CN106906426B - A kind of high tenacity high corrosion resistant type weather-resistant steel plate and its manufacturing method - Google Patents
A kind of high tenacity high corrosion resistant type weather-resistant steel plate and its manufacturing method Download PDFInfo
- Publication number
- CN106906426B CN106906426B CN201710169452.6A CN201710169452A CN106906426B CN 106906426 B CN106906426 B CN 106906426B CN 201710169452 A CN201710169452 A CN 201710169452A CN 106906426 B CN106906426 B CN 106906426B
- Authority
- CN
- China
- Prior art keywords
- steel plate
- temperature
- corrosion resistant
- type weather
- control
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to a kind of high tenacity high corrosion resistant type weather-resistant steel plate, chemical component weight percentage composition is C :≤0.03%;Si :≤0.10%;Mn:0.10~0.50%;P :≤0.015%;S :≤0.005%;Nb:0.030~0.050%;Ti:0.020~0.050%;Cr:4.0~6.0%;Ni:0.40~0.60%;Cu:0.40~0.60%;Al:0.020~0.060%;Surplus is Fe and is inevitably mingled with;It by molten iron pretreatment, converter smelting, refining, continuous casting, hot continuous rolling, section cooling, batches, can guarantee the steady production of steel plate.Steel plate yield strength produced is 480~550MPa, and tensile strength is 600~700MPa, elongation percentage 24-30%, and at a temperature of -80 DEG C, steel plate charpy V impact energy is greater than 100J.
Description
Technical field
The present invention relates to weathering steel manufacturing fields, and in particular to a kind of high tenacity high corrosion resistant type high-strength weather-proof steel plate and its
Manufacturing method.
Background technique
The elements such as phosphorus, copper, chromium, nickel are added in weather-proof Steel material, surface forms the fine and close and strong protective film of adhesion, hinders
Corrosion inward spread and develop, protect rusty scale under matrix, slow down its corrosion rate, apply container railway, rail truck,
On the steel construction that bridge, pylon, harbour building etc. are exposed to the atmosphere for a long time, there is good atmospheric corrosion resistance.With
The development such as the structural members such as container, rail truck, pylon ever-increasing long-life, heavy duty, special-shaped structure piece forming, welding
It is required that weathering steel material technology also develops to high anti-corrosion, high-strength, high tenacity, the easily directions such as welding.
The patent that high corrosion resistant type weathering steel and its manufacturing method are declared has multinomial.Such as: patent CN 102409253A is public
Opened a kind of high-corrosion-resisting, high strength rail truck weathering steel and its manufacturing method, chemical component be C:0.015~
0.065%;Si:0.1~0.50%;Mn:0.20~0.60%;P≤0.015;S≤0.008;Cu:0.20~0.60;Ni:
0.12~1.0;Cr:2.15~4.0;Nb:0.005~0.05%;Ti:0.01~0.08%;Al:0.01~0.05%;Surplus
For Fe and inevitably it is mingled with.It is heated using 1200-1260 DEG C of slab, 880-950 DEG C of finishing temperature, two sections is used after rolling
Section cooling mode and 560~660 DEG C of coiling temperature productions, yield strength >=550MPa, tensile strength >=650MPa, -40 DEG C
Charpy V impact energy=65-98J.Patent CN 10212717A disclose a kind of good-toughness the anti-corrosion weathering steel containing Cr of height and
Its manufacturing method, chemical component are C:0.01~0.06%;Si:0.1~0.4%;Mn:0.2~0.8%;P≤0.01;S≤
0.006;Cu:0.2~0.5;Ni:0.2~1.2;Cr:2.5~7.0;Ti:0.01~0.1%;Al:0.01~0.05%;N :≤
0.005%;Surplus is Fe and is inevitably mingled with.It is heated using 1200-1250 DEG C of slab, 800-900 DEG C of finishing temperature, volume
Take 550~650 DEG C of temperature, yield strength >=460MPa, anti-40 DEG C of charpy V impact energy >=60J.Patent CN 101376953A
Disclose a kind of high-corrosion resistant high-strength weather resisting steel and its manufacturing method, chemical component C:0.002~0.005%;Si:0.20~
0.40%;Mn:0.01~0.05%;P≤0.020;S≤0.008;Cu:0.20~0.40;Ni :≤0.40;Cr:4.50~
5.50;Ca:0.001~0.006%;N:0.001~0.006;Ti :≤0.03%;Al:0.01~0.05%;;Surplus be Fe and
Inevitably it is mingled with, is heated using >=1200 DEG C of slabs, using the cooling rate of 5-8 DEG C/S, 600~650 DEG C of coiling temperature,
Yield strength >=700MPa belongs to a kind of weathering steel of high intensity high corrosion resistance, but does not provide impact flexibility index.Patent CN
103074548A discloses a kind of high-corrosion-resisting, high strength weather-resistant steel plate containing Al and its manufacturing method, and chemical component C:0.02~
0.07%;Si:0.20~1.0%;Mn:0.2~2.2%;P≤0.01%;S≤0.006%;Cu:0.2~0.5%;Ni:
0.2-1.2%;Cr:0.5~3.5%;Al:0.4~4.0%;N :≤0.005;V:0.02-0.10%;And Al/Cr is 0.5-
8.0;Surplus is Fe and is inevitably mingled with, and is heated using >=1220 DEG C of slabs, 720-800 DEG C of finishing temperature, using 10-40
DEG C/cooling rate of S, charpy V impact energy under the conditions of 460~520 DEG C of coiling temperature, yield strength 350-500MPa, -40 DEG C
In 60J or more.
The above patent be not directed to -80 DEG C of temperature charpy V impact energies in 100J or more high tenacity high corrosion resistant type weathering steel and
Its manufacturing method.
Summary of the invention
For the above prior art problem, the purpose of the present invention is develop a kind of high tenacity high corrosion resistant type weathering steel steel plate.
This steel plate is produced by smelting chemical ingredient and technique appropriate, have high corrosion resisting property, good cold formability energy,
Good welding performance has good impact flexibility under the conditions of -80 DEG C of temperature.This steel plate is suitable for long-life rail truck
Structural member, cold forming special-shaped structure piece and extremely cold climatological region atmospheric corrosion resistance structural member manufacture etc..Specific technical solution is as follows:
A kind of high tenacity high corrosion resistant type weather-resistant steel plate, chemical component weight percentage composition are C :≤0.03%;Si :≤
0.10%;Mn:0.10~0.50%;P :≤0.015%;S :≤0.005%;Nb:0.030~0.050%;Ti:0.020~
0.050%;Cr:4.0~6.0%;Ni:0.40~0.60%;Cu:0.40~0.60%;Al:0.020~0.060%;Surplus
For Fe and inevitably it is mingled with;
Further, a kind of high tenacity high corrosion resistant type weather-resistant steel plate of the invention, metallographic structure are polygonal ferrite list
Phase fine grained texture, ferrite grain size are 12~13 grades;
High tenacity high corrosion resistant type weather-resistant steel plate manufacturing method of the present invention includes the following steps: molten iron pretreatment, converter smelting
Refining, continuous casting, hot continuous rolling, section cooling, is batched at refining, it is characterised in that:
1) molten iron pretreatment desulfurizing control [S]≤0.0050%;Refining using RH vacuum outgas and LF furnace carry out it is above-mentioned at
Sub-control system, N content≤60ppm in steel, H content≤2ppm;
2) for packet liquidus temperature at 10~30 DEG C, and using wick-containing slighter compress, control slab center C class is inclined in continuous casting control
Analysis is less than 1.5 grades;
3) by the molten steel smelted with the chemical component in step (1), it is casting continuously to form the slab with a thickness of 230mm or 250mm, with
Upper slab, which is reheated, can enter furnace using cold charge, can also enter furnace using hot charging;
4) slab heats 3~4 hours in heating furnace, controls slab tapping temperature at 1150~1200 DEG C, then in heat
Continuous mill train carries out roughing and finish rolling, and finish rolling start rolling temperature controls≤1030 DEG C, and finishing temperature control is at 800~860 DEG C;
5) steel plate controls coiler plate after cooling using continuous section cooling, control cooling velocity≤20 DEG C after finish rolling
Temperature is at 580~640 DEG C.
Further, high tenacity high corrosion resistant type weather-resistant steel plate manufacturing method of the present invention, the hot rolled coil of hot tandem production
It naturally cools to crosscutting at scale steel plate after uncoiling, aligning after room temperature.
Compared with prior art, the present invention high tenacity high corrosion resistant type weather-resistant steel plate of the present invention has the following advantages that and effect:
1) steel plate produced using chemical component of the invention, technique and specific method, yield strength 480-550MPa,
Tensile strength is 600-700MPa, elongation percentage=24-30%.
2) there is excellent low-temperature flexibility using steel plate produced by the invention, at a temperature of -80 DEG C, the impact of steel plate Charpy V-type
Function is greater than 100J (impact specimen size: 5 × 10 × 55mm).
3) there is excellent atmospheric corrosion resistance using steel plate produced by the invention.It is pair with ordinary carbon steel Q345B
Than sample, the period soaking corrosion for carrying out 72 hours with weathering steel alternate-immersion test method (TB/T2375-93) by railway is rotten
Erosion experiment, relatively corrosive rate≤28%.
4) there is good welding performance and cold formability energy using steel plate produced by the invention, is suitable for using welding
Or the modes such as rolling formation or bending and forming manufacture atmospheric corrosion resistance structural member.
Detailed description of the invention
Fig. 1 is product metallographic structure figure
Specific embodiment
Below according to attached drawing, the present invention will be described in detail, is that one of numerous embodiments of the present invention are preferred real
Apply example.
Use steel plate metallographic structure produced by the invention for the single-phase fine grained texture of shape changeable ferrite, ferrite grain size 12
~13 grades.Typical metallographic structure pattern is shown in Fig. 1.
Selecting chemical component steel shown in table 1 is raw material, and continuous casting steel billet is having a size of 230mm or 250mm.By slab by adding
Then hot stove heating is rolled through hot tandem, cooled down and is batched.Control heating temperature, finishing temperature, section cooling speed
Degree and coiling temperature.Embodiment chemical component is shown in Table 1, and embodiment rolling and cooling technique are shown in Table 2, and embodiment mechanical property is shown in Table
3, embodiment series of temperatures ballistic work is shown in Table 4, and embodiment atmospheric corrosion resistance test result is shown in Table 5.
1 embodiment of table surveys chemical component (mass percent, wt%, surplus Fe)
Number | C | Si | Mn | P | S | Al | Nb | Ti | Cr | Cu | Ni |
S1 | 0.010 | 0.10 | 0.45 | 0.012 | 0.004 | 0.025 | 0.040 | 0.020 | 4.8 | 0.44 | 0.43 |
S2 | 0.020 | 0.08 | 0.25 | 0.010 | 0.003 | 0.020 | 0.035 | 0.015 | 4.2 | 0.43 | 0.45 |
S3 | 0.015 | 0.05 | 0.38 | 0.008 | 0.002 | 0.030 | 0.042 | 0.035 | 5.2 | 0.42 | 0.43 |
The rolling of 2 embodiment of table and cooling technique parameter
3 embodiment mechanical property of table
4 embodiment impact property of table
5 embodiment atmospheric corrosion resistance test result of table
The present invention is exemplarily described above in conjunction with attached drawing, it is clear that the present invention implements not by aforesaid way
Limitation, as long as using the various improvement that the inventive concept and technical scheme of the present invention carry out, or not improved direct application
It is within the scope of the present invention in other occasions.
Claims (2)
1. a kind of high tenacity high corrosion resistant type weather-resistant steel plate, chemical component weight percentage composition is C :≤0.03%;Si :≤
0.10%;Mn:0.10~0.50%;P :≤0.015%;S :≤0.005%;Nb:0.030~0.050%;Ti:0.020~
0.050%;Cr:4.0~6.0%;Ni:0.40~0.60%;Cu:0.40~0.60%;Al:0.020~0.060%;Surplus
For Fe and inevitably it is mingled with, the high tenacity high corrosion resistant type weather-resistant steel plate, metallographic structure is that polygonal ferrite is single-phase thin
Crystalline substance tissue, ferrite grain size are 12~13 grades;At a temperature of -80 DEG C, steel plate charpy V impact energy is greater than 100J;
The high tenacity high corrosion resistant type weather-resistant steel plate manufacturing method, include the following steps: molten iron pretreatment, converter smelting, refining,
Continuous casting, section cooling, batches hot continuous rolling, it is characterised in that:
1) molten iron pretreatment desulfurizing control [S]≤0.0050%;Refining carries out mentioned component control using RH vacuum outgas and LF furnace
It makes, N content≤60ppm in steel, H content≤2ppm;
2) by the molten steel smelted with the chemical component in step (1), the slab with a thickness of 230mm or 250mm, the casting are casting continuously to form
Base, which is reheated, can enter furnace using cold charge, can also enter furnace using hot charging;Continuous casting control in packet liquidus temperature at 10~30 DEG C,
And wick-containing slighter compress is used, control slab center C class segregation is less than 1.5 grades;
3) slab heats 3~4 hours in heating furnace, controls slab tapping temperature at 1150~1200 DEG C, then in hot continuous rolling
Unit carries out roughing and finish rolling, and finish rolling start rolling temperature controls≤1030 DEG C, and finishing temperature control is at 800~860 DEG C;
4) steel plate controls coiler plate temperature after cooling using continuous section cooling, control cooling velocity≤20 DEG C after finish rolling
At 580~640 DEG C.
2. high tenacity high corrosion resistant type weather-resistant steel plate as described in claim 1, the hot rolled coil of the hot tandem production is certainly
It is so cooled to crosscutting at scale steel plate after uncoiling, aligning after room temperature.