CN107034572A - A kind of composite enhanced terylene bag fabric and preparation method thereof - Google Patents
A kind of composite enhanced terylene bag fabric and preparation method thereof Download PDFInfo
- Publication number
- CN107034572A CN107034572A CN201710196952.9A CN201710196952A CN107034572A CN 107034572 A CN107034572 A CN 107034572A CN 201710196952 A CN201710196952 A CN 201710196952A CN 107034572 A CN107034572 A CN 107034572A
- Authority
- CN
- China
- Prior art keywords
- terylene
- composite
- parts
- bag fabric
- enhanced
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of composite enhanced terylene bag fabric and preparation method thereof, blending production terylene is carried out by using PET and PBT, on the one hand it make use of the resistance to elevated temperatures of PET material, anti-wear performance and good creep-resistant property, on the other hand it make use of PBT ageing-resistant performance and fire resistance, the composite terylene for producing blending not only has good intensity and durability, and the toughness that toughener improve composite terylene finished product is also added into the feed, make the spun polyester thread produced that there is good toughness and intensity after fabric is woven into, and antiseptic is also added into composite terylene production process to improve the fungicidal properties and anti-microbial property of the follow-up fabric that interweaves, avoid going mouldy and the problem of bacteria breed, also the ageing-resistant performance of fabric is further improved by adding antioxidant, the combination property of terylene bag fabric is set to be greatly enhanced.
Description
Technical field
The present invention relates to bag fabric field, especially a kind of composite enhanced terylene bag fabric and preparation method thereof.
Background technology
The article that case and bag are commonly used as people's go off daily, its saturation is big, be easy to store and enjoy consumers in general's
Pro-gaze, requirement more and more higher however as people to quality of the life and is become increasingly complex using the environment of case and bag, for case and bag
Wearability and Water-proof and oil-proof, the requirement also more and more higher of stain resistant, because existing box material species is various, and terylene
Material is made due to one of fabric as existing main flow case and bag with good wearability and intensity using polyester fabric
Case and bag not only appearance looks elegant, and intensity height can bear heavier article and be unlikely to deform tear, but case and bag are due to tying
Require that it has good waterproof and oilproof performance and tensile strength in structure design, during especially as knapsack, often user exists
Can be shaken in walking process and so that knapsack usually has stress concentration and situation about pullling, after long-term use, if the back of the body
The strength character of bag can not be kept, then will occur the situation of fabric tear.
The content of the invention
It is an object of the invention to provide the composite enhanced terylene case and bag face that a kind of bulk strength is high, tensile resistance is strong
Material and preparation method thereof.
In order to realize above-mentioned technical purpose, the technical scheme is that:
A kind of composite enhanced terylene bag fabric, its by 65%~70% percentage by weight warp thread and 30%~35% weight percent
The weft yarns of ratio are formed, and described warp thread and weft yarn is composite terylene, and the raw material composition of the composite terylene includes:
PET cuts into slices 60~75 parts;
PBT cuts into slices 20~25 parts;
0.5~1 part of sodium methoxide;
1~3 part of lubricant;
2~3 parts of toughener;
2~5 parts of fire retardant;
1~3 part of antiseptic;
1~1.5 part of antioxidant;
0.5~1.5 part of IPBC.
Further, the trade mark of the toughener is Du Pont AC1125, A Kema AX8900 or clock source M-521.
Further, described fire retardant is pentaerythritol stearate.
Further, described lubricant is diethylene glycol.
Further, described antiseptic is zeolite antibacterial agent, salt of phosphoric acid antiseptic or nano silver antimicrobials.
Further, the antioxidant is N, N'- is double-(3- (3,5- di-tert-butyl-hydroxy phenyl) propiono) oneself two
Amine.
It is preferred that, a kind of composite enhanced terylene bag fabric, its by 65% percentage by weight warp thread and 35% weight hundred
The weft yarns of ratio are divided to form, described warp thread and weft yarn is composite terylene, the raw material composition of the composite terylene includes:
PET cuts into slices 70 parts;
PBT cuts into slices 23 parts;
0.8 part of sodium methoxide;
2 parts of lubricant;
2.5 parts of toughener;
3 parts of fire retardant;
2 parts of antiseptic;
1.3 parts of antioxidant;
1 part of IPBC.
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)PET sections and PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with stirring for 200~400 rmp
Mix speed and be stirred 2~3h of mixing;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, sodium methoxide, lubrication are then sequentially added again
Agent, toughener, fire retardant, antiseptic, antioxidant and IPBC, and under constant temperature, with
200~400rmp mixing speed is stirred 1~1.5h of mixing;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 65%~75% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight, weft yarn percentage by weight 30%~
35% ratio carries out longitude and latitude and is woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
Further, the trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-7500, AG-710 or AG-7600.
Further, described water-refusing oil-refusing finishing agent is applied on terylene bag fabric by 10~30g/L applied amount.
Using above-mentioned technical scheme, beneficial effects of the present invention are:Blending production is carried out by using PET and PBT to wash
Synthetic fibre, on the one hand make use of resistance to elevated temperatures, anti-wear performance and the good creep-resistant property of PET material, on the other hand make use of
PBT ageing-resistant performance and fire resistance, the composite terylene for producing blending not only has good intensity and durability, and
And the toughness that toughener improve composite terylene finished product is also added into the feed, it is being woven into the spun polyester thread produced
There is good toughness and intensity after fabric, and be also added into antiseptic to improve follow-up friendship in composite terylene production process
The fungicidal properties and anti-microbial property of the fabric woven, it is to avoid go mouldy and the problem of bacteria breed, it is also anti-oxidant by adding
Agent further improves the ageing-resistant performance of fabric, the combination property of terylene bag fabric is greatly enhanced.
Embodiment
A kind of composite enhanced terylene bag fabric, its by 65%~70% percentage by weight warp thread and 30%~35% weight
The weft yarns of percentage are formed, and described warp thread and weft yarn is composite terylene, and the raw material composition of the composite terylene includes:
PET cuts into slices 60~75 parts;
PBT cuts into slices 20~25 parts;
0.5~1 part of sodium methoxide;
1~3 part of lubricant;
2~3 parts of toughener;
2~5 parts of fire retardant;
1~3 part of antiseptic;
1~1.5 part of antioxidant;
0.5~1.5 part of IPBC.
Further, the trade mark of the toughener is Du Pont AC1125, A Kema AX8900 or clock source M-521.
Further, described fire retardant is pentaerythritol stearate.
Further, described lubricant is diethylene glycol.
Further, described antiseptic is zeolite antibacterial agent, salt of phosphoric acid antiseptic or nano silver antimicrobials.
Further, the antioxidant is N, N'- is double-(3- (3,5- di-tert-butyl-hydroxy phenyl) propiono) oneself two
Amine.
It is preferred that, a kind of composite enhanced terylene bag fabric, its by 65% percentage by weight warp thread and 35% weight hundred
The weft yarns of ratio are divided to form, described warp thread and weft yarn is composite terylene, the raw material composition of the composite terylene includes:
PET cuts into slices 70 parts;
PBT cuts into slices 23 parts;
0.8 part of sodium methoxide;
2 parts of lubricant;
2.5 parts of toughener;
3 parts of fire retardant;
2 parts of antiseptic;
1.3 parts of antioxidant;
1 part of IPBC.
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)PET sections and PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with stirring for 200~400 rmp
Mix speed and be stirred 2~3h of mixing;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, sodium methoxide, lubrication are then sequentially added again
Agent, toughener, fire retardant, antiseptic, antioxidant and IPBC, and under constant temperature, with
200~400rmp mixing speed is stirred 1~1.5h of mixing;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 65%~75% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight, weft yarn percentage by weight 30%~
35% ratio carries out longitude and latitude and is woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
Further, the trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-7500, AG-710 or AG-7600.
Further, described water-refusing oil-refusing finishing agent is applied on terylene bag fabric by 10~30g/L applied amount.
Embodiment 1
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)60 parts of PET sections and 20 parts of PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with 200 rmp
Mixing speed be stirred mixing 3h;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, then sequentially add again 0.5 part of sodium methoxide,
1 part of diethylene glycol, 2 parts of Du Pont AC1125,2 parts of pentaerythritol stearates, 1 part of zeolite antibacterial agent, 1 part of N, N'- pairs-(3- (3,
5- di-tert-butyl-hydroxy phenyls) propiono) hexamethylene diamine and 0.5 part of IPBC, and in constant temperature bar
Under part, mixing 1.5h is stirred with 200rmp mixing speed;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 65%, the ratio of weft yarn percentage by weight 35% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight
Carry out longitude and latitude and be woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
The trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-710, and applied amount is 15g/L.
Embodiment 2
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)65 parts of PET sections and 22 parts of PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with 300 rmp
Mixing speed be stirred mixing 2.5h;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, then sequentially add again 0.7 part of sodium methoxide,
1.5 parts of diethylene glycols, 2.3 parts of A Kema AX8900,3 parts of pentaerythritol stearates, 2 parts of salt of phosphoric acid antiseptics, 1.2 parts of N,
N'- pairs-(3- (3,5- di-tert-butyl-hydroxy phenyls) propiono) hexamethylene diamine and 0.9 part of iodo propinyl butylamino formic acid
Ester, and under constant temperature, mixing 1h is stirred with 400rmp mixing speed;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 67%, the ratio of weft yarn percentage by weight 33% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight
Carry out longitude and latitude and be woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
The trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-7500, and applied amount is 10g/L.
Embodiment 3
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)70 parts of PET sections and 23 parts of PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with 400 rmp
Mixing speed be stirred mixing 2h;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, then sequentially add again 0.8 part of sodium methoxide,
2 parts of diethylene glycols, 2.5 parts of A Kema AX8900,3 parts of pentaerythritol stearates, 2 parts of salt of phosphoric acid antiseptics, 1.3 parts of N,
N'- pairs-(3- (3,5- di-tert-butyl-hydroxy phenyl) propiono) hexamethylene diamine and 1 part of IPBC,
And under constant temperature, mixing 1.3h is stirred with 300rmp mixing speed;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 65%, the ratio of weft yarn percentage by weight 35% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight
Carry out longitude and latitude and be woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
The trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-7500, and applied amount is 20g/L.
Embodiment 4
A kind of preparation method of composite enhanced terylene bag fabric, it comprises the following steps:
(1)75 parts of PET sections and 25 parts of PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with 300 rmp
Mixing speed be stirred mixing 2.5h;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, 1 part of sodium methoxide, 3 are then sequentially added again
Part diethylene glycol, 3 parts of clock deep pool M-521,5 parts of pentaerythritol stearates, 3 parts of nano silver antimicrobials, 1.5 parts of N, N'- couples-(3-
(3,5- di-tert-butyl-hydroxy phenyl) propiono) hexamethylene diamine and 1.5 parts of IPBCs, and in perseverance
Under the conditions of temperature, mixing 1h is stirred with 400rmp mixing speed;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 70%, the ratio of weft yarn percentage by weight 30% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight
Carry out longitude and latitude and be woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
The trade mark of described water-refusing oil-refusing finishing agent is Asahi Glass AG-7600, and applied amount is 30g/L.
Described above is embodiments of the invention, for the ordinary skill in the art, according to the religion of the present invention
Lead, without departing from the principles and spirit of the present invention all equivalent changes done according to scope of the present invention patent, repair
Change, replace and modification, should all belong to the covering scope of the present invention.
Claims (10)
1. a kind of composite enhanced terylene bag fabric, it is characterised in that:It is by the warp thread of 65%~70% percentage by weight and 30%
The weft yarns of~35% percentage by weight are formed, and described warp thread and weft yarn is composite terylene, the raw material of the composite terylene
Composition includes:
PET cuts into slices 60~75 parts;
PBT cuts into slices 20~25 parts;
0.5~1 part of sodium methoxide;
1~3 part of lubricant;
2~3 parts of toughener;
2~5 parts of fire retardant;
1~3 part of antiseptic;
1~1.5 part of antioxidant;
0.5~1.5 part of IPBC.
2. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:The board of the toughener
Number be Du Pont AC1125, A Kema AX8900 or clock source M-521.
3. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:Described fire retardant is
Pentaerythritol stearate.
4. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:Described lubricant is
Diethylene glycol.
5. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:Described antiseptic is
Zeolite antibacterial agent, salt of phosphoric acid antiseptic or nano silver antimicrobials.
6. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:The antioxidant is
N, N'- pairs-(3- (3,5- di-tert-butyl-hydroxy phenyls) propiono) hexamethylene diamine.
7. a kind of composite enhanced terylene bag fabric according to claim 1, it is characterised in that:It is by 65% weight hundred
The warp thread of ratio and the weft yarns of 35% percentage by weight are divided to form, described warp thread and weft yarn is composite terylene, it is described compound
The raw material composition of terylene includes:
PET cuts into slices 70 parts;
PBT cuts into slices 23 parts;
0.8 part of sodium methoxide;
2 parts of lubricant;
2.5 parts of toughener;
3 parts of fire retardant;
2 parts of antiseptic;
1.3 parts of antioxidant;
1 part of IPBC.
8. a kind of preparation method of composite enhanced terylene bag fabric according to any of the above-described claim, its feature exists
In:It comprises the following steps:
(1)PET sections and PBT sections are added in batch mixer, at a temperature of 120~130 DEG C, with stirring for 200~400 rmp
Mix speed and be stirred 2~3h of mixing;
(2)After the completion of above-mentioned stirring, temperature of charge is naturally cooled to 70~80 DEG C, sodium methoxide, lubrication are then sequentially added again
Agent, toughener, fire retardant, antiseptic, antioxidant and IPBC, and under constant temperature, with
200~400rmp mixing speed is stirred 1~1.5h of mixing;
(3)By step(2)Stir mixed material and be added in spinning-drawing machine and carry out spinning, you can obtain composite terylene;
(4)It is 65%~75% that composite terylene made from above-mentioned spinning is pressed into warp thread percentage by weight, weft yarn percentage by weight 30%~
35% ratio carries out longitude and latitude and is woven into polyester fabric;
(5)The outer surface of polyester fabric obtained above is carried out to pad water-refusing oil-refusing finishing agent and drying, you can be made compound
Enhanced terylene bag fabric.
9. a kind of preparation method of composite enhanced terylene bag fabric according to claim 8, it is characterised in that:It is described
Water-refusing oil-refusing finishing agent the trade mark be Asahi Glass AG-7500, AG-710 or AG-7600.
10. a kind of preparation method of composite enhanced terylene bag fabric according to claim 8, it is characterised in that:Institute
The water-refusing oil-refusing finishing agent stated is applied on terylene bag fabric by 10~30g/L applied amount.