煅烧50~55min,取出自然冷却后至室温,研磨粉碎并过150~200目筛,得到贝壳粉;
按照配比称取纳米粒子与前述得到的贝壳粉混合,放入煅烧炉,在400~450摄氏度高温下煅烧5~20min,然后放入40~50%的乙醇溶液中,以200~300r/min的转速搅拌1~2h,过滤保留滤渣,将滤渣在200~300摄氏度高温下继续煅烧30~40min,研磨粉碎并过200~300目筛,得到改性贝壳粉,备用;
(2)、按照配比称取剩余原料,依次加入至步骤(1)得到的改性贝壳粉,以300~400r/min的转速搅拌,分散均匀,得到所述供水管道防腐涂料。
本发明的有益效果:具有抗菌抑菌作用,施工方便,防腐性能、抗菌性能优异,具体如下:
(1)、本发明在原料中添加改性硫酸钙晶须,采用硫酸钙晶须和硅烷偶联剂制成,硫酸钙晶须具有均匀的横截面,完整的内部结构,细微的尺寸,提高涂料与水管表面的界面黏结力,另外,由于硫酸钙晶须为无机物,以微米级的形式均匀分布,不易团聚,从而提高涂料整体的耐热和耐水性能;
(2)、本发明在原料中添加深海扇贝贝壳,含有丰富的天然甲壳素类粘结剂及活性物质,完全无毒,制成贝壳粉后,具有良好的粘结性能和抗水抗蚀性能,强化粘结效果,用于提高附着力,防止涂膜脱落;经过改性后的贝壳粉,提高了涂料的防腐能力;
(3)、本发明在原料中添加松香脂和丙烯酸乳液,松香树脂为天然树脂,起到提高涂料干燥性、硬度、防腐、耐水性的作用,将松香树脂与丙烯酸乳液混合,具有协同增效效果,可以增加松香树脂的粘接能力,还可以使得涂料具有较好的防腐性;
(4)、本发明在原料中添加白炭黑,具有超微细无机多孔结构,由于其粒径很小,具有比表面积大、表面吸附力强、分散性能好等特点,添加在涂料中还可以起到提高稳定性、补强性、增稠性、附着力和触变性等作用;
(5)、本发明在原料中添加竹醋液,能够对硫化物、氢化物、甲醇、苯、酚等有害化学物质起到吸收、分解异味和消臭作用,使得本发明的涂料涂覆在水管表面后,可以起到除臭净味,防止异味从水管管道进入室内;
(6)、本发明在原料中添加抗菌剂,采用氧化银、氧化锌、植物精油和珍珠岩制备抗菌剂,可以起到抗菌抑菌的效果;
(7)、本发明可以常温固化,施工方便,可以喷涂、刷涂、滚涂、涂层厚度可根据需要任意调整。
具体实施方式
下面结合具体实施例,进一步阐述本发明。这些实施例仅用于说明本发明而不用于限制本发明的范围。
实施例1
一种供水管道防腐涂料,包括以下份计的原料:丙烯酸乳液60份、松香脂50份、白炭黑35份、竹醋液30份、石墨粉28份、抗菌剂22份、改性硫酸钙晶须19份、深海扇贝贝壳15份、纳米粒子11份、助剂10份和水65份;
所述助剂包括以下份计的原料:分散剂4份、成膜助剂3份、增塑剂2份和增稠剂1份。
其中,
所述抗菌剂包括以下份计的原料:氧化银11份、氧化锌9份、植物精油8份和珍珠岩5份。
所述植物精油以木香、丁香、肉桂、银杏叶和野菊花为原料制备得到。
所述抗菌剂的制备方法为:按照配比称取氧化银、氧化锌和珍珠岩,充分混合均匀在400摄氏度高温下灼烧2h,冷却后过200目筛,与植物精油混合均匀,得到所述抗菌剂。
所述改性硫酸钙晶须的制备方法为:将直径10微米的硫酸钙晶须和硅烷偶联剂加入到高速混合机中,以500r/min的转速混合15min,即得所述改性硫酸钙晶须,所述硫酸钙晶须和偶联剂的质量比为6:1。
所述纳米粒子为纳米氧化铝。
所述分散剂为三聚磷酸钠,所述成膜助剂为乙二醇***,所述增塑剂为邻苯二甲酸二丁酯,所述增稠剂为水性膨润土。
本实施例中提供一种供水管道防腐涂料的制备方法,包括如下步骤:
(1)、制备改性贝壳粉
称取深海扇贝贝壳,放入煅烧炉,在300摄氏度高温下煅烧50min,取出自然冷却后至室温,研磨粉碎并过150目筛,得到贝壳粉;
按照配比称取纳米粒子与前述得到的贝壳粉混合,放入煅烧炉,在400摄氏度高温下煅烧5min,然后放入40%的乙醇溶液中,以200r/min的转速搅拌1h,过滤保留滤渣,将滤渣在200摄氏度高温下继续煅烧30min,研磨粉碎并过200目筛,得到改性贝壳粉,备用;
(2)、按照配比称取剩余原料,依次加入至步骤(1)得到的改性贝壳粉,以300r/min的转速搅拌,分散均匀,得到所述供水管道防腐涂料。
实施例2
一种供水管道防腐涂料,包括以下份计的原料:丙烯酸乳液65份、松香脂52份、白炭黑40份、竹醋液33份、石墨粉29份、抗菌剂25份、改性硫酸钙晶须21份、深海扇贝贝壳17份、纳米粒子13份、助剂11份和水70份;
所述助剂包括以下份计的原料:分散剂6份、成膜助剂4份、增塑剂3份和增稠剂2份。
其中,
所述抗菌剂包括以下份计的原料:氧化银13份、氧化锌10份、植物精油9份和珍珠岩7份。
所述植物精油以木香、丁香、肉桂、银杏叶和野菊花为原料制备得到。
所述抗菌剂的制备方法为:按照配比称取氧化银、氧化锌和珍珠岩,充分混合均匀在500摄氏度高温下灼烧3h,冷却后过300目筛,与植物精油混合均匀,得到所述抗菌剂。
所述改性硫酸钙晶须的制备方法为:将直径20微米的硫酸钙晶须和硅烷偶联剂加入到高速混合机中,以600r/min的转速混合20min,即得所述改性硫酸钙晶须,所述硫酸钙晶须和偶联剂的质量比为7:1。
所述纳米粒子为纳米氧化硅。
所述分散剂为四聚磷酸钠,所述成膜助剂为乙二醇丁醚,所述增塑剂为邻苯二甲酸辛酯,所述增稠剂为水性膨润土。
本实施例中提供一种供水管道防腐涂料的制备方法,包括如下步骤:
(1)、制备改性贝壳粉
称取深海扇贝贝壳,放入煅烧炉,在450摄氏度高温下煅烧55min,取出自然冷却后至室温,研磨粉碎并过200目筛,得到贝壳粉;
按照配比称取纳米粒子与前述得到的贝壳粉混合,放入煅烧炉,在450摄氏度高温下煅烧20min,然后放入50%的乙醇溶液中,以300r/min的转速搅拌2h,过滤保留滤渣,将滤渣在300摄氏度高温下继续煅烧40min,研磨粉碎并过300目筛,得到改性贝壳粉,备用;
(2)、按照配比称取剩余原料,依次加入至步骤(1)得到的改性贝壳粉,以400r/min的转速搅拌,分散均匀,得到所述供水管道防腐涂料。
实施例3
一种供水管道防腐涂料,包括以下份计的原料:丙烯酸乳液62份、松香脂51份、白炭黑37份、竹醋液32份、石墨粉28.5份、抗菌剂23份、改性硫酸钙晶须20份、深海扇贝贝壳16份、纳米粒子12份、助剂10.5份和水68份;
所述助剂包括以下份计的原料:分散剂5份、成膜助剂3.5份、增塑剂2.5份和增稠剂1.5份。
其中,
所述抗菌剂包括以下份计的原料:氧化银11~13份、氧化锌9~10份、植物精油8~9份和珍珠岩5~7份。
所述植物精油以木香、丁香、肉桂、银杏叶和野菊花为原料制备得到。
所述抗菌剂的制备方法为:按照配比称取氧化银、氧化锌和珍珠岩,充分混合均匀在450摄氏度高温下灼烧2.5h,冷却后过250目筛,与植物精油混合均匀,得到所述抗菌剂。
所述改性硫酸钙晶须的制备方法为:将直径15微米的硫酸钙晶须和硅烷偶联剂加入到高速混合机中,以550r/min的转速混合16min,即得所述改性硫酸钙晶须,所述硫酸钙晶须和偶联剂的质量比为6:1。
所述纳米粒子为纳米二氧化锰。
所述分散剂为四聚磷酸钠,所述成膜助剂为丙二醇,所述增塑剂为邻苯二甲酸二丁酯,所述增稠剂为水性膨润土。
本实施例中提供一种供水管道防腐涂料的制备方法,包括如下步骤:
(1)、制备改性贝壳粉
称取深海扇贝贝壳,放入煅烧炉,在400摄氏度高温下煅烧52min,取出自然冷却后至室温,研磨粉碎并过175目筛,得到贝壳粉;
按照配比称取纳米粒子与前述得到的贝壳粉混合,放入煅烧炉,在425摄氏度高温下煅烧10min,然后放入45%的乙醇溶液中,以250r/min的转速搅拌1.5h,过滤保留滤渣,将滤渣在250摄氏度高温下继续煅烧35min,研磨粉碎并过250目筛,得到改性贝壳粉,备用;
(2)、按照配比称取剩余原料,依次加入至步骤(1)得到的改性贝壳粉,以350r/min的转速搅拌,分散均匀,得到所述供水管道防腐涂料。
参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (9)
1.一种供水管道防腐涂料,其特征在于,包括以下份计的原料:丙烯酸乳液60~65份、松香脂50~52份、白炭黑35~40份、竹醋液30~33份、石墨粉28~29份、抗菌剂22~25份、改性硫酸钙晶须19~21份、深海扇贝贝壳15~17份、纳米粒子11~13份、助剂10~11份和水65~70份;
所述助剂包括以下份计的原料:分散剂4~6份、成膜助剂3~4份、增塑剂2~3份和增稠剂1~2份。
2.根据权利要求1所述的供水管道防腐涂料,其特征在于,包括以下份计的原料:丙烯酸乳液62份、松香脂51份、白炭黑37份、竹醋液32份、石墨粉28.5份、抗菌剂23份、改性硫酸钙晶须20份、深海扇贝贝壳16份、纳米粒子12份、助剂10.5份和水68份;
所述助剂包括以下份计的原料:分散剂5份、成膜助剂3.5份、增塑剂2.5份和增稠剂1.5份。
3.根据权利要求1所述的供水管道防腐涂料,其特征在于,所述抗菌剂包括以下份计的原料:氧化银11~13份、氧化锌9~10份、植物精油8~9份和珍珠岩5~7份。
4.根据权利要求3所述的供水管道防腐涂料,其特征在于,所述植物精油以木香、丁香、肉桂、银杏叶和野菊花为原料制备得到。
5.根据权利要求3所述的供水管道防腐涂料,其特征在于,所述抗菌剂的制备方法为:按照配比称取氧化银、氧化锌和珍珠岩,充分混合均匀在400~500摄氏度高温下灼烧2~3h,冷却后过200~300目筛,与植物精油混合均匀,得到所述抗菌剂。
6.根据权利要求1所述的供水管道防腐涂料,其特征在于,所述改性硫酸钙晶须的制备方法为:将直径10~20微米的硫酸钙晶须和硅烷偶联剂加入到高速混合机中,以500~600r/min的转速混合15~20min,即得所述改性硫酸钙晶须,所述硫酸钙晶须和偶联剂的质量比为6~7:1。
7.根据权利要求1所述的供水管道防腐涂料,其特征在于,所述纳米粒子为纳米氧化铝、纳米氧化硅和纳米二氧化锰中的一种或几种。
8.根据权利要求1所述的供水管道防腐涂料,其特征在于,所述分散剂为三聚磷酸钠、四聚磷酸钠或六偏磷酸钠中的一种或几种,所述成膜助剂为乙二醇***、乙二醇丁醚、乙二醇和丙二醇中的一种或几种,所述增塑剂为邻苯二甲酸二丁酯或邻苯二甲酸辛酯,所述增稠剂为水性膨润土。
9.一种根据权利要求1~8任一项所述的供水管道防腐涂料的制备方法,其特征在于,包括如下步骤:
(1)、制备改性贝壳粉
称取深海扇贝贝壳,放入煅烧炉,在300~450摄氏度高温下煅烧50~55min,取出自然冷却后至室温,研磨粉碎并过150~200目筛,得到贝壳粉;
按照配比称取纳米粒子与前述得到的贝壳粉混合,放入煅烧炉,在400~450摄氏度高温下煅烧5~20min,然后放入40~50%的乙醇溶液中,以200~300r/min的转速搅拌1~2h,过滤保留滤渣,将滤渣在200~300摄氏度高温下继续煅烧30~40min,研磨粉碎并过200~300目筛,得到改性贝壳粉,备用;
(2)、按照配比称取剩余原料,依次加入至步骤(1)得到的改性贝壳粉,以300~400r/min的转速搅拌,分散均匀,得到所述供水管道防腐涂料。