CN107042114A - The preparation method of ozone Heterogeneous oxidation solid catalyst - Google Patents
The preparation method of ozone Heterogeneous oxidation solid catalyst Download PDFInfo
- Publication number
- CN107042114A CN107042114A CN201710274449.0A CN201710274449A CN107042114A CN 107042114 A CN107042114 A CN 107042114A CN 201710274449 A CN201710274449 A CN 201710274449A CN 107042114 A CN107042114 A CN 107042114A
- Authority
- CN
- China
- Prior art keywords
- weight
- component
- double
- iii
- solid catalyst
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and technical field of chemical engineering catalysts.It is pure with diatom, kyanite, hydrotalcite, alunite, cubric niter and dolomite make carrier after lithium hypochlorite and double (acetylacetone,2,4-pentanedione) beryllium reamings, add surfactant Cationic surfucant and activation process is carried out under ul-trasonic irradiation, then carrier in hydrothermal reaction kettle with composite mineralizer borax and potassium sulfate, catalytic activity auxiliary agent predecessor three (hexafluoroacetylacetone) yttrium (III) dihydrate, three cyclopentadiene promethiums, three (6, 6, 7, 7, 8, 8, 8 seven fluorine 2, 2 dimethyl 3, 5 octene diketone) dysprosium (III), three (trifluoromethanesulfonimide) ytterbiums, catalytic active center predecessor pyruvic acid isonicotinoyl hydrazone vanadium, cobalt edetate and six nitroso rhodium trisodiums, chlordene osmium dipotassium, hydro-thermal reaction is carried out under the double dodecyl dimethyl ammonium effects of emulsifying agent chlorination, drying is removed after moisture, calcination obtains ozone Heterogeneous oxidation solid catalyst in Muffle furnace.
Description
Technical field
The present invention relates to a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, category environmental protection and chemical catalyst skill
Art field.
Background technology
Ozonation technology using ozone oxidation ability it is strong the characteristics of, can be by many organic pollution oxidation Decompositions, extensively
For wastewater treatment.Catalytic ozonation technology is divided into ozone homogeneous catalytic oxidation and ozone heterogeneous catalytic oxidation, and ozone is equal
Phase catalysis oxidation has that the more difficult separation and recovery of catalyst is reused, ozone utilization rate is low causes water process operating cost higher,
Organic pollutant removal rate is relatively low simultaneously and easily causing secondary pollution of water is limited to its application；Ozone heterogeneous catalysis oxygen
There is change technology catalyst to be easily isolated and recycled and reusable, ozone utilization rate is high, organic pollutant removal rate is higher, drop
Low water process operating cost and receive significant attention its application the advantages of do not result in secondary pollution.Ozone heterogeneous catalysis
It is to reach local organic matter enrichment by catalyst surface absorption organic matter that oxidation of organic compounds, which is decomposed, while ozone molecule absorption exists
The hydroxyl radical free radical that catalyst surface produces high activity under catalyst action decomposes organic matter.Ozone heterogeneous catalytic oxidation
Handle in waste water technology, core technology is the preparation of ozone Heterogeneous oxidation solid catalyst.
Ozone Heterogeneous oxidation solid catalyst is generally made up of carrier, activated centre and auxiliary agent.Due to being polluted in waste water
Species are various, complex chemical composition feature, can produce harmful effect to performance such as absorption, the mithridatism of catalyst.
Prepare that the carrier structure that ozone Heterogeneous oxidation solid catalyst uses is more single at present, adsorptivity is relatively low；Activated centre is universal
Using normal transition metal salt, mithridatism is poor；Preparation method mainly has infusion process, the precipitation method, mixing method and collosol and gel etc.
Method attachment activity center and adjuvant component are easily liquated out in carrier surface, activated centre and adjuvant component, cause catalyst
Easily lose catalytic activity.For exist in current ozone Heterogeneous oxidation solid catalyst preparation method Catalyst Adsorption compared with
Low, mithridatism is poor and easily loses catalytic activity problem, and exploitation is strengthened using multicomponent porous carrier through reaming, surface active
Catalyst Adsorption, makees catalytic activity auxiliary agent predecessor, normal transition Organometallic using Rare-earth chemicals and closes
Thing and precious metal chemical complex are made catalytic active center predecessor and contained with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering preparation
The ozone Heterogeneous oxidation solid catalyst of multi-element metal has to improve the preparation method of catalyst mithridatism and catalytic activity
Larger environmental benefit and higher practical value.
The content of the invention
For existing in current ozone Heterogeneous oxidation solid catalyst preparation method, Catalyst Adsorption is relatively low, mithridatism
Poor to lose catalytic activity problem with easy, exploitation strengthens catalyst using multicomponent porous carrier through reaming, surface active
Adsorptivity, catalytic activity auxiliary agent predecessor, normal transition metallo-organic compound and expensive are made using Rare-earth chemicals
Metallic compound is made catalytic active center predecessor and prepared with multicomponent porous carrier through hydro-thermal reaction, high temperature sintering containing polynary gold
The ozone Heterogeneous oxidation solid catalyst of category to improve the preparation method of catalyst mithridatism and catalytic activity, it is characterized in that
Component A can be added in closed reactor and deionized water stirring prepares the aqueous solution, the weight concentration for control component A is 2%~6%,
After the completion of prepared by solution, B component is added under agitation, 35 DEG C~50 DEG C are warming up to, continues stirring reaction 3h~6h, is filtered, instead
Product is answered to obtain reaming modified support after 102 DEG C~106 DEG C dry constant weights；Reaming modified support puts into ultrasound reactor,
The aqueous solution prepared by component C and deionized water is added, the weight concentration of component C is 3%~8%, is uniformly mixed, and control is super
Sound power density is 0.3~0.8W/m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasound
Surface active carrier mixed liquor；Ultrasonic surface activated carrier mixed liquor is transferred in hydrothermal reaction kettle, add D components and go from
The aqueous solution that sub- water is prepared, the weight concentration of D components is 40%~55%, by weight, D component deionized water solutions:Ultrasonic table
Weight ratio=1 of face activated carrier mixed liquor:（1.5~2）, control 120 DEG C~180 DEG C of temperature, the hydro-thermal reaction time be 8h~
16h, then dries to obtain fine particle；Fine particle is in Muffle furnace, 600 DEG C~950 DEG C, and calcination 3h~8h obtains ozone non-
Homogeneous oxidizing solid catalyst.The component A is made up of lithium hypochlorite, double (acetylacetone,2,4-pentanedione) berylliums, by weight, lithium hypochlorite:
Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:（1~1.6）, B component is by diatom is pure, kyanite, hydrotalcite, alunite, saliter
Stone, dolomite composition, by weight, diatom is pure:Kyanite:Hydrotalcite:Alunite:Cubric niter:Dolomitic weight ratio=（5
~15）:（7~17）:（9~19）:（11~21）:（13~23）:（15~25）, by weight, component A:The weight of B component it
Than=1:（10~20）, component C is Cationic surfucant, by weight, component C:Reaming modified support
Weight ratio=1:（5~10）, D components are by composite mineralizer borax, potassium sulfate, (the hexafluoro acetyl of catalytic activity auxiliary agent predecessor three
Acetone) yttrium (III) dihydrate, three cyclopentadiene promethiums, three (the fluoro- 2,2- dimethyl -3,5- octenes of 6,6,7,7,8,8,8- seven
Diketone) dysprosium (III), three (trifluoromethanesulfonimide) ytterbium Rare-earth chemicals, catalytic active center predecessor is common
Transition metal organometallic compound pyruvic acid isonicotinoyl hydrazone vanadium, cobalt edetate and the nitroso rhodium trisodium of precious metal chemical complex six, six
Chlorine osmium dipotassium, the double dodecyl dimethyl ammonium compositions of emulsifying agent chlorination, by weight, borax:Potassium sulfate:Three (hexafluoroacetylacetonates
Ketone) yttrium (III) dihydrate:Three cyclopentadiene promethiums:Three (the fluoro- 2,2- dimethyl -3,5- octenes two of 6,6,7,7,8,8,8- seven
Ketone) dysprosium (III):Three (trifluoromethanesulfonimide) ytterbiums:Pyruvic acid isonicotinoyl hydrazone vanadium:Cobalt edetate:Six nitroso rhodium trisodiums:
Chlordene osmium dipotassium:The weight ratio of the double dodecyl dimethyl ammoniums of chlorination=（4~8）:（6~10）:（3~6）:（4~7）:（5~
8）:（6~9）:（10~15）:（12~18）:（4~7）:（6~9）:（6~20）.The diatom of the B component is pure, kyanite, water
Talcum, alunite, cubric niter, dolomite are crushed respectively, and deionized water washing, which is dried, to be removed after moisture, is entered through standard screen
- 200 mesh of row ,+400 mesh sieves point, it is the mm of 0.0370mm~0.0750 control particle diameter.
What the technical method of the present invention was realized in：Lithium hypochlorite LiClO, double (second can be being added in closed reactor
Acyl acetone) beryllium C10H14BeO4The aqueous solution is prepared with deionized water stirring, it is 0.0370mm~0.0750mm to add particle diameter after screening
Diatom is pure, kyanite, hydrotalcite, alunite, cubric niter and dolomite porous material carrier, in certain temperature and stirring condition
Under, the small Be of aqueous solution Ionic Radius2+（0.31Å）、Li+（0.60Å）Displace part ion radius in porous material big
Ca2+（0.99Å）、K+（1.33Å）、Ba2+（1.35Å）Plasma, the aperture of porous material carrier becomes big, surface roughness increase,
Filtering, dries the reaming modified support input ultrasound reactor after constant weight, adds chlorination dodecyl dimethyl ethoxy
Ammonium [C12H25N(CH3)2CH2CH2OH]+Cl-The aqueous solution, when control ultrasonic power density, ultrasonic frequency, temperature and sonic oscillation
Between, under ultrasonic cavitation effect, Cationic surfucant [C12H25N(CH3)2CH2CH2OH]+Cl-It is easy to
Reaming modified support duct is escaped into from the aqueous solution or reaming modified support surface is attached to, and is beneficial to the mutual of carrier duct
Connection and carrier surface activation, enhance adsorptivity；After the completion of ultrasonic activation, ultrasonic surface activated carrier mixed liquor is transferred to water
In thermal response kettle, with borax Na2B4O7·10H2O, potassium sulfate K2SO4The composite mineralizer, (hexafluoro of catalytic activity auxiliary agent predecessor three
Acetylacetone,2,4-pentanedione) yttrium (III) dihydrate C15H3F18O6Y·2H2O, three cyclopentadiene promethium Pm (C5H5)3, three (6,6,7,7,8,8,
The fluoro- 2,2- dimethyl -3,5- octenes diketone of 8- seven) dysprosium (III) C30H30DyF21O6, three (trifluoromethanesulfonimide) ytterbiums
[(CF3SO2)2N]3Yb Rare-earth chemicals, catalytic active center component predecessor normal transition metallo-organic compound
Pyruvic acid isonicotinoyl hydrazone vanadium [VO2(C9H8N3O5)] (C5H5N), cobalt edetate C12H22 O14Co and the nitrous of precious metal chemical complex six
Base rhodium trisodium Na3Rh(NO2)6, chlordene osmium dipotassium K2OsCl6, in double dodecyl dimethyl the ammonium [(C of emulsifying agent chlorination12H25)2N
(CH3)2]+Cl-Effect is lower to carry out hydro-thermal reaction, and mineralizer accelerates diffusion, activates reactant lattice, promotes solid phase anti-
The progress answered, ultrasonic surface activated carrier and Rare-earth chemicals, normal transition metallo-organic compound, noble metal
Compound Uniform Doped, the double dodecyl dimethyl ammoniums of emulsifying agent chlorination make reaction solution form quasi-stationary emulsion to prevent solid-liquid point
From, sedimentation, while to the further surface active of porous carrier, by the way that in certain temperature, the hydro-thermal reaction of time, drying is obtained
The fine silt thing of even doping；The fine silt thing of Uniform Doped is in Muffle furnace, through high temperature sintering, organic matter carbonization therein
The microcellular structure of porous carrier is further enhanced, porous carrier supported rare earth metal oxide, transition metal oxide is obtained
With the ozone Heterogeneous oxidation solid catalyst of the catalytic active center of noble metal formation, improve the mithridatism of catalyst and urge
Change activity.
Relative to art methods, outstanding feature of the present invention is using diatom is pure, kyanite, neatly in technology of preparing
Stone, alunite, cubric niter, dolomite porous material make carrier, due to lithium hypochlorite LiClO and double (acetylacetone,2,4-pentanedione) berylliums
C10H14BeO4Reaming effect, Cationic surfucant [C12H25N(CH3)2 CH2CH2OH]+Cl-, chlorination it is double
Dodecyl dimethyl ammonium [(C12H25)2N(CH3)2]+Cl-The interconnected and surface activation in duct；Pass through hydro-thermal reaction
Rare-earth chemicals, normal transition metallo-organic compound and precious metal chemical complex is set to reach Uniform Doped and be attached to
In carrier surface and duct, high temperature sintering makes organic matter carbonization strengthen and form multi-level microcellular structure, porous load
The multi-element metal catalytic active center of body supported rare earth metal oxide, transition metal oxide and noble metal formation is carried with porous
Body combination is more firm, and the ozone Heterogeneous oxidation solid catalyst of preparation has stronger adsorptivity, the collaboration of multi-element metal
Effect, stability and high activity that particularly doped precious metal has, can suppress liquating out for metal catalytic activity component, carry
The mithridatism and catalytic activity of high catalyst, with good environmental benefit and economic benefit.
Embodiment
Embodiment 1:1.35g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 1.65g, 140ml deionized waters, being added to volume is
500ml's can be uniformly mixed in closed reactor, and the weight concentration of the aqueous solution is 2.1%, lithium hypochlorite:Double (levulinics
Ketone) beryllium weight ratio=1:1.2；Add deionized water wash to it is neutral, 103 DEG C dry remove -200 mesh of sieving after moisture~+
The 2.75g diatoms of 400 mesh standard sieves are pure, 3.75g kyanites, 4.75g hydrotalcites, 5.75g alunites, 6.75g cubric niters,
The weight of 7.75g dolomites, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums（3g）:The weight of porous material（31.5g）=1:10.5,
36 DEG C are warming up to, reaming modified support 31g is obtained after continuing stirring reaction 3.2h, filtering, 103 DEG C of dry constant weights；It is super in 500ml
In sound wave reactor, reaming modified support 31g is put into, 3.25g Cationic surfucants is added and is dissolved in
The aqueous solution of 100ml deionized waters, the weight concentration of the aqueous solution is 3.1%, is uniformly mixed, chlorination dimethyl
Base hydroxyethyl ammonium（3.25g）:Reaming modified support（31g ）=1:9.5；It is 0.4W/m to control ultrasonic power density3, ultrasonic wave frequency
41 DEG C of rate 21kHz, temperature, sonic oscillation 2.2h；After the completion of ultrasonic activation, the ultrasonic surface in ultrasound reactor is activated and carried
Body mixed liquor is transferred in 500ml hydrothermal reaction kettles, is added by 2.1g boraxs, 3.05g potassium sulfates, (the hexafluoro acetyl of 1.6g tri-
Acetone) yttrium (III) dihydrate, the cyclopentadiene promethiums of 2.05g tri-, 2.6g tri- (the fluoro- 2,2- dimethyl of 6,6,7,7,8,8,8- seven-
3,5- octenes diketone) dysprosium (III), 3.05g tri- (trifluoromethanesulfonimide) ytterbium, 5.05g pyruvic acid isonicotinoyl hydrazones vanadium, 6.1g
Cobalt edetate, the nitroso rhodium trisodiums of 2.05g six, 3.1g chlordene osmiums dipotassium, the double dodecyl dimethyl ammoniums of 3.05g chlorinations and
The aqueous solution that 50ml deionized waters are prepared, the weight concentration of the aqueous solution is 40.3%, the weight of the aqueous solution:Ultrasonic surface is lived
Change weight=83.8g of carrier mixed liquor:134.25g=1:1.6,125 DEG C of temperature is controlled, the hydro-thermal reaction time is 8.3h, then
105 DEG C dry to obtain fine silt thing；Fine silt thing is in Muffle furnace, 620 DEG C, calcination 3.2h, after cooling down, can obtain fine powder
Granular ozone Heterogeneous oxidation solid catalyst.
Embodiment 2:0.24g lithium hypochlorites, double (acetylacetone,2,4-pentanedione) berylliums of 0.36g, 10ml deionized waters, being added to volume is
100ml's can be uniformly mixed in closed reactor, and the weight concentration of the aqueous solution is 5.7%, lithium hypochlorite:Double (levulinics
Ketone) beryllium weight ratio=1:1.5；Add deionized water wash to it is neutral, 103 DEG C dry remove -200 mesh of sieving after moisture~+
The 1.45g diatoms of 400 mesh standard sieves are pure, 1.65g kyanites, 1.85g hydrotalcites, 2.05g alunites, 2.25g cubric niters,
The weight of 2.45g dolomites, lithium hypochlorite and double (acetylacetone,2,4-pentanedione) berylliums（0.6g）:The weight of porous material（11.7g）=1:
19.5,48 DEG C are warming up to, reaming modified support 11.5g is obtained after continuing stirring reaction 5.8h, filtering, 105 DEG C of dry constant weights；
In 100ml ultrasound reactors, reaming modified support 11.5g is put into, 2.2g chlorination dodecyl dimethyl ethoxys are added
Ammonium is dissolved in the aqueous solution of 26ml deionized waters, and the weight concentration of the aqueous solution is 7.8%, is uniformly mixed, chlorination dodecyl
Dimethyl hydroxyethyl ammonium（2.2g）:Reaming modified support（11.5g ）=1:5.2；It is 0.7W/m to control ultrasonic power density3, it is super
54 DEG C of frequency of sound wave 29kHz, temperature, sonic oscillation 4.7h；After the completion of ultrasonic activation, the ultrasonic surface in ultrasound reactor
Activated carrier mixed liquor is transferred in 100ml hydrothermal reaction kettles, is added by 0.78g boraxs, 0.97g potassium sulfates, 0.58g tri-
(hexafluoroacetylacetone) yttrium (III) dihydrate, the cyclopentadiene promethiums of 0.67g tri-, (6,6,7,7,8,8,8- seven is fluoro- by 0.78g tri-
2,2- dimethyl -3,5- octenes diketone) dysprosium (III), 0.87g tri- (trifluoromethanesulfonimide) ytterbium, the different cigarette of 1.48g pyruvic acid
Acylhydrazone vanadium, 1.77g cobalt edetates, the nitroso rhodium trisodiums of 0.68g six, 0.87g chlordene osmiums dipotassium, the double dodecanes of 1.98g chlorinations
The aqueous solution that base Dimethyl Ammonium and 10ml deionized waters are prepared, the weight concentration of the aqueous solution is 53.3%, the weight of the aqueous solution
Amount:Weight=21.43g of ultrasonic surface activated carrier mixed liquor:39.7g=1:1.9, control 175 DEG C of temperature, the hydro-thermal reaction time
For 15.5h, then fine silt thing is dried to obtain for 105 DEG C；Fine silt thing is in Muffle furnace, 930 DEG C, calcination 7.5h, after cooling down,
It can obtain the ozone Heterogeneous oxidation solid catalyst of fine particle shape.
Claims (2)
1. a kind of preparation method of ozone Heterogeneous oxidation solid catalyst, it is characterized in that A groups can added in closed reactor
Divide and deionized water stirring prepares the aqueous solution, the weight concentration for controlling component A is 2%~6%, after the completion of prepared by solution, in stirring
Lower addition B component, is warming up to 35 DEG C~50 DEG C, continues stirring reaction 3h~6h, and filtering, reaction product is dry at 102 DEG C~106 DEG C
Reaming modified support is obtained after dry constant weight, reaming modified support input ultrasound reactor, addition is matched somebody with somebody by component C and deionized water
The aqueous solution of system, the weight concentration of component C is 3%~8%, is uniformly mixed, and it is 0.3~0.8W/ to control ultrasonic power density
m3, frequency 20kHz~30kHz, 40 DEG C~55 DEG C, sonic oscillation 2h~5h obtains ultrasonic surface activated carrier mixed liquor, transfer
Into hydrothermal reaction kettle, the aqueous solution that D components and deionized water are prepared is added, the weight concentration of D components is 40%~55%, is pressed
Weight meter, D component deionized water solutions:Weight ratio=1 of ultrasonic surface activated carrier mixed liquor:（1.5~2）, control temperature
120 DEG C~180 DEG C, the hydro-thermal reaction time is 8h~16h, then dries to obtain fine silt thing, fine silt thing is in Muffle furnace, 600
DEG C~950 DEG C, calcination 3h~8h obtains ozone Heterogeneous oxidation solid catalyst；The component A by expanding agent lithium hypochlorite,
Double (acetylacetone,2,4-pentanedione) beryllium compositions, by weight, lithium hypochlorite:Weight ratio=1 of double (acetylacetone,2,4-pentanedione) berylliums:（1~1.6）, B groups
Point by diatom is pure, kyanite, hydrotalcite, alunite, cubric niter and dolomite are constituted, by weight, diatom is pure:Kyanite:
Hydrotalcite:Alunite:Cubric niter:Dolomitic weight ratio=（5~15）:（7~17）:（9~19）:（11~21）:
（13~23）:（15~25）, by weight, component A:Weight ratio=1 of B component:（10~20）, component C is chlorination dodecane
Base dimethyl hydroxyethyl ammonium, by weight, component C:Weight ratio=1 of reaming modified support:（5~10）, D components are by being combined
Mineralizer borax, potassium sulfate, catalytic activity auxiliary agent predecessor three (hexafluoroacetylacetone) yttrium (III) dihydrate, three rings penta 2
Alkene promethium, three (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosiums (III), three (fluoroform sulphonyl Asias
Amine) ytterbium Rare-earth chemicals, the different nicotinoyl of catalytic active center predecessor normal transition metallo-organic compound pyruvic acid
Hydrazone vanadium, cobalt edetate and the nitroso rhodium trisodium of precious metal chemical complex six, chlordene osmium dipotassium, the double dodecyls two of emulsifying agent chlorination
Ammonium methyl is constituted, by weight, borax:Potassium sulfate:Three (hexafluoroacetylacetone) yttrium (III) dihydrates:Three cyclopentadiene
Promethium:Three (the fluoro- 2,2- dimethyl -3,5- octenes diketone of 6,6,7,7,8,8,8- seven) dysprosiums (III):Three (fluoroform sulphonyl Asias
Amine) ytterbium:Pyruvic acid isonicotinoyl hydrazone vanadium:Cobalt edetate:Six nitroso rhodium trisodiums:Chlordene osmium dipotassium:The double dodecanes of chlorination
The weight ratio of base Dimethyl Ammonium=（4~8）:（6~10）:（3~6）:（4~7）:（5~8）:（6~9）:（10~15）:（12
~18）:（4~7）:（6~9）:（6~20）.
2. according to claim 1 B component by diatom is pure, kyanite, hydrotalcite, alunite, cubric niter and dolomite group
Into diatom is pure, kyanite, hydrotalcite, alunite, cubric niter and dolomite are crushed respectively, and deionized water washing drying is removed
Go after moisture, sieved through standard screen, it is 0.0370mm~0.0750mm to control particle diameter.