CN106957516A - 一种不饱和聚酯树脂挂饰工艺品制作方法 - Google Patents

一种不饱和聚酯树脂挂饰工艺品制作方法 Download PDF

Info

Publication number
CN106957516A
CN106957516A CN201610010961.XA CN201610010961A CN106957516A CN 106957516 A CN106957516 A CN 106957516A CN 201610010961 A CN201610010961 A CN 201610010961A CN 106957516 A CN106957516 A CN 106957516A
Authority
CN
China
Prior art keywords
resin
unsaturated polyester
polyester resin
mould
ornament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610010961.XA
Other languages
English (en)
Inventor
王春红
陈祯
刘胜凯
李锡伯
张桂燕
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TIANJIN TEDA JINSHAN PACKING MANUFACTURE CO Ltd
Original Assignee
TIANJIN TEDA JINSHAN PACKING MANUFACTURE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TIANJIN TEDA JINSHAN PACKING MANUFACTURE CO Ltd filed Critical TIANJIN TEDA JINSHAN PACKING MANUFACTURE CO Ltd
Priority to CN201610010961.XA priority Critical patent/CN106957516A/zh
Publication of CN106957516A publication Critical patent/CN106957516A/zh
Pending legal-status Critical Current

Abstract

本发明公布了一种不饱和聚酯树脂挂饰工艺品制作方法，本发明通过下述技术方案来实现：（1）取一定质量的不饱和聚酯树脂，按照上述比例加入促进剂和固化剂，搅拌均匀，放入真空烘箱中抽真空5~10min去除搅拌产生的气泡；（2）将挂链一端放入模具中，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；（3）向模具中倒入抽完真空的树脂，在0℃~80℃烘箱中树脂固化成型，将模具打开取出粗品打磨光滑制得成品，本发明可以用于制作手链、脚链、项链等挂饰工艺品，省时省力，降低了制作成本。

Description

一种不饱和聚酯树脂挂饰工艺品制作方法
技术领域
本发明涉及树脂工艺品制作领域，具体为一种不饱和聚酯树脂挂饰工艺品制作方法。
背景技术
近年来，随着国家经济的迅速发展，人们的生活水平的快速提高，树脂工艺品越来越受使用者的青睐。目前市场上的树脂工艺品挂饰，挂链和树脂饰品基本都是分离开的，佩戴过程中容易脱落，而且制作费时费力，无意中提高了成本；本发明提供一种不饱和聚酯树脂挂饰工艺品制作方法，可以用于制作手链、脚链、项链等挂饰工艺品，省时省力，降低了制作成本。
发明内容
本发明提供一种不饱和聚酯树脂挂饰工艺品制作方法，旨在降低树脂挂饰工艺品的制作成本和制作时间，本发明通过下述技术方案来实现：
一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，本工艺品树脂部分由以下原料组成：一定量的不饱和聚酯树脂，以及占树脂质量0~4%的促进剂和树脂质量1~3%的固化剂。
一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，制作挂饰的挂链可以是金属挂链、织物编织挂链或者塑料挂链。
一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；
所述的不饱和聚酯树脂的型号可以是196S；
所述的促进剂可以是对苯二胺，固化剂可以是过氧化苯甲酰；
本发明不饱和聚酯树脂挂饰工艺品的制作方法：（1）取一定质量的不饱和聚酯树脂，按照上述比例加入促进剂和固化剂，搅拌均匀，放入真空烘箱中抽真空5~10min去除搅拌产生的气泡；（2）将挂链一端放入模具中，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；（3）向模具中倒入抽完真空的树脂，在0℃~80℃烘箱中树脂固化成型，将模具打开取出粗品打磨光滑制得成品。
具体实施方式：
实施例1
取100g不饱和聚酯树脂，加入树脂质量2%的固化剂和2%的促进剂，搅拌均匀，放入真空烘箱中抽真空10min去除搅拌产生的气泡；将织物编制挂链对折，闭口一端放入准备好的模具中然后将抽完真空的树脂倒入模具中，在真空烘箱中常温下树脂固化成型将模具打开取出粗品打磨光滑制得成品。
实施例2
取100g不饱和聚酯树脂，加入树脂质量2%的固化剂和0%的促进剂，搅拌均匀，放入真空烘箱中抽真空10min去除搅拌产生的气泡；将塑料挂链一端放入准备好的模具中并放入干燥植物作为装饰用品，然后将抽完真空的树脂倒入模具中，在80℃烘箱中树脂固化成型将模具打开取出粗品打磨光滑制得成品。

Claims (2)

1.一种不饱和聚酯树脂挂饰工艺品制作方法，其特征在于，本工艺品树脂部分由以下原料组成：一定量的不饱和聚酯树脂，以及占树脂质量0~4%的促进剂和树脂质量1~3%的固化剂。
2.根据权利要求1所述的一种不饱和聚酯树脂挂饰工艺品制作方法如下所示，（1）取一定质量的不饱和聚酯树脂，按照一定比例加入促进剂和固化剂，搅拌均匀，放入真空烘箱中抽真空5~10min去除搅拌产生的气泡；（2）将挂链一端放入模具中，也可在模具中放入干燥后的植物、塑料制品等作为工艺品的装饰物；（3）向模具中倒入抽完真空的树脂，在0℃~80℃烘箱中树脂固化成型，将模具打开取出粗品打磨光滑制得成品。
CN201610010961.XA 2016-01-10 2016-01-10 一种不饱和聚酯树脂挂饰工艺品制作方法 Pending CN106957516A (zh)