CN107089715A - 一种不锈钢酸洗废水碱性中和剂 - Google Patents
一种不锈钢酸洗废水碱性中和剂 Download PDFInfo
- Publication number
- CN107089715A CN107089715A CN201710398657.1A CN201710398657A CN107089715A CN 107089715 A CN107089715 A CN 107089715A CN 201710398657 A CN201710398657 A CN 201710398657A CN 107089715 A CN107089715 A CN 107089715A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- raw material
- contain
- stainless steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明提供一种不锈钢酸洗废水碱性中和剂，由以下重量份的原料构成：环己胺8‑12重量份，甲醇3‑4重量份，二甲硅油5‑8重量份，多乙烯多胺1‑4重量份，石灰35‑47重量份，溶剂25‑48重量份；与现有技术相比，本发明具有如下的有益效果：可有有效控制水质中的PH值，可以有效中和酸性介质，同时原料简单，方便配制，成本低廉，可以在大多数废酸液处理中得到应用。
Description
技术领域
本发明是一种不锈钢酸洗废水碱性中和剂，属于钢铁及冶金行业工业废酸及废水处理领域。
背景技术
不锈钢可以按用途、化学成分及金相组织来大体分类。以奥氏体系类的不锈钢类由18％铬-8％镍为基本组成，各元素的加入量变化的不同，而开发各种用途的不锈钢钢种。
不锈钢由于具有耐酸腐蚀、耐热性好、抗高温氧化性能好等许多优点，因此被广泛应用于石油、化工、动力、核工程、航空航天、医疗机械、轻工产品、个人住宅装饰、高级宾馆设施等领域。不锈钢材在成形和热处理过程中，表面会产生一层黑色的氧化皮，这类氧化皮结构致密，与基体附着力强，含有Fe、Cr、Ni、少量C和Si，有些产品可能存在Mn、Ti、Mo、Cu和W等元素，氧化物结构为：氧化亚铁、氧化铁、四氧化三铁、氧化铬、氧化镍、二氧化硅、铬尖晶石(Cr2O3·FeO)和镍尖晶石(NiO·Fe2O3)等。不锈钢氧化皮不仅破坏了钢材表面的美观性，又会加快金属表面的电化学腐蚀，而且其存在的表面应力会加快钢材表面的应力腐蚀。因此，不锈钢表面的氧化皮必须在后续加工前去除干净。
工程上，常使用酸洗工艺去除热轧及退火过程中在不锈钢钢材表面形成的氧化皮，同时对不锈钢表面进行钝化处理，使其更具耐蚀性。
酸洗过程中，主要存在两类酸性废液。其一为硫酸酸洗废酸液，其二为硝酸氢氟酸混合废酸液。根据酸洗工艺的不同，废酸液中游离酸含量和金属离子含量有所不同。在自动生成线上，由于需要提高生产效率，酸洗过程配制的硝酸氢氟酸混合酸液浓度适当提高。当酸洗液中铁离子浓度达到40-50g/l时，去除氧化皮的效率会降低，需要更换新酸。这时，溶液中硝酸的浓度仍有12-18％，氢氟酸浓度3-5％。采用硫酸预酸洗时，当酸液中铁离子浓度大于60g/l时，去除氧化皮的效率会降低，整个酸洗速度变慢，必须更换新酸。这时，废酸洗液中残留的硫酸浓度仍有15-20％。在酸洗工艺结束后，必须用水冲洗金属表面，冲洗水量较大，这部分水含酸量及金属离子量都相对较少，冲洗废水的pH大多在1-4之间
目前，大多数废酸液处理采用石灰一步中和沉淀法，将水中的残余酸中和，形成硫酸钙或氟化钙或金属氢氧化物的共沉淀污泥。该方法优点是工艺简单，设备投资少，出水水质较好，含盐量较低。缺点是在pH＝6-9范围，部分金属氢氧化物沉淀不完全，水处理产生的污泥量较多，沉淀物中含大量重金属，需按工业危险废物管理，污泥处置费用大。
现有市面上急需一种新型的中和剂，用于处理上述问题。
发明内容
针对现有技术存在的不足，本发明目的是提供一种不锈钢酸洗废水碱性中和剂，以解决上述背景技术中提出的问题。
为了实现上述目的，本发明是通过如下的技术方案来实现：一种不锈钢酸洗废水碱性中和剂，由以下重量份的原料构成：环己胺8-12重量份，甲醇3-4重量份，二甲硅油5-8重量份，多乙烯多胺1-4重量份，石灰35-47重量份，溶剂25-48重量份。
进一步地，所述环己胺由苯胺催化加氢而得。
进一步地，由原油、重油或轻油为原料，经造气净化变换，除去二氧化碳，配制成一定的一氧化碳和氢，在催化剂存在下，与合成氨联产甲醇（将合成后的粗甲醇，经预精馏脱除甲醚，精馏而得原料中甲醇甲醇。
进一步地，所述石灰为一种生石灰粉。
进一步地，所述溶剂为柴油或煤油。
进一步地，每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇4重量份，每100重量份的原料中含有二甲硅油5重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰35重量份，每100重量份的原料中含有溶剂40重量份。
进一步地，每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇3重量份，每100重量份的原料中含有二甲硅油8重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰36重量份，每100重量份的原料中含有溶剂37重量份。
本发明的有益效果：本发明的一种不锈钢酸洗废水碱性中和剂，可有有效控制水质中的PH值，可以有效中和酸性介质，同时原料简单，方便配制，成本低廉，可以在大多数废酸液处理中得到应用。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
本发明提供一种技术方案：一种不锈钢酸洗废水碱性中和剂，由以下重量份的原料构成：环己胺8-12重量份，甲醇3-4重量份，二甲硅油5-8重量份，多乙烯多胺1-4重量份，石灰35-47重量份，溶剂25-48重量份。
环己胺由苯胺催化加氢而得，石灰为一种生石灰粉，溶剂为柴油或煤油。
由原油、重油或轻油为原料，经造气净化变换，除去二氧化碳，配制成一定的一氧化碳和氢，在催化剂存在下，与合成氨联产甲醇（将合成后的粗甲醇，经预精馏脱除甲醚，精馏而得原料中甲醇甲醇。
做为本发明的一个实施例：每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇4重量份，每100重量份的原料中含有二甲硅油5重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰35重量份，每100重量份的原料中含有溶剂40重量份。
做为本发明的一个实施例：每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇3重量份，每100重量份的原料中含有二甲硅油8重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰36重量份，每100重量份的原料中含有溶剂37重量份。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
此外，应当理解，虽然本说明书按照实施方式加以描述，但并非每个实施方式仅包含一个独立的技术方案，说明书的这种叙述方式仅仅是为清楚起见，本领域技术人员应当将说明书作为一个整体，各实施例中的技术方案也可以经适当组合，形成本领域技术人员可以理解的其他实施方式。
Claims (7)
1.一种不锈钢酸洗废水碱性中和剂，其特征在于：由以下重量份的原料构成：环己胺8-12重量份，甲醇3-4重量份，二甲硅油5-8重量份，多乙烯多胺1-4重量份，石灰35-47重量份，溶剂25-48重量份。
2.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：所述环己胺由苯胺催化加氢而得。
3.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：由原油、重油或轻油为原料，经造气净化变换，除去二氧化碳，配制成一定的一氧化碳和氢，在催化剂存在下，与合成氨联产甲醇（将合成后的粗甲醇，经预精馏脱除甲醚，精馏而得原料中甲醇甲醇。
4.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：所述石灰为一种生石灰粉。
5.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：所述溶剂为柴油或煤油。
6.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇4重量份，每100重量份的原料中含有二甲硅油5重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰35重量份，每100重量份的原料中含有溶剂40重量份。
7.根据权利要求1所述的一种不锈钢酸洗废水碱性中和剂，其特征在于：每100重量份的原料中含有环己胺12重量份，每100重量份的原料中含有甲醇3重量份，每100重量份的原料中含有二甲硅油8重量份，每100重量份的原料中含有多乙烯多胺4重量份，每100重量份的原料中含有石灰36重量份，每100重量份的原料中含有溶剂37重量份。