CN107119454A - A kind of real silk fabric anti-crease finishing technique - Google Patents
A kind of real silk fabric anti-crease finishing technique Download PDFInfo
- Publication number
- CN107119454A CN107119454A CN201710329808.8A CN201710329808A CN107119454A CN 107119454 A CN107119454 A CN 107119454A CN 201710329808 A CN201710329808 A CN 201710329808A CN 107119454 A CN107119454 A CN 107119454A
- Authority
- CN
- China
- Prior art keywords
- silk fabric
- real silk
- crease finishing
- finishing technique
- dressing liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of anti-crease finishing technique of real silk fabric, silk sample is immersed in wrinkle proofing liquid in padder, two leachings two is carried out and rolls, washing drying afterwards completes the anti-crease finishing technique of real silk fabric；It the advantage is that：By adding citric acid in dressing liquid, the discharge of formaldehyde is reduced, has not only ensured anti-wrinkle effect but also environmental protection, safety；By reasonably controlling catalyst, softening agent and the amount of strong protecting agent, effective control bakes time and baking temperature, it will be apparent that improve the anti-wrinkle effect of real silk fabric.
Description
Technical field
The invention belongs to fabric post-treatment technical field, and in particular to a kind of real silk fabric anti-crease finishing technique.
Background technology
Real silk fabric has good dress ornament performance, and its feature is frivolous quality, good hygroscopicity, graceful gloss, softness
Feel, excellent thermal property.But its fatal weakness, wrinkle resistance is poor, irradiated in ultraviolet under the erosion with salt, pole
Easy yellowing, influences its dress ornament and performance.
2D resin finishing agents are the most frequently used one kind in N- methylol amide resinoid wash and wear finishers, its anti-crease finishing effect
Fruit is good, but it damages serious and burst size of methanal to fabric strength greatly, easily pollutes environment, security is poor, to health
It is unfavorable.
The content of the invention
In view of the above-mentioned deficiencies in the prior art, it is an object of the present invention to which existing provide a kind of environmental protection, safety and can increase crease-resistant effect
The anti-crease finishing technique of the real silk fabric of fruit.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of anti-crease finishing technique of real silk fabric,
Its innovative point is：Rolled by the preparation of dressing liquid, dipping, two leachings two and wash baking step, complete the crease-resistant of real silk fabric
Finishing technique；The step is specific as follows：
（1）The preparation of dressing liquid：By 100-200g/L citric acids, 20-60g/L catalyst, 10-60g/L silicone softening agents, 2-
6g/L bleeding agents and 5-8g/L strong protecting agents are well mixed, complete the preparation of dressing liquid；
（2）Dipping：Real silk fabric is immersed in dressing liquid, the maceration extract bath raio is 1:15-30, the dip time is
15-30min；
（3）Two leachings two are rolled：Real silk fabric after dipping is padded in padding machine；
（4）Washing drying:Real silk fabric after padding carries out preliminary drying, then bakes, then uses hot water wash successively 3-5 times, cold
Water washing 3-5 times, is finally dried, and completes the anti-crease finishing of real silk fabric.
Further, the step（1）Middle catalyst is one in sodium hypophosphite, sodium thiosulfate or sodium acid carbonate
Kind.
Further, the step（1）Middle strong protecting agent is one kind of triethylamine or glyoxal.
Further, the step（1）Middle bleeding agent is one kind in penetrating agent JFC, paregal O or turkey red oil.
Further, the step（1）Middle silicone softening agent is polyether type organic silicone softening agent, polyurethane type organosilicon
One kind in softening agent or polysiloxane-based softening agent.
Further, the step（3）Middle first time soak time is 3-5min, and second of soak time is 3-5 min,
Pick-up rate is 75-90%.
Further, the step（4）Middle preliminary drying temperature is 60-80 DEG C, and preliminary drying time is 3-5min, and baking temperature is
150-170 DEG C, the time is baked for 2-3min, and hot water temperature is 40-50 DEG C, and cold water temperature is 20-25 DEG C, and drying temperature is 60-
80 DEG C, drying time is 5-8min.
Beneficial effects of the present invention are as follows：The present invention by the way that silk sample is immersed in wrinkle proofing liquid in padder,
Carry out two leachings two to roll, washing drying afterwards completes the anti-crease finishing technique of real silk fabric；By adding lemon in dressing liquid
Acid, reduces the discharge of formaldehyde, has not only ensured anti-wrinkle effect but also environmental protection, safety；By reasonably controlling catalyst, softening agent and strong
The protectant amount of power, effective control bakes time and baking temperature, it will be apparent that improve the anti-wrinkle effect of real silk fabric.
Embodiment
Embodiments of the present invention are illustrated by particular specific embodiment below, those skilled in the art can be by this explanation
Content disclosed by book understands other advantages and effect of the present invention easily.
Embodiment 1
A kind of anti-crease finishing technique of real silk fabric, rolls by the preparation of dressing liquid, dipping, two leachings two and washes baking step,
Complete the anti-crease finishing technique of real silk fabric；Step is specific as follows：
（1）The preparation of dressing liquid：By 100g/L citric acids, 20g/L sodium hypophosphites, 10g/L polyether type organic silicones softening agent,
2g/L penetrating agent JFCs and 5g/L triethylamines are well mixed, complete the preparation of dressing liquid；
（2）Dipping：Real silk fabric is immersed in dressing liquid, maceration extract bath raio is 1:15, dip time is 15min；
（3）Two leachings two are rolled：Real silk fabric after dipping is padded in padding machine, first time soak time is 3min, second
Secondary soak time is 3min, and pick-up rate is 75%；
（4）Washing drying：Real silk fabric after padding is subjected to preliminary drying at 60 DEG C, preliminary drying time is 3min, then 150 DEG C
Under bake, bake the time for 2min, then successively with 40 DEG C of hot water wash 3 times, 20 DEG C of cold water are washed 3 times, last 60 DEG C of drying, are dried
Time is 5min, completes the anti-crease finishing of real silk fabric.
Embodiment 2
A kind of anti-crease finishing technique of real silk fabric, rolls by the preparation of dressing liquid, dipping, two leachings two and washes baking step,
Complete the anti-crease finishing technique of real silk fabric；Step is specific as follows：
（1）The preparation of dressing liquid：By 200g/L citric acids, 60g/L sodium thiosulfate, 60g/L polyurethane types silicone softening agent,
6g/L paregal Os and 8g/L glyoxals are well mixed, complete the preparation of dressing liquid；
（2）Dipping：Real silk fabric is immersed in dressing liquid, maceration extract bath raio is 1:30, dip time is 30min；
（3）Two leachings two are rolled：Real silk fabric after dipping is padded in padding machine, first time soak time is 5min, second
Secondary soak time is 5min, and pick-up rate is 90%；
（4）Washing drying：Real silk fabric after padding is subjected to preliminary drying at 80 DEG C, preliminary drying time is 5min, then 170 DEG C
Under bake, bake the time for 5min, then successively with 50 DEG C of hot water wash 5 times, 25 DEG C of cold water are washed 5 times, last 80 DEG C of drying, are dried
Time is 8min, completes the anti-crease finishing of real silk fabric.
Embodiment 3
A kind of anti-crease finishing technique of real silk fabric, rolls by the preparation of dressing liquid, dipping, two leachings two and washes baking step,
Complete the anti-crease finishing technique of real silk fabric；Step is specific as follows：
（1）The preparation of dressing liquid：By 150g/L citric acids, 40g/L sodium acid carbonates, the polysiloxane-based softening agents of 35g/L, 4g/L soil
Its chilli oil of ear and 7g/L glyoxals are well mixed, complete the preparation of dressing liquid；
（2）Dipping：Real silk fabric is immersed in dressing liquid, maceration extract bath raio is 1:23, dip time is 25min；
（3）Two leachings two are rolled：Real silk fabric after dipping is padded in padding machine, first time soak time is 4min, second
Secondary soak time is 4in, and pick-up rate is 80%；
（4）Washing drying：Real silk fabric after padding is subjected to preliminary drying at 70 DEG C, preliminary drying time is 4min, then 160 DEG C
It is lower to be baked, the time is baked for 4min, then successively with 45 DEG C of hot water wash 4 times, 23 DEG C of cold water are washed 4 times, and last 70 DEG C dry,
Drying time is 6min, completes the anti-crease finishing of real silk fabric.
The present invention by the way that silk sample is immersed in wrinkle proofing liquid in padder, by the preparation of dressing liquid, dipping,
Two leachings two are rolled and wash baking step；By adding citric acid in dressing liquid, the discharge of formaldehyde is reduced, has both ensured crease-resistant effect
Fruit is again environmentally friendly, safety；By reasonably controlling catalyst, softening agent and the amount of strong protecting agent, effective control bakes the time
And baking temperature, it will be apparent that improve the anti-wrinkle effect of real silk fabric.
Above-described embodiment is presently preferred embodiments of the present invention, is not the limitation to technical solution of the present invention, as long as
The technical scheme that can be realized without creative work on the basis of above-described embodiment, is regarded as falling into patent of the present invention
Rights protection scope in.
Claims (7)
1. a kind of real silk fabric anti-crease finishing technique, it is characterised in that：Rolled and water by the preparation of dressing liquid, dipping, two leachings two
Baking step is washed, the anti-crease finishing technique of real silk fabric is completed；The step is specific as follows：
The preparation of dressing liquid：By 100-200g/L citric acids, 20-60g/L catalyst, 10-60g/L silicone softening agents, 2-6g/
L bleeding agents and 5-8g/L strong protecting agents are well mixed, complete the preparation of dressing liquid；
Dipping：Real silk fabric is immersed in dressing liquid, the maceration extract bath raio is 1:15-30, the dip time is 15-
30min；
Two leachings two are rolled：Real silk fabric after dipping is padded in padding machine；
Washing drying：Real silk fabric after padding carries out preliminary drying, then bakes, then uses hot water wash successively 3-5 times, and cold water is washed
Wash 3-5 times, finally dry, complete the anti-crease finishing of real silk fabric.
2. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（1）In urge
Agent is one kind in sodium hypophosphite, sodium thiosulfate or sodium acid carbonate.
3. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（1）In it is strong
Power protective agent is one kind of triethylamine or glyoxal.
4. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（1）In ooze
Saturating agent is one kind in penetrating agent JFC, paregal O or turkey red oil.
5. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（1）In have
Machine silicone softener is one in polyether type organic silicone softening agent, polyurethane type silicone softening agent or polysiloxane-based softening agent
Kind.
6. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（3）In, the
Soak time is 3-5min, and second of soak time is 3-5 min, and pick-up rate is 75-90%.
7. a kind of real silk fabric anti-crease finishing technique according to claim 1, it is characterised in that：The step（4）In, in advance
It is 60-80 DEG C to dry temperature, and preliminary drying time is 3-5min, and baking temperature is 150-170 DEG C, bakes the time for 2-3min, hot water temperature
Spend for 40-50 DEG C, cold water temperature is 20-25 DEG C, and drying temperature is 60-80 DEG C, and drying time is 5-8min.