CN107022837A - A kind of preparation method of suede class man textile fabric - Google Patents
A kind of preparation method of suede class man textile fabric Download PDFInfo
- Publication number
- CN107022837A CN107022837A CN201610066126.8A CN201610066126A CN107022837A CN 107022837 A CN107022837 A CN 107022837A CN 201610066126 A CN201610066126 A CN 201610066126A CN 107022837 A CN107022837 A CN 107022837A
- Authority
- CN
- China
- Prior art keywords
- fabric
- preparation
- temperature
- textile fabric
- speed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation method of suede class man textile fabric, its preparation method comprises the following steps：(1) weave, (2) pre-treatment, (3) pre-setting, (4) fluffing, (5) hot light, (6) stamp, (7) drying, (8) cut boiling hot, (9) sizing, last finished product fabric.The fabric that the present invention is prepared is soft fluffy, and comfortable warming, outward appearance flower pattern solid is beautiful.
Description
Technical field
The present invention relates to the preparation method of a kind of textile fabric, more particularly to a kind of preparation of suede class man textile fabric
Method.
Background technology
With the improvement of people ' s living standards with the improvement of quality, people are to comfortable warming-type man textile fabric
The market demand constantly expands；Suede class man textile fabric always gives people a kind of extremely warm sensation, is well suited for winter and makes
With.In recent years, suede class man's textile fabric is with relatively low price, and higher quality, warm sense of touch is deep to be disappeared
Expense person's likes, achieves good achievement of sale；But because polyester fiber water imbibition is poor, intensity is high, resistance to
The characteristic of mill also causes its printing technology to have colouring difficult, the shortcomings of stamp color fastness is weak.One piece of good quality,
The suede class man textile fabric that class is high, outward appearance is beautiful will by consumers in general pro-gaze！
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of preparation method of suede class man textile fabric.
To reach above-mentioned purpose, technical scheme is as follows：
A kind of preparation method of suede class man textile fabric, the preparation method comprises the following steps：
(1) weave
From 75dtex/144f low elastic polyester filaments, bottom silk and middle silk select 50dtex/24f low elastic polyester filaments,
Prepare fabric；
(2) pre-treatment
Once wash, the pack of above-mentioned fabric is rubbed and once washed into rinsing machine；The specific step once washed
Rapid bleeding agent and 2g/L to add 1g/L in rinsing machine contaminates refining agent, and temperature is 40 DEG C, and bath raio is
1:16, the immersion laggard water-fillings of 20min are washed, and washing time is 35min；
Secondary washing；Concretely comprising the following steps for secondary washing adds 3g/L hydrogen peroxide after once washing,
Carry out secondary water after immersion treatment 25min to wash, temperature is 35 DEG C, bath raio 1:16, washing time is 35min；
(3) pre-setting
Presetting technology：Temperature 2O0~300 DEG C, speed 20m/min, air quantity 1800L/min, door width
255~260cm, pick-up 70%, finishing agent mass fraction is 2%, overfeeding 10%~15%；
(4) fluff
Using steel-wire napper, several raising machines continuously work；
(5) hot light
120~150 DEG C of temperature, speed 30m/min scalds roller rotating speed 1200r/min；
(6) stamp
Fabric after pre-treatment is subjected to printing technology processing, wherein thickening agent using the method for spray printing
Preparation prepared by weight according to formula as below：Oxidation dye 15%-50%, silicon mosanom 10%-25%,
Ultra-violet absorber 0.5%-5%, synthetic thickening agent 0.5%-2%, sodium chloride 1%-5%, the water of surplus；It is all
After raw material is ready in the desired amount, heats water to after 35-45min and add remaining raw material, mix
55-65 DEG C is warming up to after 15min, PH to 6-7 is adjusted；
(7) dry
150~180 DEG C of temperature, 18~22m/min of speed, air quantity 1800L/min, 260~270cm of door,
Pick-up 60%, overfeeding 15%~30%；
(8) scald and cut
The fabric after cutting will be scalded in 150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door,
0~15% time progress heat treatment of overfeeding, last finished product fabric；
(9) shape
150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door, overfeeding 0~15%.
By above-mentioned technical proposal, the beneficial effects of the invention are as follows：
The tricot knitting undercoat velvet fabric that the present invention is used, the fabric produced with tricot knitting undercoat down as raw material has
The characteristics such as feel is fine and smooth, softness, drapability is good, wearability is strong, gloss is soft.Along with introduction South Korea
Three-dimensional carving technology, the fabric made is soft fluffy, and comfortable warming, outward appearance flower pattern solid is beautiful, has
Not in the common suede class fabric on open market, class is higher, and more preferably, outward appearance is unique for quality.
Embodiment
In order that the technical means, the inventive features, the objects and the advantages of the present invention are easy to understand,
The present invention is further elucidated below.
The invention discloses a kind of preparation method of suede class man textile fabric, the preparation method comprises the following steps：
(1) weave
From 75dtex/144f low elastic polyester filaments, bottom silk and middle silk select 50dtex/24f low elastic polyester filaments,
Prepare fabric；
(2) pre-treatment
Once wash, the pack of above-mentioned fabric is rubbed and once washed into rinsing machine；The specific step once washed
Rapid bleeding agent and 2g/L to add 1g/L in rinsing machine contaminates refining agent, and temperature is 40 DEG C, and bath raio is
1:16, the immersion laggard water-fillings of 20min are washed, and washing time is 35min；Bleeding agent is nonionic penetrant,
Finishing agent is softening agent；Purpose is to improve the pliability of fabric, frictional force during fluffing is reduced, to obtain
Plentiful hairy effect；
Secondary washing；Concretely comprising the following steps for secondary washing adds 3g/L hydrogen peroxide after once washing,
Carry out secondary water after immersion treatment 25min to wash, temperature is 35 DEG C, bath raio 1:16, washing time is 35min；
Because the warping before the textile fabric braiding of suede class man will add warping oil, to be added in raw material spinning process
Spinning oil, thus pre-treatment purpose seek to remove fiber surface spinning oil, while fiber table can be removed
The oligomer in face, is conducive to even dyeing and the finished textile product coloured light after dyeing can be made soft.
(3) pre-setting
Presetting technology：Temperature 2O0~300 DEG C, speed 20m/min, air quantity 1800L/min, door width
255~260cm, pick-up 70%, finishing agent mass fraction is 2%, overfeeding 10%~15%；
(4) fluff
Using steel-wire napper, several raising machines continuously work；
(5) hot light
120~150 DEG C of temperature, speed 30m/min scalds roller rotating speed 1200r/min；Hot light technique is mainly
Remove the broken wool that plucking is produced；Scald roller and play beating to fabric, unnecessary tomentum, which is patted, to be left after fabric
Enter dust bag with suction channel, hot light temperature is 120 DEG C；For high below the 3mm of hair fabric, hot light temperature
Spend for 120 DEG C；For high more than the 3mm of hair fabric, hot light temperature is 150 DEG C；
(6) stamp
Fabric after pre-treatment is subjected to printing technology processing, wherein thickening agent using the method for spray printing
Preparation prepared by weight according to formula as below：Oxidation dye 15%-50%, silicon mosanom 10%-25%,
Ultra-violet absorber 0.5%-5%, synthetic thickening agent 0.5%-2%, sodium chloride 1%-5%, the water of surplus；It is all
After raw material is ready in the desired amount, heats water to after 35-45min and add remaining raw material, mix
55-65 DEG C is warming up to after 15min, PH to 6-7 is adjusted；Programming rate is 1-2 DEG C/min；
(7) dry
150~180 DEG C of temperature, 18~22m/min of speed, air quantity 1800L/min, 260~270cm of door,
Pick-up 60%, overfeeding 15%~30%；Fabric will remain low-tension relaxed state after baking oven is entered,
When hot blast blows, fabric is fluctuated up and down in baking oven, is played and is patted soft effect；Knitted in drying course
Fine hair is distinguished on thing during machine to swing to, is entered downwards with the head end direction (along hair) of envers arrow and fine hair
Machine；
(8) scald and cut
The fabric after cutting will be scalded in 150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door,
0~15% time progress heat treatment of overfeeding, last finished product fabric；
(9) shape
150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door, overfeeding 0~15%.
Fabric fine hair downwards, enters to open windward in machine, baking oven along hair, closes leeward；Fabric must be tightened before entering baking oven,
When so fabric is entered after baking oven by upper wind, fine hair will not just encounter leeboard, prevent fine hair from encountering
Leeboard and be ruined.
The fabric washing size changing rate that the present invention is prepared is warp-wise >=-5%, broadwise >=-5%；Fluff
Ball performance：>=3 grades；Strongly >=220cN, product bleaching >=75；Washable (discoloration, staining) >=3 grades；
Perspiration resistance (discoloration, staining) >=3 grades, rub resistance >=3 grade, content of formaldehyde ＜ 75mg/kg.
The general principle and principal character and advantages of the present invention of the present invention has been shown and described above.The industry
Technical staff it should be appreciated that the present invention is not limited to the above embodiments, in above-described embodiment and specification
Merely illustrating the principles of the invention for description, it is without departing from the spirit and scope of the present invention, of the invention
Various changes and modifications are also had, these changes and improvements all fall within the protetion scope of the claimed invention.This
The claimed scope of invention is by appended claims and its equivalent thereof.
Claims (6)
1. the preparation method of a kind of suede class man textile fabric, it is characterised in that the preparation method includes as follows
Step：
(1) weave
From 75dtex/144f low elastic polyester filaments, bottom silk and middle silk select 50dtex/24f low elastic polyester filaments,
Prepare fabric；
(2) pre-treatment
Once wash, the pack of above-mentioned fabric is rubbed and once washed into rinsing machine；The specific step once washed
Rapid bleeding agent and 2g/L to add 1g/L in rinsing machine contaminates refining agent, and temperature is 40 DEG C, and bath raio is
1:16, the immersion laggard water-fillings of 20min are washed, and washing time is 35min；
Secondary washing；Concretely comprising the following steps for secondary washing adds 3g/L hydrogen peroxide after once washing,
Carry out secondary water after immersion treatment 25min to wash, temperature is 35 DEG C, bath raio 1:16, washing time is 35min；
(3) pre-setting
Presetting technology：Temperature 2O0~300 DEG C, speed 20m/min, air quantity 1800L/min, door width
255~260cm, pick-up 70%, finishing agent mass fraction is 2%, overfeeding 10%~15%；
(4) fluff
Using steel-wire napper, several raising machines continuously work；
(5) hot light
120~150 DEG C of temperature, speed 30m/min scalds roller rotating speed 1200r/min；
(6) stamp
Fabric after pre-treatment is subjected to printing technology processing, wherein thickening agent using the method for spray printing
Preparation prepared by weight according to formula as below：Oxidation dye 15%-50%, silicon mosanom 10%-25%,
Ultra-violet absorber 0.5%-5%, synthetic thickening agent 0.5%-2%, sodium chloride 1%-5%, the water of surplus；It is all
After raw material is ready in the desired amount, heats water to after 35-45min and add remaining raw material, mix
55-65 DEG C is warming up to after 15min, PH to 6-7 is adjusted；
(7) dry
150~180 DEG C of temperature, 18~22m/min of speed, air quantity 1800L/min, 260~270cm of door,
Pick-up 60%, overfeeding 15%~30%；
(8) scald and cut
The fabric after cutting will be scalded in 150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door,
0~15% time progress heat treatment of overfeeding, last finished product fabric；
(9) shape
150~180 DEG C of temperature, 25~30m/min of speed, 260~270cm of door, overfeeding 0~15%.
2. a kind of preparation method of suede class man textile fabric according to claim 1, it is characterised in that：It is described
Bleeding agent in step (2) is nonionic penetrant.
3. a kind of preparation method of suede class man textile fabric according to claim 1, it is characterised in that：
The finishing agent used in the step (3) is softening agent.
4. a kind of preparation method of suede class man textile fabric according to claim 1, it is characterised in that：
For high below the 3mm of hair fabric in the step (5), hot light temperature is 120 DEG C；For the high 3mm of hair
Fabric above, hot light temperature is 150 DEG C.
5. a kind of preparation method of suede class man textile fabric according to claim 1, it is characterised in that：
Programming rate in the step (6) is 1-2 DEG C/min.
6. a kind of preparation method of suede class man textile fabric according to claim 1, it is characterised in that：
Fabric will remain low-tension relaxed state after baking oven is entered in the step (7), hot blast blow when
Wait, fabric is fluctuated up and down in baking oven, play and pat soft effect；Will during machine on fabric in drying course
Distinguish fine hair to swing to, with the head end direction of envers arrow (along hair) and fine hair enters downwards machine.